Downconversion （DC） with emission of two near-infrared photons about 1000 nm for each blue photon absorbed was obtained in thulium （Tm3＋） and ytterbium （Yb3＋） codoped yt- trium lithium fluoride （LiYF4） singl...Downconversion （DC） with emission of two near-infrared photons about 1000 nm for each blue photon absorbed was obtained in thulium （Tm3＋） and ytterbium （Yb3＋） codoped yt- trium lithium fluoride （LiYF4） single crystals grown by an improved Bridgman method. The luminescent properties of the crystals were measured through photoluminescence excitation, emission spectra and decay curves. Luminescence between 960 and 1050 nm from yb3＋： 2Fs/2--＋2FT/2 transition, which was originated from the DC from Tm3＋ ions to Yb3＋ ions, was observed under the excitation of blue photon at 465 nm. Moreover, the energy transfer processes were studied based on the Inokuti-Hirayama model, and the results indicated that the energy transfer from Tm3＋ to Yb3＋ was an electric dipole-dipole interaction. The max- imum quantum cutting efficiency approached with 0.49mo1% Tm3＋ and 5.99mo1% Yb3＋. increasing the energy efficiency of crystalline energy part of the solar spectrum. up to 167.5% in LiYF4 single crystal codoped Application of this crystal has prospects for Si solar cells by photon doubling of the high展开更多
Lutetium oxide nanocrystals codoped with Tm3＋ and Yb3＋ were synthesized by the reverse-like co-precipitation method, using ammonium hydrogen carbonate as precipitant. Effects of the Tm3＋, Yb3＋ molar fractions and ...Lutetium oxide nanocrystals codoped with Tm3＋ and Yb3＋ were synthesized by the reverse-like co-precipitation method, using ammonium hydrogen carbonate as precipitant. Effects of the Tm3＋, Yb3＋ molar fractions and calcination temperature on the structural and upconversion luminescent properties of the Lu2O3 nanocrystals were investigated. The XRD results show that all the prepared nanocrystals can be readily indexed to pure cubic phase of Lu2O3 and indicate good crystallinity. The experimental results show that concentration quenching occurs when the mole fraction of Tm3＋ is above 0.2%. The optimal Tm3＋ and Yb3＋ doped molar fractions are 0.2% and 2%, respectively. The strong blue （490 nm） and the weak red （653 nm） emissions from the prepared nanocrystals were observed under 980 nm laser excitation, and attributed to the 1G4→3H6 and IG4→3F4 transitions of Tm3＋, respectively. Power-dependent study reveals that the 1G4 levels of Tm3＋ can be populated by three-step energy transfer process. The upconversion emission intensities of 490 nm and 653 nm increase gradually with the increase of calcination temperature. The enhancement of the upconversion luminescence is suggested to be the consequence of reducing number of OH- groups and the enlarged nanoerystal size.展开更多
文摘Downconversion （DC） with emission of two near-infrared photons about 1000 nm for each blue photon absorbed was obtained in thulium （Tm3＋） and ytterbium （Yb3＋） codoped yt- trium lithium fluoride （LiYF4） single crystals grown by an improved Bridgman method. The luminescent properties of the crystals were measured through photoluminescence excitation, emission spectra and decay curves. Luminescence between 960 and 1050 nm from yb3＋： 2Fs/2--＋2FT/2 transition, which was originated from the DC from Tm3＋ ions to Yb3＋ ions, was observed under the excitation of blue photon at 465 nm. Moreover, the energy transfer processes were studied based on the Inokuti-Hirayama model, and the results indicated that the energy transfer from Tm3＋ to Yb3＋ was an electric dipole-dipole interaction. The max- imum quantum cutting efficiency approached with 0.49mo1% Tm3＋ and 5.99mo1% Yb3＋. increasing the energy efficiency of crystalline energy part of the solar spectrum. up to 167.5% in LiYF4 single crystal codoped Application of this crystal has prospects for Si solar cells by photon doubling of the high
基金Foundation item: Projects (10704090,10774140,11047147)supported by the National Natural Science Foundation of ChinaProjects (KJ090514,KJTD201016)supported by the Natural Science Foundation of Chongqing Municipal Education Commission,China
文摘Lutetium oxide nanocrystals codoped with Tm3＋ and Yb3＋ were synthesized by the reverse-like co-precipitation method, using ammonium hydrogen carbonate as precipitant. Effects of the Tm3＋, Yb3＋ molar fractions and calcination temperature on the structural and upconversion luminescent properties of the Lu2O3 nanocrystals were investigated. The XRD results show that all the prepared nanocrystals can be readily indexed to pure cubic phase of Lu2O3 and indicate good crystallinity. The experimental results show that concentration quenching occurs when the mole fraction of Tm3＋ is above 0.2%. The optimal Tm3＋ and Yb3＋ doped molar fractions are 0.2% and 2%, respectively. The strong blue （490 nm） and the weak red （653 nm） emissions from the prepared nanocrystals were observed under 980 nm laser excitation, and attributed to the 1G4→3H6 and IG4→3F4 transitions of Tm3＋, respectively. Power-dependent study reveals that the 1G4 levels of Tm3＋ can be populated by three-step energy transfer process. The upconversion emission intensities of 490 nm and 653 nm increase gradually with the increase of calcination temperature. The enhancement of the upconversion luminescence is suggested to be the consequence of reducing number of OH- groups and the enlarged nanoerystal size.