A novel catalyst precursor, La2NiO4, was investigated to synthesize carbon nanotubes,obtained from catalytic disproportionation of CO. The morphology of carbon nanotubes has been examined by TEM (transmission electro...A novel catalyst precursor, La2NiO4, was investigated to synthesize carbon nanotubes,obtained from catalytic disproportionation of CO. The morphology of carbon nanotubes has been examined by TEM (transmission electron micrograph) and SEM (scaning electron micrograph). It was observed that the Ni nano-particle size formed at different reducing temperatures was a key factor to the yield and diameter of carbon nanotubes.展开更多
In this work,La_(2)NiO_(4+δ)-Ce_(0.55)La_(0.45)O_(2−δ)(denoted as LNO-xLDC)with various LDC contents(x=0,10,20,30,and 40 wt%)were prepared and evaluated as bifunctional oxygen electrodes for reversible solid oxide c...In this work,La_(2)NiO_(4+δ)-Ce_(0.55)La_(0.45)O_(2−δ)(denoted as LNO-xLDC)with various LDC contents(x=0,10,20,30,and 40 wt%)were prepared and evaluated as bifunctional oxygen electrodes for reversible solid oxide cells(RSOCs).Compared with the pure LNO,the optimum composition of LNO-30LDC exhibited the lowest polarization resistance(Rp)of 0.53 and 0.12Ω·cm^(2)in air at 650 and 750℃,respectively.The enhanced electrochemical performance of LNO-30LDC oxygen electrode was mainly attributed to the extended triple phase boundary and more oxygen ionic transfer channels.The hydrogen electrode supported single cell with LNO-30LDC oxygen electrode displayed peak power densities of 276,401,and 521 mW·cm^(−2)at 700,750,and 800℃,respectively.Moreover,the electrolysis current density of the single cell demonstrated 526.39 mA·cm^(−2) under 1.5 V at 800℃,and the corresponding hydrogen production rate was 220.03 mL·cm^(−2)·h^(−1).The encouraging results indicated that LNO-30LDC was a promising bifunctional oxygen electrode material for RSOCs.展开更多
Pr_(2)(Zr_(1−x)Ti_(x))_(3)(MoO_(4))_(9)(x=0.1-1.0)ceramics were prepared via a conventional solid-state method,the dependence of crystal structure and bond characteristics on microwave dielectric properties was invest...Pr_(2)(Zr_(1−x)Ti_(x))_(3)(MoO_(4))_(9)(x=0.1-1.0)ceramics were prepared via a conventional solid-state method,the dependence of crystal structure and bond characteristics on microwave dielectric properties was investigated systemically.The X-ray diffraction patterns indicated that the single-phase Pr_(2)Zr_(3)(MoO_(4))_(9)structure was formed in all the specimens.As the Ti^(4+)content increased,the lattice volume gradually decreased,which was ascribed to the fact that the ionic radius of Ti^(4+)was smaller than that of Zr^(4+).Notably,outstanding microwave dielectric properties withεr of 10.73-16.35,Q·f values of 80,696-18,726 GHz and minorτ_(f) values−14.1-−2.6 ppm/℃were achieved in Pr_(2)(Zr_(1−x)Ti_(x))_(3)(MoO_(4))_(9)ceramics.Theε_(r) increased with the rising x values,which was associated with the increase ofα/Vm values.The decreasing Q·f was affected by the decline of lattice energy of[Zr/TiO_(6)]octahedral.Theτf value was dominated by[Zr/TiO_(6)]octahedral distortion,Mo-O bond energy,bond strength and B-site bond valence.Furthermore,infrared reflection spectra suggested that the properties were mainly caused by the absorption of phonon,and the dielectric loss could be further reduced by optimizing the experimental process.展开更多
文摘A novel catalyst precursor, La2NiO4, was investigated to synthesize carbon nanotubes,obtained from catalytic disproportionation of CO. The morphology of carbon nanotubes has been examined by TEM (transmission electron micrograph) and SEM (scaning electron micrograph). It was observed that the Ni nano-particle size formed at different reducing temperatures was a key factor to the yield and diameter of carbon nanotubes.
基金Science and Technology Project of Jiangxi Provincial Education Department(GJJ190734)The National Natural Science Foundation of China(51962015)。
文摘In this work,La_(2)NiO_(4+δ)-Ce_(0.55)La_(0.45)O_(2−δ)(denoted as LNO-xLDC)with various LDC contents(x=0,10,20,30,and 40 wt%)were prepared and evaluated as bifunctional oxygen electrodes for reversible solid oxide cells(RSOCs).Compared with the pure LNO,the optimum composition of LNO-30LDC exhibited the lowest polarization resistance(Rp)of 0.53 and 0.12Ω·cm^(2)in air at 650 and 750℃,respectively.The enhanced electrochemical performance of LNO-30LDC oxygen electrode was mainly attributed to the extended triple phase boundary and more oxygen ionic transfer channels.The hydrogen electrode supported single cell with LNO-30LDC oxygen electrode displayed peak power densities of 276,401,and 521 mW·cm^(−2)at 700,750,and 800℃,respectively.Moreover,the electrolysis current density of the single cell demonstrated 526.39 mA·cm^(−2) under 1.5 V at 800℃,and the corresponding hydrogen production rate was 220.03 mL·cm^(−2)·h^(−1).The encouraging results indicated that LNO-30LDC was a promising bifunctional oxygen electrode material for RSOCs.
基金supported by the National Natural Science Foundation of China(No.51972143)supported by State Key Laboratory of New Ceramic and Fine Processing Tsinghua University(No.KFZD202101)。
文摘Pr_(2)(Zr_(1−x)Ti_(x))_(3)(MoO_(4))_(9)(x=0.1-1.0)ceramics were prepared via a conventional solid-state method,the dependence of crystal structure and bond characteristics on microwave dielectric properties was investigated systemically.The X-ray diffraction patterns indicated that the single-phase Pr_(2)Zr_(3)(MoO_(4))_(9)structure was formed in all the specimens.As the Ti^(4+)content increased,the lattice volume gradually decreased,which was ascribed to the fact that the ionic radius of Ti^(4+)was smaller than that of Zr^(4+).Notably,outstanding microwave dielectric properties withεr of 10.73-16.35,Q·f values of 80,696-18,726 GHz and minorτ_(f) values−14.1-−2.6 ppm/℃were achieved in Pr_(2)(Zr_(1−x)Ti_(x))_(3)(MoO_(4))_(9)ceramics.Theε_(r) increased with the rising x values,which was associated with the increase ofα/Vm values.The decreasing Q·f was affected by the decline of lattice energy of[Zr/TiO_(6)]octahedral.Theτf value was dominated by[Zr/TiO_(6)]octahedral distortion,Mo-O bond energy,bond strength and B-site bond valence.Furthermore,infrared reflection spectra suggested that the properties were mainly caused by the absorption of phonon,and the dielectric loss could be further reduced by optimizing the experimental process.