The mechanisms of oxide metallurgy include inducing the formation of intragranular acicular ferrite(IAF)using micron-sized inclusions and restricting the growth of prior austenite grains(PAGs)by nanosized particles du...The mechanisms of oxide metallurgy include inducing the formation of intragranular acicular ferrite(IAF)using micron-sized inclusions and restricting the growth of prior austenite grains(PAGs)by nanosized particles during welding.The chaotically oriented IAF and refined PAGs inhibit crack initiation and propagation in the steel,resulting in high impact toughness.This work summarizes the com-bined effect of deoxidizers and alloying elements,with the aim to provide a new perspective for the research and practice related to im-proving the impact toughness of the heat affected zone(HAZ)during the high heat input welding.Ti complex deoxidation with other strong deoxidants,such as Mg,Ca,Zr,and rare earth metals(REMs),can improve the toughness of the heat-affected zone(HAZ)by re-fining PAGs or increasing IAF contents.However,it is difficult to identify the specific phase responsible for IAF nucleation because ef-fective inclusions formed by complex deoxidation are usually multiphase.Increasing alloying elements,such as C,Si,Al,Nb,or Cr,con-tents can impair HAZ toughness.A high C content typically increases the number of coarse carbides and decreases the potency of IAF formation.Si,Cr,or Al addition leads to the formation of undesirable microstructures.Nb reduces the high-temperature stability of the precipitates.Mo,V,and B can enhance HAZ toughness.Mo-containing precipitates present good thermal stability.VN or V(C,N)is ef-fective in promoting IAF nucleation due to its good coherent crystallographic relationship with ferrite.The formation of the B-depleted zone around the inclusion promotes IAF formation.The interactions between alloying elements are complex,and the effect of adding dif-ferent alloying elements remains to be evaluated.In the future,the interactions between various alloying elements and their effects on ox-ide metallurgy,as well as the calculation of the nucleation effects of effective inclusions using first principles calculations will become the focus of oxide metallurgy.展开更多
The aspects of two pipeline steels with different technologies were investigated by using transmission electron microscopy （TEM） and electron back-scattered diffraction （EBSD）. The microstructure presents a typica...The aspects of two pipeline steels with different technologies were investigated by using transmission electron microscopy （TEM） and electron back-scattered diffraction （EBSD）. The microstructure presents a typical acicular ferrite characteristic with fine particles of martensite/austenite （M/A） constituent, which distributes in grains and at grain boundaries. The bulk textures of the pipeline steel plate are {112}〈110〉 and 〈111〉 fibers, respectively, and the {112}〈110〉 component is the favorable texture benefiting for drop weight tear test. Moreover, low angle boundaries and low coincidence site lattice boundaries are inactive and more resistant to fracture than high energy random boundaries.展开更多
The formation mechanism of acicular ferrite and its microstructural characteristics in 430 ferrite stainless steel with TiC additions were studied by theory and experiment.Using an"edge?to?edge matching"mode...The formation mechanism of acicular ferrite and its microstructural characteristics in 430 ferrite stainless steel with TiC additions were studied by theory and experiment.Using an"edge?to?edge matching"model,a 5.25 mismatch between TiC(FCC structure)and ferritic stainless steel(BCC structure)was identified,which met the mismatch requirement for the heterogeneous nucleation of 430 ferritic stainless steel.TiC was found to be an effective nucleation site for the formation of acicular ferrite in a smelting experiment,as analyzed by metallographic examination,Image-Pro Plus 6.0 analysis software,and SEM–EDS.Furthermore,small inclusions in the size of 2–4?m increased the probability of acicular ferrite nucleation,and the secondary acicular ferrite would grow sympathetically from the initial acicular ferrite to produce multi-dimensional acicular ferrites.Moreover,the addition of Ti C can increase the average microstrain and dislocation density of 430 ferrite stainless steel,as calculated by Williamson-Hall(WH)method,which could play some role in strengthening the dislocation.展开更多
