A crack-free AlN film with 4.5 μm thickness was grown on a 2-inch hole-type nano-patterned sapphire substrates(NPSSs) by hydride vapor phase epitaxy(HVPE). The coalescence, stress evolution, and dislocation annihilat...A crack-free AlN film with 4.5 μm thickness was grown on a 2-inch hole-type nano-patterned sapphire substrates(NPSSs) by hydride vapor phase epitaxy(HVPE). The coalescence, stress evolution, and dislocation annihilation mechanisms in the AlN layer have been investigated. The large voids located on the pattern region were caused by the undesirable parasitic crystallites grown on the sidewalls of the nano-pattern in the early growth stage. The coalescence of the c-plane AlN was hindered by these three-fold crystallites and the special triangle void appeared. The cross-sectional Raman line scan was used to characterize the change of stress with film thickness, which corresponds to the characteristics of different growth stages of AlN. Threading dislocations(TDs) mainly originate from the boundary between misaligned crystallites and the c-plane AlN and the coalescence of two adjacent c-plane AlN crystals, rather than the interface between sapphire and AlN.展开更多
The epitaxial growths of GaN films and GaN-based LEDs on various patterned sapphire substrates （PSSes） with different values of fill factor （f） and slanted angle （0） are investigated in detail. The threading dis...The epitaxial growths of GaN films and GaN-based LEDs on various patterned sapphire substrates （PSSes） with different values of fill factor （f） and slanted angle （0） are investigated in detail. The threading dislocation （TD） density is lower in the film grown on the PSS with a smaller fill factor, resulting in a higher internal quantum efficiency （IQE）. Also the ability of the LED to withstand the electrostatic discharge （ESD） increases as the fill factor decreases. The illumination output power of the LED is affected by both 0 and f. It is found that the illumination output power of the LED grown on the PSS with a lower production of tan 0 and f is higher than that with a higher production of tan 0 and f.展开更多
InN films with highly c-axis preferred orientation were deposited on sapphire substrate by low-temperature electron cyclotron resonance plasma-enhanced metal organic chemical vapor deposition (ECR-PEMOCVD). Trimethyl ...InN films with highly c-axis preferred orientation were deposited on sapphire substrate by low-temperature electron cyclotron resonance plasma-enhanced metal organic chemical vapor deposition (ECR-PEMOCVD). Trimethyl indium (TMIn) and N 2 were applied as precursors of In and N, respectively. The quality of as-grown InN films were systematically investigated as a function of TMIn fluxes by means of reflection high-energy electron diffraction (RHEED), X-ray diffraction analysis (XRD), and atomic force microscopy (AFM). The results show that the dense and uniform InN films with highly c-axis preferred orientation are successfully achieved on sapphire substrates under optimized TMIn flux of 0.8 ml min 1 . The InN films reported here will provide various opportunities for the development of high efficiency and high-performance semiconductor devices based on InN material.展开更多
The effect of a self-organized SiNs interlayer on the defect density of （1122） semipolar GaN grown on 7n-plane sapphire is studied by transmission electron microscopy, atomic force microscopy and high resolution x-r...The effect of a self-organized SiNs interlayer on the defect density of （1122） semipolar GaN grown on 7n-plane sapphire is studied by transmission electron microscopy, atomic force microscopy and high resolution x-ray diffrac- tion. The SiNx interlayer reduces the c-type dislocation density from 2.5 ×10^10 cm^-2 to 5 ×10^8 cm 2. The SiNx interlayer produces regions that are free from basal plane stacking faults （BSFs） and dislocations. The overall BSF density is reduced from 2.1×10^5 cm-1 to 1.3×10^4 cm^-1. The large dislocations and BSF reduction in semipolar （1122） GaN with the SiNx, interlayer result from two primary mechanisms. The first mechanism is the direct dislocation blocking by the SiNx interlayer, and the second mechanism is associated with the unique structure character of （1122） semipolar GaN.展开更多
Nearly lattice-matched InAIGaN/GaN heterostructure is grown on sapphire substrates by pulsed metal organic chemical vapor deposition and excellent high electron mobility transistors are fabricated on this heterostruct...Nearly lattice-matched InAIGaN/GaN heterostructure is grown on sapphire substrates by pulsed metal organic chemical vapor deposition and excellent high electron mobility transistors are fabricated on this heterostructure. The electron mobility is 1668.08cm2/V.s together with a high two-dimensional-electron-gas density of 1.43 × 10^13 cm-2 for the InAlCaN/CaN heterostructure of 2Onto InAlCaN quaternary barrier. High electron mobility transistors with gate dimensions of 1 × 50 μm2 and 4μm source-drain distance exhibit the maximum drain current of 763.91 mA/mm, the maximum extrinsic transconductance of 163.13 mS/mm, and current gain and maximum oscillation cutoff frequencies of 11 GHz and 21 GHz, respectively.展开更多
