Direct reduction based on hydrogen metallurgical gas-based shaft furnace is a promising technology for the efficient and low-carbon smelting of vanadium-titanium magnetite.However,in this process,the sticking of pelle...Direct reduction based on hydrogen metallurgical gas-based shaft furnace is a promising technology for the efficient and low-carbon smelting of vanadium-titanium magnetite.However,in this process,the sticking of pellets occurs due to the aggregation of metal-lic iron between the contact surfaces of adjacent pellets and has a serious negative effect on the continuous operation.This paper presents a detailed experimental study of the effect of TiO2 on the sticking behavior of pellets during direct reduction under different conditions.Results showed that the sticking index(SI)decreased linearly with the increasing TiO2 addition.This phenomenon can be attributed to the increase in unreduced FeTiO3 during reduction,leading to a decrease in the number and strength of metallic iron interconnections at the sticking interface.When the TiO2 addition amount was raised from 0 to 15wt%at 1100°C,the SI also increased from 0.71%to 59.91%.The connection of the slag phase could be attributed to the sticking at a low reduction temperature,corresponding to the low sticking strength.Moreover,the interconnection of metallic iron became the dominant factor,and the SI increased sharply with the increase in re-duction temperature.TiO2 had a greater effect on SI at a high reduction temperature than at a low reduction temperature.展开更多
Purpose: Needle-stick injury (NSI) is one of the most potential occupational hazards for healthcare workers because of the transmission of blood-borne pathogens. As per recent data, around 30 lakh healthcare workers s...Purpose: Needle-stick injury (NSI) is one of the most potential occupational hazards for healthcare workers because of the transmission of blood-borne pathogens. As per recent data, around 30 lakh healthcare workers sustain Needle stick injuries each year. This study was conducted to assess healthcare workers’ knowledge, attitude and practices regarding needle stick injury. Materials & Methods: A cross-sectional study was conducted in a Tertiary Care Hospital over the period of 3 months. The study population consisted of Intern Doctors, Post Graduate resident Doctors, Staff Nurses, laboratory technicians of Government Medical College and New Civil Hospital, Surat (n = 300). The data were collected using a self-administered questionnaire via the means of Google Forms. Questionnaire was made with prior review literature. The data obtained were entered and analysed in Microsoft Excel. Results: The prevalence of NSI in our study was 46%, with a higher prevalence among the PG residents (72%). Overall scores regarding knowledge and attitude were better in PG residents (knowledge score > 7 in 71% and Attitude Score > 7 in 68% of PG Residents). Even though the PG residents scored highest in the knowledge category, the majority of them suffered needle stick injuries as a result of poor practice scores. Among those who had NSI (n = 139/300), 70% of study participants had superficial injuries, only 9% reported the incident, 18% got medical attention within 2 hours of the incident, and 7% followed up to recheck their viral markers status. Most incidents of NSI were due to hypodermic needles while recapping needles. Conclusion: Exposure to needle stick injuries and their underreporting remains a common problem. It is imperative that healthcare workers receive regular training on the proper handling of sharp objects. We can also draw the conclusion that preventing NSIs requires putting knowledge into practice.展开更多
Objective: To study the application effect of mouth-opening training sticks combined with oral massage on patients with mouth-opening difficulty after treatment for head and neck cancer. Methods: Using convenient samp...Objective: To study the application effect of mouth-opening training sticks combined with oral massage on patients with mouth-opening difficulty after treatment for head and neck cancer. Methods: Using convenient sampling, 60 patients with mouth-opening difficulty after treatment for head and neck cancer admitted to the Oncology Department from February 2022 to October 2023 were selected for a 2-week exercise and nursing program. The patients were divided into a control group (February 1, 2022 to November 30, 2022) and an observation group (December 1, 2022 to October 31, 2023), with 30 patients in each group. The control group underwent routine mouth-opening functional exercises combined with cork for oral support training, while the observation group underwent routine mouth-opening functional exercises combined with oral massage and mouth-opening training sticks for oral support training. The mouth-opening degree, mouth-opening difficulty level, comfort level, compliance, and quality of life were observed in both groups. Results: Before the intervention, there were no statistically significant differences in mouth-opening degree and mouth-opening difficulty level between the two groups (P > 0.05). After the intervention, the mouth-opening degree, mouth-opening difficulty level, oral comfort level, compliance, and QLICP-HN scores in the observation group were all better than those in the control group, with statistically significant differences (P < 0.05). Conclusion: The combination of mouth-opening training sticks and oral massage with mouth-opening functional exercises can effectively improve the degree of mouth-opening difficulty, enhance oral comfort, increase compliance with mouth-opening exercises, and improve quality of life.展开更多