An ultra-low carbon acicular ferrite steel heavy plate was obtained with an advanced thermo-mechanical control process-relaxed precipitation controlled transformation （TMCP-RPC） at Xiangtan Steel, Valin Group. The h...An ultra-low carbon acicular ferrite steel heavy plate was obtained with an advanced thermo-mechanical control process-relaxed precipitation controlled transformation （TMCP-RPC） at Xiangtan Steel, Valin Group. The heavy plate has a tensile strength of approximately 600 MPa with a lower yield ratio. The impact toughness of the heavy plate achieves 280 J at ？40°C. The fine-grained mixed microstructures of the heavy plate mainly consist of acicular ferrite, granular bainite, and polygonal ferrite. The high strength and excellent toughness of the heavy plate are attributed to the formation of acicular ferrite microstructure. The prevention of blocks of martensite/retained austenite （M/A） and the higher cleanness are also responsible for the superior toughness.展开更多
The morphology, structure, and chemical composition of precipitates in the final microstructure of Nb-V-Ti microalloyed X70 acicular ferrite pipeline steel were investigated using transmission electron microscopy （TE...The morphology, structure, and chemical composition of precipitates in the final microstructure of Nb-V-Ti microalloyed X70 acicular ferrite pipeline steel were investigated using transmission electron microscopy （TEM） and energy dispersive X-ray spectroscopy （EDS）. Precipitates observed by TEM can be classified into two groups. The large precipitates are complex compounds that comprise square-shaped TiN precipitate as core with fine Nb-containing precipitate nucleated on pre-existing TiN precipitate as caps on one or more faces at high temperature. In contrast, the fine and spherical Nb carbides and/or carbonitrides precipitate heterogeneously on dislocations and sub-boundaries at low temperature. From the analysis in terms of thermodynamics, EDS and chemical cornposition of the steel, NbC precipitation is considered to be the predominant precipitation behavior in the tested steel under the processing conditions of this research.展开更多
Nucleation of acicular ferrite and its influence factors in non quenched-and-tempered steel was studied by using TEM and thermodynamic calculation. The results show that the complex particles with a center made of Ti ...Nucleation of acicular ferrite and its influence factors in non quenched-and-tempered steel was studied by using TEM and thermodynamic calculation. The results show that the complex particles with a center made of Ti oxide, Al2O3, and silicate and an outside made of a small quantity of mixture of TiN and MnS are able to act as ferrite nucleation nuclei. The acicular ferrite percentage changes little with Ti. When the oxygen content was 80 ppm, the volume percentage of acicular ferrite decreased due to an increase in allotriomorphic ferrite. The larger the cooling rate and the shorter the incubation time, the finer the titanium oxide and the higher the nucleation ratio of acicular ferrite.展开更多
Acicular ferrite microstructure was achieved for an ultralow carbon pipeline steel through the improved thermome chanical control process (TMCP), which was based on the transformation process of deformed austenite of ...Acicular ferrite microstructure was achieved for an ultralow carbon pipeline steel through the improved thermome chanical control process (TMCP), which was based on the transformation process of deformed austenite of steel. Compared with commercial pipeline steels, the experimental ultralow carbon pipeline steel possessed the satisfied strength and toughness behaviors under the current improved TMCP, although it contained only approximately 0.025% C, vvhich should mainly be attributed to the microstructural characteristics of acicular ferrite.展开更多
The effect of acicular ferrite （AF） on banded structures in low-carbon microalloyed steel with Mn segregation during both iso- thermal transformation and continuous cooling processes was studied by dilatometry and m...The effect of acicular ferrite （AF） on banded structures in low-carbon microalloyed steel with Mn segregation during both iso- thermal transformation and continuous cooling processes was studied by dilatometry and microscopic observation. With respect to the iso- thermal transformation process, the specimen isothermed at 550℃ consisted of AF in Mn-poor bands and martensite in Mn-rich bands, whereas the specimen isothermed at 450℃ exhibited two different morphologies of AF that appeared as bands. At a continuous cooling rate in the range of 4 to 50℃/s, a mixture of AF and martensite formed in both segregated bands, and the volume fraction of martensite in Mn-rich bands was always higher than that in Mn-poor bands. An increased cooling rate resulted in a decrease in the difference of martensite volume fraction between Mn-rich and Mn-poor bands and thereby leaded to less distinct microstrucmral banding. The results show that Mn segregation and cooling rate strongly affect the formation of AF-containing banded structures. The formation mechanism of microstructural banding was also discussed.展开更多