Gallium nitride(GaN) thin film of the nitrogen polarity(N-polar) was grown on C-plane sapphire and misoriented C-plane sapphire substrates respectively by metal-organic chemical vapor deposition(MOCVD). The misorienta...Gallium nitride(GaN) thin film of the nitrogen polarity(N-polar) was grown on C-plane sapphire and misoriented C-plane sapphire substrates respectively by metal-organic chemical vapor deposition(MOCVD). The misorientation angle is off-axis from C-plane toward M-plane of the substrates, and the angle is 2°and 4°respectively. The nitrogen polarity was confirmed by examining the images of the scanning electron microscope before and after the wet etching in potassium hydroxide(KOH) solution. The morphology was studied by the optical microscope and atomic force microscope. The crystalline quality was characterized by the x-ray diffraction. The lateral coherence length, the tilt angle, the vertical coherence length, and the vertical lattice-strain were acquired using the pseudo-Voigt function to fit the x-ray diffraction curves and then calculating with four empirical formulae. The lateral coherence length increases with the misorientation angle, because higher step density and shorter distance between adjacent steps can lead to larger lateral coherence length.The tilt angle increases with the misorientation angle, which means that the misoriented substrate can degrade the identity of crystal orientation of the N-polar GaN film. The vertical lattice-strain decreases with the misorientation angle. The vertical coherence length does not change a lot as the misorientation angle increases and this value of all samples is close to the nominal thickness of the N-polar GaN layer. This study helps to understand the influence of the misorientation angle of misoriented C-plane sapphire on the morphology, the crystalline quality, and the microstructure of N-polar GaN films.展开更多
A new method for patterned sapphire substrate （PSS） design is developed and proven to be reliable and cost-effective. As progress is made with LEDs＇ luminous efficiency, the pattern units of PSS become more complic...A new method for patterned sapphire substrate （PSS） design is developed and proven to be reliable and cost-effective. As progress is made with LEDs＇ luminous efficiency, the pattern units of PSS become more complicated, and the effect of complicated geometrical features is almost impossible to study systematically by experiments only. By employing our new method, the influence of pattern parameters can be systematically studied, and various novel patterns are designed and optimized within a reasonable time span, with great improvement in LEDs＇ light extraction efficiency （LEE）. Clearly, PSS pattern design with such a method deserves particular attention. We foresee that GaN-based LEDs on these newly designed PSSs will achieve more progress in the coming years.展开更多
A method for growing graphene on a sapphire substrate by depositing an SiC buffer layer and then annealing at high temperature in solid source molecular beam epitaxy（SSMBE） equipment was presented.The structural and...A method for growing graphene on a sapphire substrate by depositing an SiC buffer layer and then annealing at high temperature in solid source molecular beam epitaxy（SSMBE） equipment was presented.The structural and electronic properties of the samples were characterized by reflection high energy diffraction（RHEED）,X-ray diffraction Φ scans,Raman spectroscopy,and near edge X-ray absorption fine structure（NEXAFS） spectroscopy.The results of the RHEED and Φ scan,as well as the Raman spectra,showed that an epitaxial hexagonal α-SiC layer was grown on the sapphire substrate.The results of the Raman and NEXAFS spectra revealed that the graphene films with the AB Bernal stacking structure were formed on the sapphire substrate after annealing.The layer number of the graphene was between four and five,and the thickness of the unreacted SiC layer was about 1-1.5 nm.展开更多
Epitaxiai CeO_2 thin films have ben grown on in situ (1102) sapphire subetrate by planar target rf mag-netron sputtering methed. The CeO_2 thin films have perfect (002) orientation with CeO_2(001)∥Al_2O_3(1102). The ...Epitaxiai CeO_2 thin films have ben grown on in situ (1102) sapphire subetrate by planar target rf mag-netron sputtering methed. The CeO_2 thin films have perfect (002) orientation with CeO_2(001)∥Al_2O_3(1102). The X-ray 2θ-θ diffraction, ω scan, Φ scan and electron channelling pattern (ECP) shown that thefilms liave high lattice perfection. The relation of growth conditions and film structure was also studied. Thespudering gas presure and subetrate temperature are the most important parameters preparing fer high qualitybeO_2 films.展开更多
In this paper, the enhanced performance of InGaN/GaN multiple quantum well solar cells grown on patterned sapphire substrates （PSS） was demonstrated. The short-circuit current （Jsc） density of the solar cell grown...In this paper, the enhanced performance of InGaN/GaN multiple quantum well solar cells grown on patterned sapphire substrates （PSS） was demonstrated. The short-circuit current （Jsc） density of the solar cell grown on PSS showed an improvement of 60%, compared to that of solar cells grown on conventional sapphire substrate. The improved performance is primarily due to the reduction of edge dislocations and the increased light absorption path by the scattering from the textured surface of the PSS. It shows that the patterned sapphire technology can effectively alleviate the problem of high-density dislocations and low Jsc caused by thinner absorption layers of the InGaN based solar cell, and it is promising to improve the efficiency of the solar cell.展开更多
