The purpose of this paper is to examine the effect of processing parameters and subsequent heat treatments on the microstructures and bonding strengths of Ti-6Al-4V/AA1050 laminations formed via a non-equal channel la...The purpose of this paper is to examine the effect of processing parameters and subsequent heat treatments on the microstructures and bonding strengths of Ti-6Al-4V/AA1050 laminations formed via a non-equal channel lateral co-extrusion process.The microstructural evolution and growth mechanism in the diffusion layer were discussed further to optimize the bonding quality by appropriately adjusting process parameters.Scanning electron microscopes(SEM),energy dispersive spectrometer(EDS),and X-ray diffraction(XRD)were used to characterize interfacial diffusion layers.The shear test was used to determine the mechanical properties of the interfacial diffusion layer.The experimental results indicate that it is possible to co-extrusion Ti-6Al-4V/AA1050 compound profiles using non-equal channel lateral co-extrusion.Different heat treatment processes affect the thickness of the diffusion layer.When the temperature and time of heat treatment increase,the thickness of the reaction layers increases dramatically.Additionally,the shear strength of the Ti-6Al-4V/AA1050 composite interface is proportional to the diffusion layer thickness.It is observed that a medium interface thickness results in superior mechanical performance when compared to neither a greater nor a lesser interface thickness.Microstructural characterization of all heat treatments reveals that the only intermetallic compound observed in the diffusion layers is TiAl_(3).Due to the inter-diffusion of Ti and Al atoms,the TiAl_(3) layer grows primarily at AA1050/TiAl_(3) interfaces.展开更多
The performance of solid solution aging treatment on aluminum matrix composites prepared by powder metallurgy and reinforced with 6061 aluminum alloy powder as matrix;meanwhile, nano silicon carbide particles(nm Si Cp...The performance of solid solution aging treatment on aluminum matrix composites prepared by powder metallurgy and reinforced with 6061 aluminum alloy powder as matrix;meanwhile, nano silicon carbide particles(nm Si Cp), submicron silicon carbide particles(1 μm Si Cp) and Ti particles were studied. The Al/Si Cp composite powder was prepared by high-energy ball milling, and then cold-pressed, sintered, hotextruded, and then heat-treated with different solution temperatures and aging times for the extruded composites. Optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy(EDS), X-ray diffractometer(XRD) and extrusion testing were used to analyze and test the microstructure and mechanical properties of aluminum matrix composites. The results show that after the multi-stage solid solution at 530 ℃×2 h+535 ℃×2 h+540 ℃×2 h, the particles are mainly equiaxed grains and uniformly distributed. There is no reinforcement agglomeration, and the surface is dense and the insoluble phase is basically dissolved. In the matrix, the strengthening effect is good, and the hardness and compressive strength are 179.43 HV and 680.42 MPa, respectively. Under this solution process, when the aluminum matrix composites are aged at 170 ℃ for 10 h, the hardness and compressive strength can reach their peaks and increase to 195.82 HV and 721.48 MPa, respectively.展开更多
Multidirectional forging(MDF)was successfully applied to fabricate large-size Mg-Gd-Y-Zn-Zr-Ag alloy in this work and effects of T4,T5 and T6 treatments on the microstructure and mechanical properties of the as-forged...Multidirectional forging(MDF)was successfully applied to fabricate large-size Mg-Gd-Y-Zn-Zr-Ag alloy in this work and effects of T4,T5 and T6 treatments on the microstructure and mechanical properties of the as-forged alloy were analyzed.Results show that dynamic recrystallization(DRX)occurs and second phase particles precipitate along the grain boundary during the MDF process.After annealing treatment(T4),the volume fraction and size of dynamic precipitates slightly increase at a lower temperature(430℃)compared with those of MDFed sample,while they are dissolved into theα-Mg matrix at a higher temperature(450℃).At the meantime,short plate-shaped long-period stacking ordered(LPSO)phases are observed in the DRX grains of the MDFed sample and then dissolved into theα-Mg matrix during annealing at both temperatures.Typical basal texture is identified in the MDFed sample,but the basal pole tilts away from final forging direction and rare-earth texture component with<1121>orientation parallel to penultimate forging direction becomes visible after annealing.The T6 sample annealing at 430℃for 4 h and ageing at 200℃for 34 h exhibits the superior strength and ductility in this study.The ultimate tensile strength,tensile yield strength and elongation to failure,which is 455 MPa,308 MPa and 7.7%,respectively,are overall improved compared with the directly-aged(T5)sample.This paper provides a superior heat treatment schedule to manufacture high-performance large-scale Mg-Gd-Y-Zn-Zr-Ag components for industrial production.展开更多
To enhance the performance of in-situ synthesized 6vol.%(Ti C+Ti B)/TC4 titanium matrix composites fabricated by casting,a variety of heat treatment processes were carried out.Upon conducting microstructure observatio...To enhance the performance of in-situ synthesized 6vol.%(Ti C+Ti B)/TC4 titanium matrix composites fabricated by casting,a variety of heat treatment processes were carried out.Upon conducting microstructure observations following various heat treatments,it was found that the composites exhibit a basketweave microstructure,consisting of an α phase and a transformed β phase.The sizes of(α+β) phases were found to be refined to varying degrees after the heat treatment processes,while the morphology of Ti B remains largely unchanged and Ti C becomes granulated.Compressive testing revealed that all composites subjected to different heat treatments demonstrate a notable increase in ultimate compressive strength as well as a slight improvement in plasticity compared to the as-cast state.The results of the tribological performance test indicated that the heat-treated composites exhibit lower average friction coefficient,specific wear rate,and worn surface roughness compared to the as-cast composite.Among the heat treatment processes studied,the composite solution heated at 1,150 °C/1 h followed by air cooling,then 950 °C/1 h followed by air cooling,and finally 500 °C/4 h followed by air cooling,demonstrates the highest levels of hardness,compressive strength,and wear resistance.These improvements are attributed to the combined effects of solid solution strengthening,grain refinement,and the pinning of dislocation slip.展开更多