Drying is a complicated physical process which involves simultaneous heat and mass transfer in the removal of solvents inside propellants.Inappropriate drying techniques may result in the formation of a hard skin laye...Drying is a complicated physical process which involves simultaneous heat and mass transfer in the removal of solvents inside propellants.Inappropriate drying techniques may result in the formation of a hard skin layer near the surface to block the free access of most solvent through for long stick propellants with large web thickness,which lead to lower drying efficiency and worse drying quality.This study aims to gain a comprehensive understanding of drying process and clarify the mechanism of the blocked layer near the propellant surface.A new three-dimensional coupled heat and mass transfer(3D-CHMT)model was successfully developed under transient conditions.The drying experiment results show that the 3DCHMT model could be applied to describe the drying process well since the relative error of the content of solvent between simulation and experiment values is only 5.5%.The solvent behavior simulation demonstrates that the mass transfer process can be divided into super-fast(SF)and subsequent minorfast(MF)stages,and the SF stage is vital to the prevention of the blocked layer against the free access for solvent molecules inside propellant grains.The effective solvent diffusion coefficient(Deff)of the propellant surface initially increases from 3.4×10^(-6)to 5.3×10^(-6)m^(2)/s as the temperature increases,and then decreases to 4.1×10^(-8)m^(2)/s at 60-100 min.The value of Deffof surface between 0-1.4 mm has a unique trend of change compared with other regions,and it is much lower than that of the internal at100 min under simulation conditions.Meanwhile,the temperature of the propellant surface increases rapidly at the SF stage(0-100 min)and then very slowly thereafter.Both the evolution of Deffand temperature distribution demonstrate that the blocked layer near the propellant surface has been formed in the time period of approximately 0-100 min and its thickness is about 1.4 mm.To mitigate the formation of blocked layer and improve its drying quality of finial propellant products effectively,it should be initially dried at lower drying temperature(30-40℃)in 0-100 min and then dried at higher drying temperature(50-60℃)to reduce drying time for later drying process in double base gun propellants.The present results can provide theoretical guidance for drying process and optimization of drying parameters for long stick propellants with large web thickness.展开更多
Sticking is the most serious cause of failure in complex drilling operations.In the present work a novel“early warning”method based on an artificial intelligence algorithm is proposed to overcome some of the known pr...Sticking is the most serious cause of failure in complex drilling operations.In the present work a novel“early warning”method based on an artificial intelligence algorithm is proposed to overcome some of the known pro-blems associated with existing sticking-identification technologies.The method is tested against a practical case study(Southern Sichuan shale gas drilling operations).It is shown that the twelve sets of sticking fault diagnostic results obtained from a simulation are all consistent with the actual downhole state;furthermore,the results from four groups of verification samples are also consistent with the actual downhole state.This shows that the pro-posed training-based model can effectively be applied to practical situations.展开更多
In the paper, the effects of linear expansion coefficient and basic index of melting slag on the detachability of self shielded flux cored electrode (SSFCE) are investigated. An equation is obtained on the principles ...In the paper, the effects of linear expansion coefficient and basic index of melting slag on the detachability of self shielded flux cored electrode (SSFCE) are investigated. An equation is obtained on the principles of ceramics and mineralography which predict the detachability of basic SSFCE. In addition, stick slag mechanism of SSFCE is analyzed.展开更多
The effects of rice transplanters＇ transplanting settings（plant spacing and finger sticking area） on rice yield were investigated in two early-season rice cultivars：hybrid rice cultivar（Zhuliangyou 819） and conv...The effects of rice transplanters＇ transplanting settings（plant spacing and finger sticking area） on rice yield were investigated in two early-season rice cultivars：hybrid rice cultivar（Zhuliangyou 819） and conventional rice cultivar（Zhongjiazao 17）.The results showed that,different transplanting settings resulted in different numbers of transplanted basic seedlings,and the rice yield was significantly correlated with the number of transplanted basic seedlings.The number of transplanted basic seedlings increased with the decrease of plant spacing and the increase of finger sticking area.The rate of lost hills of machine transplanting decreased with the increase of finger sticking area.The leaf area index and amount of dry matter accumulation were highly correlated with the number of transplanted basic seedlings.The average yield of the rice transplanted with a plant spacing of11.5 cm was higher than that with a plant spacing of 13.8 cm.In the field transplanted with the rice under the plant spacing of 13.8 cm,the rice yield increased with the increase of finger sticking area,and the finger sticking area of 2.23 cm2 showed the highest rice yield of 8 174.16 kg/hm2 of Zhuliangyou 819 and 7 925.54kg/hm2 of Zhongjiaozao17.In the field transplanted with the rice under the plant spacing of 11.5 cm,the rice yield was the highest with the finger sticking area of 1.83 cm2,and then decreased with the large finger sticking area.Under the plant spacing of 11.5 cm,the highest rice yields of Zhuliangyou 819 and Zhongjiaozao17 were 8 492.94 kg/hm2 and 8 000.23 kg/hm2,respectively.Therefore,the preferred machine transplanting settings for double-season early rice are a plant spacing of11.5 cm and a finger sticking area of 1.83 cm2,while the finger sticking area should be increased to 2.23 cm2 for conventional rice cultivars.展开更多
