Surface metallization of glass fiber(GF)/polyetheretherketone(PEEK)[GF/PEEK] is conducted by coating copper using electroplating and magnetron sputtering and the properties are determined by X-ray diffraction(XRD), sc...Surface metallization of glass fiber(GF)/polyetheretherketone(PEEK)[GF/PEEK] is conducted by coating copper using electroplating and magnetron sputtering and the properties are determined by X-ray diffraction(XRD), scanning electron microscopy(SEM), and electron backscatter diffraction(EBSD).The coating bonding strength is assessed by pull-out tests and scribing in accordance with GB/T 9286-1998.The results show that the Cu coating with a thickness of 30 μm deposited on GF/PEEK by magnetron sputtering has lower roughness, finer grain size, higher crystallinity, as well as better macroscopic compressive stress,bonding strength, and electrical conductivity than the Cu coating deposited by electroplating.展开更多
To achieve high microwave permeability in wide-band for the micron-thick magnetic films,[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer structure was proposed by co-sputtering Fe and FeNi to form the magnetic layers and Cr to f...To achieve high microwave permeability in wide-band for the micron-thick magnetic films,[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer structure was proposed by co-sputtering Fe and FeNi to form the magnetic layers and Cr to form the interlayers.The multilayer structure contributes to the high permeability by reducing the coercivity and diminishing out-of-plane magnetization.The maximum imaginary permeability of[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer film reaches a large value of 800 at 0.52 GHz even though its overall thickness exceeds 1μm.Besides,the magnetic resonance frequency of the multilayer film can be modulated from 0.52 to 1.35 GHz by adjusting the sputtering power of Fe from 0 to 86 W,and its bandwidth for μ’’>200(Δf) is as large as 2.0 GHz.The desirable broad Δf of magnetic permeability,which can be well fitted by the Landau-Lifshitz-Gilbert equations,is due to dual magnetic resonances originated from double magnetic phases of Fe and FeNi that are of different saturation magnetization.The micron-thick multilayer films with high permeability in extended waveband are promising candidate for electromagnetic noise suppression application.展开更多
Sputtering is a crucial technology in fields such as electric propulsion, materials processing and semiconductors. Modeling of sputtering is significant for improving thruster design and designing material processing ...Sputtering is a crucial technology in fields such as electric propulsion, materials processing and semiconductors. Modeling of sputtering is significant for improving thruster design and designing material processing control algorithms. In this study we use the hierarchical clustering analysis algorithm to perform cluster analysis on 17 descriptors related to sputtering. These descriptors are divided into four fundamental groups, with representative descriptors being the mass of the incident ion, the formation energy of the incident ion, the mass of the target and the formation energy of the target. We further discuss the possible physical processes and significance involved in the classification process, including cascade collisions, energy transfer and other processes. Finally, based on the analysis of the above descriptors, several neural network models are constructed for the regression of sputtering threshold E_(th), maximum sputtering energy E_(max) and maximum sputtering yield SY_(max). In the regression model based on 267 samples, the four descriptor attributes showed higher accuracy than the 17 descriptors(R^(2) evaluation) in the same neural network structure, with the 5×5 neural network structure achieving the highest accuracy, having an R^(2) of 0.92. Additionally, simple sputtering test data also demonstrated the generalization ability of the 5×5 neural network model, the error in maximum sputtering yield being less than 5%.展开更多
Pure cobalt(Co)thin films were fabricated by direct current magnetron sputtering,and the effects of sputtering power and pres-sure on the microstructure and electromagnetic properties of the films were investigated.As...Pure cobalt(Co)thin films were fabricated by direct current magnetron sputtering,and the effects of sputtering power and pres-sure on the microstructure and electromagnetic properties of the films were investigated.As the sputtering power increases from 15 to 60 W,the Co thin films transition from an amorphous to a polycrystalline state,accompanied by an increase in the intercrystal pore width.Simultaneously,the resistivity decreases from 276 to 99μΩ·cm,coercivity increases from 162 to 293 Oe,and in-plane magnetic aniso-tropy disappears.As the sputtering pressure decreases from 1.6 to 0.2 Pa,grain size significantly increases,resistivity significantly de-creases,and the coercivity significantly increases(from 67 to 280 Oe),which can be attributed to the increase in defect width.Corres-pondingly,a quantitative model for the coercivity of Co thin films was formulated.The polycrystalline films sputtered under pressures of 0.2 and 0.4 Pa exhibit significant in-plane magnetic anisotropy,which is primarily attributable to increased microstress.展开更多
We deposited indium-tin-oxide(ITO)films on silicon and quartz substrates by magnetron sputtering technology in pure argon.Using electrostatic quadrupole plasma diagnostic technology,we investigate the effects of disch...We deposited indium-tin-oxide(ITO)films on silicon and quartz substrates by magnetron sputtering technology in pure argon.Using electrostatic quadrupole plasma diagnostic technology,we investigate the effects of discharge power and discharge pressure on the ion flux and energy distribution function of incidence on the substrate surface,with special attention to the production of high-energy negative oxygen ions,and elucidate the mechanism behind its production.At the same time,the structure and properties of ITO films are systematically characterized to understand the potential effects of high energy oxygen ions on the growth of ITO films.Combining with the kinetic property analysis of sputtering damage mechanism of transparent conductive oxide(TCO)thin films,this study provides valuable physical understanding of optimization of TCO thin film deposition process.展开更多