Natural foods,such as whole pulses,are recommended in the dietary guidelines of the US and China.The plant cell wall structure in whole pulses has important implications for the nutritional functionalities of starch.I...Natural foods,such as whole pulses,are recommended in the dietary guidelines of the US and China.The plant cell wall structure in whole pulses has important implications for the nutritional functionalities of starch.In this study,garbanzo bean cells with varying degrees of cell wall integrity were subjected to dry heat treatment(DHT)and used to elucidate the food structure-starch digestion properties of pulse food.The morphological features suggested that all cell samples do not exhibit remarkable changes after being subjected to DHT.Molecular rearrangement and the crystallite disruption of starch granules entrapped in cells occurred during DHT as assessed by the crystal structure and thermal properties.DHT decreased the inhibitory effects of enzymes of both the soluble and insoluble components,but the digestion rate and extent of slightly and highly damaged cell samples did not exhibit significant differences compared with their native counterparts.We concluded that the starch digestion of pulse cotyledon cells is primarily determined by the intactness of the cellular structure.This study reveals the role of food structure on the ability to retain the desirable nutritional properties of starch after subjection to physical modification.展开更多
The wear behavior of an as-received Mg-Zn-Y-Zr alloy before and after a facile heat treatment was investigated under sliding in air and 0.5 wt.%NaCl solution.Results revealed that the wear resistance of the alloy was ...The wear behavior of an as-received Mg-Zn-Y-Zr alloy before and after a facile heat treatment was investigated under sliding in air and 0.5 wt.%NaCl solution.Results revealed that the wear resistance of the alloy was remarkably enhanced after the heat treatment,irrespective of testing condition.The wear mechanism was predominantly abrasive wear accompanied by oxidation under the dry sliding condition,while corrosive wear was dominant under sliding in the NaCl solution.The superior corrosive wear resistance was attributed to the homogenous distribution of fine I-phase precipitates in the alloy by the heat treatment,leading to a reduction in wear,corrosion as well as wear-corrosion synergy.The wear-accelerated corrosion rate was remarkably alleviated after the heat treatment.展开更多
The metastableβtitanium alloy TB8(Ti-12.76Mo-2.13Nb-2.73A1-0.16Si)was used as the original material,and the secondary processing method combining equal channel angular pressing(ECAP)and heat treatment was adopted.Wit...The metastableβtitanium alloy TB8(Ti-12.76Mo-2.13Nb-2.73A1-0.16Si)was used as the original material,and the secondary processing method combining equal channel angular pressing(ECAP)and heat treatment was adopted.With the help of optical microscope(OM),scanning electron microscope(SEM)and X-ray diffractometer(XRD),the corrosion behavior of TB8 titanium alloy after different secondary processing(800℃/850℃solid solution-520℃aging,ECAP-800℃/850℃solid solution-520℃aging,and800℃/850℃solid solution-ECAP-520℃aging)was studied.The experimental results show that the hot corrosion products of the six samples are similar,mainly Na_(2)Si_(2)O_(5),MoS_(2),TiCl_(2),Ti(SO_(4))_(2),and TiS.Due to the grains of the TB8 titanium alloy treated by 850℃solid solution-ECAP-520℃aging are obviously refined,the surface structure is the most smooth and dense,forming a continuous Al2O3protective film,and the surface defects are the least after corrosion.Its corrosion layer thickness is the lowest(102.3μm),only 36.5%-81.4%of that of other secondary processing titanium alloys.In addition,the corrosion kinetics curves of the six materials all follow parabolic laws,and the minimum corrosion weight gain of the samples after 850℃solutionECAP-520℃aging treatment is 0.7507 mg·mm^(-2),showing better hot corrosion resistance.展开更多
The evolution of microstructure and formation mechanism of incipient melting microstructure of DD5 single crystal superalloy during solution heat treatment were studied by scanning electron microscopy(SEM),electron pr...The evolution of microstructure and formation mechanism of incipient melting microstructure of DD5 single crystal superalloy during solution heat treatment were studied by scanning electron microscopy(SEM),electron probe microanalysis(EPMA),and energy dispersive spectroscopy(EDS).The solidus and liquidus of single crystal alloy were obtained by differential scanning calorimetry(DSC).Results show that the mosaic-like eutectic and fan-like eutectic are dissolved at first,and the coarseγ'phase is dissolved later during the solution heat treatment of 1,390°C/2 h+1,310°C/4 h+1,320°C/10 h+air cooling(AC).The composition segregations of Al,Ta,W and Re are 0.99,0.96,1.04 and 1.16,respectively,which close to 1.The incipient melting is caused by the low local temperature of the alloy,and the micropore region with a lower melting point is the preferred position for incipient melting.展开更多
[Objectives]This study was conducted to explore the effects of heat treatment on processing characteristics of pork.[Methods]The effects of low-temperature long-term cooking(LTLT),high-temperature vacuum cooking,high-...[Objectives]This study was conducted to explore the effects of heat treatment on processing characteristics of pork.[Methods]The effects of low-temperature long-term cooking(LTLT),high-temperature vacuum cooking,high-temperature cooking and high-temperature steaming on some indexes of pork products were studied,and principal component analysis was carried out.[Results]LTLT had significant effects on the total sensory score,moisture content,cooking loss rate,a value,shear force,and TBARS of pork,and the corresponding optimal product indicators were 71.40 points,72.36%,14.20%,4.79,7089.87 g,and 0.05 mg/kg,respectively.The microstructure changes in the LTLT group were relatively small,as the muscle fiber structure was relatively dense and uniform,and the gaps between muscle fibers were small.A total of 30 volatile flavor compounds were detected in the four groups,mainly alcohols,alkenes,alkanes,lipids,ketones,and aldehydes,and the LTLT group had more types and high contents.PCA analysis showed that the sensory evaluation,moisture content,elasticity,a value and LTLT were positively correlated with principal component 1.[Conclusions]Various indexes comprehensively showed that the LTLT group had better meat color,flavor,texture characteristics and lower oxidation degree than traditional cooking and steaming methods,which provides a theoretical reference for its large-scale application in the processing of prepared meat products.展开更多