The effect of patterned sapphire substrate（PSS） on the top-surface（P-Ga N-surface） and the bottomsurface（sapphire-surface） of the light output power（LOP） of Ga N-based LEDs was investigated, in order to study ...The effect of patterned sapphire substrate（PSS） on the top-surface（P-Ga N-surface） and the bottomsurface（sapphire-surface） of the light output power（LOP） of Ga N-based LEDs was investigated, in order to study the changes in reflection and transmission of the Ga N-sapphire interface. Experimental research and computer simulations were combined to reveal a great enhancement in LOP from either the top or bottom surface of Ga N-based LEDs, which are prepared on patterned sapphire substrates（PSS-LEDs）. Furthermore, the results were compared to those of the conventional LEDs prepared on the planar sapphire substrates（CSS-LEDs）. A detailed theoretical analysis was also presented to further support the explanation for the increase in both the effective reflection and transmission of PSS-Ga N interface layers and to explain the causes of increased LOP values. Moreover, the bottom-surface of the PSS-LED chip shows slightly increased light output performance when compared to that of the top-surface. Therefore, the light extraction efficiency（LEE） can be further enhanced by integrating the method of PSS and flip-chip structure design.展开更多
In this paper, the cone-shaped patterned sapphire substrates (PSS) were etched by an inductively couple plasma with BCl 3 as the reacting gas. The influence of the operating pressure and the RF bias power on subtrench...In this paper, the cone-shaped patterned sapphire substrates (PSS) were etched by an inductively couple plasma with BCl 3 as the reacting gas. The influence of the operating pressure and the RF bias power on subtrenches of the cone-shaped PSS and the formation mechanism of subtrenches were investigated. The profiles of patterns were characterized by FESEM (field emission scanning electron microscope). It showed that the subtrench size varied with the operating pressure and the RF bias power. As the operating pressure increased from 0.2 Pa to 0.9 Pa, the subtrenches changed from narrow and deep to wide and shallow; then to narrower and shallower. When the RF bias power varied from 200 W to 600 W, the subtrenches gradually became noticeable. The FESEM results also indicated that the subtrenches were formed due to the ion scattering effect which was caused by tapered sidewalls and charges accumulation. It is discovered that the scattering effect is closely related with the operating pressure and RF bias power.展开更多
Cone-shaped patterned sapphire substrate was prepared by inductively coupled plasma etching and GaN nucleation layer was grown on it by metal-organic chemical vapor deposition.A selective growth of GaN nucleation laye...Cone-shaped patterned sapphire substrate was prepared by inductively coupled plasma etching and GaN nucleation layer was grown on it by metal-organic chemical vapor deposition.A selective growth of GaN nucleation layer was found on the slope of the cone-shaped patterned sapphire substrat,and the distribution morphology of GaN had significantly changed after it was recrystallized.GaN selective growth and redistribution were analyzed by investigating the distribution of crystallographic planes on the cone surface and the atom array of specific planes at atom level.展开更多
Unintentionally doped AlGaN thin films are grown on c-plane(0001) sapphire substrate by metal-organic chemical vapor deposition, and low-temperature AlN is deposited onto sapphire substrate used as a bu?er layer. AlGa...Unintentionally doped AlGaN thin films are grown on c-plane(0001) sapphire substrate by metal-organic chemical vapor deposition, and low-temperature AlN is deposited onto sapphire substrate used as a bu?er layer. AlGaN metal-semiconductor-metal ultraviolet photodetectors with Ni/Au interdigitated contact electrodes are then fabricated by lift-off technology. The dark current of the AlGaN photodetectors is 5.61×10-9 A at 2-V applied bias and the peak response occurrs at 294 nm.展开更多
The growth process of three-dimensional growth mode（3D） switching to two-dimensional growth mode （2D） is investigated when GaN films are grown on cone-shaped patterned sapphire substrates by metal-organic chemical...The growth process of three-dimensional growth mode（3D） switching to two-dimensional growth mode （2D） is investigated when GaN films are grown on cone-shaped patterned sapphire substrates by metal-organic chemical vapor deposition.The growth condition of the 3D-2D growth process is optimized to reduce the threading dislocation density（TDD）.It is found that the condition of the 3D layer is critical.The 3D layer keeps growing under the conditions of lowⅤ/Ⅲratio,low temperature,and high pressure until its thickness is comparable to the height of the cone-shaped patterns.Then the 3D layer surrounds the cone-shaped patterns and has inclined side facets and a top（0001） plane.In the following 2D-growth process,inclined side facets coalesce quickly and the interaction of TDs with the side facets causes the TDs to bend over.As a result,the TDD of GaN films can decrease to 1×10~8 cm^（-2）,giving full-width at half maximum values of 211 and 219 arcsec for（002） and（102） omega scans, respectively.展开更多
MOCVD-grown 0.25μm gate-length AlGaN/GaN high electron mobility transistors （HEMTs） are fabricated on sapphire substrates. A peak extrinsic transconductance of 250mS/mm and a unity current gain cutoff frequency （f...MOCVD-grown 0.25μm gate-length AlGaN/GaN high electron mobility transistors （HEMTs） are fabricated on sapphire substrates. A peak extrinsic transconductance of 250mS/mm and a unity current gain cutoff frequency （fT） of 77GHz are obtained for a 0.25μm gate-length single finger device. These power devices exhibit a maximum drain current density as high as 1.07A/mm. On-chip testing yielded a continuous-wave output power of 27. 04dBm at 8GHz with an associated power-added efficiency of 26. 5% for an 80 × 10μm device.展开更多