Magnetron sputtering deposition with regulated Cu target power was used for depositing Cu-containing high-entropy alloy nitride(Cu-(HEA)N)films on TC4 titanium alloy substrates.The microscopic morphologies,surface com...Magnetron sputtering deposition with regulated Cu target power was used for depositing Cu-containing high-entropy alloy nitride(Cu-(HEA)N)films on TC4 titanium alloy substrates.The microscopic morphologies,surface compositions,and thicknesses of the films were characterized using SEM+EDS;the anti-corrosion,wear resistance and antibacterial properties of the films in simulated seawater were investigated.The experimental results show that all four Cu-(HEA)N films are uniformly dense and contained nanoparticles.The film with Cu doping come into contact with oxygen in the air to form cuprous oxide.The corrosion resistance of the(HEA)N film without Cu doping on titanium alloy is better than the films with Cu doping.The Cu-(HEA)N film with Cu target power of 16 W shows the best wear resistance and antibacterial performance,which is attributed to the fact that Cu can reduce the coefficient of friction and exacerbate corrosion,and the formation of cuprous oxide has antibacterial properties.The findings of this study provide insights for engineering applications of TC4 in the marine field.展开更多
This study delves into ion behavior at the substrate position within RF magnetron discharges utilizing an indium tin oxide(ITO)target.The positive ion energies exhibit an upward trajectory with increasing RF power,att...This study delves into ion behavior at the substrate position within RF magnetron discharges utilizing an indium tin oxide(ITO)target.The positive ion energies exhibit an upward trajectory with increasing RF power,attributed to heightened plasma potential and initial emergent energy.Simultaneously,the positive ion flux escalates owing to amplified sputtering rates and electron density.Conversely,negative ions exhibit broad ion energy distribution functions(IEDFs)characterized by multiple peaks.These patterns are clarified by a combination of radiofrequency oscillation of cathode voltage and plasma potential,alongside ion transport time.This elucidation finds validation in a one-dimensional model encompassing the initial ion energy.At higher RF power,negative ions surpassing 100 e V escalate in both flux and energy,posing a potential risk of sputtering damages to ITO layers.展开更多
Cadmium sulfide(CdS)is an n-type semiconductor with excellent electrical conductivity that is widely used as an electron transport material(ETM)in solar cells.At present,numerous methods for preparing CdS thin films h...Cadmium sulfide(CdS)is an n-type semiconductor with excellent electrical conductivity that is widely used as an electron transport material(ETM)in solar cells.At present,numerous methods for preparing CdS thin films have emerged,among which magnetron sputtering(MS)is one of the most commonly used vacuum techniques.For this type of technique,the substrate temperature is one of the key deposition parameters that affects the interfacial properties between the target film and substrate,determining the specific growth habits of the films.Herein,the effect of substrate temperature on the microstructure and electrical properties of magnetron-sputtered CdS(MS-CdS)films was studied and applied for the first time in hydrothermally deposited antimony selenosulfide(Sb_(2)(S,Se)_(3))solar cells.Adjusting the substrate temperature not only results in the design of the flat and dense film with enhanced crystallinity but also leads to the formation of an energy level arrangement with a Sb_(2)(S,Se)_(3)layer that is more favorable for electron transfer.In addition,we developed an oxygen plasma treatment for CdS,reducing the parasitic absorption of the device and resulting in an increase in the short-circuit current density of the solar cell.This study demonstrates the feasibility of MS-CdS in the fabrication of hydrothermal Sb_(2)(S,Se)_(3)solar cells and provides interface optimization strategies to improve device performance.展开更多
The mechanical and frictional properties of ta-C coatings deposited on the substrate surface affect applications in the field of cutting tools and wear-resistant components.In this paper,the effect of bias parameters ...The mechanical and frictional properties of ta-C coatings deposited on the substrate surface affect applications in the field of cutting tools and wear-resistant components.In this paper,the effect of bias parameters on the performance of ta-C coatings was investigated based on high power impulse magnetron sputtering(HiPIMS)technology.The results show that bias voltage has a significant effect on the deposition rate,structure,and wear resistance of the coating.In the range of bias voltage−50 V to−200 V,the ta-C coating performance was the best under bias voltage−150 V.The thickness reached 530.4 nm,the hardness value reached 35.996 GPa,and the bonding force in-creased to 14.2 N.The maximum sp3 bond content was 59.53% at this condition.展开更多
Al_(1-x)In_(x)N, a Ⅲ-nitride semiconductor material, is currently of great research interest due to its remarkable physical properties and chemical stability. When the Al and In compositions are tuned, its band-gap e...Al_(1-x)In_(x)N, a Ⅲ-nitride semiconductor material, is currently of great research interest due to its remarkable physical properties and chemical stability. When the Al and In compositions are tuned, its band-gap energy varies from 0.7 eV to 6.2 eV, which shows great potential for application in photodetectors. Here, we report the fabrication and performance evaluation of integrated Al_(1-x)In_(x)N on a free-standing GaN substrate through direct radio-frequency magnetron sputtering.The optical properties of Al_(1-x)In_(x)N will be enhanced by the polarization effect of a heterostructure composed of Al_(1-x)In_(x)N and other Ⅲ-nitride materials. An Al_(1-x)In_(x)N/Ga N visible-light photodetector was prepared by semiconductor fabrication technologies such as lithography and metal deposition. The highest photoresponsivity achieved was 1.52 A·W^(-1)under 365 nm wavelength illumination and the photodetector was determined to have the composition Al0.75In0.25N/GaN.A rise time of 0.55 s was observed after transient analysis of the device. The prepared Al_(1-x)In_(x)N visible-light photodetector had a low dark current, high photoresponsivity and fast response speed. By promoting a low-cost, simple fabrication method,this study expands the application of ternary alloy Al_(1-x)In_(x)N visible-light photodetectors in optical communication.展开更多