In the past tens of years,the power conversion efficiency of Cu(In,Ga)Se2(CIGS)has continuously improved and been one of the fastest growing photovoltaic technologies that can also help us achieve the goal of carbon e...In the past tens of years,the power conversion efficiency of Cu(In,Ga)Se2(CIGS)has continuously improved and been one of the fastest growing photovoltaic technologies that can also help us achieve the goal of carbon emissions reduction.Among several key advances,the alkali element post-deposition treatment(AlK PDT)is regarded as the most important finding in the last 10 years,which has led to the improvement of CIGS solar cell efficiency from 20.4%to 23.35%.A profound understanding of the influence of alkali element on the chemical and electrical properties of the CIGS absorber along with the underlying mechanisms is of great importance.In this review,we summarize the strategies of the alkali element doping in CIGS solar cell,the problems to be noted in the PDT process,the effects on the CdS buffer layer,the effects of different alkali elements on the structure and morphology of the CIGS absorber layer,and retrospect the progress in the CIGS solar cell with emphasis on the alkali element post deposition treatment.展开更多
In this study, we thoroughly examined the impact of heat treatments and hole count (p) on the properties of LnSrBaCu<sub>3</sub>O<sub>6+z</sub> (Ln = Eu, Sm, Nd) compounds. We focused on prepar...In this study, we thoroughly examined the impact of heat treatments and hole count (p) on the properties of LnSrBaCu<sub>3</sub>O<sub>6+z</sub> (Ln = Eu, Sm, Nd) compounds. We focused on preparation, X-ray diffraction with Rietveld refinement, AC susceptibility, DC resistivity measurements, and heat treatment effects. Two heat treatment types were applied: oxygen annealing [O] and argon annealing followed by oxygen annealing [AO]. As the rare earth Ln’s ionic radius increased, certain parameters notably changed. Specifically, c parameter, surface area S, and volume V increased, while critical temperature Tc and holes (p) in the CuO<sub>2</sub> plane decreased. The evolution of these parameters with rare earth Ln’s ionic radius in [AO] heat treatment is linear. Regardless of the treatment, the structure is orthorhombic for Ln = Eu, tetragonal for Ln = Nd, orthorhombic for Ln = Sm [AO], and pseudo-tetragonal for Sm [O]. The highest critical temperature is reached with Ln = Eu (Tc [AO] = 87.1 K). Notably, for each sample, Tc [AO] surpasses Tc [O]. Observed data stems from factors including rare earth ionic size, improved cationic and oxygen chain order, holes count p in Cu(2)O<sub>2</sub> planes, and in-phase purity of [AO] samples. Our research strives to clearly demonstrate that the density of holes (p) within the copper plane stands as a determinant impacting the structural, electrical, and superconducting properties of these samples. Meanwhile, the other aforementioned parameters contribute to shaping this density (p).展开更多
In this paper, a modified temperature-phase transformation-stress/strain field coupled 3D non-linear mathematical model was used in the computer simulation on heat treatment processes of workpieces including catch jaw...In this paper, a modified temperature-phase transformation-stress/strain field coupled 3D non-linear mathematical model was used in the computer simulation on heat treatment processes of workpieces including catch jaw, anchor ring, cold roller, large-scale bearing roller, nitriding crank shaft, etc. The simulation on complicated technologies such as pre-cooled quenching, double media quenching, self-tempering, difference temperature heating, nitriding distortion was carried out. The optimum design of heat treatment technology has been realized. The successful application of computer simulation on heat treatment have also been demonstrated.展开更多
A method to simulate processes of forging and subsequent heat treatment of an axial symmetric rod is formulated in eulerian description and the feasibility is investigated. This method uses finite volume mushes for tr...A method to simulate processes of forging and subsequent heat treatment of an axial symmetric rod is formulated in eulerian description and the feasibility is investigated. This method uses finite volume mushes for troching material deformation and an automatically refined facet surface to accurately trace the free surface of the deforming material.In the method,the deforming work piece flows through fixed finite volume meshes using eulerian formulation to describe the conservation laws,Fixed finite volume meshing is particularly suitable for large three-dimensional deformation such as forging because remeshing techniques are not required, which are commonly considered to be the main bottelencek in the ssimulations of large defromation by using the finite element method,By means of this finite volume method, an approach has been developed in the framework of "metallo-thermo-mechanics" to simulate metallic structure, temperature and stress/strain coupled in the heat treatment process.In a first step of simulation, the heat treatment solver is limited in small deformation hypothesis,and un- coupled with forging. The material is considered as elastic-plastic and takes into account of strain, strain rate and temperature effects on the yield stress.Heat generation due to deformation,heat con- duction and thermal stress are considered.Temperature - dependent phase transformation,stress-in- duced phase transformation,latent heat,transformation stress and strain are included.These ap- proaches are implemented into the commerical commercial computer program MSC/SuperForge and a verification example with experimental date is given as comparison.展开更多
