New phosphors Sr2ZnSi2O7： M （M=Mn2＋, Tb3＋） were synthesized through solid-state reaction, and their photoluminescent properties under UV and VUV region were investigated. The results showed that Sr2ZnSi2O7：Mn2＋...New phosphors Sr2ZnSi2O7： M （M=Mn2＋, Tb3＋） were synthesized through solid-state reaction, and their photoluminescent properties under UV and VUV region were investigated. The results showed that Sr2ZnSi2O7：Mn2＋ emitted green light with the strongest emission peak centered at 525 nm, and its quenching concentration under 254 and 147 nm excitation occurred at x = 0.08 and 0.06, respectively. Sr2ZnSi2O7： Th3＋ emitted green light with the strongest emission peak centered at 541 nm, and its quenching concentration under 254 and 147 nm excitation also appeared at y = 0.25. At 147 nm excitation, the emission intensities of Sr2Zn0.54Si2O7： 0.06Mn2＋ and Sr1.75ZnSi2O7： 0.25Tb3＋ phosphors were 54% and 36% of that of Zn1.96SiO4：0.04Mn2＋, respectively. And their decay times （τ1/e） were about 3.18 ms and 3.9 ms, respectively.展开更多
Long lasting phosphorescence phosphors with composition of (Sr1–xSmx)2ZnSi2O7 were prepared by conventional high-temperature solid-state method. Their properties were systematically investigated utilizing XRD, photol...Long lasting phosphorescence phosphors with composition of (Sr1–xSmx)2ZnSi2O7 were prepared by conventional high-temperature solid-state method. Their properties were systematically investigated utilizing XRD, photoluminescence, phosphorescence and thermoluminescence spectra. The results showed that these phosphors emitted reddish orange light that corresponds to the characteristic emission due to the 4G5/2→6H5/2, 6H7/2 and 6H9/2 transitions of Sm3+. After the UV light excitation source was switched off, th...展开更多
基金Funded by Key Project of Natural Science for Education Department of Sichuan Province(No.14ZA0102)State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials,Southwest University of Science and Technology,Mianyang
文摘New phosphors Sr2ZnSi2O7： M （M=Mn2＋, Tb3＋） were synthesized through solid-state reaction, and their photoluminescent properties under UV and VUV region were investigated. The results showed that Sr2ZnSi2O7：Mn2＋ emitted green light with the strongest emission peak centered at 525 nm, and its quenching concentration under 254 and 147 nm excitation occurred at x = 0.08 and 0.06, respectively. Sr2ZnSi2O7： Th3＋ emitted green light with the strongest emission peak centered at 541 nm, and its quenching concentration under 254 and 147 nm excitation also appeared at y = 0.25. At 147 nm excitation, the emission intensities of Sr2Zn0.54Si2O7： 0.06Mn2＋ and Sr1.75ZnSi2O7： 0.25Tb3＋ phosphors were 54% and 36% of that of Zn1.96SiO4：0.04Mn2＋, respectively. And their decay times （τ1/e） were about 3.18 ms and 3.9 ms, respectively.
基金Project supported by the National Basic Research Program of China (2007CB935502)
文摘Long lasting phosphorescence phosphors with composition of (Sr1–xSmx)2ZnSi2O7 were prepared by conventional high-temperature solid-state method. Their properties were systematically investigated utilizing XRD, photoluminescence, phosphorescence and thermoluminescence spectra. The results showed that these phosphors emitted reddish orange light that corresponds to the characteristic emission due to the 4G5/2→6H5/2, 6H7/2 and 6H9/2 transitions of Sm3+. After the UV light excitation source was switched off, th...