Low pressure sputtering with a controlled ratio of ion flux to deposited atom flux at the condensing surface is one of the main directions of development of magnetron sputtering methods. Unbalanced magnetron sputterin...Low pressure sputtering with a controlled ratio of ion flux to deposited atom flux at the condensing surface is one of the main directions of development of magnetron sputtering methods. Unbalanced magnetron sputtering, by producing dense secondary plasma around the substrate, provides a high ion current density. The closed-field unbalanced magnetron sputtering system （CFUBMS） has been established as a versatile technique for high-rate deposition high-quality metal, alloy, and ceramic thin films. The＇key factor in the CFUBMS system is the ability to transport high ion currents to the substrate, which can enhance the formation of full dense coatings at relatively low value homologous temperature. The investigation shows that the energy of ions incidenced at the substrate and the ratio of the flux of these ions to the flux of condensing atoms are the fundamental parameters in determining the structure and properties of films produced by ion-assisted deposition processes. Increasing ion bombardment during deposition combined with increasing mobility of the condensing atoms favors the formation of a dense microstructure and a smooth surface.展开更多
The principle of magnetron sputtering is introduced andthe balanced and unbalanced magnetrons are compared andthe necessity of unbalanced magnetrons is explained as well. Several recent developments in plasma magnetro...The principle of magnetron sputtering is introduced andthe balanced and unbalanced magnetrons are compared andthe necessity of unbalanced magnetrons is explained as well. Several recent developments in plasma magnetron sputtering, i.e., unbalanced magnetron sputtering, pulsed magnetron sputtering and ion assisted sputtering, are discussed. The recent developments of unbalanced magnetron systems and their incorporation with ion sources result in an understanding in growingimportance of the magnetron sputtering technology, which makes the technology an applicable deposition process for a variety of important films, such as wear-resistant films and decorative films.展开更多
Al-doped ZnO （AZO） target was prepared by hot pressing using ZnO and Al2O3 powder in mass ratio of 98：2.The effects of hot pressing conditions including temperature,pressure and preserving time on relative density ...Al-doped ZnO （AZO） target was prepared by hot pressing using ZnO and Al2O3 powder in mass ratio of 98：2.The effects of hot pressing conditions including temperature,pressure and preserving time on relative density were investigated.Pore evolution and phase structure change during densification process were studied.The results show that AZO target with super high relative density of 99% was prepared by two-stage hot pressing method under pressure of 35MPa,temperature of 1 050℃ and 1 150℃ with preserving time of 1 h,respectively.At temperature around 1 050℃,the number of isolated pore wasminimum.At temperature lower than 900℃,there existed Al2O3 phase.At temperature higher than 1 000℃,ZnAl2O4 phase was generated and its content was increased with temperature increasing.Hot pressing method had the advantage over pressureless sintering that the content of ZnAl2O4 was lower and sintering temperature could be also lower.With increasing the hot pressing temperature and preserving time,the electric resistivity of AZO target decreased greatly.A low resistivity of 3 10-3 cm was achieved under the temperature of 1 100℃,pressure of 35MPa and preserving time of 10 h.展开更多
One-dimensional ZnO nanorods are synthesized by ox idating thin metal zinc films deposited on Si(111) substrates with radio frequen cy magnetron sputtering.The crystal structure,surface morphology,and optical pro per...One-dimensional ZnO nanorods are synthesized by ox idating thin metal zinc films deposited on Si(111) substrates with radio frequen cy magnetron sputtering.The crystal structure,surface morphology,and optical pro perties of nanorods are investigated.X-ray diffraction(XRD) pattern,scanning el ectron microscopy(SEM),and transmission electron microscopy(TEM) analyses show t hat the synthesized single-crystal ZnO nanorods develop like hairpins along dif ferent radials,with a hexagonal wurtzite structure.The diameters of nanorods ran ge between 30 and 60nm and lengths up to micrometers.Photoluminescence(PL) analy sis shows that,under 280nm light excitation,a strong and sharp near band-edge U V light emission band at 372nm and a relatively weak green deep-level light emi ssion band at 516nm are observed from the ZnO nanorods,which indicates excellent crystallization and optical quality of the fabricated ZnO nanorods.展开更多
Al-doped ZnO thin films were prepared on glass substrate using an ultra-high density target by RF magnetron sputtering at room temperature. The microstructure, surface morphology, optical and electrical properties of ...Al-doped ZnO thin films were prepared on glass substrate using an ultra-high density target by RF magnetron sputtering at room temperature. The microstructure, surface morphology, optical and electrical properties of AZO thin films were investigated by X-ray diffractometer, scanning electron microscope, UV-visible spectrophotometer, four-point probe method, and Hall-effect measurement system. The results showed that all the films obtained were polycrystalline with a hexagonal structure and average optical transmittance of AZO thin films was over 85 % at different sputtering powers. The sputtering power had a great effect on optoelectronic properties of the AZO thin films, especially on the resistivity. The lowest resistivity of 4.5×10^-4 Ω·cm combined with the transmittance of 87.1% was obtained at sputtering power of 200 W. The optical band gap varied between 3.48 and 3.68 eV.展开更多
Wurtzite aluminum nitride（AlN） films were deposited on Si（100） wafers under various sputtering pressures by radio-frequency（RF） reactive magnetron sputtering. The film properties were investigated by XRD, SEM, A...Wurtzite aluminum nitride（AlN） films were deposited on Si（100） wafers under various sputtering pressures by radio-frequency（RF） reactive magnetron sputtering. The film properties were investigated by XRD, SEM, AFM, XPS and nanoindenter techniques. It is suggested from the XRD patterns that highly c-axis oriented films grow preferentially at low pressures and the growth of（100） planes are preferred at higher pressures. The SEM and AFM images both reveal that the deposition rate and the surface roughness decrease while the average grain size increases with increasing the sputtering pressure. XPS results show that lowering the sputtering pressure is a useful way to minimize the incorporation of oxygen atoms into the AlN films and hence a film with closer stoichiometric composition is obtained. From the measurement of nanomechanical properties of AlN thin films, the largest hardness and elastic modulus are obtained at 0.30 Pa.展开更多