To improve the microstructure and properties of the electron beam welded joints, the vacuum or furnace whole post weld heat treatment (FWPWHT) usually should be done on it. The electron beam local post weld heat treat...To improve the microstructure and properties of the electron beam welded joints, the vacuum or furnace whole post weld heat treatment (FWPWHT) usually should be done on it. The electron beam local post weld heat treatment (EBLPWHT) is a rather new heat treatment procedure that provides the advantages of high precision, flexibility and efficiency, energy saving and higher productivity. In this paper, the microstructure, mechanical properties, fracture toughness and fatigue properties of electron beam welded joints of 30CrMnSiNi2A steel in as-welded (AW) and EBLPWHT conditions have been investigated respectively. The results show that the microstructures of different zones of joints in as-welded condition are changed by EBLPWHT procedure, in which the welds from coarse needle martensite into lath-shaped martensite; the main structures of heat affected zones (HAZ) from lath-shaped martensite into lower bainite. The properties of welded joints can be improved by the EBLPWHT in some extent, especially the fracture toughness of the welds and the fatigue crack resistance of welded joints can be sufficiently improved. However, more appropriate heat treatment parameters of the EBLPWHT have to be studied in order to increase the mechanical properties of base metal near by the HAZ.展开更多
Heat stroke(HS)is a fatal disease caused by thermal damage in the body,and it has a very high mortality rate.In 2015,the People’s Liberation Army Professional Committee of Critical Care Medicine published the first e...Heat stroke(HS)is a fatal disease caused by thermal damage in the body,and it has a very high mortality rate.In 2015,the People’s Liberation Army Professional Committee of Critical Care Medicine published the first expert consensus on HS in China,Expert consensus on standardized diagnosis and treatment for heat stroke.With an increased understanding of HS and new issues that emerged during the HS treatment in China in recent years,the 2015 consensus no longer meet the requirements for HS prevention and treatment.It is necessary to update the consensus to include the latest research evidence and establish a new consensus that has broader coverage,is more practical and is more in line with China’s national conditions.This new expert consensus includes new concept of HS,recommendations for laboratory tests and auxiliary examinations,new understanding of diagnosis and differential diagnosis,On-site emergency treatment and In-hospital treatment,translocation of HS patients and prevention of HS.展开更多
The AZ91 D magnesium alloy containing rare earth Gd was prepared in this study, and the effect of semi-solid isothermal heat treatment on the microstructure of the alloy was investigated to obtain an optimum semi-soli...The AZ91 D magnesium alloy containing rare earth Gd was prepared in this study, and the effect of semi-solid isothermal heat treatment on the microstructure of the alloy was investigated to obtain an optimum semi-solid structure. Results show that Gd can refine the microstructure of AZ91 D magnesium alloy, and the optimum semi-solid AZ91 D microstructure can be achieved by adding 1.5wt.% Gd. After treated at 585 °C for 30 min, the well distributed rose-shaped and near-spherical semi-solid microstructures of AZ91D+1.5wt.%Gd alloy can be obtained. The liquid phase of the semi-solid alloy consists of three components, namely, the molten pool, the "entrapped liquid" pool and the liner liquid film which separates two neighbor particles. The solid phase is composed of two phases, the primary α-Mg particles and the α-Mg phase formed in the second stage of solidification. With the increase of holding time, melting which causes the decrease of the primary α-Mg particle size is the dominant mechanism in the initial stage while coalescence and Ostwald ripening tend to be the principles later.展开更多
The development of simulation model and benchmark work have expanded in the past decade and many models and soft ware are introduced. The leading software "Hearts’ developed by Prof Inoue[1] and several other ha...The development of simulation model and benchmark work have expanded in the past decade and many models and soft ware are introduced. The leading software "Hearts’ developed by Prof Inoue[1] and several other have proved the effectiveness as the pre-production simulation work at many part of heat treatment processes[2-10]. Although, numerous other models and simulation studies dealt with many fundamental factors are reported at many conferences except very few models have not completed three dimensional computation methods, or lack of validation work to evaluate their tools exactly. In this paper, several distortion case studies will be introduced and the needs of fundamental study of distortion and internationally collaborative program on model evaluation and construction of materials database are proposed.展开更多
The composite plate made by explosion welding technology generally has high residual stress and bed plasticity due to the explosion reinforcement. The heat treatment can play a part of eliminating stress and recoverin...The composite plate made by explosion welding technology generally has high residual stress and bed plasticity due to the explosion reinforcement. The heat treatment can play a part of eliminating stress and recovering property.In this study,TA1/Q345 clad plate made by explosive welding was annealed at different temperatures.The microstructure,micro-hardness,and tensile,shear,and bending properties were analyzed after anneal.The result shows that there is fibrous structure in the bonding zone and the plastic deformation is severe,the grain growth and fibrous structure dribbles away with the temperature increasing.Micro-hardness in the interface is bigger than it on the both sides. Tensile and shear strength reduced with the temperature of heat treatment increasing.The propel anneal temperature for TA1/Q345 clad plate is 600展开更多
The characteristics of nanosized precipitates in steels depend on the heat-treatment parameters. The effects of characteristics of vanadium precipitates formed during isothermal heat treatment on the hardness of the f...The characteristics of nanosized precipitates in steels depend on the heat-treatment parameters. The effects of characteristics of vanadium precipitates formed during isothermal heat treatment on the hardness of the ferrite matrix in low-carbon vanadium-alloyed steel were investigated through analysis of transmission electron microscopy images and microhardness measurements. The results show that, during isothermal holding in the temperature range from 675 to 750℃, only interphase precipitation occurs, whereas only random precipitation occurs in the ferrite matrix during holding at 600℃. Furthermore, during isothermal heat treatment between 600 and 675℃, both random and interphase precipitates occurred in the ferrite. Nanoscale vanadium carbides with different atomic ratios of vanadium(V) and carbon(C) were the dominant precipitates in the random and interphase precipitates. The sizes of random precipitation carbides were smaller than those of interphase ones. Also, the sample isothermally heat treated at 650℃ for 900s exhibited a higher hardness with a narrower hardness distribution.展开更多