This paper makes use of the method of testing and measuring the human body tibia by using2-D moire interferometry of sticking film. hased on the J'--y direction moire patterns recorded synchronously by 2-D optical...This paper makes use of the method of testing and measuring the human body tibia by using2-D moire interferometry of sticking film. hased on the J'--y direction moire patterns recorded synchronously by 2-D optical path,the elastic constant,strain and displacement of the tibia are measured.Compared with the electric measuring method the error is samll and the sensitivity is high.展开更多
Of 149 cases.infantile diarrhea were treated with Zhou’s multiapplied rapid-sticking herbomoxa-pen.The main acupoints selected were Auriculoapex,Tianshu(ST 25),Zusanli(ST 36),Shenshu(BL 23),etc.TWO groups were observ...Of 149 cases.infantile diarrhea were treated with Zhou’s multiapplied rapid-sticking herbomoxa-pen.The main acupoints selected were Auriculoapex,Tianshu(ST 25),Zusanli(ST 36),Shenshu(BL 23),etc.TWO groups were observed,32 cases from the 149 cases as therapid-sticking moxatherapy(RSMT)group who suffered from the acute diarrhea without any thera-peutics before,and the other 35 cases with western medicine as the control group.Results showedthat the recovering rate and the average therapeutic course of healing in RSMT group were higher andshorter than that in control one(P【0.05;P【0.01),even without marked difference of the total ef-fective rates between the two groups(P】0.05).Of 149 cases with RSMT,the therapeutic effect onacute ones was better than those on delayed and chronic ones(P【0.05),yet the difference was notmarked in therapeutic effects between the etiological causes of infections and non-infections(P】 0.0.5).It is therefore worthy of popularizing RSMT due to its remarked curative results without anyside-effect,simply-manipulated and well-accepted features.展开更多
The sticking phenomenon during hot rolling of SUS 430 ferritic stainless steel was investigated by means of a two-disc type high-temperature wear tester. The test results indicate that sticking particles on the surfac...The sticking phenomenon during hot rolling of SUS 430 ferritic stainless steel was investigated by means of a two-disc type high-temperature wear tester. The test results indicate that sticking particles on the surfaces of high chromium steel （HiCr） and high-speed steel （HSS） rolls undergo nucleation, growth, and saturation stages. Grooves on the roll surface generated by grinding provide nucleation sites for sticking particles. The number of sticking particles on the HiCr roll surface is greater than that on the HSS roll surface. The average surface roughnesses （Ra） of HiCr and HSS rolls change from 0.502 and 0.493 μm at the initial stage to 0.837 and 0.530 μm at the saturation stage, respectively. The test further proves that the sticking behavior is strongly dependent on roll materials, and the HSS roll is more benefi- cial to prevent particles sticking compared with the HiCr roll under the same hot-rolling conditions.展开更多
AIM: To assess the value of a new test for the diagnosis of Helicobacter pylori (H. pylori) infection, Rapirun<sup>®</sup>H. pylori Antibody Stick (Rapirun<sup>®</sup> S...AIM: To assess the value of a new test for the diagnosis of Helicobacter pylori (H. pylori) infection, Rapirun<sup>®</sup>H. pylori Antibody Stick (Rapirun<sup>®</sup> Stick), in a Vietnamese population.展开更多
A series of reduction experiments of iron ore pellets with hydrogen,carbon monoxide and their mixture were carried out in a laboratory scale shaft furnace.The sticking behavior accompanying reduction of iron ore pelle...A series of reduction experiments of iron ore pellets with hydrogen,carbon monoxide and their mixture were carried out in a laboratory scale shaft furnace.The sticking behavior accompanying reduction of iron ore pellets was investigated.And morphology of the sticking interface forming during reduction was analyzed by SEM equipped with EDS.In order to evaluate the effects of the temperature and gas composition on sticking properties,reduction of iron ore pellets were conducted at 800-1000 ℃.The results show that the sticking strength of the pellets increases with temperature,however,decreases with hydrogen content in reducing gas.For an efficient shaft furnace operation in direct reduction(DR),relative prevention of sticking such as coating of pellets was also developed to solve sticking problem.The results show that CaO is a suitable material for the coating method.展开更多
基金the National Natural Science Foundation of China(No.51904063)the Science and Technology Plan Project of Liaoning Province,China(No.2022JH24/10200027)+1 种基金the Key Research and Development Project of Hebei Province,China(No.21314001D)the seventh batch of the Ten Thousand Talents Plan(No.ZX20220553).