A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of...A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of the composite films was studied in the conditions of the ambient air and N2 gas atmosphere by ball-on-disk tester.The results indicate that the composite films show dense and amorphous microstructure.The WCx and WSx compounds are found in amorphous diamond like carbon matrix in the top layers of W-S-C.A proper WSx content is beneficial for improving the adhesion of the composite films.In air atmosphere,the composite films with high C content have better wear resistance and the friction coefficients range from 0.15 to 0.25.In N2 condition,high WSx content is benefit for the wear resistance and the friction coefficients of the composite films range from 0.03 to 0.1.展开更多
In order to study the effect of the microstructure with Al and V added TiN coatings, TiN, TiAlN and TiAlVN coatings were deposited on AISI M2 high-speed steels by magnetron reactive sputtering. The microstructures of ...In order to study the effect of the microstructure with Al and V added TiN coatings, TiN, TiAlN and TiAlVN coatings were deposited on AISI M2 high-speed steels by magnetron reactive sputtering. The microstructures of all the coatings were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results indicate that the addition of Al into TiN coatings reduces their lattice constant, but a further addition of V into TiAlN coatings increases their lattice constant. Moreover, the growth morphologies for TiN, TiAlN, and TiAlVN indicate that adding Al and V has a tendency to improve the columnar structure. The (111) and (200) orientations of TiN, TiAlN, and TiAlVN are identified. Theε(Fe3N-Fe2N) phase occurs because a small amount of Fe is present in the coatings. The interlayers of TiAlN and TiAlVN have the preferred (01 1 0) orientation. The texture (columnar) structure of the (111) and (200) orientations is observed in the TiAlN and TiAlVN coatings. An orientation relationship of (01 1 0)α-Ti//(110)T.M occurs between the interlayer and tempered martensite (T.M) in TiAlVN.展开更多
Series of TiO 2-ZnO heterojunction composite films with different n（Zn）/n（Ti） ratios were prepared by UDP450 magnetron sputter ion plating equipment, and the mole ratio of Zn to Ti was controlled by adjusting the ...Series of TiO 2-ZnO heterojunction composite films with different n（Zn）/n（Ti） ratios were prepared by UDP450 magnetron sputter ion plating equipment, and the mole ratio of Zn to Ti was controlled by adjusting the current values of sputtering target. The effects of n（Zn）/n（Ti） on the microstructures of TiO2-ZnO films were investigated by SEM, AFM, Raman and XPS, and their photocatalytic decomposition of methyl orange solutions was evaluated. The results show that an increase in n（Zn）/n（Ti） typically results in a decrease in the grain size of composite films firstly and then an increase of grain size, while an increase in n（Zn）/n（Ti） leads to an increase in film roughness firstly and then a decrease in film roughness. Both grain size and roughness of TiO2-ZnO films reach the maximum and minimum at n（Zn）/n（Ti） of 1/9.3, respectively. The n（Zn）/n（Ti） shows little effect on the valences of Zn and Ti elements, which mainly exist in the form of TiO2 and ZnO phases. The n（Zn）/n（Ti） has influence on the amount of anatase/rutile TiO2 heterojunction in the film. With increase of the n（Zn）/n（Ti）, the absorption intensity of the composite film increases and the absorption region extends to 450 nm, which is redshifted as much as 150 nm in comparison with the pure TiO2 films. However, the photocatalytic abilities of heterogeneous composite films do not depend on the n（Zn）/n（Ti） but rather on the microstructures of the TiO2-ZnO composite films. Degradation rate of the film reaches the maximum and the photocatalytic decomposition of pollutants works best when n（Zn）/n（Ti）=1：9.3.展开更多
Nano-scaled ZrNbAlN films with different negative bias voltages（Vb） were deposited on bronze substrate and Si（100） wafers by a reactive unbalanced magnetron sputtering technique. Composition and structure properti...Nano-scaled ZrNbAlN films with different negative bias voltages（Vb） were deposited on bronze substrate and Si（100） wafers by a reactive unbalanced magnetron sputtering technique. Composition and structure properties were characterized by X-ray photoelectron spectroscopy and X-ray diffraction. It is found that mole concentrations of Zr and Nb are affected by Vb, which leads to the increase of binding energy of N 1s and Al 2p and decrease of binding energy of Zr 3d5/2 and Nb 3d5/2. Surface morphologies evolution controlled by Vb could be observed. Furthermore, X-ray diffraction patterns reveal that these films show a（111） preferred orientation. Moreover, mechanical property and corrosion behavior of ZrNbAlN films were characterized by nanoindentation test and corrosion test, respectively. A maximum value of 21.85 GPa at-70 V occurs in the ZrNbAlN- bronze system, which outperforms uncoated bronze. Corrosion experiments in 0.5 mol/L NaCl and 0.5 mol/L HCl solution show that corrosion potential and corrosion current are dependent on Vb, and better anti-corrosion property could be obtained at-90 V.展开更多
基金Funded by Shenzhen-Hong Kong Innovative Collaborative Research and Development Program (Nos.SGLH20181109 110802117, CityU 9240014)Innovation Project of Southwestern Institute of Physics (Nos.202001XWCXYD002, 202301XWCX003)CNNC Young Talent Program (No.2023JZYF-01)。
文摘Surface metallization of glass fiber(GF)/polyetheretherketone(PEEK)[GF/PEEK] is conducted by coating copper using electroplating and magnetron sputtering and the properties are determined by X-ray diffraction(XRD), scanning electron microscopy(SEM), and electron backscatter diffraction(EBSD).The coating bonding strength is assessed by pull-out tests and scribing in accordance with GB/T 9286-1998.The results show that the Cu coating with a thickness of 30 μm deposited on GF/PEEK by magnetron sputtering has lower roughness, finer grain size, higher crystallinity, as well as better macroscopic compressive stress,bonding strength, and electrical conductivity than the Cu coating deposited by electroplating.
