In order to enhance the strength of sustainable walnut shell/Co-PES(WSPC)sintered parts,wax-filtrated posttreatment was carried out.The effects of treating fluid temperature,preheating time and immersion time on the b...In order to enhance the strength of sustainable walnut shell/Co-PES(WSPC)sintered parts,wax-filtrated posttreatment was carried out.The effects of treating fluid temperature,preheating time and immersion time on the bending strength of WSPC wax-filtrated parts were analyzed by single factor analysis method.To obtain an accurate model for predicting the bending strength of the WSPC wax-filtrated part,the experiments were involved by using Box-Behnken design(BBD).Main parameters,such as treating fluid temperature,preheating time and immersion time,and their interactive effects were analyzed through analysis of variance(ANOVA)and graphical contours.The results demonstrated that all parameters’direct effects were significant to bending strength of the WSPC wax-filtrated part.Its optimum value was 5.0 MPa when the treating fluid temperature of 70°C,preheating time of 50 min,and immersion time of 20 s.The predicted models effectively validated had good predicting accuracy.The WSPC wax-filtrated part using optimal processing parameters was processed by investment casting,and then the metal casting of dimensional stability and smooth surface was obtained.Investment casting was done using WSPC wax-filtrated parts under optimal process parameters and then metal parts with stable structure size and smooth surface can be obtained,which indicates that WSPC material can be used for investment casting.展开更多
A calculation model of stress field in laser additive manufacturing of walnut shell composite powder(walnut shell/Co-PES powder)was established.The DFLUX subroutine was used to implement the moveable application of a ...A calculation model of stress field in laser additive manufacturing of walnut shell composite powder(walnut shell/Co-PES powder)was established.The DFLUX subroutine was used to implement the moveable application of a double ellipsoid heat source by considering the mechanical properties varying with temperature.The stress field was simulated by the sequential coupling method,and the experimental results were in good accordance with the simulation results.In addition,the distribution and variation of stress and strain field were obtained in the process of laser additive manufacturing of walnut shell composite powder.The displacement of laser additive manufacturing walnut shell composite parts gradually decreased with increasing preheating temperature,decreasing laser power and increasing scanning speed.During the cooling process,the displacement of laser additive manufacturing of walnut shell composite parts gradually increased with the increasing preheating temperature,decreasing scanning speed and increasing laser power.展开更多
基金This study was supported by Scientific Research Staring Foundation of Northeast Petroleum University(1305021868)the National Natural Science Foundation of China(51475089)+3 种基金the National Key R&D Program of China(2017YFD0601004)the Natural Science Foundation of Heilongjiang Province(ZD2017009)Fundamental Research Funds for the Central Universities(2572017PZ06)the Special Project of Scientific and Technological Development of Central Guidance for Local(ZY16C03).
文摘In order to enhance the strength of sustainable walnut shell/Co-PES(WSPC)sintered parts,wax-filtrated posttreatment was carried out.The effects of treating fluid temperature,preheating time and immersion time on the bending strength of WSPC wax-filtrated parts were analyzed by single factor analysis method.To obtain an accurate model for predicting the bending strength of the WSPC wax-filtrated part,the experiments were involved by using Box-Behnken design(BBD).Main parameters,such as treating fluid temperature,preheating time and immersion time,and their interactive effects were analyzed through analysis of variance(ANOVA)and graphical contours.The results demonstrated that all parameters’direct effects were significant to bending strength of the WSPC wax-filtrated part.Its optimum value was 5.0 MPa when the treating fluid temperature of 70°C,preheating time of 50 min,and immersion time of 20 s.The predicted models effectively validated had good predicting accuracy.The WSPC wax-filtrated part using optimal processing parameters was processed by investment casting,and then the metal casting of dimensional stability and smooth surface was obtained.Investment casting was done using WSPC wax-filtrated parts under optimal process parameters and then metal parts with stable structure size and smooth surface can be obtained,which indicates that WSPC material can be used for investment casting.
基金Supported by the Scientific Research Start-Up Fund Project of Northeast Petroleum University(2019KQ67 and 2021KQ09)the Guiding Innovation Fund Project of Northeast Petroleum University(2021YDL-13)+1 种基金National Natural Science Foundation of China(52075090)Supported by the National Key R&D Program of China(2017YFD0601004).
文摘A calculation model of stress field in laser additive manufacturing of walnut shell composite powder(walnut shell/Co-PES powder)was established.The DFLUX subroutine was used to implement the moveable application of a double ellipsoid heat source by considering the mechanical properties varying with temperature.The stress field was simulated by the sequential coupling method,and the experimental results were in good accordance with the simulation results.In addition,the distribution and variation of stress and strain field were obtained in the process of laser additive manufacturing of walnut shell composite powder.The displacement of laser additive manufacturing walnut shell composite parts gradually decreased with increasing preheating temperature,decreasing laser power and increasing scanning speed.During the cooling process,the displacement of laser additive manufacturing of walnut shell composite parts gradually increased with the increasing preheating temperature,decreasing scanning speed and increasing laser power.