The effect of aging on the mechanical properties and microstructures of a new ZG12Cr9 MolColNiVNbNB ferritic heat resistant steel was investigated in this work to satisfy the high steam parameters of the ultra-supercr...The effect of aging on the mechanical properties and microstructures of a new ZG12Cr9 MolColNiVNbNB ferritic heat resistant steel was investigated in this work to satisfy the high steam parameters of the ultra-supercritical power plant.The results show that the main precipitates during aging are Fe（Cr,Mo）23C6,V（Nb）C,and（Fe2Mo） Laves in the steel.The amounts of the precipitated phases increase during aging,and correspondingly,the morphologies of phases are similar to be round.Fe（Cr,Mo）23C6 appears along boundaries and grows with increasing temperature.In addition,it is revealed that the martensitic laths are coarsened and eventually happen to be polygonization.The hardness and strength decrease gradually,whereas the plasticity of the steel increases.What＇s more,the hardness of this steel after creep is similar to that of other 9%-12%Cr ferritic steels.Thus,ZG12Cr9 MolColNiVNbNB can be used in the project.展开更多
Thermal stabilities of microstructure and mechanical property have been investigated on superalloy U720Li, which is of great interest of application for jet engine and land-based turbine disc. The results showed that,...Thermal stabilities of microstructure and mechanical property have been investigated on superalloy U720Li, which is of great interest of application for jet engine and land-based turbine disc. The results showed that, the primary and secondary gamma' particles maintain good thermal stability at 650 and 700 degreesC with aging time up to 3000 h, while the tertiary gamma' is apparently dependent on aging temperature and time. The tertiary gamma' particles undergo a procedure of coarsening, dissolution and eventually complete disappearance with the increasing of aging time and temperature. They exhibit unusual high sensibility upon aging temperature, which is attributed to the lattice misfit between the gamma' precipitates and the matrix in the alloy. The grain boundary phase M23C6 remains stable without forming of sigma phase even with aging time up to 3000 h at 700 degreesC. Microhardness decreases apparently with increasing aging time and aging temperature. Theoretical analysis based on dislocation mechanism indicates that the change of microhardness should be attributed to the evolution of the tertiary gamma' during aging.展开更多
Microstructure evolution and the changes in mechanical properties of HR3 Csteel during long-term aging at650,700 and 750℃ were investigated.The precipitated phases of the aging steel included M23C6 carbides,Z-phase a...Microstructure evolution and the changes in mechanical properties of HR3 Csteel during long-term aging at650,700 and 750℃ were investigated.The precipitated phases of the aging steel included M23C6 carbides,Z-phase and a trace amount of Nb（C,N）.The M23C6 carbides were distributed mainly at the grain boundary,while Z-phase was mainly inside the grains.Amounts of both M23C6 carbides and Z-phase during the aging process increased with increasing aging period and temperature.Coarsening of M23C6 carbides was influenced significantly by aging time and temperature,while the size of the Z-phase was relatively less affected by the aging time and temperature,which had a steady strengthening effect.Coarsening of the M23C6 carbides was the main reason for the decline in high temperature yield strength during long-term aging at 750℃.The M23C6 carbides were linked into a continuous chain along the grain boundary which accounted for the decrease of toughness during aging.展开更多
The effects of different aging processes on the microstructure and mechanical properties of a novel Al-Cu-Li alloy have been investigated by X-ray diffraction, scanning electron microscopy and transmission electron mi...The effects of different aging processes on the microstructure and mechanical properties of a novel Al-Cu-Li alloy have been investigated by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. It is found that the tensile properties of a novel Al-Cu-Li alloy are sensitive to aging processes, which correspond to different microstructures. σ（Al_5Cu_6Mg_2） and T_1（Al_2CuLi） phases are the major precipitates for the alloy in T6 aging condition（165 ℃/60 h）. After duplex aging condition（150 ℃/24 h ＋ 180 ℃/12 h）, σ, θ＇（Al_2Cu） and T_1 phases are detected. Only the T_1 phases can be found in the T8 state alloy（6% pre-strain＋135 ℃/60 h）. The failure modes of alloy in T6 and duplex aging conditions are dimple-intergranular fracture, while typical quasi-cleavage fracture in T8 condition.展开更多
The fiber properties depending on the coating thickness and long-term time aging were investigated. The coating strip forces of optical fiber were strongly increased with secondary coating thickness. But it did not ch...The fiber properties depending on the coating thickness and long-term time aging were investigated. The coating strip forces of optical fiber were strongly increased with secondary coating thickness. But it did not change with time aging up to 90 days. The tensile strength and stress corrosion parameters of coated fiber were increased with time aging also but the increasing rate was quite different depending on the coating展开更多