基金Funded by the Young Top-notch Talent Cultivation Program of Hubei Provincethe Fundamental Research Funds for the Central Universities(WUT:2021IVA116 and WUT:2021CG015)。
文摘To achieve high microwave permeability in wide-band for the micron-thick magnetic films,[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer structure was proposed by co-sputtering Fe and FeNi to form the magnetic layers and Cr to form the interlayers.The multilayer structure contributes to the high permeability by reducing the coercivity and diminishing out-of-plane magnetization.The maximum imaginary permeability of[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer film reaches a large value of 800 at 0.52 GHz even though its overall thickness exceeds 1μm.Besides,the magnetic resonance frequency of the multilayer film can be modulated from 0.52 to 1.35 GHz by adjusting the sputtering power of Fe from 0 to 86 W,and its bandwidth for μ’’>200(Δf) is as large as 2.0 GHz.The desirable broad Δf of magnetic permeability,which can be well fitted by the Landau-Lifshitz-Gilbert equations,is due to dual magnetic resonances originated from double magnetic phases of Fe and FeNi that are of different saturation magnetization.The micron-thick multilayer films with high permeability in extended waveband are promising candidate for electromagnetic noise suppression application.
基金supported by the National Key Research and Development Program of China (No. 2020YFC2201101)the Shenzhen Key Laboratory of Intelligent Microsatellite Constellation (No. ZDSYS20210623091808026)Guangdong Basic and Applied Basic Research Foundation (No. 2021A1515110500)。
文摘Sputtering is a crucial technology in fields such as electric propulsion, materials processing and semiconductors. Modeling of sputtering is significant for improving thruster design and designing material processing control algorithms. In this study we use the hierarchical clustering analysis algorithm to perform cluster analysis on 17 descriptors related to sputtering. These descriptors are divided into four fundamental groups, with representative descriptors being the mass of the incident ion, the formation energy of the incident ion, the mass of the target and the formation energy of the target. We further discuss the possible physical processes and significance involved in the classification process, including cascade collisions, energy transfer and other processes. Finally, based on the analysis of the above descriptors, several neural network models are constructed for the regression of sputtering threshold E_(th), maximum sputtering energy E_(max) and maximum sputtering yield SY_(max). In the regression model based on 267 samples, the four descriptor attributes showed higher accuracy than the 17 descriptors(R^(2) evaluation) in the same neural network structure, with the 5×5 neural network structure achieving the highest accuracy, having an R^(2) of 0.92. Additionally, simple sputtering test data also demonstrated the generalization ability of the 5×5 neural network model, the error in maximum sputtering yield being less than 5%.
基金the financial support from the National Key Research and Development Program of China(No.2017YFB0305500)the State Key Laboratory of Powder Metallurgy,Central South University,Changsha,China.
文摘Pure cobalt(Co)thin films were fabricated by direct current magnetron sputtering,and the effects of sputtering power and pres-sure on the microstructure and electromagnetic properties of the films were investigated.As the sputtering power increases from 15 to 60 W,the Co thin films transition from an amorphous to a polycrystalline state,accompanied by an increase in the intercrystal pore width.Simultaneously,the resistivity decreases from 276 to 99μΩ·cm,coercivity increases from 162 to 293 Oe,and in-plane magnetic aniso-tropy disappears.As the sputtering pressure decreases from 1.6 to 0.2 Pa,grain size significantly increases,resistivity significantly de-creases,and the coercivity significantly increases(from 67 to 280 Oe),which can be attributed to the increase in defect width.Corres-pondingly,a quantitative model for the coercivity of Co thin films was formulated.The polycrystalline films sputtered under pressures of 0.2 and 0.4 Pa exhibit significant in-plane magnetic anisotropy,which is primarily attributable to increased microstress.
基金supported by the National Key R&D Program of China(Grant No.2022YFE03050001)the National Natural Science Foundation of China(Grant Nos.12175160 and 12305284).The authors thank Suzhou Maxwell Technologies Co.,Ltd.for partial hardware and particle financial support to carry out the research.
文摘We deposited indium-tin-oxide(ITO)films on silicon and quartz substrates by magnetron sputtering technology in pure argon.Using electrostatic quadrupole plasma diagnostic technology,we investigate the effects of discharge power and discharge pressure on the ion flux and energy distribution function of incidence on the substrate surface,with special attention to the production of high-energy negative oxygen ions,and elucidate the mechanism behind its production.At the same time,the structure and properties of ITO films are systematically characterized to understand the potential effects of high energy oxygen ions on the growth of ITO films.Combining with the kinetic property analysis of sputtering damage mechanism of transparent conductive oxide(TCO)thin films,this study provides valuable physical understanding of optimization of TCO thin film deposition process.