We differentiated the effects of Cu films deposited on single crystalline a-,r-,and c-plane sapphire substrates upon graphene films synthesized with atmospheric pressure chemical vapor deposition(CVD).The data illustr...We differentiated the effects of Cu films deposited on single crystalline a-,r-,and c-plane sapphire substrates upon graphene films synthesized with atmospheric pressure chemical vapor deposition(CVD).The data illustrate that the realization of high-crystalline Cu film is dependent not only on the crystallinity of underlying substrate,but also on the symmetric match of crystallographic geometry between metal film and substrate.We also systematically investigated the effects of PMMA removal on the Raman ID/IG and IG/I2D values of transferred graphene.The results reveal that different PMMA removal methods do not alter the ID/IG values;instead,the residue of PMMA increases the IG/I2D values and the thermal decomposition of PMMA leads to higher IG/I2D values than the removal of PMMA with acetone.The effects of PMMA removal on variations of the Raman spectra are also discussed.展开更多
High-quality MgxZn1-xO thin films were grown on sapphire（0001 ） substrates with a ZnO buffer layer of different thicknesses by means of metal-organic chemical vapor deposition. Diethyl zinc, bis-cyclopentadienyl-Mg ...High-quality MgxZn1-xO thin films were grown on sapphire（0001 ） substrates with a ZnO buffer layer of different thicknesses by means of metal-organic chemical vapor deposition. Diethyl zinc, bis-cyclopentadienyl-Mg and oxygen were used as the precursor materials. The crystalline quality, surface morphologies and optical properties of the Mg, Zn1-xO films were investigated by X-ray diffraction, atomic force microscopy and photoluminescence spectrometry. It was shown that the quality of the MgxZn1-xO thin films depends on the thickness of the ZnO buffer layer and an Mg, Zn1-xO thin film with a ZnO buffer layer whose thickness was 20 nm exhibited the best crystal-quality, optical properties and a flat and dense surface.展开更多
Canti-bridged epitaxial lateral overgrowth （CBELO） of GaN is performed by metalorganic chemical vapour deposition （MOCVD） on maskless V-grooved sapphire substrates prepared by wet chemical etching with different m...Canti-bridged epitaxial lateral overgrowth （CBELO） of GaN is performed by metalorganic chemical vapour deposition （MOCVD） on maskless V-grooved sapphire substrates prepared by wet chemical etching with different mesa widths. The wing tilt usually observed in ELO is not found in the CBELO GaN with wide mesa widths, while it can be detected obviously in the GaN with narrow mesa widths. The wing tilt of CBELO GaN grown on a grooved sapphire substrate with narrow mesa can be controlled by adjusting the thickness of the nucleation layer. The dependence of the wing tilt on the nucleation layer thickness is studied. Cross-sectional scanning electron microscopy is used to characterize the geometry of the wing regions, and double crystal x-ray diffraction is used to analyse the structural characteristics and to measure the magnitude of the crystalline wing tilt. It is found that the crystalline wing tilt can be eliminated completely by first growth of a thin nucleation GaN layer then the CBELO GaN. Possible reason and the origin of the wing tilt in CBELO GaN films are also discussed.展开更多
Progress with GaN-based light emitting diodes （LEDs） that incorporate nanostructures is reviewed, especially the re- cent achievements in our research group. Nano-patterned sapphire substrates have been used to grow...Progress with GaN-based light emitting diodes （LEDs） that incorporate nanostructures is reviewed, especially the re- cent achievements in our research group. Nano-patterned sapphire substrates have been used to grow an A1N template layer for deep-ultraviolet （DUV） LEDs. One efficient surface nano-texturing technology, hemisphere-cones-hybrid nanostruc- tures, was employed to enhance the extraction efficiency of InGaN flip-chip LEDs. Hexagonal nanopyramid GaN-based LEDs have been fabricated and show electrically driven color modification and phosphor-free white light emission because of the linearly increased quantum well width and indium incorporation from the shell to the core. Based on the nanostruc- tures, we have also fabricated surface plasmon-enhanced nanoporous GaN-based green LEDs using AAO membrane as a mask. Benefitting from the strong lateral SP coupling as well as good electrical protection by a passivation layer, the EL intensity of an SP-enhanced nanoporous LED was significantly enhanced by 380%. Furthermore, nanostructures have been used for the growth of GaN LEDs on amorphous substrates, the fabrication of stretchable LEDs, and for increasing the 3-dB modulation bandwidth for visible light communication.展开更多
基金supported by the National Natural Science Foundation of China (Grant No. 61974158)the Natural Science Fund of Jiangsu Province, China (Grant No. BK20191456)。
文摘A crack-free AlN film with 4.5 μm thickness was grown on a 2-inch hole-type nano-patterned sapphire substrates(NPSSs) by hydride vapor phase epitaxy(HVPE). The coalescence, stress evolution, and dislocation annihilation mechanisms in the AlN layer have been investigated. The large voids located on the pattern region were caused by the undesirable parasitic crystallites grown on the sidewalls of the nano-pattern in the early growth stage. The coalescence of the c-plane AlN was hindered by these three-fold crystallites and the special triangle void appeared. The cross-sectional Raman line scan was used to characterize the change of stress with film thickness, which corresponds to the characteristics of different growth stages of AlN. Threading dislocations(TDs) mainly originate from the boundary between misaligned crystallites and the c-plane AlN and the coalescence of two adjacent c-plane AlN crystals, rather than the interface between sapphire and AlN.