To investigate the effect of high temperature ageing on the microstructure and mechanical properties of S31042steel,solid solution treatment at 700℃ was carried out for various time from 10to 6 000h.Experimental resu...To investigate the effect of high temperature ageing on the microstructure and mechanical properties of S31042steel,solid solution treatment at 700℃ was carried out for various time from 10to 6 000h.Experimental results showed that the change of mechanical properties is closely related to the amount of precipitated phases.During ageing from 10to 300h,precipitation in the tested steel increases rapidly,and correspondingly,the high temperature yield strength and room temperature hardness of tested steel increase rapidly.Meanwhile,the thickness of the secondary phase on grain boundaries widens sharply and the room temperature Charpy impact absorb energy decreases.Ageing beyond 300h,the precipitation in the steel increases gradually and the precipitates coarsen to a certain extent.The high temperature yield strength of the steel keeps stable,and the room temperature Charpy impact energy and hardness decrease slowly.Ageing beyond 3 000h,the mechanical properties of the steel tend to be stable.The main precipitates are M23C6,NbCrN and NbC in the tested steel.展开更多
Al-Si-Fe-Cu-Mg alloy was prepared by spray deposition and was further processed by hot extrusion as well as T6heat-treatment.The results indicate that the microstructure of the deposited alloy is composed of primary S...Al-Si-Fe-Cu-Mg alloy was prepared by spray deposition and was further processed by hot extrusion as well as T6heat-treatment.The results indicate that the microstructure of the deposited alloy is composed of primary Si particles with average size of less than 5μm,α-Al,Al_2CuMg,β-Al_5FeSi andδ-Al_4FeSi_2（rectangular shape）,and no eutectic silicon is found due to the special solidification behavior.The age hardening curves reveal two peaks.The uniform ultimate tensile strength（UTS）and the elongation of the peak-aged Al-Si-Fe-Cu-Mg alloy are 468.3 MPa,0.61% at 298 Kand 267.4MPa,6.42% at 573 K,respectively.The fracture surfaces display brittle fracture morphology at 298 K,whereas it varies to mixture of brittle and ductile failure with increasing the temperature.展开更多
The microstructural evolution and mechanical properties of a spray-formed superalloy were studied in this paper. Based on a better understanding of the microstructural evolution of the spray-formed superalloy during s...The microstructural evolution and mechanical properties of a spray-formed superalloy were studied in this paper. Based on a better understanding of the microstructural evolution of the spray-formed superalloy during solution treatment, an optimum solution treatment process was obtained, namely, at 1,140 °C for 6 h, and air cooling（AC）. The effects of the ageing treatments on the mechanical properties of the post-solution-treated spray-formed superalloy were evaluated using ageing harden curves and tensile testing. The results indicated that the maximum hardness value was achieved at 850 °C for 8 h, AC. Due to co-precipitation of primary and secondary c0 precipitates during the heat treatment,the spray-formed superalloy obtained an excellent combination of yield strength（YS = 1,110 MPa）, ultimate tensile strength（UTS = 1,503 MPa）, ductility（elongation, EL = 21%） and excellent stress rupture properties at 650 °C（UTS = 1,209 MPa, EL = 15.8%）. The heat treatment also improved the rupture life at 650 °C/950 MPa and 750 °C/539 MPa up to 140 h without rupturing. The tensile-fractured surfaces exhibit ductile transgranular failure feature. The optimum heat treatment process was determined to be 1,140 °C/6 h＋850 °C/8 h＋AC.展开更多
To evaluate the property of the organic coatings in oil and gas plants, the aging process was studied in high temperature and high CO_2 partial pressure environment. Correlations were developed between the macroscopic...To evaluate the property of the organic coatings in oil and gas plants, the aging process was studied in high temperature and high CO_2 partial pressure environment. Correlations were developed between the macroscopic properties and microstructure of the organic coatings. The surface appearance, mechanical properties, and permeability of the organic coatings were measured. Furthermore, the crystal structure of the organic coatings was investigated through synchrotron radiation grazing incidence X-ray diffraction（GIXRD） on the BL14B1 beam line in Shanghai Synchrotron Radiation Facility. Combined with the Fourier transform infrared spectroscopy, the molecular structure of the organic coatings was investigated. The experimental results indicate that the thickness variation and weight loss of the organic coatings increase with the immersion time, and the penetration resistance of the coating obviously decreases as the temperature rises. Moreover, the degradation of the organic coatings with immersion time in high temperature and high CO_2 partial pressure environment is caused by the amorphization of the organic coatings as the groups and bonds of the organic coatings were not damaged.展开更多
