The parasitic hydrogen evolution reaction(HER)in the negative half-cell of vanadium redox flow batteries(VRFBs)causes severe efficiency losses.Thus,a deeper understanding of this process and the accompanying bubble fo...The parasitic hydrogen evolution reaction(HER)in the negative half-cell of vanadium redox flow batteries(VRFBs)causes severe efficiency losses.Thus,a deeper understanding of this process and the accompanying bubble formation is crucial.This benchmarking study locally analyzes the bubble distribution in thick,porous electrodes for the first time using deep learning-based image segmentation of synchrotron X-ray micro-tomograms.Each large three-dimensional data set was processed precisely in less than one minute while minimizing human errors and pointing out areas of increased HER activity in VRFBs.The study systematically varies the electrode potential and material,concluding that more negative electrode potentials of-200 m V vs.reversible hydrogen electrode(RHE)and lower cause more substantial bubble formation,resulting in bubble fractions of around 15%–20%in carbon felt electrodes.Contrarily,the bubble fractions stay only around 2%in an electrode combining carbon felt and carbon paper.The detected areas with high HER activity,such as the border subregion with more than 30%bubble fraction in carbon felt electrodes,the cutting edges,and preferential spots in the electrode bulk,are potential-independent and suggest that larger electrodes with a higher bulk-to-border ratio might reduce HER-related performance losses.The described combination of electrochemical measurements,local X-ray microtomography,AI-based segmentation,and 3D morphometric analysis is a powerful and novel approach for local bubble analysis in three-dimensional porous electrodes,providing an essential toolkit for a broad community working on bubble-generating electrochemical systems.展开更多
Pseudocapacitive materials that store charges via reversible surface or near-surface faradaic reactions are capable of overcoming the capacity limitations of electrical double-layer capacitors.Revealing the structure...Pseudocapacitive materials that store charges via reversible surface or near-surface faradaic reactions are capable of overcoming the capacity limitations of electrical double-layer capacitors.Revealing the structure–activity relationship between the microstructural features of pseudocapacitive materials and their electrochemical performance on the atomic scale is the key to build high-performance capacitor-type devices containing ideal pseudocapacitance effect.Currently,the high brightness(flux),and spectral and coherent nature of synchrotron X-ray analytical techniques make it a powerful tool for probing the structure–property relationship of pseudocapacitive materials.Herein,we report a comprehensive and systematic review of four typical characterization techniques(synchrotron X-ray diffraction,pair distribution function[PDF]analysis,soft X-ray absorption spectroscopy,and hard X-ray absorption spectroscopy)for the study of pseudocapacitance mechanisms.In addition,we offered significant insights for understanding and identifying pseudocapacitance mechanisms(surface redox pseudocapacitance,intercalation pseudocapacitance,and the extrinsic pseudocapacitance phenomenon in battery materials)by combining in situ hard XAS and electrochemical analyses.Finally,a perspective for further depth of understanding into the pseudocapacitance mechanism using synchrotron X-ray analytical techniques is proposed.展开更多
The unit-cell parameters and volumes of geikielite(MgTiO_(3))and ilmenite(FeTiO_(3))were investigated at high temperatures up to 700 K and ambient pressure,using in-situ angle-dispersive synchrotron X-ray diffraction....The unit-cell parameters and volumes of geikielite(MgTiO_(3))and ilmenite(FeTiO_(3))were investigated at high temperatures up to 700 K and ambient pressure,using in-situ angle-dispersive synchrotron X-ray diffraction.No phase transition was detected over the experimental temperature range.Using(Berman in J Petrol29:445-522,1988.10.1093/petrology/29.2.445)equations to fit the temperature-volume data,the volumetric thermal expansion coefficients at ambient conditions(α_(V0))of MgTiO_(3) and FeTiO_(3) were obtained as follows:2.55(6)×10^(-5)K^(-1)and 2.82(10)×10^(-5)K^(-1),respectively.We infer that the larger effective ionic radius of Fe^(2+)(Ⅵ)(0.78 A)than that of Mg^(2+)(Ⅵ)(0.72?)renders FeTiO_(3)has a larger volumetric thermal expansivity than MgTiO_(3).Simultaneously,the refined axial thermal expansion coefficients under ambient conditions areα_(a0)=0.74(3)×10^(-5)K^(-1)andα_(c0)=1.08(5)×10^(-5)K^(-1)for the aaxis and c-axis of MgTiO_(3),respectively,andα_(a0)=0.95(5)×10^(-5)K^(-1)andα_(c0)=0.92(12)×10^(-5)K^(-1)for the aaxis and c-axis of FeTiO_(3),respectively.The axial thermal expansivity of MgTiO_(3) is anisotropic,but that of FeTiO_(3) is nearly isotropic.We infer that the main reason for the different axial thermal expansivity between MgTiO_(3) and FeTiO_(3) is that the thermal expansion mode of the Mg-O bond in MgTiO_(3) is different from that of the Fe-O bonds in FeTiO_(3).展开更多
The load partitioning between the magnesium and titanium phases in an extruded Mg-15%Ti(vol.%) composite from room temperature up to 300 ℃ using synchrotron radiation diffraction during in-situ compression tests. Dur...The load partitioning between the magnesium and titanium phases in an extruded Mg-15%Ti(vol.%) composite from room temperature up to 300 ℃ using synchrotron radiation diffraction during in-situ compression tests. During compression, the magnesium matrix composite deforms mainly by the activation of the extension twinning system up to 200 ℃. The volume fraction of twins increases with the plastic strain but decrease with the compression temperature. Hard titanium particles bear an additional load transferred by the soft magnesium matrix from room temperature up to 300 ℃. This effect is amplified after yield stress during plastic deformation. Additionally, twins within magnesium grains behaves as an additional reinforcement at low temperature(below 200 ℃) inducing an increase in the work hardening of the composite.展开更多
Because of its excellent dose distribution,proton therapy is becoming increasingly popular in the medical application of cancer treatment.A synchrotron-based proton therapy facility was designed and constructed in Sha...Because of its excellent dose distribution,proton therapy is becoming increasingly popular in the medical application of cancer treatment.A synchrotron-based proton therapy facility was designed and constructed in Shanghai.The synchrotron,beam delivery system,and other technical systems were commissioned and reached their expected performances.After a clinical trial of 47 patients was finished,the proton therapy facility obtained a registration certificate from the National Medical Products Administration.The characteristics of the accelerator and treatment systems are described in this article.展开更多