基金Project supported by the National Natural Science Foundation of China (Grant Nos. 61006084 and 61076119)the Technical Corporation Innovation Foundation of Suzhou Industrial Park,China (Grant No. SG0962)
文摘The epitaxial growths of GaN films and GaN-based LEDs on various patterned sapphire substrates （PSSes） with different values of fill factor （f） and slanted angle （0） are investigated in detail. The threading dislocation （TD） density is lower in the film grown on the PSS with a smaller fill factor, resulting in a higher internal quantum efficiency （IQE）. Also the ability of the LED to withstand the electrostatic discharge （ESD） increases as the fill factor decreases. The illumination output power of the LED is affected by both 0 and f. It is found that the illumination output power of the LED grown on the PSS with a lower production of tan 0 and f is higher than that with a higher production of tan 0 and f.
基金supported by the National Natural Science Foundation of China (No. 61040058) (No. 60976006)the Fundamental Research Funds for the Central Universities (No.DUT10LK01)the Science and Technology Foundation for Higher Education of Liaoning Province, China and Science and Technology Innovation Project Foundation for Higher Education School (No.707015)
文摘InN films with highly c-axis preferred orientation were deposited on sapphire substrate by low-temperature electron cyclotron resonance plasma-enhanced metal organic chemical vapor deposition (ECR-PEMOCVD). Trimethyl indium (TMIn) and N 2 were applied as precursors of In and N, respectively. The quality of as-grown InN films were systematically investigated as a function of TMIn fluxes by means of reflection high-energy electron diffraction (RHEED), X-ray diffraction analysis (XRD), and atomic force microscopy (AFM). The results show that the dense and uniform InN films with highly c-axis preferred orientation are successfully achieved on sapphire substrates under optimized TMIn flux of 0.8 ml min 1 . The InN films reported here will provide various opportunities for the development of high efficiency and high-performance semiconductor devices based on InN material.
基金Supported by the National Natural Science Foundation of China under Grant Nos 61204006 and 61574108the Fundamental Research Funds for the Central Universities under Grant No JB141101the Foundation of Key Laboratory of Nanodevices and Applications of Suzhou Institute of Nano-Tech and Nano-Bionics of Chinese Academy of Sciences under Grant No 15CS01
文摘The effect of a self-organized SiNs interlayer on the defect density of （1122） semipolar GaN grown on 7n-plane sapphire is studied by transmission electron microscopy, atomic force microscopy and high resolution x-ray diffrac- tion. The SiNx interlayer reduces the c-type dislocation density from 2.5 ×10^10 cm^-2 to 5 ×10^8 cm 2. The SiNx interlayer produces regions that are free from basal plane stacking faults （BSFs） and dislocations. The overall BSF density is reduced from 2.1×10^5 cm-1 to 1.3×10^4 cm^-1. The large dislocations and BSF reduction in semipolar （1122） GaN with the SiNx, interlayer result from two primary mechanisms. The first mechanism is the direct dislocation blocking by the SiNx interlayer, and the second mechanism is associated with the unique structure character of （1122） semipolar GaN.
基金Supported by the National Science and Technology Major Project of China under Grant No 2013ZX02308-002the National Natural Sciences Foundation of China under Grant Nos 61574108,61334002,61474086 and 61306017
文摘Nearly lattice-matched InAIGaN/GaN heterostructure is grown on sapphire substrates by pulsed metal organic chemical vapor deposition and excellent high electron mobility transistors are fabricated on this heterostructure. The electron mobility is 1668.08cm2/V.s together with a high two-dimensional-electron-gas density of 1.43 × 10^13 cm-2 for the InAlCaN/CaN heterostructure of 2Onto InAlCaN quaternary barrier. High electron mobility transistors with gate dimensions of 1 × 50 μm2 and 4μm source-drain distance exhibit the maximum drain current of 763.91 mA/mm, the maximum extrinsic transconductance of 163.13 mS/mm, and current gain and maximum oscillation cutoff frequencies of 11 GHz and 21 GHz, respectively.