文摘Direct reduction based on hydrogen metallurgical gas-based shaft furnace is a promising technology for the efficient and low-carbon smelting of vanadium-titanium magnetite.However,in this process,the sticking of pellets occurs due to the aggregation of metal-lic iron between the contact surfaces of adjacent pellets and has a serious negative effect on the continuous operation.This paper presents a detailed experimental study of the effect of TiO2 on the sticking behavior of pellets during direct reduction under different conditions.Results showed that the sticking index(SI)decreased linearly with the increasing TiO2 addition.This phenomenon can be attributed to the increase in unreduced FeTiO3 during reduction,leading to a decrease in the number and strength of metallic iron interconnections at the sticking interface.When the TiO2 addition amount was raised from 0 to 15wt%at 1100°C,the SI also increased from 0.71%to 59.91%.The connection of the slag phase could be attributed to the sticking at a low reduction temperature,corresponding to the low sticking strength.Moreover,the interconnection of metallic iron became the dominant factor,and the SI increased sharply with the increase in re-duction temperature.TiO2 had a greater effect on SI at a high reduction temperature than at a low reduction temperature.
文摘Purpose: Needle-stick injury (NSI) is one of the most potential occupational hazards for healthcare workers because of the transmission of blood-borne pathogens. As per recent data, around 30 lakh healthcare workers sustain Needle stick injuries each year. This study was conducted to assess healthcare workers’ knowledge, attitude and practices regarding needle stick injury. Materials & Methods: A cross-sectional study was conducted in a Tertiary Care Hospital over the period of 3 months. The study population consisted of Intern Doctors, Post Graduate resident Doctors, Staff Nurses, laboratory technicians of Government Medical College and New Civil Hospital, Surat (n = 300). The data were collected using a self-administered questionnaire via the means of Google Forms. Questionnaire was made with prior review literature. The data obtained were entered and analysed in Microsoft Excel. Results: The prevalence of NSI in our study was 46%, with a higher prevalence among the PG residents (72%). Overall scores regarding knowledge and attitude were better in PG residents (knowledge score > 7 in 71% and Attitude Score > 7 in 68% of PG Residents). Even though the PG residents scored highest in the knowledge category, the majority of them suffered needle stick injuries as a result of poor practice scores. Among those who had NSI (n = 139/300), 70% of study participants had superficial injuries, only 9% reported the incident, 18% got medical attention within 2 hours of the incident, and 7% followed up to recheck their viral markers status. Most incidents of NSI were due to hypodermic needles while recapping needles. Conclusion: Exposure to needle stick injuries and their underreporting remains a common problem. It is imperative that healthcare workers receive regular training on the proper handling of sharp objects. We can also draw the conclusion that preventing NSIs requires putting knowledge into practice.
文摘Objective: To study the application effect of mouth-opening training sticks combined with oral massage on patients with mouth-opening difficulty after treatment for head and neck cancer. Methods: Using convenient sampling, 60 patients with mouth-opening difficulty after treatment for head and neck cancer admitted to the Oncology Department from February 2022 to October 2023 were selected for a 2-week exercise and nursing program. The patients were divided into a control group (February 1, 2022 to November 30, 2022) and an observation group (December 1, 2022 to October 31, 2023), with 30 patients in each group. The control group underwent routine mouth-opening functional exercises combined with cork for oral support training, while the observation group underwent routine mouth-opening functional exercises combined with oral massage and mouth-opening training sticks for oral support training. The mouth-opening degree, mouth-opening difficulty level, comfort level, compliance, and quality of life were observed in both groups. Results: Before the intervention, there were no statistically significant differences in mouth-opening degree and mouth-opening difficulty level between the two groups (P > 0.05). After the intervention, the mouth-opening degree, mouth-opening difficulty level, oral comfort level, compliance, and QLICP-HN scores in the observation group were all better than those in the control group, with statistically significant differences (P < 0.05). Conclusion: The combination of mouth-opening training sticks and oral massage with mouth-opening functional exercises can effectively improve the degree of mouth-opening difficulty, enhance oral comfort, increase compliance with mouth-opening exercises, and improve quality of life.