Transition metal sulfides have been regarded as promising anode materials for sodium-ion batteries(SIB).However,they face the challenges of poor electronic conductivity and large volume change,which result in capacity...Transition metal sulfides have been regarded as promising anode materials for sodium-ion batteries(SIB).However,they face the challenges of poor electronic conductivity and large volume change,which result in capacity fade and low rate capability.In this work,a composite containing ultrasmall CoS(~7 nm)nanoparticles embedded in heteroatom(N,S,and O)-doped carbon was synthesized by an efficient one-step sulfidation process using a Co(Salen)precursor.The ultrasmall CoS nanoparticles are beneficial for mechanical stability and shortening Na-ions diffusion pathways.Furthermore,the N,S,and O-doped defect-rich carbon provides a robust and highly conductive framework enriched with active sites for sodium storage as well as mitigates volume expansion and polysulfide shuttle.As anode for SIB,CoS@HDC exhibits a high initial capacity of 906 mA h g^(-1)at 100 mA g^(-1)and a stable long-term cycling life with over 1000 cycles at 500 mA g^(-1),showing a reversible capacity of 330 mA h g^(-1).Meanwhile,the CoS@HDC anode is proven to maintain its structural integrity and compositional reversibility during cycling.Furthermore,Na-ion full batteries based on the CoS@HDC anode and Na_(3)V_(2)(PO_(4))_(3)cathode demonstrate a stable cycling behavior with a reversible specific capacity of~200 m A h g^(-1)at least for 100 cycles.Moreover,advanced synchrotron operando X-ray diffraction,ex-situ X-ray absorption spectroscopy,and comprehensive electrochemical tests reveal the structural transformation and the Co coordination chemistry evolution of the CoS@HDC during cycling,providing fundamental insights into the sodium storage mechanism.展开更多
The relative intensities of L-subshell x-ray fluorescence(XRF)for elements with atomic numbers 62≤Z≤83 were measured at two excitation energies,18 keV and 23 keV,using a synchrotron radiation source at a beamline of...The relative intensities of L-subshell x-ray fluorescence(XRF)for elements with atomic numbers 62≤Z≤83 were measured at two excitation energies,18 keV and 23 keV,using a synchrotron radiation source at a beamline of the Synchrotron Light Center for Experimental Science and Applications in the Middle East(SESAME),Jordan.The experimentally measured results of the relative intensities were compared with the calculated results using the subshell fluorescence yield and the Coster-Kronig transition probabilities recommended by Campbell and the values based on the Dirac-Hartree-Slater model by Puri.The experimental and theoretical results are in agreement.In this work,L XRF relative intensities for the elements Sm,Gd,Tb,Er,Ta,W,Re,Hg,Pb and Bi at energies of 18 keV and 23 keV were measured.展开更多
BL10U2 is an undulator-based macromolecular crystallography(MX)beamline located at the 3.5-GeV Shanghai Synchrotron Radiation Facility.BL10U2 is specifically designed for conducting routine and biosafety level-2(BSL-2...BL10U2 is an undulator-based macromolecular crystallography(MX)beamline located at the 3.5-GeV Shanghai Synchrotron Radiation Facility.BL10U2 is specifically designed for conducting routine and biosafety level-2(BSL-2)MX experiments utilizing high-flux tunable X-rays with energies from 7 to 18 keV,providing a beam spot size of 20μm(horizontal)×10μm(vertical)at the sample point.Certification by the Shanghai Pudong Municipal Health Commission confirmed the capability to perform BSL-2 MX experiments.The beamline is currently equipped with an Eiger X 16 M detector and two newly developed in-house high-precision diffractometers that can be switched to perform conventional or in situ crystal diffraction experiments.An automatic sample changer developed in-house allows fast sample exchange in less than 30 s,supporting high-throughput MX experimentation and rapid crystal screening.Data collection from both the diffractometer and detector was controlled by an in-house developed data collection software(Finback)with a user-friendly interface for convenient operation.This study presents a comprehensive overview of the facilities,experimental methods,and performance characteristics of the BL10U2 beamline.展开更多
The purpose of this study was to design a rapid-cycling synchrotron, making it capable of proton beam ultrahigh dose rate irradiation, inspired by laser accelerators. The design had to be cheap and simple. We consider...The purpose of this study was to design a rapid-cycling synchrotron, making it capable of proton beam ultrahigh dose rate irradiation, inspired by laser accelerators. The design had to be cheap and simple. We consider our design from six aspects: the lattice, injection, extraction, space charge effects, eddy current effects and energy switching. Efficiency and particle quantity must be addressed when injected. The space charge effects at the injection could affect particles' number. The eddy current effects in the vacuum chambers would affect the magnetic field itself and generate heat, all of which need to be taken into account. Fast extraction can obtain 10^(10) protons/pulse, equal to instantaneous dose rate up to 10~7 Gy/s in a very short time, while changing various extraction energies rapidly and easily to various deposition depths. In the further research, we expect to combine a delivery system with this accelerator to realize the FLASH irradiation.展开更多
Macromolecular crystallography beamline BL17U1 at the Shanghai Synchrotron Radiation Facility has been relocated,upgraded,and given a new ID(BL02U1).It now delivers X-rays in the energy range of 6–16 keV,with a focus...Macromolecular crystallography beamline BL17U1 at the Shanghai Synchrotron Radiation Facility has been relocated,upgraded,and given a new ID(BL02U1).It now delivers X-rays in the energy range of 6–16 keV,with a focused beam of 11.6μm×4.8μm and photon flux greater than 1012 phs/s.The high credibility and stability of the beam and good timing synchronization of the equipment significantly improve the experimental efficiency.Since June 2021,when it officially opened to users,over 4200 h of beamtime have been provided to over 200 research groups to collect data at the beamline.Its good performance and stable operation have led to the resolution of several structures based on data collected at the beamline.展开更多
From a safety point of view, it is important to study the damages and reliability of molten salt reactor structural alloy materials, which are subjected to extreme environments due to neutron irradiation, molten salt ...From a safety point of view, it is important to study the damages and reliability of molten salt reactor structural alloy materials, which are subjected to extreme environments due to neutron irradiation, molten salt corrosion, fission product attacks, thermal stress, and even combinations of these. In the past few years, synchrotron radiation-based materials characterization techniques have proven to be effective in revealing the microstructural evolution and failure mechanisms of the alloys under surrogating operation conditions. Here, we review the recent progress in the investigations of molten salt corrosion,tellurium(Te) corrosion, and alloy design. The valence states and distribution of chromium(Cr) atoms, and the diffusion and local atomic structure of Te atoms near the surface of corroded alloys have been investigated using synchrotron radiation techniques, which considerably deepen the understandings on the molten salt and Te corrosion behaviors. Furthermore, the structure and size distribution of the second phases in the alloys have been obtained, which are helpful for the future development of new alloy materials.展开更多