The volume fraction and morphology of acicular ferrite evolution in a high strength high toughness weld metal were studied and the mechanical properties of weld metal under heat input of 21 kJ/cm with and without fast...The volume fraction and morphology of acicular ferrite evolution in a high strength high toughness weld metal were studied and the mechanical properties of weld metal under heat input of 21 kJ/cm with and without fast cooling were tested. The results show the weld metal can obtain a large proportion of acicular ferrite during a wide range of cooling rate and the sizes of acicular ferrite in length and thickness decrease with cooling rate increasing. The weld metal exhibited high tensile strength （895 MPa and 870 MPa） and good low temperature toughness （average AKv-30℃ 104 J and 79. 2 J）. The higher tensile strength and better low temperature toughness of the weld metal under fast cooling are due to the more refined grain of acicular ferrite.展开更多
Acicular Ferrite(AF) is beneficial in welds because it provides a tough and strong microstructure.Therefore,much works have been done in the study of the effect of alloying elements and welding conditions aimed at obt...Acicular Ferrite(AF) is beneficial in welds because it provides a tough and strong microstructure.Therefore,much works have been done in the study of the effect of alloying elements and welding conditions aimed at obtaining more AF in the weld metal.However,the knowledge about the nature of AF is limited due to the lack of kinetics researches.In this paper,the kinetic curves of AF transformation in an X65 weld metal were established by means of welding thermal simulation test.The results showed that AF transformation is a typical diffusion process of nucleation and growth with incubation period.AF transformation in weld metal obeys the relationship described by JMA Equation.The effect of welding heat input was also studied.展开更多
Theacicular austeniteformation process duringintercritical annealing atslow heating speedof0 5 ℃/ min isinvestigated using TEMin the sample of 30 CrMnSiA. The resultsshow thatinthe preliminarystage, austenitesnucle...Theacicular austeniteformation process duringintercritical annealing atslow heating speedof0 5 ℃/ min isinvestigated using TEMin the sample of 30 CrMnSiA. The resultsshow thatinthe preliminarystage, austenitesnucleateintheform ofshortneedle atshort rod like cementites, which hasthesame orientation and precipitates along the boundary of original martensitelathes. Asthetemperatureincreasingslowly, the austenites grow up and connect witheach other alongtheboundaryoftheoriginallathesso astoform acicular austenite. At last,the fully grown austenite connectsin the direction verticalto the boundary of lathes, leavingthe remnant ferrites appear in the shape of rhombus, the original austenite grainshaperecovers and the feature of thethick lath remains. The superledgeinterface has been found and someaustenitegrowsintoferritein theshapeoflath.展开更多
基金supported by the National Natural Science Foundation of China(No.U1960202).
文摘The mechanisms of oxide metallurgy include inducing the formation of intragranular acicular ferrite(IAF)using micron-sized inclusions and restricting the growth of prior austenite grains(PAGs)by nanosized particles during welding.The chaotically oriented IAF and refined PAGs inhibit crack initiation and propagation in the steel,resulting in high impact toughness.This work summarizes the com-bined effect of deoxidizers and alloying elements,with the aim to provide a new perspective for the research and practice related to im-proving the impact toughness of the heat affected zone(HAZ)during the high heat input welding.Ti complex deoxidation with other strong deoxidants,such as Mg,Ca,Zr,and rare earth metals(REMs),can improve the toughness of the heat-affected zone(HAZ)by re-fining PAGs or increasing IAF contents.However,it is difficult to identify the specific phase responsible for IAF nucleation because ef-fective inclusions formed by complex deoxidation are usually multiphase.Increasing alloying elements,such as C,Si,Al,Nb,or Cr,con-tents can impair HAZ toughness.A high C content typically increases the number of coarse carbides and decreases the potency of IAF formation.Si,Cr,or Al addition leads to the formation of undesirable microstructures.Nb reduces the high-temperature stability of the precipitates.Mo,V,and B can enhance HAZ toughness.Mo-containing precipitates present good thermal stability.VN or V(C,N)is ef-fective in promoting IAF nucleation due to its good coherent crystallographic relationship with ferrite.The formation of the B-depleted zone around the inclusion promotes IAF formation.The interactions between alloying elements are complex,and the effect of adding dif-ferent alloying elements remains to be evaluated.In the future,the interactions between various alloying elements and their effects on ox-ide metallurgy,as well as the calculation of the nucleation effects of effective inclusions using first principles calculations will become the focus of oxide metallurgy.