The effects of heat treatment on the microstructure and mechanical properties of intermetallic compounds in the interface of stainless steel 321 explosively bonded to aluminum 1230 were investigated in this study. Exp...The effects of heat treatment on the microstructure and mechanical properties of intermetallic compounds in the interface of stainless steel 321 explosively bonded to aluminum 1230 were investigated in this study. Experimental investigations were performed by optical microscopy, scanning electron microscopy, and microhardness and shear tensile strength testing. Prior to heat treatment, increasing the stand-off distance between samples from 1 to 2.5 mm caused their interface to become wavy and the thickness of intermetallic layers to increase from 3.5 to 102.3 μm. The microhardness increased from HV 766 in the sample prepared at a stand-off distance of 1 mm to HV 927 in the sample prepared at a stand-off distance of 2.5 mm; in addition, the sample strength increased from 103.2 to 214.5 MPa. Heat treatment at 450°C for 6 h increased the thickness of intermetallic compound layers to 4.4 and 118.5 μm in the samples prepared at stand-off distances of 1 and 2.5 mm, respectively. These results indicated that increasing the duration and temperature of heat treatment decreased the microhardness and strength of the interface of explosively welded stainless steel 321-Al 1230 and increased the thickness of the intermetallic region.展开更多
基金the financial support by the National Natural Science Foundation of China(No.12272094,51805087 and 51705080)the Natural Science Foundation of Fujian Province of China(No.2022J01541)。
文摘The purpose of this paper is to examine the effect of processing parameters and subsequent heat treatments on the microstructures and bonding strengths of Ti-6Al-4V/AA1050 laminations formed via a non-equal channel lateral co-extrusion process.The microstructural evolution and growth mechanism in the diffusion layer were discussed further to optimize the bonding quality by appropriately adjusting process parameters.Scanning electron microscopes(SEM),energy dispersive spectrometer(EDS),and X-ray diffraction(XRD)were used to characterize interfacial diffusion layers.The shear test was used to determine the mechanical properties of the interfacial diffusion layer.The experimental results indicate that it is possible to co-extrusion Ti-6Al-4V/AA1050 compound profiles using non-equal channel lateral co-extrusion.Different heat treatment processes affect the thickness of the diffusion layer.When the temperature and time of heat treatment increase,the thickness of the reaction layers increases dramatically.Additionally,the shear strength of the Ti-6Al-4V/AA1050 composite interface is proportional to the diffusion layer thickness.It is observed that a medium interface thickness results in superior mechanical performance when compared to neither a greater nor a lesser interface thickness.Microstructural characterization of all heat treatments reveals that the only intermetallic compound observed in the diffusion layers is TiAl_(3).Due to the inter-diffusion of Ti and Al atoms,the TiAl_(3) layer grows primarily at AA1050/TiAl_(3) interfaces.
基金the Key Projects of Equipment Pre-research Foundation of the Ministry of Equipment Development of the Central Military Commission of China (No.6140922010201)the Key R&D Plan of Zhenjiang in 2018(No.GY2018021)。
文摘The performance of solid solution aging treatment on aluminum matrix composites prepared by powder metallurgy and reinforced with 6061 aluminum alloy powder as matrix;meanwhile, nano silicon carbide particles(nm Si Cp), submicron silicon carbide particles(1 μm Si Cp) and Ti particles were studied. The Al/Si Cp composite powder was prepared by high-energy ball milling, and then cold-pressed, sintered, hotextruded, and then heat-treated with different solution temperatures and aging times for the extruded composites. Optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy(EDS), X-ray diffractometer(XRD) and extrusion testing were used to analyze and test the microstructure and mechanical properties of aluminum matrix composites. The results show that after the multi-stage solid solution at 530 ℃×2 h+535 ℃×2 h+540 ℃×2 h, the particles are mainly equiaxed grains and uniformly distributed. There is no reinforcement agglomeration, and the surface is dense and the insoluble phase is basically dissolved. In the matrix, the strengthening effect is good, and the hardness and compressive strength are 179.43 HV and 680.42 MPa, respectively. Under this solution process, when the aluminum matrix composites are aged at 170 ℃ for 10 h, the hardness and compressive strength can reach their peaks and increase to 195.82 HV and 721.48 MPa, respectively.
基金supported by National Natural Science Foundation of China(Grant No.51874367 and 51574291)。
文摘Multidirectional forging(MDF)was successfully applied to fabricate large-size Mg-Gd-Y-Zn-Zr-Ag alloy in this work and effects of T4,T5 and T6 treatments on the microstructure and mechanical properties of the as-forged alloy were analyzed.Results show that dynamic recrystallization(DRX)occurs and second phase particles precipitate along the grain boundary during the MDF process.After annealing treatment(T4),the volume fraction and size of dynamic precipitates slightly increase at a lower temperature(430℃)compared with those of MDFed sample,while they are dissolved into theα-Mg matrix at a higher temperature(450℃).At the meantime,short plate-shaped long-period stacking ordered(LPSO)phases are observed in the DRX grains of the MDFed sample and then dissolved into theα-Mg matrix during annealing at both temperatures.Typical basal texture is identified in the MDFed sample,but the basal pole tilts away from final forging direction and rare-earth texture component with<1121>orientation parallel to penultimate forging direction becomes visible after annealing.The T6 sample annealing at 430℃for 4 h and ageing at 200℃for 34 h exhibits the superior strength and ductility in this study.The ultimate tensile strength,tensile yield strength and elongation to failure,which is 455 MPa,308 MPa and 7.7%,respectively,are overall improved compared with the directly-aged(T5)sample.This paper provides a superior heat treatment schedule to manufacture high-performance large-scale Mg-Gd-Y-Zn-Zr-Ag components for industrial production.