The protein complex crystallographic beamline BL19U1 at the Shanghai Synchrotron Radiation Facility is one of the five beamlines dedicated to protein sciences operated by National Facility for Protein Science(Shanghai...The protein complex crystallographic beamline BL19U1 at the Shanghai Synchrotron Radiation Facility is one of the five beamlines dedicated to protein sciences operated by National Facility for Protein Science(Shanghai,China).The beamline,which features a small-gap invacuum undulator,has been officially open to users since March 2015.This beamline delivers X-ray in the energy range 7–15 keV.With its high flux,low divergence beam and a large active area detector,BL19U1 is designed for proteins with large molecular weight and large crystallographic unit cell dimensions.Good performance and stable operation of the beamline have allowed the number of Protein Data Bank(PDB)depositions and the number of articles published based on data collected at this beamline to increase steadily.To date,over 300 research groups have collected data at the beamline.More than 600 PDB entries have been deposited at the PDB(www.pdb.org).More than 300 papers have been published that include data collected at the beamline,including 21 research articles published in the top-level journals Cell,Nature,and Science.展开更多
Beam lifetime is dominated by Touschek scattering at the Shanghai Synchrotron Radiation Facility(SSRF).Touschek loss rate is affected by probability for scattering beyond the RF acceptance and the volume charge densit...Beam lifetime is dominated by Touschek scattering at the Shanghai Synchrotron Radiation Facility(SSRF).Touschek loss rate is affected by probability for scattering beyond the RF acceptance and the volume charge density of the bench.In the phaseⅡupgrade of the SSRF,a third harmonic superconducting cavity will be used to enhance the Touschek lifetime by lengthening the bunches.The Touschek lifetime improvement factor is affected by the voltage of a harmonic cavity.To stabilize the cavity voltage,a tuning control system was designed to control it.The design of the tuning control system was based on the SSRF third-generation low-level RF control system.Some hardware and specialized algorithms were redesigned to fit the harmonic cavity control.The design of the tuning control system is complete,and the control system has been tested.The test result shows that the fluctuation of amplitude is<±0.34%within 1.5 h,which satisfies the stability requirement.展开更多
We report the design of a wide-range energy material beamline(E-line) with multiple experimental techniques at the Shanghai Synchrotron Radiation Facility.The undulators consisted of an elliptically polarizing undulat...We report the design of a wide-range energy material beamline(E-line) with multiple experimental techniques at the Shanghai Synchrotron Radiation Facility.The undulators consisted of an elliptically polarizing undulator and in-vacuum undulator that generate the soft and hard X-rays, respectively. The beamline covered a wide energy range from 130 to 18 ke V with both a high photon flux([ 10^(12) phs/s with exit silt 30 lm in soft X-ray and [ 5 9 10^(12) phs/s in hard X-ray within 0.1%BW bandwidth) and promising resolving power(maximum E/DE [ 15,000 in soft X-ray with exit silt 30 lm and [6000 in hard X-ray). Moreover, the beam spots from the soft and hard X-rays were focused to the same sample position with a high overlap ratio, so that the surfaces, interfaces, and bulk properties were characterized in situ by changing the probing depth.展开更多
Traditional Fourier transform infrared(FTIR)spectroscopy has been recognized as a valuable method to characterize and classify kinds of microorganisms.In this study,combined with multivariate statistical analysis,sync...Traditional Fourier transform infrared(FTIR)spectroscopy has been recognized as a valuable method to characterize and classify kinds of microorganisms.In this study,combined with multivariate statistical analysis,synchrotron radiation-based FTIR(SR-FTIR) microspectroscopy was applied to identify and discriminate ten foodborne bacterial strains.Our results show that the whole spectra(3000-900 cm^(-1)) and three subdivided spectral regions(3000-2800,1800-1500 and 1200-900 cm^(-1),representing lipids,proteins and polysaccharides,respectively) can be used to type bacteria.Either the whole spectra or the three subdivided spectra are good for discriminating the bacteria at levels of species and subspecies,but the whole spectra should be given preference at the genus level.The findings demonstrate that SR-FTIR microspectroscopy is a powerful tool to identify and classify foodborne pathogenic bacteria at the genus,species and subspecies level.展开更多
The increased use of rechargeable batteries in portable electronic devices and the continuous development of novel applications(e.g. transportation and large scale energy storage), have raised a strong demand for high...The increased use of rechargeable batteries in portable electronic devices and the continuous development of novel applications(e.g. transportation and large scale energy storage), have raised a strong demand for high performance batteries with increased energy density, cycle and calendar life, safety and lower costs. This triggers significant efforts to reveal the fundamental mechanism determining battery performance with the use of advanced analytical techniques. However, the inherently complex characteristics of battery systems make the mechanism analysis sophisticated and difficult. Synchrotron radiation is an advanced collimated light source with high intensity and tunable energies. It has particular advantages in electronic structure and geometric structure(both the short-range and long-range structure)analysis of materials on different length and time scales. In the past decades, synchrotron X-ray techniques have been widely used to understand the fundamental mechanism and guide the technological optimization of batteries. In particular, in situ and operando techniques with high spatial and temporal resolution, enable the nondestructive, real time dynamic investigation of the electrochemical reaction,and lead to significant deep insights into the battery operation mechanism.This review gives a brief introduction of the application of synchrotron X-ray techniques to the investigation of battery systems. The five widely implicated techniques, including X-ray diffraction(XRD), Pair Distribution Function(PDF), Hard and Soft X-ray absorption spectroscopy(XAS) and X-ray photoelectron spectroscopy(XPS) will be reviewed, with the emphasis on their in situ studies of battery systems during cycling.展开更多