基金supported by the National Natural Science Foundation of China (Grant No. 61991441)the Strategic Priority Research Program of Chinese Academy of Sciences (Grant No. XDB33000000)Youth Innovation Promotion Association of Chinese Academy of Sciences。
文摘Gallium nitride(GaN) thin film of the nitrogen polarity(N-polar) was grown on C-plane sapphire and misoriented C-plane sapphire substrates respectively by metal-organic chemical vapor deposition(MOCVD). The misorientation angle is off-axis from C-plane toward M-plane of the substrates, and the angle is 2°and 4°respectively. The nitrogen polarity was confirmed by examining the images of the scanning electron microscope before and after the wet etching in potassium hydroxide(KOH) solution. The morphology was studied by the optical microscope and atomic force microscope. The crystalline quality was characterized by the x-ray diffraction. The lateral coherence length, the tilt angle, the vertical coherence length, and the vertical lattice-strain were acquired using the pseudo-Voigt function to fit the x-ray diffraction curves and then calculating with four empirical formulae. The lateral coherence length increases with the misorientation angle, because higher step density and shorter distance between adjacent steps can lead to larger lateral coherence length.The tilt angle increases with the misorientation angle, which means that the misoriented substrate can degrade the identity of crystal orientation of the N-polar GaN film. The vertical lattice-strain decreases with the misorientation angle. The vertical coherence length does not change a lot as the misorientation angle increases and this value of all samples is close to the nominal thickness of the N-polar GaN layer. This study helps to understand the influence of the misorientation angle of misoriented C-plane sapphire on the morphology, the crystalline quality, and the microstructure of N-polar GaN films.
基金Project supported by the National Natural Science Fundation for Excellent Young Scholars of China(Grant No.51422203)the National Natural Science Foundation of China(Grant No.51372001)+1 种基金the Outstanding Youth Foundation of Guangdong Scientific Committee(Grant No.S2013050013882)the Strategic Special Funds for LEDs of Guangdong Province,China(Grant Nos.2011A081301010,2011A081301012,2012A080302002,and 2012A080302004)
文摘A new method for patterned sapphire substrate （PSS） design is developed and proven to be reliable and cost-effective. As progress is made with LEDs＇ luminous efficiency, the pattern units of PSS become more complicated, and the effect of complicated geometrical features is almost impossible to study systematically by experiments only. By employing our new method, the influence of pattern parameters can be systematically studied, and various novel patterns are designed and optimized within a reasonable time span, with great improvement in LEDs＇ light extraction efficiency （LEE）. Clearly, PSS pattern design with such a method deserves particular attention. We foresee that GaN-based LEDs on these newly designed PSSs will achieve more progress in the coming years.
基金Project supported by the National Natural Science Foundation of China (Grant No. 50872128)the Anhui Provincial Natural Science Foundation,China (Grant No. 11040606M64)the Anhui Provincial Natural Science Foundation of Higher Education Institutions,China (Grant No. KJ2010B189)
文摘A method for growing graphene on a sapphire substrate by depositing an SiC buffer layer and then annealing at high temperature in solid source molecular beam epitaxy（SSMBE） equipment was presented.The structural and electronic properties of the samples were characterized by reflection high energy diffraction（RHEED）,X-ray diffraction Φ scans,Raman spectroscopy,and near edge X-ray absorption fine structure（NEXAFS） spectroscopy.The results of the RHEED and Φ scan,as well as the Raman spectra,showed that an epitaxial hexagonal α-SiC layer was grown on the sapphire substrate.The results of the Raman and NEXAFS spectra revealed that the graphene films with the AB Bernal stacking structure were formed on the sapphire substrate after annealing.The layer number of the graphene was between four and five,and the thickness of the unreacted SiC layer was about 1-1.5 nm.
文摘Epitaxiai CeO_2 thin films have ben grown on in situ (1102) sapphire subetrate by planar target rf mag-netron sputtering methed. The CeO_2 thin films have perfect (002) orientation with CeO_2(001)∥Al_2O_3(1102). The X-ray 2θ-θ diffraction, ω scan, Φ scan and electron channelling pattern (ECP) shown that thefilms liave high lattice perfection. The relation of growth conditions and film structure was also studied. Thespudering gas presure and subetrate temperature are the most important parameters preparing fer high qualitybeO_2 films.
基金Project supported by the National Natural Science Foundation of China(Nos.61076052,60906006)the State Key Development Program for Basic Research of China(No.2012CB619303)the National High Technology Research and Development Program of China(No.2011AA050514)
文摘In this paper, the enhanced performance of InGaN/GaN multiple quantum well solar cells grown on patterned sapphire substrates （PSS） was demonstrated. The short-circuit current （Jsc） density of the solar cell grown on PSS showed an improvement of 60%, compared to that of solar cells grown on conventional sapphire substrate. The improved performance is primarily due to the reduction of edge dislocations and the increased light absorption path by the scattering from the textured surface of the PSS. It shows that the patterned sapphire technology can effectively alleviate the problem of high-density dislocations and low Jsc caused by thinner absorption layers of the InGaN based solar cell, and it is promising to improve the efficiency of the solar cell.