基金supported by the National Natural Science Foundation of China(Grant No.22075146)。
文摘Drying is a complicated physical process which involves simultaneous heat and mass transfer in the removal of solvents inside propellants.Inappropriate drying techniques may result in the formation of a hard skin layer near the surface to block the free access of most solvent through for long stick propellants with large web thickness,which lead to lower drying efficiency and worse drying quality.This study aims to gain a comprehensive understanding of drying process and clarify the mechanism of the blocked layer near the propellant surface.A new three-dimensional coupled heat and mass transfer(3D-CHMT)model was successfully developed under transient conditions.The drying experiment results show that the 3DCHMT model could be applied to describe the drying process well since the relative error of the content of solvent between simulation and experiment values is only 5.5%.The solvent behavior simulation demonstrates that the mass transfer process can be divided into super-fast(SF)and subsequent minorfast(MF)stages,and the SF stage is vital to the prevention of the blocked layer against the free access for solvent molecules inside propellant grains.The effective solvent diffusion coefficient(Deff)of the propellant surface initially increases from 3.4×10^(-6)to 5.3×10^(-6)m^(2)/s as the temperature increases,and then decreases to 4.1×10^(-8)m^(2)/s at 60-100 min.The value of Deffof surface between 0-1.4 mm has a unique trend of change compared with other regions,and it is much lower than that of the internal at100 min under simulation conditions.Meanwhile,the temperature of the propellant surface increases rapidly at the SF stage(0-100 min)and then very slowly thereafter.Both the evolution of Deffand temperature distribution demonstrate that the blocked layer near the propellant surface has been formed in the time period of approximately 0-100 min and its thickness is about 1.4 mm.To mitigate the formation of blocked layer and improve its drying quality of finial propellant products effectively,it should be initially dried at lower drying temperature(30-40℃)in 0-100 min and then dried at higher drying temperature(50-60℃)to reduce drying time for later drying process in double base gun propellants.The present results can provide theoretical guidance for drying process and optimization of drying parameters for long stick propellants with large web thickness.
基金The project is supported by CNPC Key Core Technology Research Projects(2022ZG06)received by Qing Wangproject funded by China Postdoctoral Science Foundation(2021M693508)received by Qing Wang.Basic Research and Strategic Reserve Technology Research Fund Project of Institutes directly under CNPC received by Qing Wang.
文摘Sticking is the most serious cause of failure in complex drilling operations.In the present work a novel“early warning”method based on an artificial intelligence algorithm is proposed to overcome some of the known pro-blems associated with existing sticking-identification technologies.The method is tested against a practical case study(Southern Sichuan shale gas drilling operations).It is shown that the twelve sets of sticking fault diagnostic results obtained from a simulation are all consistent with the actual downhole state;furthermore,the results from four groups of verification samples are also consistent with the actual downhole state.This shows that the pro-posed training-based model can effectively be applied to practical situations.
文摘In the paper, the effects of linear expansion coefficient and basic index of melting slag on the detachability of self shielded flux cored electrode (SSFCE) are investigated. An equation is obtained on the principles of ceramics and mineralography which predict the detachability of basic SSFCE. In addition, stick slag mechanism of SSFCE is analyzed.