The compressive deformation behavior of the extruded WZ42(Mg98.5Y1Zn0.5 in at.%)magnesium alloy containing a low amount of long-period stacking ordered(LPSO)phase was studied by in-situ synchrotron radiation diffracti...The compressive deformation behavior of the extruded WZ42(Mg98.5Y1Zn0.5 in at.%)magnesium alloy containing a low amount of long-period stacking ordered(LPSO)phase was studied by in-situ synchrotron radiation diffraction technique.Tests were conducted at temperatures between room temperature and 350℃.Detailed microstructure investigation was provided by scanning electron microscopy,particularly the backscattered electron imaging and electron backscatter diffraction technique.The results show that twinning lost its dominance and kinking of the LPSO phase became more pronounced with increasing deformation temperature.No cracks of the LPSO phase and no debonding r at the interface between the LPSO phase and the Mg matrix were observed at temperatures above 200℃.At 350℃,the LPSO phase lost its strengthening effect and the deformation of the alloy was mainly realized by the dynamic recrystallization of the Mg matrix.展开更多
The synchrotron radiation technology has recently emerged as a powerful tool to characterize the real-time microstructure evolution during solidification of alloys.Compared with other methods,the synchrotron radiation...The synchrotron radiation technology has recently emerged as a powerful tool to characterize the real-time microstructure evolution during solidification of alloys.Compared with other methods,the synchrotron radiation technology,along with its unique advantages of strong brightness,high energy,excellent resolution,and good monochromaticity,allows for capturing the dendrite evolution behavior of alloys in real time and can be dynamically coordinated with high-resolution CCD(Charge-coupled Device)imaging systems.This paper briefly reviews the recent advances in developing synchrotron radiation for solidification of alloys with low,medium,and high melting points,and under the external electric,magnetic,and ultrasonic fields.Furthermore,a series of microstructural features and behaviors such as dendrite morphology,growth orientation,dendrite fracture,and rotation are described in detail.Finally,the development trends and application prospects of synchrotron radiation technology in alloy solidification are forecasted.展开更多
This study investigated the formulation mechanism of microspheres via internal surfactant distribution. Eudragit L100 based microspheres loaded with bovine serum albumin were prepared by solid in oil in oil emulsion s...This study investigated the formulation mechanism of microspheres via internal surfactant distribution. Eudragit L100 based microspheres loaded with bovine serum albumin were prepared by solid in oil in oil emulsion solvent evaporation method using acetone and liquid paraffin system containing sucrose stearate as a surfactant. The fabricated microspheres were evaluated for encapsulation efficiency, particle size, production yield, and in vitro release characteristics. The internal structures of microspheres were characterized using synchrotron radiation X-ray microcomputed tomography(SR-μCT). The enhanced contrast made the sucrose stearate distinguished from Eudragit to have its three dimensional(3D) distribution. Results indicated that the content and concentration determined the state of sucrose stearate and had significant influences on the release kinetics of protein. The dispersity of sucrose stearate was the primary factor that controlled the structure of the microspheres and further affected the encapsulation efficiency, effective drug loading, as well as in vitro release behavior. In conclusion, the 3D internal distribution of surfactant in microspheres and its effects on protein release behaviors have been revealed for the first time. The highly resolved 3D architecture provides new evidence for the deep understanding of the microsphere formation mechanism.展开更多
The aging behavior of Al-Cu-Mg-Ag alloys with high Cu/Mg was studied by transmission electron microscopy (TEM) and small-angle X-ray scattering (SAXS) using synchrotron radiation. TEM study reveals that the major stre...The aging behavior of Al-Cu-Mg-Ag alloys with high Cu/Mg was studied by transmission electron microscopy (TEM) and small-angle X-ray scattering (SAXS) using synchrotron radiation. TEM study reveals that the major strengthening phases of the alloy after aging at 160?C for 10 h are Ω and less θ′. SAXS study shows that the scattering patterns are composed of several concentric circles at the beginning of aging process, which is replaced by the butterfly-wings scattering patterns with the increase of aging time. The butterfly-wings scattering patterns are composed of several branches. The angles between the branches are roughly equal to that between the habit planes of precipitates. The evolution of Guinier radius with aging time indicates the good coarsening resistance of the precipitates. The evolution of integrated intensity is consistent with the classical two-step precipitation process.展开更多
基金financial support through a KekuléPh.D.fellowship by the Fonds der Chemischen Industrie(FCI)support from the China Scholarship Council(No.202106950013)。
文摘The parasitic hydrogen evolution reaction(HER)in the negative half-cell of vanadium redox flow batteries(VRFBs)causes severe efficiency losses.Thus,a deeper understanding of this process and the accompanying bubble formation is crucial.This benchmarking study locally analyzes the bubble distribution in thick,porous electrodes for the first time using deep learning-based image segmentation of synchrotron X-ray micro-tomograms.Each large three-dimensional data set was processed precisely in less than one minute while minimizing human errors and pointing out areas of increased HER activity in VRFBs.The study systematically varies the electrode potential and material,concluding that more negative electrode potentials of-200 m V vs.reversible hydrogen electrode(RHE)and lower cause more substantial bubble formation,resulting in bubble fractions of around 15%–20%in carbon felt electrodes.Contrarily,the bubble fractions stay only around 2%in an electrode combining carbon felt and carbon paper.The detected areas with high HER activity,such as the border subregion with more than 30%bubble fraction in carbon felt electrodes,the cutting edges,and preferential spots in the electrode bulk,are potential-independent and suggest that larger electrodes with a higher bulk-to-border ratio might reduce HER-related performance losses.The described combination of electrochemical measurements,local X-ray microtomography,AI-based segmentation,and 3D morphometric analysis is a powerful and novel approach for local bubble analysis in three-dimensional porous electrodes,providing an essential toolkit for a broad community working on bubble-generating electrochemical systems.