基金Project supported by the National High Technology Program of China (No.Y48A040000)
文摘The effect of patterned sapphire substrate（PSS） on the top-surface（P-Ga N-surface） and the bottomsurface（sapphire-surface） of the light output power（LOP） of Ga N-based LEDs was investigated, in order to study the changes in reflection and transmission of the Ga N-sapphire interface. Experimental research and computer simulations were combined to reveal a great enhancement in LOP from either the top or bottom surface of Ga N-based LEDs, which are prepared on patterned sapphire substrates（PSS-LEDs）. Furthermore, the results were compared to those of the conventional LEDs prepared on the planar sapphire substrates（CSS-LEDs）. A detailed theoretical analysis was also presented to further support the explanation for the increase in both the effective reflection and transmission of PSS-Ga N interface layers and to explain the causes of increased LOP values. Moreover, the bottom-surface of the PSS-LED chip shows slightly increased light output performance when compared to that of the top-surface. Therefore, the light extraction efficiency（LEE） can be further enhanced by integrating the method of PSS and flip-chip structure design.
基金supported by the National Key Project of China (No. 2009ZX02037-005)
文摘In this paper, the cone-shaped patterned sapphire substrates (PSS) were etched by an inductively couple plasma with BCl 3 as the reacting gas. The influence of the operating pressure and the RF bias power on subtrenches of the cone-shaped PSS and the formation mechanism of subtrenches were investigated. The profiles of patterns were characterized by FESEM (field emission scanning electron microscope). It showed that the subtrench size varied with the operating pressure and the RF bias power. As the operating pressure increased from 0.2 Pa to 0.9 Pa, the subtrenches changed from narrow and deep to wide and shallow; then to narrower and shallower. When the RF bias power varied from 200 W to 600 W, the subtrenches gradually became noticeable. The FESEM results also indicated that the subtrenches were formed due to the ion scattering effect which was caused by tapered sidewalls and charges accumulation. It is discovered that the scattering effect is closely related with the operating pressure and RF bias power.
基金Supported by the National Natural Science Foundation of China（Nos.61223005, 61376046）, the Program for New Century Excellent Talents in University of China（Nos.NCET-12-0236, NCET-13-0254）, the Science and Technology Developing Project of Jilin Province, China （No.20130204032GX） and the Opening Project of Science and Technology on Reliability Physics and Application Technology of Electronic Component Laboratory in the Fifth Electronics Research Institute of Ministry of Industry and Information Technology of China（No.ZHD201204）.
文摘Cone-shaped patterned sapphire substrate was prepared by inductively coupled plasma etching and GaN nucleation layer was grown on it by metal-organic chemical vapor deposition.A selective growth of GaN nucleation layer was found on the slope of the cone-shaped patterned sapphire substrat,and the distribution morphology of GaN had significantly changed after it was recrystallized.GaN selective growth and redistribution were analyzed by investigating the distribution of crystallographic planes on the cone surface and the atom array of specific planes at atom level.
基金supported by the National Natural Science Foundation of China(No.61006052)the Fundamental Research Funds for the Central Universities(No.K5051325009)
文摘Unintentionally doped AlGaN thin films are grown on c-plane(0001) sapphire substrate by metal-organic chemical vapor deposition, and low-temperature AlN is deposited onto sapphire substrate used as a bu?er layer. AlGaN metal-semiconductor-metal ultraviolet photodetectors with Ni/Au interdigitated contact electrodes are then fabricated by lift-off technology. The dark current of the AlGaN photodetectors is 5.61×10-9 A at 2-V applied bias and the peak response occurrs at 294 nm.
文摘The growth process of three-dimensional growth mode（3D） switching to two-dimensional growth mode （2D） is investigated when GaN films are grown on cone-shaped patterned sapphire substrates by metal-organic chemical vapor deposition.The growth condition of the 3D-2D growth process is optimized to reduce the threading dislocation density（TDD）.It is found that the condition of the 3D layer is critical.The 3D layer keeps growing under the conditions of lowⅤ/Ⅲratio,low temperature,and high pressure until its thickness is comparable to the height of the cone-shaped patterns.Then the 3D layer surrounds the cone-shaped patterns and has inclined side facets and a top（0001） plane.In the following 2D-growth process,inclined side facets coalesce quickly and the interaction of TDs with the side facets causes the TDs to bend over.As a result,the TDD of GaN films can decrease to 1×10~8 cm^（-2）,giving full-width at half maximum values of 211 and 219 arcsec for（002） and（102） omega scans, respectively.