In this paper,the evolutions of microstructure and mechanical properties of Cu-l.9Be-0.3Ni-0.15Co alloy were studied.The alloys in the condition of the solution treated（soft state） and 37% cold rolled（hard state） ...In this paper,the evolutions of microstructure and mechanical properties of Cu-l.9Be-0.3Ni-0.15Co alloy were studied.The alloys in the condition of the solution treated（soft state） and 37% cold rolled（hard state） were aged at 320 ℃for different time,respectively.The mechanical properties,electrical conductivity and microstructure of the alloy aged for different time were analyzed.Additionally,the precipitation kinetics of Cu-1.9Be-0.3Ni-0.15Co alloys was investigated.X-ray diffraction and transmission electron microscopy results reveal that both continuous precipitation and discontinuous precipitation existed in the hard-state Cu-l.9Be-0.3Ni-0.15Co alloy during the whole aging process;the sequence of continuous precipitation is G.P.zone →γ″→γ′→γ.Furthermore,the precipitation transformation mechanism of softstate alloy is homogeneous nucleation,while hard-state alloy shows the heterogeneous nucleation（interface nucleation）with the nucleation rate of both states decaying rapidly to zero during aging at 320 ℃.展开更多
Oxide-dispersion-strengthened （ODS） ferritic steels are promising candidates for structural applications in the future nuclear reactors. The higher chromium contents of ODS ferritic steels, the better the corrosion ...Oxide-dispersion-strengthened （ODS） ferritic steels are promising candidates for structural applications in the future nuclear reactors. The higher chromium contents of ODS ferritic steels, the better the corrosion resistance, which can meet the harsh corrosion environment of the advanced reactors. However, increasing the Cr content may also lead to the brittleness of the ODS steels when serving at high temperatures. The ODS ferritic steels with different Cr contents （12, 16 and 18 wt% Cr, respectively） were fabricated by mechanical alloying, hot isostatic pressing and forging. Mechanical properties and microstructure evolution of the ODS ferritic steels after aging at 753 K for 2000 h were investigated. It is found that both Vickers hardness and yield strength of 18%Cr ODS ferritic steel were strongly increased and the impact energy was decreased after aging at 753 K. In order to explore the reasons for changes in the mechanical properties, the fracture surfaces were characterized by scanning electron microscopy, and microstructures after aging were observed by transmission electron microscopy. The impact fracture of 18%Cr ODS ferritic steel belongs to quasi-cleavage facture, which is consistent with its very low impact energy. The grain size and dispersed oxide particles of different ODS steels are very stable. M23C6 carbide and M2C carbide were found in 12%Cr ODS steel and 16%Cr ODS steels, respectively.展开更多
基金supported by the Science and Technology Program of Sichuan Province,China(No.2013GZX0146)
文摘The effect of aging on the mechanical properties and microstructures of a new ZG12Cr9 MolColNiVNbNB ferritic heat resistant steel was investigated in this work to satisfy the high steam parameters of the ultra-supercritical power plant.The results show that the main precipitates during aging are Fe（Cr,Mo）23C6,V（Nb）C,and（Fe2Mo） Laves in the steel.The amounts of the precipitated phases increase during aging,and correspondingly,the morphologies of phases are similar to be round.Fe（Cr,Mo）23C6 appears along boundaries and grows with increasing temperature.In addition,it is revealed that the martensitic laths are coarsened and eventually happen to be polygonization.The hardness and strength decrease gradually,whereas the plasticity of the steel increases.What＇s more,the hardness of this steel after creep is similar to that of other 9%-12%Cr ferritic steels.Thus,ZG12Cr9 MolColNiVNbNB can be used in the project.
文摘Thermal stabilities of microstructure and mechanical property have been investigated on superalloy U720Li, which is of great interest of application for jet engine and land-based turbine disc. The results showed that, the primary and secondary gamma' particles maintain good thermal stability at 650 and 700 degreesC with aging time up to 3000 h, while the tertiary gamma' is apparently dependent on aging temperature and time. The tertiary gamma' particles undergo a procedure of coarsening, dissolution and eventually complete disappearance with the increasing of aging time and temperature. They exhibit unusual high sensibility upon aging temperature, which is attributed to the lattice misfit between the gamma' precipitates and the matrix in the alloy. The grain boundary phase M23C6 remains stable without forming of sigma phase even with aging time up to 3000 h at 700 degreesC. Microhardness decreases apparently with increasing aging time and aging temperature. Theoretical analysis based on dislocation mechanism indicates that the change of microhardness should be attributed to the evolution of the tertiary gamma' during aging.