基金financially supported by the Scientific Research Fund of Liaoning Provincial Education Department, China (No.LJKZ0122)。
文摘To enhance the performance of in-situ synthesized 6vol.%(Ti C+Ti B)/TC4 titanium matrix composites fabricated by casting,a variety of heat treatment processes were carried out.Upon conducting microstructure observations following various heat treatments,it was found that the composites exhibit a basketweave microstructure,consisting of an α phase and a transformed β phase.The sizes of(α+β) phases were found to be refined to varying degrees after the heat treatment processes,while the morphology of Ti B remains largely unchanged and Ti C becomes granulated.Compressive testing revealed that all composites subjected to different heat treatments demonstrate a notable increase in ultimate compressive strength as well as a slight improvement in plasticity compared to the as-cast state.The results of the tribological performance test indicated that the heat-treated composites exhibit lower average friction coefficient,specific wear rate,and worn surface roughness compared to the as-cast composite.Among the heat treatment processes studied,the composite solution heated at 1,150 °C/1 h followed by air cooling,then 950 °C/1 h followed by air cooling,and finally 500 °C/4 h followed by air cooling,demonstrates the highest levels of hardness,compressive strength,and wear resistance.These improvements are attributed to the combined effects of solid solution strengthening,grain refinement,and the pinning of dislocation slip.
基金the National Natural Science Foundation of China(31701546)the Fundamental Research Funds for the Central Universities of China(2019ZD40)+5 种基金the 111 Project(B17018)for financial supportPearl River Talent Recruitment Program of Guangdong Province(2017GC010229)the Pearl River Nova Program of Guangzhou(201906010079)the National Natural Science Foundation of China(32001691)the special fund for scientific innovation strategyconstruction of high-level academy of agriculture science(R2019YJYB1001)the Application-oriented Projects of Guangdong Province(2017B020232002)。
文摘Natural foods,such as whole pulses,are recommended in the dietary guidelines of the US and China.The plant cell wall structure in whole pulses has important implications for the nutritional functionalities of starch.In this study,garbanzo bean cells with varying degrees of cell wall integrity were subjected to dry heat treatment(DHT)and used to elucidate the food structure-starch digestion properties of pulse food.The morphological features suggested that all cell samples do not exhibit remarkable changes after being subjected to DHT.Molecular rearrangement and the crystallite disruption of starch granules entrapped in cells occurred during DHT as assessed by the crystal structure and thermal properties.DHT decreased the inhibitory effects of enzymes of both the soluble and insoluble components,but the digestion rate and extent of slightly and highly damaged cell samples did not exhibit significant differences compared with their native counterparts.We concluded that the starch digestion of pulse cotyledon cells is primarily determined by the intactness of the cellular structure.This study reveals the role of food structure on the ability to retain the desirable nutritional properties of starch after subjection to physical modification.
基金the National Natural Science Foundation of China Projects under Grant[Nos.5207011217,51871211 and 51701129]。
文摘The wear behavior of an as-received Mg-Zn-Y-Zr alloy before and after a facile heat treatment was investigated under sliding in air and 0.5 wt.%NaCl solution.Results revealed that the wear resistance of the alloy was remarkably enhanced after the heat treatment,irrespective of testing condition.The wear mechanism was predominantly abrasive wear accompanied by oxidation under the dry sliding condition,while corrosive wear was dominant under sliding in the NaCl solution.The superior corrosive wear resistance was attributed to the homogenous distribution of fine I-phase precipitates in the alloy by the heat treatment,leading to a reduction in wear,corrosion as well as wear-corrosion synergy.The wear-accelerated corrosion rate was remarkably alleviated after the heat treatment.
基金Funded by the Key Projects of Equipment Pre-research Foundation of the Ministry of Equipment Development of the Central Military Commission of China(No.6140922010201)the Key R&D Plan of Zhenjiang(No.GY2018021)。
文摘The metastableβtitanium alloy TB8(Ti-12.76Mo-2.13Nb-2.73A1-0.16Si)was used as the original material,and the secondary processing method combining equal channel angular pressing(ECAP)and heat treatment was adopted.With the help of optical microscope(OM),scanning electron microscope(SEM)and X-ray diffractometer(XRD),the corrosion behavior of TB8 titanium alloy after different secondary processing(800℃/850℃solid solution-520℃aging,ECAP-800℃/850℃solid solution-520℃aging,and800℃/850℃solid solution-ECAP-520℃aging)was studied.The experimental results show that the hot corrosion products of the six samples are similar,mainly Na_(2)Si_(2)O_(5),MoS_(2),TiCl_(2),Ti(SO_(4))_(2),and TiS.Due to the grains of the TB8 titanium alloy treated by 850℃solid solution-ECAP-520℃aging are obviously refined,the surface structure is the most smooth and dense,forming a continuous Al2O3protective film,and the surface defects are the least after corrosion.Its corrosion layer thickness is the lowest(102.3μm),only 36.5%-81.4%of that of other secondary processing titanium alloys.In addition,the corrosion kinetics curves of the six materials all follow parabolic laws,and the minimum corrosion weight gain of the samples after 850℃solutionECAP-520℃aging treatment is 0.7507 mg·mm^(-2),showing better hot corrosion resistance.
基金The authors would like to express their sincere thanks to the financial support from the Key Project of National Natural Science Foundation of China(No.U16642548).
文摘The evolution of microstructure and formation mechanism of incipient melting microstructure of DD5 single crystal superalloy during solution heat treatment were studied by scanning electron microscopy(SEM),electron probe microanalysis(EPMA),and energy dispersive spectroscopy(EDS).The solidus and liquidus of single crystal alloy were obtained by differential scanning calorimetry(DSC).Results show that the mosaic-like eutectic and fan-like eutectic are dissolved at first,and the coarseγ'phase is dissolved later during the solution heat treatment of 1,390°C/2 h+1,310°C/4 h+1,320°C/10 h+air cooling(AC).The composition segregations of Al,Ta,W and Re are 0.99,0.96,1.04 and 1.16,respectively,which close to 1.The incipient melting is caused by the low local temperature of the alloy,and the micropore region with a lower melting point is the preferred position for incipient melting.
基金Supported by Natural Science Foundation of Sichuan Province(2022NSFSC1644)Science and Technology Achievement Transfer and Transformation Demonstration Project of Sichuan Province(2022ZHCG0063)Sichuan Pig Innovation Team of the National Modern Agricultural Industry Technology System(scsztd-2023-08-07).