基金financialy supported by National Key R&D Program of China(2022YFB2402600)the National Natural Science Foundation of China(22279166)+1 种基金the Research Start-up Funds from Sun Yat-Sen University(200306)the Fundamental Research Funds for the Central Universities,Sun Yat-Sen University(22qntd0101 and 22dfx01)
文摘Pseudocapacitive materials that store charges via reversible surface or near-surface faradaic reactions are capable of overcoming the capacity limitations of electrical double-layer capacitors.Revealing the structure–activity relationship between the microstructural features of pseudocapacitive materials and their electrochemical performance on the atomic scale is the key to build high-performance capacitor-type devices containing ideal pseudocapacitance effect.Currently,the high brightness(flux),and spectral and coherent nature of synchrotron X-ray analytical techniques make it a powerful tool for probing the structure–property relationship of pseudocapacitive materials.Herein,we report a comprehensive and systematic review of four typical characterization techniques(synchrotron X-ray diffraction,pair distribution function[PDF]analysis,soft X-ray absorption spectroscopy,and hard X-ray absorption spectroscopy)for the study of pseudocapacitance mechanisms.In addition,we offered significant insights for understanding and identifying pseudocapacitance mechanisms(surface redox pseudocapacitance,intercalation pseudocapacitance,and the extrinsic pseudocapacitance phenomenon in battery materials)by combining in situ hard XAS and electrochemical analyses.Finally,a perspective for further depth of understanding into the pseudocapacitance mechanism using synchrotron X-ray analytical techniques is proposed.
基金supported by National Natural Science Foundation of China(U2032118 and 42172048)Guizhou Provincial Science and Technology Projects(QKHPTRCYQK[2023]035 and QKHJC-ZK[2021]ZD042)+1 种基金Hundred Talents Program of the Chinese Academy of SciencesGuizhou Provincial 2020 and 2021 Science and Technology Subsidies(Nos.GZ2020SIG and GZ2021SIG)。
文摘The unit-cell parameters and volumes of geikielite(MgTiO_(3))and ilmenite(FeTiO_(3))were investigated at high temperatures up to 700 K and ambient pressure,using in-situ angle-dispersive synchrotron X-ray diffraction.No phase transition was detected over the experimental temperature range.Using(Berman in J Petrol29:445-522,1988.10.1093/petrology/29.2.445)equations to fit the temperature-volume data,the volumetric thermal expansion coefficients at ambient conditions(α_(V0))of MgTiO_(3) and FeTiO_(3) were obtained as follows:2.55(6)×10^(-5)K^(-1)and 2.82(10)×10^(-5)K^(-1),respectively.We infer that the larger effective ionic radius of Fe^(2+)(Ⅵ)(0.78 A)than that of Mg^(2+)(Ⅵ)(0.72?)renders FeTiO_(3)has a larger volumetric thermal expansivity than MgTiO_(3).Simultaneously,the refined axial thermal expansion coefficients under ambient conditions areα_(a0)=0.74(3)×10^(-5)K^(-1)andα_(c0)=1.08(5)×10^(-5)K^(-1)for the aaxis and c-axis of MgTiO_(3),respectively,andα_(a0)=0.95(5)×10^(-5)K^(-1)andα_(c0)=0.92(12)×10^(-5)K^(-1)for the aaxis and c-axis of FeTiO_(3),respectively.The axial thermal expansivity of MgTiO_(3) is anisotropic,but that of FeTiO_(3) is nearly isotropic.We infer that the main reason for the different axial thermal expansivity between MgTiO_(3) and FeTiO_(3) is that the thermal expansion mode of the Mg-O bond in MgTiO_(3) is different from that of the Fe-O bonds in FeTiO_(3).
基金financial support of the Spanish Ministry of Economy and Competitiveness under project number MAT2016-78850-Rprovision of beamtime at the P07 beamline of the Petra Ⅲ synchrotron facility under the project I-20170054EC。
文摘The load partitioning between the magnesium and titanium phases in an extruded Mg-15%Ti(vol.%) composite from room temperature up to 300 ℃ using synchrotron radiation diffraction during in-situ compression tests. During compression, the magnesium matrix composite deforms mainly by the activation of the extension twinning system up to 200 ℃. The volume fraction of twins increases with the plastic strain but decrease with the compression temperature. Hard titanium particles bear an additional load transferred by the soft magnesium matrix from room temperature up to 300 ℃. This effect is amplified after yield stress during plastic deformation. Additionally, twins within magnesium grains behaves as an additional reinforcement at low temperature(below 200 ℃) inducing an increase in the work hardening of the composite.