基金Funded by the National Natural Science Foundation of China(No.52071252)the Key Research and Development Plan of Shaanxi Province Industrial Project(Nos.2021GY-208,2022GY-407,and 2021ZDLSF03-11)the China Postdoctoral Science Foundation(No.2020M683670XB)。
文摘Magnetron sputtering deposition with regulated Cu target power was used for depositing Cu-containing high-entropy alloy nitride(Cu-(HEA)N)films on TC4 titanium alloy substrates.The microscopic morphologies,surface compositions,and thicknesses of the films were characterized using SEM+EDS;the anti-corrosion,wear resistance and antibacterial properties of the films in simulated seawater were investigated.The experimental results show that all four Cu-(HEA)N films are uniformly dense and contained nanoparticles.The film with Cu doping come into contact with oxygen in the air to form cuprous oxide.The corrosion resistance of the(HEA)N film without Cu doping on titanium alloy is better than the films with Cu doping.The Cu-(HEA)N film with Cu target power of 16 W shows the best wear resistance and antibacterial performance,which is attributed to the fact that Cu can reduce the coefficient of friction and exacerbate corrosion,and the formation of cuprous oxide has antibacterial properties.The findings of this study provide insights for engineering applications of TC4 in the marine field.
基金financial supports by National Natural Science Foundation of China(Nos.11975163 and 12175160)Nantong Basic Science Research-General Program(No.JC22022034)Natural Science Research Fund of Jiangsu College of Engineering and Technology(No.GYKY/2023/2)。
文摘This study delves into ion behavior at the substrate position within RF magnetron discharges utilizing an indium tin oxide(ITO)target.The positive ion energies exhibit an upward trajectory with increasing RF power,attributed to heightened plasma potential and initial emergent energy.Simultaneously,the positive ion flux escalates owing to amplified sputtering rates and electron density.Conversely,negative ions exhibit broad ion energy distribution functions(IEDFs)characterized by multiple peaks.These patterns are clarified by a combination of radiofrequency oscillation of cathode voltage and plasma potential,alongside ion transport time.This elucidation finds validation in a one-dimensional model encompassing the initial ion energy.At higher RF power,negative ions surpassing 100 e V escalate in both flux and energy,posing a potential risk of sputtering damages to ITO layers.
基金supported by the National Natural Science Foundation of China(22275180)the National Key Research and Development Program of China(2019YFA0405600)the Collaborative Innovation Program of Hefei Science Center,CAS,and the University Synergy Innovation Program of Anhui Province(GXXT-2023-031).
文摘Cadmium sulfide(CdS)is an n-type semiconductor with excellent electrical conductivity that is widely used as an electron transport material(ETM)in solar cells.At present,numerous methods for preparing CdS thin films have emerged,among which magnetron sputtering(MS)is one of the most commonly used vacuum techniques.For this type of technique,the substrate temperature is one of the key deposition parameters that affects the interfacial properties between the target film and substrate,determining the specific growth habits of the films.Herein,the effect of substrate temperature on the microstructure and electrical properties of magnetron-sputtered CdS(MS-CdS)films was studied and applied for the first time in hydrothermally deposited antimony selenosulfide(Sb_(2)(S,Se)_(3))solar cells.Adjusting the substrate temperature not only results in the design of the flat and dense film with enhanced crystallinity but also leads to the formation of an energy level arrangement with a Sb_(2)(S,Se)_(3)layer that is more favorable for electron transfer.In addition,we developed an oxygen plasma treatment for CdS,reducing the parasitic absorption of the device and resulting in an increase in the short-circuit current density of the solar cell.This study demonstrates the feasibility of MS-CdS in the fabrication of hydrothermal Sb_(2)(S,Se)_(3)solar cells and provides interface optimization strategies to improve device performance.
基金supported by the National Key R&D Program of China(No.2019YFE0123900)the National Natural Sci-ence Foundation of China(Grant No.51974069)the Special Fund for Basic Scientific Research of Central Colleges(N2125035).
文摘The mechanical and frictional properties of ta-C coatings deposited on the substrate surface affect applications in the field of cutting tools and wear-resistant components.In this paper,the effect of bias parameters on the performance of ta-C coatings was investigated based on high power impulse magnetron sputtering(HiPIMS)technology.The results show that bias voltage has a significant effect on the deposition rate,structure,and wear resistance of the coating.In the range of bias voltage−50 V to−200 V,the ta-C coating performance was the best under bias voltage−150 V.The thickness reached 530.4 nm,the hardness value reached 35.996 GPa,and the bonding force in-creased to 14.2 N.The maximum sp3 bond content was 59.53% at this condition.
