The effect of strain rate and deformation temperature on theα→βphase transformation in 47Zr-45Ti-5Al-3V alloy with an initial widmanstattenαstructure was investigated.At the deformation temperature of 550°C,t...The effect of strain rate and deformation temperature on theα→βphase transformation in 47Zr-45Ti-5Al-3V alloy with an initial widmanstattenαstructure was investigated.At the deformation temperature of 550°C,the volume fraction ofαphase decreased with increasing strain rate.At 600 and 650°C,the volume fraction ofαphase firstly increased to a maximum value with increasing strain rate from 1×10-3 to 1×10-2 s-1,and then decreased.At 700°C,the microstructure consisted of singleβphase.At a given strain rate,the volume fraction ofαphase decreased with increasing deformation temperature.With decreasing strain rate and increasing deformation temperature,the volume fraction and size of globularαphase increased.At 650°C and 1×10-3 s-1,the lamellarαphase was fully globularized.The variation in the volume fraction and morphology ofαphase with strain rate and deformation temperature significantly affected the hardness of 47Zr-45Ti-5Al-3V alloy.展开更多
Hot deformation behaviors and microstructure evolution of Ti-3Al-5Mo-4Cr-2Zr-1Fe(Ti-35421)alloy in theβsingle field are investigated by isothermal compression tests on a Gleeble-3500 simulator at temperatures of 820-...Hot deformation behaviors and microstructure evolution of Ti-3Al-5Mo-4Cr-2Zr-1Fe(Ti-35421)alloy in theβsingle field are investigated by isothermal compression tests on a Gleeble-3500 simulator at temperatures of 820-900°C and strain rates of 0.001-1 s^(-1).The research results show that discontinuous yield phenomenon and rheological softening are affected by the strain rates and deformation temperatures.The critical conditions for dynamic recrystallization and kinetic model of Ti-35421 alloy are determined,and the Arrhenius constitutive model is constructed.The rheological behaviors of Ti-35421 alloys aboveβphase transformation temperature are predicted by the constitutive model accurately.The EBSD analysis proves that the deformation softening is controlled by dynamic recovery and dynamic recrystallization.In addition,continuous dynamic recrystallization is determined during hot deformation,and the calculation model for recrystallization grain sizes is established.Good linear dependency between the experimental and simulated values of recrystallized grain sizes indicates that the present model can be used for the prediction of recrystallized grain size with high accuracy.展开更多
基金Project(201629) supported by the Scientific Research Foundation for Introduced Talent of Guizhou University,ChinaProjects(20164014,20165654) supported by the Hundred-level Innovative Talents Project of Guizhou Province,ChinaProject(20146013) supported by the Science and Technology of Guizhou Province,China
文摘The effect of strain rate and deformation temperature on theα→βphase transformation in 47Zr-45Ti-5Al-3V alloy with an initial widmanstattenαstructure was investigated.At the deformation temperature of 550°C,the volume fraction ofαphase decreased with increasing strain rate.At 600 and 650°C,the volume fraction ofαphase firstly increased to a maximum value with increasing strain rate from 1×10-3 to 1×10-2 s-1,and then decreased.At 700°C,the microstructure consisted of singleβphase.At a given strain rate,the volume fraction ofαphase decreased with increasing deformation temperature.With decreasing strain rate and increasing deformation temperature,the volume fraction and size of globularαphase increased.At 650°C and 1×10-3 s-1,the lamellarαphase was fully globularized.The variation in the volume fraction and morphology ofαphase with strain rate and deformation temperature significantly affected the hardness of 47Zr-45Ti-5Al-3V alloy.
基金the financial supports from the National Natural Science Foundation of China (Nos. 52001163, 52075237)the Primary Research and Development Plan of Jiangsu Province, China (No. BE2019119)
文摘Hot deformation behaviors and microstructure evolution of Ti-3Al-5Mo-4Cr-2Zr-1Fe(Ti-35421)alloy in theβsingle field are investigated by isothermal compression tests on a Gleeble-3500 simulator at temperatures of 820-900°C and strain rates of 0.001-1 s^(-1).The research results show that discontinuous yield phenomenon and rheological softening are affected by the strain rates and deformation temperatures.The critical conditions for dynamic recrystallization and kinetic model of Ti-35421 alloy are determined,and the Arrhenius constitutive model is constructed.The rheological behaviors of Ti-35421 alloys aboveβphase transformation temperature are predicted by the constitutive model accurately.The EBSD analysis proves that the deformation softening is controlled by dynamic recovery and dynamic recrystallization.In addition,continuous dynamic recrystallization is determined during hot deformation,and the calculation model for recrystallization grain sizes is established.Good linear dependency between the experimental and simulated values of recrystallized grain sizes indicates that the present model can be used for the prediction of recrystallized grain size with high accuracy.