基金Item Sponsored by National High-Tech Research and Development Program(863Program)of China(2012AA03A501)International Science and Technology Cooperation Program of China(2012DFG51670)
文摘Microstructure evolution and the changes in mechanical properties of HR3 Csteel during long-term aging at650,700 and 750℃ were investigated.The precipitated phases of the aging steel included M23C6 carbides,Z-phase and a trace amount of Nb（C,N）.The M23C6 carbides were distributed mainly at the grain boundary,while Z-phase was mainly inside the grains.Amounts of both M23C6 carbides and Z-phase during the aging process increased with increasing aging period and temperature.Coarsening of M23C6 carbides was influenced significantly by aging time and temperature,while the size of the Z-phase was relatively less affected by the aging time and temperature,which had a steady strengthening effect.Coarsening of the M23C6 carbides was the main reason for the decline in high temperature yield strength during long-term aging at 750℃.The M23C6 carbides were linked into a continuous chain along the grain boundary which accounted for the decrease of toughness during aging.
基金the National High Technology Research and Development Program of China (Grant No.2013AA032401)
文摘The effects of different aging processes on the microstructure and mechanical properties of a novel Al-Cu-Li alloy have been investigated by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. It is found that the tensile properties of a novel Al-Cu-Li alloy are sensitive to aging processes, which correspond to different microstructures. σ（Al_5Cu_6Mg_2） and T_1（Al_2CuLi） phases are the major precipitates for the alloy in T6 aging condition（165 ℃/60 h）. After duplex aging condition（150 ℃/24 h ＋ 180 ℃/12 h）, σ, θ＇（Al_2Cu） and T_1 phases are detected. Only the T_1 phases can be found in the T8 state alloy（6% pre-strain＋135 ℃/60 h）. The failure modes of alloy in T6 and duplex aging conditions are dimple-intergranular fracture, while typical quasi-cleavage fracture in T8 condition.
文摘The fiber properties depending on the coating thickness and long-term time aging were investigated. The coating strip forces of optical fiber were strongly increased with secondary coating thickness. But it did not change with time aging up to 90 days. The tensile strength and stress corrosion parameters of coated fiber were increased with time aging also but the increasing rate was quite different depending on the coating
基金Sponsored by National Science and Technology Support Plan of China(2007BAE51B02)
文摘To investigate the effect of high temperature ageing on the microstructure and mechanical properties of S31042steel,solid solution treatment at 700℃ was carried out for various time from 10to 6 000h.Experimental results showed that the change of mechanical properties is closely related to the amount of precipitated phases.During ageing from 10to 300h,precipitation in the tested steel increases rapidly,and correspondingly,the high temperature yield strength and room temperature hardness of tested steel increase rapidly.Meanwhile,the thickness of the secondary phase on grain boundaries widens sharply and the room temperature Charpy impact absorb energy decreases.Ageing beyond 300h,the precipitation in the steel increases gradually and the precipitates coarsen to a certain extent.The high temperature yield strength of the steel keeps stable,and the room temperature Charpy impact energy and hardness decrease slowly.Ageing beyond 3 000h,the mechanical properties of the steel tend to be stable.The main precipitates are M23C6,NbCrN and NbC in the tested steel.
基金Item Sponsored by National Natural Science Foundation of China(51375110)Scientific Research Foundation of Inner Mongolia University of Technology of China(ZD201405)
文摘Al-Si-Fe-Cu-Mg alloy was prepared by spray deposition and was further processed by hot extrusion as well as T6heat-treatment.The results indicate that the microstructure of the deposited alloy is composed of primary Si particles with average size of less than 5μm,α-Al,Al_2CuMg,β-Al_5FeSi andδ-Al_4FeSi_2（rectangular shape）,and no eutectic silicon is found due to the special solidification behavior.The age hardening curves reveal two peaks.The uniform ultimate tensile strength（UTS）and the elongation of the peak-aged Al-Si-Fe-Cu-Mg alloy are 468.3 MPa,0.61% at 298 Kand 267.4MPa,6.42% at 573 K,respectively.The fracture surfaces display brittle fracture morphology at 298 K,whereas it varies to mixture of brittle and ductile failure with increasing the temperature.