文摘[Objectives]This study was conducted to explore the effects of heat treatment on processing characteristics of pork.[Methods]The effects of low-temperature long-term cooking(LTLT),high-temperature vacuum cooking,high-temperature cooking and high-temperature steaming on some indexes of pork products were studied,and principal component analysis was carried out.[Results]LTLT had significant effects on the total sensory score,moisture content,cooking loss rate,a value,shear force,and TBARS of pork,and the corresponding optimal product indicators were 71.40 points,72.36%,14.20%,4.79,7089.87 g,and 0.05 mg/kg,respectively.The microstructure changes in the LTLT group were relatively small,as the muscle fiber structure was relatively dense and uniform,and the gaps between muscle fibers were small.A total of 30 volatile flavor compounds were detected in the four groups,mainly alcohols,alkenes,alkanes,lipids,ketones,and aldehydes,and the LTLT group had more types and high contents.PCA analysis showed that the sensory evaluation,moisture content,elasticity,a value and LTLT were positively correlated with principal component 1.[Conclusions]Various indexes comprehensively showed that the LTLT group had better meat color,flavor,texture characteristics and lower oxidation degree than traditional cooking and steaming methods,which provides a theoretical reference for its large-scale application in the processing of prepared meat products.
基金supported by the National Key R&D Program of China Grant(no.2018YFB1500200)the National Natural Science Foundation of China under Grant(nos.61804159 and 52173243)+2 种基金the Natural Science Foundation of Guangdong Province,Guangzhou,China(no.2021A1515011409)Shenzhen&Hong Kong Joint Research Program(no.SGDX20201103095605015)SIAT-CUHK Joint Laboratory of Photovoltaic Solar Energy.
文摘In the past tens of years,the power conversion efficiency of Cu(In,Ga)Se2(CIGS)has continuously improved and been one of the fastest growing photovoltaic technologies that can also help us achieve the goal of carbon emissions reduction.Among several key advances,the alkali element post-deposition treatment(AlK PDT)is regarded as the most important finding in the last 10 years,which has led to the improvement of CIGS solar cell efficiency from 20.4%to 23.35%.A profound understanding of the influence of alkali element on the chemical and electrical properties of the CIGS absorber along with the underlying mechanisms is of great importance.In this review,we summarize the strategies of the alkali element doping in CIGS solar cell,the problems to be noted in the PDT process,the effects on the CdS buffer layer,the effects of different alkali elements on the structure and morphology of the CIGS absorber layer,and retrospect the progress in the CIGS solar cell with emphasis on the alkali element post deposition treatment.
文摘In this study, we thoroughly examined the impact of heat treatments and hole count (p) on the properties of LnSrBaCu<sub>3</sub>O<sub>6+z</sub> (Ln = Eu, Sm, Nd) compounds. We focused on preparation, X-ray diffraction with Rietveld refinement, AC susceptibility, DC resistivity measurements, and heat treatment effects. Two heat treatment types were applied: oxygen annealing [O] and argon annealing followed by oxygen annealing [AO]. As the rare earth Ln’s ionic radius increased, certain parameters notably changed. Specifically, c parameter, surface area S, and volume V increased, while critical temperature Tc and holes (p) in the CuO<sub>2</sub> plane decreased. The evolution of these parameters with rare earth Ln’s ionic radius in [AO] heat treatment is linear. Regardless of the treatment, the structure is orthorhombic for Ln = Eu, tetragonal for Ln = Nd, orthorhombic for Ln = Sm [AO], and pseudo-tetragonal for Sm [O]. The highest critical temperature is reached with Ln = Eu (Tc [AO] = 87.1 K). Notably, for each sample, Tc [AO] surpasses Tc [O]. Observed data stems from factors including rare earth ionic size, improved cationic and oxygen chain order, holes count p in Cu(2)O<sub>2</sub> planes, and in-phase purity of [AO] samples. Our research strives to clearly demonstrate that the density of holes (p) within the copper plane stands as a determinant impacting the structural, electrical, and superconducting properties of these samples. Meanwhile, the other aforementioned parameters contribute to shaping this density (p).
文摘In this paper, a modified temperature-phase transformation-stress/strain field coupled 3D non-linear mathematical model was used in the computer simulation on heat treatment processes of workpieces including catch jaw, anchor ring, cold roller, large-scale bearing roller, nitriding crank shaft, etc. The simulation on complicated technologies such as pre-cooled quenching, double media quenching, self-tempering, difference temperature heating, nitriding distortion was carried out. The optimum design of heat treatment technology has been realized. The successful application of computer simulation on heat treatment have also been demonstrated.
文摘A method to simulate processes of forging and subsequent heat treatment of an axial symmetric rod is formulated in eulerian description and the feasibility is investigated. This method uses finite volume mushes for troching material deformation and an automatically refined facet surface to accurately trace the free surface of the deforming material.In the method,the deforming work piece flows through fixed finite volume meshes using eulerian formulation to describe the conservation laws,Fixed finite volume meshing is particularly suitable for large three-dimensional deformation such as forging because remeshing techniques are not required, which are commonly considered to be the main bottelencek in the ssimulations of large defromation by using the finite element method,By means of this finite volume method, an approach has been developed in the framework of "metallo-thermo-mechanics" to simulate metallic structure, temperature and stress/strain coupled in the heat treatment process.In a first step of simulation, the heat treatment solver is limited in small deformation hypothesis,and un- coupled with forging. The material is considered as elastic-plastic and takes into account of strain, strain rate and temperature effects on the yield stress.Heat generation due to deformation,heat con- duction and thermal stress are considered.Temperature - dependent phase transformation,stress-in- duced phase transformation,latent heat,transformation stress and strain are included.These ap- proaches are implemented into the commerical commercial computer program MSC/SuperForge and a verification example with experimental date is given as comparison.
