The effect of rare earth on the microstructures, mechanical properties and inclu sions in low sulphur Nb-Ti-bearing steel were investigated. It is shown that t h e transverse yield point, the traverse tensile strength...The effect of rare earth on the microstructures, mechanical properties and inclu sions in low sulphur Nb-Ti-bearing steel were investigated. It is shown that t h e transverse yield point, the traverse tensile strength and elongation of testin g steels decrease initially and then rise with increasing content of rare earth. The impact energy values of the testing steels exhibit a contrary trend. Proper amount of rare earth in the steels can improve the anisotropy of impact toughne ss above -20 ℃ and it does not affect the type of microstructures which ar e st ill composed of ferrites and pearlites, but the pearlite amount increases. On one hand, rare earth cleans the molten steel and reduces the amount of inclusions; on the other hand, rare earth makes the inclusions spheroidizd, refi ned and dispersed, and thus improves the distribution of inclusions.展开更多
Transmission electron microscopy （TEM） and physics-chemical phase analysis were employed to investigate the precipitates in high strength steels microalloyed with Ti produced by compact strip production （CSP）. It ...Transmission electron microscopy （TEM） and physics-chemical phase analysis were employed to investigate the precipitates in high strength steels microalloyed with Ti produced by compact strip production （CSP）. It was seen that precipitates in Ti microalloyed steels mainly included TiN, Ti4C2S2, and TiC. The size of TiN particles varied from 50 to 500 nm, and they could precipitate during or before soaking. The Ti4C2S2 with the size of 40-100 nm might precipitate before rolling, and the TiC particles with the size of 5-50 nm precipitated heterogeneously. High Ti content would lead to the presence of bigger TiC particles that precipitated in austenite, and by contrast, TiC particles that precipitated in ferrite and the transformation of austenite to ferrite was smaller. They were less than 30 nm and mainly responsible for precipitate strengthening. It should be noted that the TiC particles in higher Ti content were generally smaller than those in the steel with a lower Ti content.展开更多
The dynamic recrystallization （DRX） behavior of Nb-Ti microalloyed steels was investigated by isothermal single compression tests in the temperature range of 900-1 150 ℃ at constant strain rates of 0.1-5 s^-1. DRX ...The dynamic recrystallization （DRX） behavior of Nb-Ti microalloyed steels was investigated by isothermal single compression tests in the temperature range of 900-1 150 ℃ at constant strain rates of 0.1-5 s^-1. DRX was retarded effectively at low temperature due to the onset of dynamic precipitation of Nb and Ti carbonitrides, resulting in higher values of the peak strain. An expression was developed for the activation energy of deformation as a function of the contents of Nb and Ti in solution as well as other alloying elements. A new value of corrective factor was determined and applied to quantify the retardation produced by increase in the amount of Nb and Ti dissolved at the reheating temperature. The ratio of critical strain to peak strain decreases with increasing equivalent Nb content. In addition, the effects of Ti content and deformation conditions on DRX kinetics and steady state grain size were determined. Finally, the kinetics of dynamic precipitation was determined and effect of dynamic precipitation on the onset of DRX was clarified based on the comparison between precipitate pinning force and recrystallization driving force.展开更多
Microstructures and inclusions in the Si-Mn-Ti deoxidized steels after cooling in the furnace were investigated. The composition and morphology of the inclusions were analyzed using a field emission scanning electron ...Microstructures and inclusions in the Si-Mn-Ti deoxidized steels after cooling in the furnace were investigated. The composition and morphology of the inclusions were analyzed using a field emission scanning electron microscope （FE-SEM） with energy dispersive X-ray spectrometry （EDS）. The kind and composition of the inclusions calculated from the thermodynamic database were in good agreement with the experimental results. There were two main kinds of inclusions formed in the Si-Mn-Ti deoxidized steels. One kind of inclusion was the manganese titanium oxide （Mn-Ti oxide）. Another kind of inclusion was the MnS inclusion with segregation points containing Ti and N. According to the thermodynamic calculation, those segregation points were TiN precipitates. The formation of intragranular ferrite （IGF） microstructures refined the grain size during the austenite-ferrite transformation. The mechanisms of IGF formation were discussed. Mn-Ti oxide inclusions with Mn-depleted zone （MDZ） were effective to be nucleation sites for IGF formation, because the MDZ increased the austenite-ferrite transformation temperature. TiN had the low misfit ratio with IGF, so the TiN precipitated on the MnS surface also promoted the formation of IGF because of decreasing interfacial energies.展开更多
文摘The effect of rare earth on the microstructures, mechanical properties and inclu sions in low sulphur Nb-Ti-bearing steel were investigated. It is shown that t h e transverse yield point, the traverse tensile strength and elongation of testin g steels decrease initially and then rise with increasing content of rare earth. The impact energy values of the testing steels exhibit a contrary trend. Proper amount of rare earth in the steels can improve the anisotropy of impact toughne ss above -20 ℃ and it does not affect the type of microstructures which ar e st ill composed of ferrites and pearlites, but the pearlite amount increases. On one hand, rare earth cleans the molten steel and reduces the amount of inclusions; on the other hand, rare earth makes the inclusions spheroidizd, refi ned and dispersed, and thus improves the distribution of inclusions.