基金financially supported by the Heilongjiang Provincial Natural Science Foundation of China (No. 201107)
文摘The microstructural evolution and mechanical properties of a spray-formed superalloy were studied in this paper. Based on a better understanding of the microstructural evolution of the spray-formed superalloy during solution treatment, an optimum solution treatment process was obtained, namely, at 1,140 °C for 6 h, and air cooling（AC）. The effects of the ageing treatments on the mechanical properties of the post-solution-treated spray-formed superalloy were evaluated using ageing harden curves and tensile testing. The results indicated that the maximum hardness value was achieved at 850 °C for 8 h, AC. Due to co-precipitation of primary and secondary c0 precipitates during the heat treatment,the spray-formed superalloy obtained an excellent combination of yield strength（YS = 1,110 MPa）, ultimate tensile strength（UTS = 1,503 MPa）, ductility（elongation, EL = 21%） and excellent stress rupture properties at 650 °C（UTS = 1,209 MPa, EL = 15.8%）. The heat treatment also improved the rupture life at 650 °C/950 MPa and 750 °C/539 MPa up to 140 h without rupturing. The tensile-fractured surfaces exhibit ductile transgranular failure feature. The optimum heat treatment process was determined to be 1,140 °C/6 h＋850 °C/8 h＋AC.
基金Funded by the National Science and Technology Major Project(2011ZX05022-013)
文摘To evaluate the property of the organic coatings in oil and gas plants, the aging process was studied in high temperature and high CO_2 partial pressure environment. Correlations were developed between the macroscopic properties and microstructure of the organic coatings. The surface appearance, mechanical properties, and permeability of the organic coatings were measured. Furthermore, the crystal structure of the organic coatings was investigated through synchrotron radiation grazing incidence X-ray diffraction（GIXRD） on the BL14B1 beam line in Shanghai Synchrotron Radiation Facility. Combined with the Fourier transform infrared spectroscopy, the molecular structure of the organic coatings was investigated. The experimental results indicate that the thickness variation and weight loss of the organic coatings increase with the immersion time, and the penetration resistance of the coating obviously decreases as the temperature rises. Moreover, the degradation of the organic coatings with immersion time in high temperature and high CO_2 partial pressure environment is caused by the amorphization of the organic coatings as the groups and bonds of the organic coatings were not damaged.
基金supported by Materials Forming Processing Control and Simulation Laboratory in University of Science and Technology BeijingCNMC Ningxia Orient Group Co.,Ltd.
文摘In this paper,the evolutions of microstructure and mechanical properties of Cu-l.9Be-0.3Ni-0.15Co alloy were studied.The alloys in the condition of the solution treated（soft state） and 37% cold rolled（hard state） were aged at 320 ℃for different time,respectively.The mechanical properties,electrical conductivity and microstructure of the alloy aged for different time were analyzed.Additionally,the precipitation kinetics of Cu-1.9Be-0.3Ni-0.15Co alloys was investigated.X-ray diffraction and transmission electron microscopy results reveal that both continuous precipitation and discontinuous precipitation existed in the hard-state Cu-l.9Be-0.3Ni-0.15Co alloy during the whole aging process;the sequence of continuous precipitation is G.P.zone →γ″→γ′→γ.Furthermore,the precipitation transformation mechanism of softstate alloy is homogeneous nucleation,while hard-state alloy shows the heterogeneous nucleation（interface nucleation）with the nucleation rate of both states decaying rapidly to zero during aging at 320 ℃.
文摘Oxide-dispersion-strengthened （ODS） ferritic steels are promising candidates for structural applications in the future nuclear reactors. The higher chromium contents of ODS ferritic steels, the better the corrosion resistance, which can meet the harsh corrosion environment of the advanced reactors. However, increasing the Cr content may also lead to the brittleness of the ODS steels when serving at high temperatures. The ODS ferritic steels with different Cr contents （12, 16 and 18 wt% Cr, respectively） were fabricated by mechanical alloying, hot isostatic pressing and forging. Mechanical properties and microstructure evolution of the ODS ferritic steels after aging at 753 K for 2000 h were investigated. It is found that both Vickers hardness and yield strength of 18%Cr ODS ferritic steel were strongly increased and the impact energy was decreased after aging at 753 K. In order to explore the reasons for changes in the mechanical properties, the fracture surfaces were characterized by scanning electron microscopy, and microstructures after aging were observed by transmission electron microscopy. The impact fracture of 18%Cr ODS ferritic steel belongs to quasi-cleavage facture, which is consistent with its very low impact energy. The grain size and dispersed oxide particles of different ODS steels are very stable. M23C6 carbide and M2C carbide were found in 12%Cr ODS steel and 16%Cr ODS steels, respectively.