文摘Because of its excellent dose distribution,proton therapy is becoming increasingly popular in the medical application of cancer treatment.A synchrotron-based proton therapy facility was designed and constructed in Shanghai.The synchrotron,beam delivery system,and other technical systems were commissioned and reached their expected performances.After a clinical trial of 47 patients was finished,the proton therapy facility obtained a registration certificate from the National Medical Products Administration.The characteristics of the accelerator and treatment systems are described in this article.
基金the financial support from China Scholarship Council(202108080263)Financial support by the Federal Ministry of Education and Research(BMBF)under the project“He Na”(03XP0390C)+1 种基金the German Research Foundation(DFG)under the joint German-Russian DFG project“KIBSS”(448719339)are acknowledgedthe financial support from the Federal Ministry of Education and Research(BMBF)under the project“Ka Si Li”(03XP0254D)in the competence cluster“Excell Batt Mat”。
文摘Transition metal sulfides have been regarded as promising anode materials for sodium-ion batteries(SIB).However,they face the challenges of poor electronic conductivity and large volume change,which result in capacity fade and low rate capability.In this work,a composite containing ultrasmall CoS(~7 nm)nanoparticles embedded in heteroatom(N,S,and O)-doped carbon was synthesized by an efficient one-step sulfidation process using a Co(Salen)precursor.The ultrasmall CoS nanoparticles are beneficial for mechanical stability and shortening Na-ions diffusion pathways.Furthermore,the N,S,and O-doped defect-rich carbon provides a robust and highly conductive framework enriched with active sites for sodium storage as well as mitigates volume expansion and polysulfide shuttle.As anode for SIB,CoS@HDC exhibits a high initial capacity of 906 mA h g^(-1)at 100 mA g^(-1)and a stable long-term cycling life with over 1000 cycles at 500 mA g^(-1),showing a reversible capacity of 330 mA h g^(-1).Meanwhile,the CoS@HDC anode is proven to maintain its structural integrity and compositional reversibility during cycling.Furthermore,Na-ion full batteries based on the CoS@HDC anode and Na_(3)V_(2)(PO_(4))_(3)cathode demonstrate a stable cycling behavior with a reversible specific capacity of~200 m A h g^(-1)at least for 100 cycles.Moreover,advanced synchrotron operando X-ray diffraction,ex-situ X-ray absorption spectroscopy,and comprehensive electrochemical tests reveal the structural transformation and the Co coordination chemistry evolution of the CoS@HDC during cycling,providing fundamental insights into the sodium storage mechanism.
基金supported by the Jordan University of Science and Technology(Grant No.20180167)the SESAME Synchrotron Center Jordan(Grant No.20185004)。
文摘The relative intensities of L-subshell x-ray fluorescence(XRF)for elements with atomic numbers 62≤Z≤83 were measured at two excitation energies,18 keV and 23 keV,using a synchrotron radiation source at a beamline of the Synchrotron Light Center for Experimental Science and Applications in the Middle East(SESAME),Jordan.The experimentally measured results of the relative intensities were compared with the calculated results using the subshell fluorescence yield and the Coster-Kronig transition probabilities recommended by Campbell and the values based on the Dirac-Hartree-Slater model by Puri.The experimental and theoretical results are in agreement.In this work,L XRF relative intensities for the elements Sm,Gd,Tb,Er,Ta,W,Re,Hg,Pb and Bi at energies of 18 keV and 23 keV were measured.
基金supported by the SSRF Phase-II projectNatural Science Foundation of Shanghai(Nos.21ZR1471800 and 23ZR1471200)National Natural Science Foundation of China(No.12005281)。
文摘BL10U2 is an undulator-based macromolecular crystallography(MX)beamline located at the 3.5-GeV Shanghai Synchrotron Radiation Facility.BL10U2 is specifically designed for conducting routine and biosafety level-2(BSL-2)MX experiments utilizing high-flux tunable X-rays with energies from 7 to 18 keV,providing a beam spot size of 20μm(horizontal)×10μm(vertical)at the sample point.Certification by the Shanghai Pudong Municipal Health Commission confirmed the capability to perform BSL-2 MX experiments.The beamline is currently equipped with an Eiger X 16 M detector and two newly developed in-house high-precision diffractometers that can be switched to perform conventional or in situ crystal diffraction experiments.An automatic sample changer developed in-house allows fast sample exchange in less than 30 s,supporting high-throughput MX experimentation and rapid crystal screening.Data collection from both the diffractometer and detector was controlled by an in-house developed data collection software(Finback)with a user-friendly interface for convenient operation.This study presents a comprehensive overview of the facilities,experimental methods,and performance characteristics of the BL10U2 beamline.
文摘The purpose of this study was to design a rapid-cycling synchrotron, making it capable of proton beam ultrahigh dose rate irradiation, inspired by laser accelerators. The design had to be cheap and simple. We consider our design from six aspects: the lattice, injection, extraction, space charge effects, eddy current effects and energy switching. Efficiency and particle quantity must be addressed when injected. The space charge effects at the injection could affect particles' number. The eddy current effects in the vacuum chambers would affect the magnetic field itself and generate heat, all of which need to be taken into account. Fast extraction can obtain 10^(10) protons/pulse, equal to instantaneous dose rate up to 10~7 Gy/s in a very short time, while changing various extraction energies rapidly and easily to various deposition depths. In the further research, we expect to combine a delivery system with this accelerator to realize the FLASH irradiation.