基金Project supported by the National Natural Science Foundation of China (Grant Nos. 61974144, 62004127, and 12074263)Key-Area Research and Development Program of Guangdong Province (Grant Nos. 2020B010174003 and 2020B010169001)+2 种基金Guangdong Science Foundation for Distinguished Young Scholars (Grant No. 2022B1515020073)the Science and Technology Foundation of Shenzhen (Grant No. JSGG20191129114216474)the Open Project of State Key Laboratory of Functional Materials for Informatics。
文摘Al_(1-x)In_(x)N, a Ⅲ-nitride semiconductor material, is currently of great research interest due to its remarkable physical properties and chemical stability. When the Al and In compositions are tuned, its band-gap energy varies from 0.7 eV to 6.2 eV, which shows great potential for application in photodetectors. Here, we report the fabrication and performance evaluation of integrated Al_(1-x)In_(x)N on a free-standing GaN substrate through direct radio-frequency magnetron sputtering.The optical properties of Al_(1-x)In_(x)N will be enhanced by the polarization effect of a heterostructure composed of Al_(1-x)In_(x)N and other Ⅲ-nitride materials. An Al_(1-x)In_(x)N/Ga N visible-light photodetector was prepared by semiconductor fabrication technologies such as lithography and metal deposition. The highest photoresponsivity achieved was 1.52 A·W^(-1)under 365 nm wavelength illumination and the photodetector was determined to have the composition Al0.75In0.25N/GaN.A rise time of 0.55 s was observed after transient analysis of the device. The prepared Al_(1-x)In_(x)N visible-light photodetector had a low dark current, high photoresponsivity and fast response speed. By promoting a low-cost, simple fabrication method,this study expands the application of ternary alloy Al_(1-x)In_(x)N visible-light photodetectors in optical communication.
文摘Low pressure sputtering with a controlled ratio of ion flux to deposited atom flux at the condensing surface is one of the main directions of development of magnetron sputtering methods. Unbalanced magnetron sputtering, by producing dense secondary plasma around the substrate, provides a high ion current density. The closed-field unbalanced magnetron sputtering system （CFUBMS） has been established as a versatile technique for high-rate deposition high-quality metal, alloy, and ceramic thin films. The＇key factor in the CFUBMS system is the ability to transport high ion currents to the substrate, which can enhance the formation of full dense coatings at relatively low value homologous temperature. The investigation shows that the energy of ions incidenced at the substrate and the ratio of the flux of these ions to the flux of condensing atoms are the fundamental parameters in determining the structure and properties of films produced by ion-assisted deposition processes. Increasing ion bombardment during deposition combined with increasing mobility of the condensing atoms favors the formation of a dense microstructure and a smooth surface.
基金supported by the National Natural Science Foundation of China (No. 50475057)the Tribology Science Fund of the State Key-laboratory of Tribology (No. Kf04.02)
文摘The principle of magnetron sputtering is introduced andthe balanced and unbalanced magnetrons are compared andthe necessity of unbalanced magnetrons is explained as well. Several recent developments in plasma magnetron sputtering, i.e., unbalanced magnetron sputtering, pulsed magnetron sputtering and ion assisted sputtering, are discussed. The recent developments of unbalanced magnetron systems and their incorporation with ion sources result in an understanding in growingimportance of the magnetron sputtering technology, which makes the technology an applicable deposition process for a variety of important films, such as wear-resistant films and decorative films.
基金Project(31001) supported by the Technology Development Foundation of Ministry of Science and Technology,China
文摘Al-doped ZnO （AZO） target was prepared by hot pressing using ZnO and Al2O3 powder in mass ratio of 98：2.The effects of hot pressing conditions including temperature,pressure and preserving time on relative density were investigated.Pore evolution and phase structure change during densification process were studied.The results show that AZO target with super high relative density of 99% was prepared by two-stage hot pressing method under pressure of 35MPa,temperature of 1 050℃ and 1 150℃ with preserving time of 1 h,respectively.At temperature around 1 050℃,the number of isolated pore wasminimum.At temperature lower than 900℃,there existed Al2O3 phase.At temperature higher than 1 000℃,ZnAl2O4 phase was generated and its content was increased with temperature increasing.Hot pressing method had the advantage over pressureless sintering that the content of ZnAl2O4 was lower and sintering temperature could be also lower.With increasing the hot pressing temperature and preserving time,the electric resistivity of AZO target decreased greatly.A low resistivity of 3 10-3 cm was achieved under the temperature of 1 100℃,pressure of 35MPa and preserving time of 10 h.
文摘One-dimensional ZnO nanorods are synthesized by ox idating thin metal zinc films deposited on Si(111) substrates with radio frequen cy magnetron sputtering.The crystal structure,surface morphology,and optical pro perties of nanorods are investigated.X-ray diffraction(XRD) pattern,scanning el ectron microscopy(SEM),and transmission electron microscopy(TEM) analyses show t hat the synthesized single-crystal ZnO nanorods develop like hairpins along dif ferent radials,with a hexagonal wurtzite structure.The diameters of nanorods ran ge between 30 and 60nm and lengths up to micrometers.Photoluminescence(PL) analy sis shows that,under 280nm light excitation,a strong and sharp near band-edge U V light emission band at 372nm and a relatively weak green deep-level light emi ssion band at 516nm are observed from the ZnO nanorods,which indicates excellent crystallization and optical quality of the fabricated ZnO nanorods.
基金supported by open research fund from Guangxi Key Laboratory of New Energy and Building Energy Saving, China
文摘Al-doped ZnO thin films were prepared on glass substrate using an ultra-high density target by RF magnetron sputtering at room temperature. The microstructure, surface morphology, optical and electrical properties of AZO thin films were investigated by X-ray diffractometer, scanning electron microscope, UV-visible spectrophotometer, four-point probe method, and Hall-effect measurement system. The results showed that all the films obtained were polycrystalline with a hexagonal structure and average optical transmittance of AZO thin films was over 85 % at different sputtering powers. The sputtering power had a great effect on optoelectronic properties of the AZO thin films, especially on the resistivity. The lowest resistivity of 4.5×10^-4 Ω·cm combined with the transmittance of 87.1% was obtained at sputtering power of 200 W. The optical band gap varied between 3.48 and 3.68 eV.