文摘MOCVD-grown 0.25μm gate-length AlGaN/GaN high electron mobility transistors （HEMTs） are fabricated on sapphire substrates. A peak extrinsic transconductance of 250mS/mm and a unity current gain cutoff frequency （fT） of 77GHz are obtained for a 0.25μm gate-length single finger device. These power devices exhibit a maximum drain current density as high as 1.07A/mm. On-chip testing yielded a continuous-wave output power of 27. 04dBm at 8GHz with an associated power-added efficiency of 26. 5% for an 80 × 10μm device.
基金supported by the National Basic Research Program of China(2012CB215500)the National Natural Science Foundation of China(51272296)+1 种基金the Natural Science Foundation of Chongqing(CSTC2012jjA50014)Fundamental Research Funds for the Central Universities(CDJZR12225501,CQDXWL-2013-016)
文摘We differentiated the effects of Cu films deposited on single crystalline a-,r-,and c-plane sapphire substrates upon graphene films synthesized with atmospheric pressure chemical vapor deposition(CVD).The data illustrate that the realization of high-crystalline Cu film is dependent not only on the crystallinity of underlying substrate,but also on the symmetric match of crystallographic geometry between metal film and substrate.We also systematically investigated the effects of PMMA removal on the Raman ID/IG and IG/I2D values of transferred graphene.The results reveal that different PMMA removal methods do not alter the ID/IG values;instead,the residue of PMMA increases the IG/I2D values and the thermal decomposition of PMMA leads to higher IG/I2D values than the removal of PMMA with acetone.The effects of PMMA removal on variations of the Raman spectra are also discussed.
文摘High-quality MgxZn1-xO thin films were grown on sapphire（0001 ） substrates with a ZnO buffer layer of different thicknesses by means of metal-organic chemical vapor deposition. Diethyl zinc, bis-cyclopentadienyl-Mg and oxygen were used as the precursor materials. The crystalline quality, surface morphologies and optical properties of the Mg, Zn1-xO films were investigated by X-ray diffraction, atomic force microscopy and photoluminescence spectrometry. It was shown that the quality of the MgxZn1-xO thin films depends on the thickness of the ZnO buffer layer and an Mg, Zn1-xO thin film with a ZnO buffer layer whose thickness was 20 nm exhibited the best crystal-quality, optical properties and a flat and dense surface.
基金Supported by the National Key Basic Research Programme of China under Grant No 2002CB311900, and the National Natural Science Foundation of China under Grant Nos 10474126 and 10574148.
文摘Canti-bridged epitaxial lateral overgrowth （CBELO） of GaN is performed by metalorganic chemical vapour deposition （MOCVD） on maskless V-grooved sapphire substrates prepared by wet chemical etching with different mesa widths. The wing tilt usually observed in ELO is not found in the CBELO GaN with wide mesa widths, while it can be detected obviously in the GaN with narrow mesa widths. The wing tilt of CBELO GaN grown on a grooved sapphire substrate with narrow mesa can be controlled by adjusting the thickness of the nucleation layer. The dependence of the wing tilt on the nucleation layer thickness is studied. Cross-sectional scanning electron microscopy is used to characterize the geometry of the wing regions, and double crystal x-ray diffraction is used to analyse the structural characteristics and to measure the magnitude of the crystalline wing tilt. It is found that the crystalline wing tilt can be eliminated completely by first growth of a thin nucleation GaN layer then the CBELO GaN. Possible reason and the origin of the wing tilt in CBELO GaN films are also discussed.
基金Project supported by the National Natural Science Foundation of China(Grant No.61334009)the National High Technology Research and Development Program of China(Grant Nos.2015AA03A101 and 2014BAK02B08)+1 种基金China International Science and Technology Cooperation Program(Grant No.2014DFG62280)the"Import Outstanding Technical Talent Plan"and"Youth Innovation Promotion Association Program"of the Chinese Academy of Sciences
文摘Progress with GaN-based light emitting diodes （LEDs） that incorporate nanostructures is reviewed, especially the re- cent achievements in our research group. Nano-patterned sapphire substrates have been used to grow an A1N template layer for deep-ultraviolet （DUV） LEDs. One efficient surface nano-texturing technology, hemisphere-cones-hybrid nanostruc- tures, was employed to enhance the extraction efficiency of InGaN flip-chip LEDs. Hexagonal nanopyramid GaN-based LEDs have been fabricated and show electrically driven color modification and phosphor-free white light emission because of the linearly increased quantum well width and indium incorporation from the shell to the core. Based on the nanostruc- tures, we have also fabricated surface plasmon-enhanced nanoporous GaN-based green LEDs using AAO membrane as a mask. Benefitting from the strong lateral SP coupling as well as good electrical protection by a passivation layer, the EL intensity of an SP-enhanced nanoporous LED was significantly enhanced by 380%. Furthermore, nanostructures have been used for the growth of GaN LEDs on amorphous substrates, the fabrication of stretchable LEDs, and for increasing the 3-dB modulation bandwidth for visible light communication.