基金supported by the National Key Research and Development Program of China(No.2021YFC2301405)the National Natural Science Foundation of China(No.31971121)Shanghai Science and Technology Plan Project(No.21ZR14718)。
文摘Macromolecular crystallography beamline BL17U1 at the Shanghai Synchrotron Radiation Facility has been relocated,upgraded,and given a new ID(BL02U1).It now delivers X-rays in the energy range of 6–16 keV,with a focused beam of 11.6μm×4.8μm and photon flux greater than 1012 phs/s.The high credibility and stability of the beam and good timing synchronization of the equipment significantly improve the experimental efficiency.Since June 2021,when it officially opened to users,over 4200 h of beamtime have been provided to over 200 research groups to collect data at the beamline.Its good performance and stable operation have led to the resolution of several structures based on data collected at the beamline.
基金supported by the National key research and development program of China(Nos.2016YFB0700401 and 2016YFB0700404)Natural Science Foundation of Shanghai(Nos.19ZR1468200 and 18ZR1448000)+2 种基金National Natural Science Foundation of China(Nos.51671154,51601213 and 51671122)Strategic Priority Research Program of the Chinese Academy of Sciences(No.XDA02004210)Youth Innovation Promotion Association,Chinese Academy of Science(No.2019264)
文摘From a safety point of view, it is important to study the damages and reliability of molten salt reactor structural alloy materials, which are subjected to extreme environments due to neutron irradiation, molten salt corrosion, fission product attacks, thermal stress, and even combinations of these. In the past few years, synchrotron radiation-based materials characterization techniques have proven to be effective in revealing the microstructural evolution and failure mechanisms of the alloys under surrogating operation conditions. Here, we review the recent progress in the investigations of molten salt corrosion,tellurium(Te) corrosion, and alloy design. The valence states and distribution of chromium(Cr) atoms, and the diffusion and local atomic structure of Te atoms near the surface of corroded alloys have been investigated using synchrotron radiation techniques, which considerably deepen the understandings on the molten salt and Te corrosion behaviors. Furthermore, the structure and size distribution of the second phases in the alloys have been obtained, which are helpful for the future development of new alloy materials.
文摘The protein complex crystallographic beamline BL19U1 at the Shanghai Synchrotron Radiation Facility is one of the five beamlines dedicated to protein sciences operated by National Facility for Protein Science(Shanghai,China).The beamline,which features a small-gap invacuum undulator,has been officially open to users since March 2015.This beamline delivers X-ray in the energy range 7–15 keV.With its high flux,low divergence beam and a large active area detector,BL19U1 is designed for proteins with large molecular weight and large crystallographic unit cell dimensions.Good performance and stable operation of the beamline have allowed the number of Protein Data Bank(PDB)depositions and the number of articles published based on data collected at this beamline to increase steadily.To date,over 300 research groups have collected data at the beamline.More than 600 PDB entries have been deposited at the PDB(www.pdb.org).More than 300 papers have been published that include data collected at the beamline,including 21 research articles published in the top-level journals Cell,Nature,and Science.
文摘Beam lifetime is dominated by Touschek scattering at the Shanghai Synchrotron Radiation Facility(SSRF).Touschek loss rate is affected by probability for scattering beyond the RF acceptance and the volume charge density of the bench.In the phaseⅡupgrade of the SSRF,a third harmonic superconducting cavity will be used to enhance the Touschek lifetime by lengthening the bunches.The Touschek lifetime improvement factor is affected by the voltage of a harmonic cavity.To stabilize the cavity voltage,a tuning control system was designed to control it.The design of the tuning control system was based on the SSRF third-generation low-level RF control system.Some hardware and specialized algorithms were redesigned to fit the harmonic cavity control.The design of the tuning control system is complete,and the control system has been tested.The test result shows that the fluctuation of amplitude is<±0.34%within 1.5 h,which satisfies the stability requirement.
基金supported by the National Development and Reform Commission(NDRC) of Chinathe National Natural Science Foundation of China(No.11505280)+1 种基金the Shanghai Youth Foundation(No.14YF1407500)the National Science Foundation of China(Nos.11475251,11225527)
文摘We report the design of a wide-range energy material beamline(E-line) with multiple experimental techniques at the Shanghai Synchrotron Radiation Facility.The undulators consisted of an elliptically polarizing undulator and in-vacuum undulator that generate the soft and hard X-rays, respectively. The beamline covered a wide energy range from 130 to 18 ke V with both a high photon flux([ 10^(12) phs/s with exit silt 30 lm in soft X-ray and [ 5 9 10^(12) phs/s in hard X-ray within 0.1%BW bandwidth) and promising resolving power(maximum E/DE [ 15,000 in soft X-ray with exit silt 30 lm and [6000 in hard X-ray). Moreover, the beam spots from the soft and hard X-rays were focused to the same sample position with a high overlap ratio, so that the surfaces, interfaces, and bulk properties were characterized in situ by changing the probing depth.
基金supported by Science Frontier Project of the Chinese Academy of Sciences(No.QYZDJ-SSW-SLH019)Open Research Fund Program of Shanghai Key Laboratory of Medical Biodefense
文摘Traditional Fourier transform infrared(FTIR)spectroscopy has been recognized as a valuable method to characterize and classify kinds of microorganisms.In this study,combined with multivariate statistical analysis,synchrotron radiation-based FTIR(SR-FTIR) microspectroscopy was applied to identify and discriminate ten foodborne bacterial strains.Our results show that the whole spectra(3000-900 cm^(-1)) and three subdivided spectral regions(3000-2800,1800-1500 and 1200-900 cm^(-1),representing lipids,proteins and polysaccharides,respectively) can be used to type bacteria.Either the whole spectra or the three subdivided spectra are good for discriminating the bacteria at levels of species and subspecies,but the whole spectra should be given preference at the genus level.The findings demonstrate that SR-FTIR microspectroscopy is a powerful tool to identify and classify foodborne pathogenic bacteria at the genus,species and subspecies level.