文摘The aspects of two pipeline steels with different technologies were investigated by using transmission electron microscopy （TEM） and electron back-scattered diffraction （EBSD）. The microstructure presents a typical acicular ferrite characteristic with fine particles of martensite/austenite （M/A） constituent, which distributes in grains and at grain boundaries. The bulk textures of the pipeline steel plate are {112}〈110〉 and 〈111〉 fibers, respectively, and the {112}〈110〉 component is the favorable texture benefiting for drop weight tear test. Moreover, low angle boundaries and low coincidence site lattice boundaries are inactive and more resistant to fracture than high energy random boundaries.
基金financially supported by the National Natural Science Foundation of China (No. 51674071)
文摘The formation mechanism of acicular ferrite and its microstructural characteristics in 430 ferrite stainless steel with TiC additions were studied by theory and experiment.Using an"edge?to?edge matching"model,a 5.25 mismatch between TiC(FCC structure)and ferritic stainless steel(BCC structure)was identified,which met the mismatch requirement for the heterogeneous nucleation of 430 ferritic stainless steel.TiC was found to be an effective nucleation site for the formation of acicular ferrite in a smelting experiment,as analyzed by metallographic examination,Image-Pro Plus 6.0 analysis software,and SEM–EDS.Furthermore,small inclusions in the size of 2–4?m increased the probability of acicular ferrite nucleation,and the secondary acicular ferrite would grow sympathetically from the initial acicular ferrite to produce multi-dimensional acicular ferrites.Moreover,the addition of Ti C can increase the average microstrain and dislocation density of 430 ferrite stainless steel,as calculated by Williamson-Hall(WH)method,which could play some role in strengthening the dislocation.
基金supported by the National Natural Science Foundation of China (Nos.50471107 and 50734004)
文摘An ultra-low carbon acicular ferrite steel heavy plate was obtained with an advanced thermo-mechanical control process-relaxed precipitation controlled transformation （TMCP-RPC） at Xiangtan Steel, Valin Group. The heavy plate has a tensile strength of approximately 600 MPa with a lower yield ratio. The impact toughness of the heavy plate achieves 280 J at ？40°C. The fine-grained mixed microstructures of the heavy plate mainly consist of acicular ferrite, granular bainite, and polygonal ferrite. The high strength and excellent toughness of the heavy plate are attributed to the formation of acicular ferrite microstructure. The prevention of blocks of martensite/retained austenite （M/A） and the higher cleanness are also responsible for the superior toughness.
文摘The morphology, structure, and chemical composition of precipitates in the final microstructure of Nb-V-Ti microalloyed X70 acicular ferrite pipeline steel were investigated using transmission electron microscopy （TEM） and energy dispersive X-ray spectroscopy （EDS）. Precipitates observed by TEM can be classified into two groups. The large precipitates are complex compounds that comprise square-shaped TiN precipitate as core with fine Nb-containing precipitate nucleated on pre-existing TiN precipitate as caps on one or more faces at high temperature. In contrast, the fine and spherical Nb carbides and/or carbonitrides precipitate heterogeneously on dislocations and sub-boundaries at low temperature. From the analysis in terms of thermodynamics, EDS and chemical cornposition of the steel, NbC precipitation is considered to be the predominant precipitation behavior in the tested steel under the processing conditions of this research.
基金This work was financially supported by the National Natural Science Foundation of China (No.50574010)the National Doctor-ate Fund of the Ministry of Education of China (No.20060008015)
文摘Nucleation of acicular ferrite and its influence factors in non quenched-and-tempered steel was studied by using TEM and thermodynamic calculation. The results show that the complex particles with a center made of Ti oxide, Al2O3, and silicate and an outside made of a small quantity of mixture of TiN and MnS are able to act as ferrite nucleation nuclei. The acicular ferrite percentage changes little with Ti. When the oxygen content was 80 ppm, the volume percentage of acicular ferrite decreased due to an increase in allotriomorphic ferrite. The larger the cooling rate and the shorter the incubation time, the finer the titanium oxide and the higher the nucleation ratio of acicular ferrite.