基金Project(21271188)supported by the National Natural Science Foundation of ChinaProject(2012M521541)supported by the China Postdoctoral Science Foundation+2 种基金Project(2012QNZT002)supported by the Fundamental Research Funds for the Central South Universities,ChinaProject(20110933K)supported by the State Key Laboratory of Powder Metallurgy,ChinaProject(CSU2012024)supported by the Open-End Fund for Valuable and Precision Instruments of Central South University,China
文摘Wurtzite aluminum nitride（AlN） films were deposited on Si（100） wafers under various sputtering pressures by radio-frequency（RF） reactive magnetron sputtering. The film properties were investigated by XRD, SEM, AFM, XPS and nanoindenter techniques. It is suggested from the XRD patterns that highly c-axis oriented films grow preferentially at low pressures and the growth of（100） planes are preferred at higher pressures. The SEM and AFM images both reveal that the deposition rate and the surface roughness decrease while the average grain size increases with increasing the sputtering pressure. XPS results show that lowering the sputtering pressure is a useful way to minimize the incorporation of oxygen atoms into the AlN films and hence a film with closer stoichiometric composition is obtained. From the measurement of nanomechanical properties of AlN thin films, the largest hardness and elastic modulus are obtained at 0.30 Pa.
文摘A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of the composite films was studied in the conditions of the ambient air and N2 gas atmosphere by ball-on-disk tester.The results indicate that the composite films show dense and amorphous microstructure.The WCx and WSx compounds are found in amorphous diamond like carbon matrix in the top layers of W-S-C.A proper WSx content is beneficial for improving the adhesion of the composite films.In air atmosphere,the composite films with high C content have better wear resistance and the friction coefficients range from 0.15 to 0.25.In N2 condition,high WSx content is benefit for the wear resistance and the friction coefficients of the composite films range from 0.03 to 0.1.
文摘In order to study the effect of the microstructure with Al and V added TiN coatings, TiN, TiAlN and TiAlVN coatings were deposited on AISI M2 high-speed steels by magnetron reactive sputtering. The microstructures of all the coatings were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results indicate that the addition of Al into TiN coatings reduces their lattice constant, but a further addition of V into TiAlN coatings increases their lattice constant. Moreover, the growth morphologies for TiN, TiAlN, and TiAlVN indicate that adding Al and V has a tendency to improve the columnar structure. The (111) and (200) orientations of TiN, TiAlN, and TiAlVN are identified. Theε(Fe3N-Fe2N) phase occurs because a small amount of Fe is present in the coatings. The interlayers of TiAlN and TiAlVN have the preferred (01 1 0) orientation. The texture (columnar) structure of the (111) and (200) orientations is observed in the TiAlN and TiAlVN coatings. An orientation relationship of (01 1 0)α-Ti//(110)T.M occurs between the interlayer and tempered martensite (T.M) in TiAlVN.
基金Project (2010JQ6008) supported by the Natural Science Foundation of Shaanxi Province,China
文摘Series of TiO 2-ZnO heterojunction composite films with different n（Zn）/n（Ti） ratios were prepared by UDP450 magnetron sputter ion plating equipment, and the mole ratio of Zn to Ti was controlled by adjusting the current values of sputtering target. The effects of n（Zn）/n（Ti） on the microstructures of TiO2-ZnO films were investigated by SEM, AFM, Raman and XPS, and their photocatalytic decomposition of methyl orange solutions was evaluated. The results show that an increase in n（Zn）/n（Ti） typically results in a decrease in the grain size of composite films firstly and then an increase of grain size, while an increase in n（Zn）/n（Ti） leads to an increase in film roughness firstly and then a decrease in film roughness. Both grain size and roughness of TiO2-ZnO films reach the maximum and minimum at n（Zn）/n（Ti） of 1/9.3, respectively. The n（Zn）/n（Ti） shows little effect on the valences of Zn and Ti elements, which mainly exist in the form of TiO2 and ZnO phases. The n（Zn）/n（Ti） has influence on the amount of anatase/rutile TiO2 heterojunction in the film. With increase of the n（Zn）/n（Ti）, the absorption intensity of the composite film increases and the absorption region extends to 450 nm, which is redshifted as much as 150 nm in comparison with the pure TiO2 films. However, the photocatalytic abilities of heterogeneous composite films do not depend on the n（Zn）/n（Ti） but rather on the microstructures of the TiO2-ZnO composite films. Degradation rate of the film reaches the maximum and the photocatalytic decomposition of pollutants works best when n（Zn）/n（Ti）=1：9.3.
基金Project(50725413)supported by the National Natural Science Foundation of ChinaProject(2010BB4290)supported by Natural Science Foundation Project of CQ CSTC,China
文摘Nano-scaled ZrNbAlN films with different negative bias voltages（Vb） were deposited on bronze substrate and Si（100） wafers by a reactive unbalanced magnetron sputtering technique. Composition and structure properties were characterized by X-ray photoelectron spectroscopy and X-ray diffraction. It is found that mole concentrations of Zr and Nb are affected by Vb, which leads to the increase of binding energy of N 1s and Al 2p and decrease of binding energy of Zr 3d5/2 and Nb 3d5/2. Surface morphologies evolution controlled by Vb could be observed. Furthermore, X-ray diffraction patterns reveal that these films show a（111） preferred orientation. Moreover, mechanical property and corrosion behavior of ZrNbAlN films were characterized by nanoindentation test and corrosion test, respectively. A maximum value of 21.85 GPa at-70 V occurs in the ZrNbAlN- bronze system, which outperforms uncoated bronze. Corrosion experiments in 0.5 mol/L NaCl and 0.5 mol/L HCl solution show that corrosion potential and corrosion current are dependent on Vb, and better anti-corrosion property could be obtained at-90 V.