基金the National Natural Science Foundation of China (Grant nos.21233004,21303147 and 21473148,etc.)the National Key Research and Development Program (Grant no.2016YFB0901500)
文摘The increased use of rechargeable batteries in portable electronic devices and the continuous development of novel applications(e.g. transportation and large scale energy storage), have raised a strong demand for high performance batteries with increased energy density, cycle and calendar life, safety and lower costs. This triggers significant efforts to reveal the fundamental mechanism determining battery performance with the use of advanced analytical techniques. However, the inherently complex characteristics of battery systems make the mechanism analysis sophisticated and difficult. Synchrotron radiation is an advanced collimated light source with high intensity and tunable energies. It has particular advantages in electronic structure and geometric structure(both the short-range and long-range structure)analysis of materials on different length and time scales. In the past decades, synchrotron X-ray techniques have been widely used to understand the fundamental mechanism and guide the technological optimization of batteries. In particular, in situ and operando techniques with high spatial and temporal resolution, enable the nondestructive, real time dynamic investigation of the electrochemical reaction,and lead to significant deep insights into the battery operation mechanism.This review gives a brief introduction of the application of synchrotron X-ray techniques to the investigation of battery systems. The five widely implicated techniques, including X-ray diffraction(XRD), Pair Distribution Function(PDF), Hard and Soft X-ray absorption spectroscopy(XAS) and X-ray photoelectron spectroscopy(XPS) will be reviewed, with the emphasis on their in situ studies of battery systems during cycling.
基金The authors acknowledge the Deutsches Elektronen-Synchrotron for the provision of facilities within the framework of the proposal I-20170459 ECThe authors are also grateful for support from the Grant Agency of the Charles University,grant number 1262217+3 种基金the grant SVV-2019-260442the Czech Science Foundation under grant 17-21855Sthe Operational Programme Research,Development and Education,The Ministry of Education,Youth and Sports(OP RDE,MEYS),grant number CZ.02.1.01/0.0/0.0/16_013/0001794GG thanks the support of the Spanish Ministry of Economy and Competitiveness,grant number MAT2016-78850-R.
文摘The compressive deformation behavior of the extruded WZ42(Mg98.5Y1Zn0.5 in at.%)magnesium alloy containing a low amount of long-period stacking ordered(LPSO)phase was studied by in-situ synchrotron radiation diffraction technique.Tests were conducted at temperatures between room temperature and 350℃.Detailed microstructure investigation was provided by scanning electron microscopy,particularly the backscattered electron imaging and electron backscatter diffraction technique.The results show that twinning lost its dominance and kinking of the LPSO phase became more pronounced with increasing deformation temperature.No cracks of the LPSO phase and no debonding r at the interface between the LPSO phase and the Mg matrix were observed at temperatures above 200℃.At 350℃,the LPSO phase lost its strengthening effect and the deformation of the alloy was mainly realized by the dynamic recrystallization of the Mg matrix.
基金The author would like to thank financial support of the National Natural Science Foundation-Youth Science Foundation Project(51901208,51771113)Henan University Key Scientific Research Project(20B430020)+1 种基金the Key scientific and technological projects in Henan Province(202102210016,202102210272)Zhengzhou University of Light Technology Doctoral Research Initiation Fund(JDG20190098).
文摘The synchrotron radiation technology has recently emerged as a powerful tool to characterize the real-time microstructure evolution during solidification of alloys.Compared with other methods,the synchrotron radiation technology,along with its unique advantages of strong brightness,high energy,excellent resolution,and good monochromaticity,allows for capturing the dendrite evolution behavior of alloys in real time and can be dynamically coordinated with high-resolution CCD(Charge-coupled Device)imaging systems.This paper briefly reviews the recent advances in developing synchrotron radiation for solidification of alloys with low,medium,and high melting points,and under the external electric,magnetic,and ultrasonic fields.Furthermore,a series of microstructural features and behaviors such as dendrite morphology,growth orientation,dendrite fracture,and rotation are described in detail.Finally,the development trends and application prospects of synchrotron radiation technology in alloy solidification are forecasted.
基金the financial support from the National Natural Science Foundation of China(No.81430087)the National Science and Technology Major Project(2013ZX09402103)
文摘This study investigated the formulation mechanism of microspheres via internal surfactant distribution. Eudragit L100 based microspheres loaded with bovine serum albumin were prepared by solid in oil in oil emulsion solvent evaporation method using acetone and liquid paraffin system containing sucrose stearate as a surfactant. The fabricated microspheres were evaluated for encapsulation efficiency, particle size, production yield, and in vitro release characteristics. The internal structures of microspheres were characterized using synchrotron radiation X-ray microcomputed tomography(SR-μCT). The enhanced contrast made the sucrose stearate distinguished from Eudragit to have its three dimensional(3D) distribution. Results indicated that the content and concentration determined the state of sucrose stearate and had significant influences on the release kinetics of protein. The dispersity of sucrose stearate was the primary factor that controlled the structure of the microspheres and further affected the encapsulation efficiency, effective drug loading, as well as in vitro release behavior. In conclusion, the 3D internal distribution of surfactant in microspheres and its effects on protein release behaviors have been revealed for the first time. The highly resolved 3D architecture provides new evidence for the deep understanding of the microsphere formation mechanism.
基金financially supported by the National Natural Science Foundation of China(No.51004018)
文摘The aging behavior of Al-Cu-Mg-Ag alloys with high Cu/Mg was studied by transmission electron microscopy (TEM) and small-angle X-ray scattering (SAXS) using synchrotron radiation. TEM study reveals that the major strengthening phases of the alloy after aging at 160?C for 10 h are Ω and less θ′. SAXS study shows that the scattering patterns are composed of several concentric circles at the beginning of aging process, which is replaced by the butterfly-wings scattering patterns with the increase of aging time. The butterfly-wings scattering patterns are composed of several branches. The angles between the branches are roughly equal to that between the habit planes of precipitates. The evolution of Guinier radius with aging time indicates the good coarsening resistance of the precipitates. The evolution of integrated intensity is consistent with the classical two-step precipitation process.