文摘The effects of rice transplanters＇ transplanting settings（plant spacing and finger sticking area） on rice yield were investigated in two early-season rice cultivars：hybrid rice cultivar（Zhuliangyou 819） and conventional rice cultivar（Zhongjiazao 17）.The results showed that,different transplanting settings resulted in different numbers of transplanted basic seedlings,and the rice yield was significantly correlated with the number of transplanted basic seedlings.The number of transplanted basic seedlings increased with the decrease of plant spacing and the increase of finger sticking area.The rate of lost hills of machine transplanting decreased with the increase of finger sticking area.The leaf area index and amount of dry matter accumulation were highly correlated with the number of transplanted basic seedlings.The average yield of the rice transplanted with a plant spacing of11.5 cm was higher than that with a plant spacing of 13.8 cm.In the field transplanted with the rice under the plant spacing of 13.8 cm,the rice yield increased with the increase of finger sticking area,and the finger sticking area of 2.23 cm2 showed the highest rice yield of 8 174.16 kg/hm2 of Zhuliangyou 819 and 7 925.54kg/hm2 of Zhongjiaozao17.In the field transplanted with the rice under the plant spacing of 11.5 cm,the rice yield was the highest with the finger sticking area of 1.83 cm2,and then decreased with the large finger sticking area.Under the plant spacing of 11.5 cm,the highest rice yields of Zhuliangyou 819 and Zhongjiaozao17 were 8 492.94 kg/hm2 and 8 000.23 kg/hm2,respectively.Therefore,the preferred machine transplanting settings for double-season early rice are a plant spacing of11.5 cm and a finger sticking area of 1.83 cm2,while the finger sticking area should be increased to 2.23 cm2 for conventional rice cultivars.
文摘This paper makes use of the method of testing and measuring the human body tibia by using2-D moire interferometry of sticking film. hased on the J'--y direction moire patterns recorded synchronously by 2-D optical path,the elastic constant,strain and displacement of the tibia are measured.Compared with the electric measuring method the error is samll and the sensitivity is high.
文摘Of 149 cases.infantile diarrhea were treated with Zhou’s multiapplied rapid-sticking herbomoxa-pen.The main acupoints selected were Auriculoapex,Tianshu(ST 25),Zusanli(ST 36),Shenshu(BL 23),etc.TWO groups were observed,32 cases from the 149 cases as therapid-sticking moxatherapy(RSMT)group who suffered from the acute diarrhea without any thera-peutics before,and the other 35 cases with western medicine as the control group.Results showedthat the recovering rate and the average therapeutic course of healing in RSMT group were higher andshorter than that in control one(P【0.05;P【0.01),even without marked difference of the total ef-fective rates between the two groups(P】0.05).Of 149 cases with RSMT,the therapeutic effect onacute ones was better than those on delayed and chronic ones(P【0.05),yet the difference was notmarked in therapeutic effects between the etiological causes of infections and non-infections(P】 0.0.5).It is therefore worthy of popularizing RSMT due to its remarked curative results without anyside-effect,simply-manipulated and well-accepted features.
文摘The sticking phenomenon during hot rolling of SUS 430 ferritic stainless steel was investigated by means of a two-disc type high-temperature wear tester. The test results indicate that sticking particles on the surfaces of high chromium steel （HiCr） and high-speed steel （HSS） rolls undergo nucleation, growth, and saturation stages. Grooves on the roll surface generated by grinding provide nucleation sites for sticking particles. The number of sticking particles on the HiCr roll surface is greater than that on the HSS roll surface. The average surface roughnesses （Ra） of HiCr and HSS rolls change from 0.502 and 0.493 μm at the initial stage to 0.837 and 0.530 μm at the saturation stage, respectively. The test further proves that the sticking behavior is strongly dependent on roll materials, and the HSS roll is more benefi- cial to prevent particles sticking compared with the HiCr roll under the same hot-rolling conditions.
基金Supported by International Collaborative Research Grant of the Japanese Society of Gastrointestinal Cancer Screening
文摘AIM: To assess the value of a new test for the diagnosis of Helicobacter pylori (H. pylori) infection, Rapirun<sup>®</sup>H. pylori Antibody Stick (Rapirun<sup>®</sup> Stick), in a Vietnamese population.
基金Project(50725416)supported by the National Natural Science Foundation for Distinguished Young Scholars of China
文摘A series of reduction experiments of iron ore pellets with hydrogen,carbon monoxide and their mixture were carried out in a laboratory scale shaft furnace.The sticking behavior accompanying reduction of iron ore pellets was investigated.And morphology of the sticking interface forming during reduction was analyzed by SEM equipped with EDS.In order to evaluate the effects of the temperature and gas composition on sticking properties,reduction of iron ore pellets were conducted at 800-1000 ℃.The results show that the sticking strength of the pellets increases with temperature,however,decreases with hydrogen content in reducing gas.For an efficient shaft furnace operation in direct reduction(DR),relative prevention of sticking such as coating of pellets was also developed to solve sticking problem.The results show that CaO is a suitable material for the coating method.