基金The present work was financially supported by a China National‘973’Project No.G1998061511the Natural Science Fund of Hebei Province No.501205.
文摘Acicular ferrite microstructure was achieved for an ultralow carbon pipeline steel through the improved thermome chanical control process (TMCP), which was based on the transformation process of deformed austenite of steel. Compared with commercial pipeline steels, the experimental ultralow carbon pipeline steel possessed the satisfied strength and toughness behaviors under the current improved TMCP, although it contained only approximately 0.025% C, vvhich should mainly be attributed to the microstructural characteristics of acicular ferrite.
基金financially supported by the China National Funds for Distinguished Young Scientists (No. 51325401)the International Thermonuclear Experimental Reactor (ITER) Program Special Project (No. 2014GB125006)+1 种基金the Major State Basic Research Development Program of China (No. 2014CB046805)the Natural Science Foundation of Tianjin City (No. 14JCZDJC38700)
文摘The effect of acicular ferrite （AF） on banded structures in low-carbon microalloyed steel with Mn segregation during both iso- thermal transformation and continuous cooling processes was studied by dilatometry and microscopic observation. With respect to the iso- thermal transformation process, the specimen isothermed at 550℃ consisted of AF in Mn-poor bands and martensite in Mn-rich bands, whereas the specimen isothermed at 450℃ exhibited two different morphologies of AF that appeared as bands. At a continuous cooling rate in the range of 4 to 50℃/s, a mixture of AF and martensite formed in both segregated bands, and the volume fraction of martensite in Mn-rich bands was always higher than that in Mn-poor bands. An increased cooling rate resulted in a decrease in the difference of martensite volume fraction between Mn-rich and Mn-poor bands and thereby leaded to less distinct microstrucmral banding. The results show that Mn segregation and cooling rate strongly affect the formation of AF-containing banded structures. The formation mechanism of microstructural banding was also discussed.
基金support from NSFC(National Natural Science Foundation of China,under Grant No. 50734004)
文摘The volume fraction and morphology of acicular ferrite evolution in a high strength high toughness weld metal were studied and the mechanical properties of weld metal under heat input of 21 kJ/cm with and without fast cooling were tested. The results show the weld metal can obtain a large proportion of acicular ferrite during a wide range of cooling rate and the sizes of acicular ferrite in length and thickness decrease with cooling rate increasing. The weld metal exhibited high tensile strength （895 MPa and 870 MPa） and good low temperature toughness （average AKv-30℃ 104 J and 79. 2 J）. The higher tensile strength and better low temperature toughness of the weld metal under fast cooling are due to the more refined grain of acicular ferrite.
文摘Acicular Ferrite(AF) is beneficial in welds because it provides a tough and strong microstructure.Therefore,much works have been done in the study of the effect of alloying elements and welding conditions aimed at obtaining more AF in the weld metal.However,the knowledge about the nature of AF is limited due to the lack of kinetics researches.In this paper,the kinetic curves of AF transformation in an X65 weld metal were established by means of welding thermal simulation test.The results showed that AF transformation is a typical diffusion process of nucleation and growth with incubation period.AF transformation in weld metal obeys the relationship described by JMA Equation.The effect of welding heat input was also studied.
文摘Theacicular austeniteformation process duringintercritical annealing atslow heating speedof0 5 ℃/ min isinvestigated using TEMin the sample of 30 CrMnSiA. The resultsshow thatinthe preliminarystage, austenitesnucleateintheform ofshortneedle atshort rod like cementites, which hasthesame orientation and precipitates along the boundary of original martensitelathes. Asthetemperatureincreasingslowly, the austenites grow up and connect witheach other alongtheboundaryoftheoriginallathesso astoform acicular austenite. At last,the fully grown austenite connectsin the direction verticalto the boundary of lathes, leavingthe remnant ferrites appear in the shape of rhombus, the original austenite grainshaperecovers and the feature of thethick lath remains. The superledgeinterface has been found and someaustenitegrowsintoferritein theshapeoflath.