文摘Transmission electron microscopy （TEM） and physics-chemical phase analysis were employed to investigate the precipitates in high strength steels microalloyed with Ti produced by compact strip production （CSP）. It was seen that precipitates in Ti microalloyed steels mainly included TiN, Ti4C2S2, and TiC. The size of TiN particles varied from 50 to 500 nm, and they could precipitate during or before soaking. The Ti4C2S2 with the size of 40-100 nm might precipitate before rolling, and the TiC particles with the size of 5-50 nm precipitated heterogeneously. High Ti content would lead to the presence of bigger TiC particles that precipitated in austenite, and by contrast, TiC particles that precipitated in ferrite and the transformation of austenite to ferrite was smaller. They were less than 30 nm and mainly responsible for precipitate strengthening. It should be noted that the TiC particles in higher Ti content were generally smaller than those in the steel with a lower Ti content.
基金the National Natural Science Foundation of China(No.50474086,50334010)the Program for New Century Excellent Talents in Universities(No.NCET-04-0278)of the Ministry of Education
文摘The dynamic recrystallization （DRX） behavior of Nb-Ti microalloyed steels was investigated by isothermal single compression tests in the temperature range of 900-1 150 ℃ at constant strain rates of 0.1-5 s^-1. DRX was retarded effectively at low temperature due to the onset of dynamic precipitation of Nb and Ti carbonitrides, resulting in higher values of the peak strain. An expression was developed for the activation energy of deformation as a function of the contents of Nb and Ti in solution as well as other alloying elements. A new value of corrective factor was determined and applied to quantify the retardation produced by increase in the amount of Nb and Ti dissolved at the reheating temperature. The ratio of critical strain to peak strain decreases with increasing equivalent Nb content. In addition, the effects of Ti content and deformation conditions on DRX kinetics and steady state grain size were determined. Finally, the kinetics of dynamic precipitation was determined and effect of dynamic precipitation on the onset of DRX was clarified based on the comparison between precipitate pinning force and recrystallization driving force.
文摘Microstructures and inclusions in the Si-Mn-Ti deoxidized steels after cooling in the furnace were investigated. The composition and morphology of the inclusions were analyzed using a field emission scanning electron microscope （FE-SEM） with energy dispersive X-ray spectrometry （EDS）. The kind and composition of the inclusions calculated from the thermodynamic database were in good agreement with the experimental results. There were two main kinds of inclusions formed in the Si-Mn-Ti deoxidized steels. One kind of inclusion was the manganese titanium oxide （Mn-Ti oxide）. Another kind of inclusion was the MnS inclusion with segregation points containing Ti and N. According to the thermodynamic calculation, those segregation points were TiN precipitates. The formation of intragranular ferrite （IGF） microstructures refined the grain size during the austenite-ferrite transformation. The mechanisms of IGF formation were discussed. Mn-Ti oxide inclusions with Mn-depleted zone （MDZ） were effective to be nucleation sites for IGF formation, because the MDZ increased the austenite-ferrite transformation temperature. TiN had the low misfit ratio with IGF, so the TiN precipitated on the MnS surface also promoted the formation of IGF because of decreasing interfacial energies.