文摘To improve the microstructure and properties of the electron beam welded joints, the vacuum or furnace whole post weld heat treatment (FWPWHT) usually should be done on it. The electron beam local post weld heat treatment (EBLPWHT) is a rather new heat treatment procedure that provides the advantages of high precision, flexibility and efficiency, energy saving and higher productivity. In this paper, the microstructure, mechanical properties, fracture toughness and fatigue properties of electron beam welded joints of 30CrMnSiNi2A steel in as-welded (AW) and EBLPWHT conditions have been investigated respectively. The results show that the microstructures of different zones of joints in as-welded condition are changed by EBLPWHT procedure, in which the welds from coarse needle martensite into lath-shaped martensite; the main structures of heat affected zones (HAZ) from lath-shaped martensite into lower bainite. The properties of welded joints can be improved by the EBLPWHT in some extent, especially the fracture toughness of the welds and the fatigue crack resistance of welded joints can be sufficiently improved. However, more appropriate heat treatment parameters of the EBLPWHT have to be studied in order to increase the mechanical properties of base metal near by the HAZ.
文摘Heat stroke(HS)is a fatal disease caused by thermal damage in the body,and it has a very high mortality rate.In 2015,the People’s Liberation Army Professional Committee of Critical Care Medicine published the first expert consensus on HS in China,Expert consensus on standardized diagnosis and treatment for heat stroke.With an increased understanding of HS and new issues that emerged during the HS treatment in China in recent years,the 2015 consensus no longer meet the requirements for HS prevention and treatment.It is necessary to update the consensus to include the latest research evidence and establish a new consensus that has broader coverage,is more practical and is more in line with China’s national conditions.This new expert consensus includes new concept of HS,recommendations for laboratory tests and auxiliary examinations,new understanding of diagnosis and differential diagnosis,On-site emergency treatment and In-hospital treatment,translocation of HS patients and prevention of HS.
基金financially supported by the Natural Science Foundation of Jiangxi,China(grant No.:20142BAB216015)Jiangxi Key Laboratory for Advanced Copper and Tungsten Materials,China(grant No.:2013-KLP-07)
文摘The AZ91 D magnesium alloy containing rare earth Gd was prepared in this study, and the effect of semi-solid isothermal heat treatment on the microstructure of the alloy was investigated to obtain an optimum semi-solid structure. Results show that Gd can refine the microstructure of AZ91 D magnesium alloy, and the optimum semi-solid AZ91 D microstructure can be achieved by adding 1.5wt.% Gd. After treated at 585 °C for 30 min, the well distributed rose-shaped and near-spherical semi-solid microstructures of AZ91D+1.5wt.%Gd alloy can be obtained. The liquid phase of the semi-solid alloy consists of three components, namely, the molten pool, the "entrapped liquid" pool and the liner liquid film which separates two neighbor particles. The solid phase is composed of two phases, the primary α-Mg particles and the α-Mg phase formed in the second stage of solidification. With the increase of holding time, melting which causes the decrease of the primary α-Mg particle size is the dominant mechanism in the initial stage while coalescence and Ostwald ripening tend to be the principles later.
文摘The development of simulation model and benchmark work have expanded in the past decade and many models and soft ware are introduced. The leading software "Hearts’ developed by Prof Inoue[1] and several other have proved the effectiveness as the pre-production simulation work at many part of heat treatment processes[2-10]. Although, numerous other models and simulation studies dealt with many fundamental factors are reported at many conferences except very few models have not completed three dimensional computation methods, or lack of validation work to evaluate their tools exactly. In this paper, several distortion case studies will be introduced and the needs of fundamental study of distortion and internationally collaborative program on model evaluation and construction of materials database are proposed.
基金supported by National Natural Science Foundation of China(Grant No.51274162)Scientific Research Plan Project of Shaanxi Education Department(Grant No.14JK1539)Collaborative Innovation Project of Shaanxi Province(Grant No.2015XT-39)
文摘The composite plate made by explosion welding technology generally has high residual stress and bed plasticity due to the explosion reinforcement. The heat treatment can play a part of eliminating stress and recovering property.In this study,TA1/Q345 clad plate made by explosive welding was annealed at different temperatures.The microstructure,micro-hardness,and tensile,shear,and bending properties were analyzed after anneal.The result shows that there is fibrous structure in the bonding zone and the plastic deformation is severe,the grain growth and fibrous structure dribbles away with the temperature increasing.Micro-hardness in the interface is bigger than it on the both sides. Tensile and shear strength reduced with the temperature of heat treatment increasing.The propel anneal temperature for TA1/Q345 clad plate is 600
文摘The characteristics of nanosized precipitates in steels depend on the heat-treatment parameters. The effects of characteristics of vanadium precipitates formed during isothermal heat treatment on the hardness of the ferrite matrix in low-carbon vanadium-alloyed steel were investigated through analysis of transmission electron microscopy images and microhardness measurements. The results show that, during isothermal holding in the temperature range from 675 to 750℃, only interphase precipitation occurs, whereas only random precipitation occurs in the ferrite matrix during holding at 600℃. Furthermore, during isothermal heat treatment between 600 and 675℃, both random and interphase precipitates occurred in the ferrite. Nanoscale vanadium carbides with different atomic ratios of vanadium(V) and carbon(C) were the dominant precipitates in the random and interphase precipitates. The sizes of random precipitation carbides were smaller than those of interphase ones. Also, the sample isothermally heat treated at 650℃ for 900s exhibited a higher hardness with a narrower hardness distribution.
文摘The effects of heat treatment on the microstructure and mechanical properties of intermetallic compounds in the interface of stainless steel 321 explosively bonded to aluminum 1230 were investigated in this study. Experimental investigations were performed by optical microscopy, scanning electron microscopy, and microhardness and shear tensile strength testing. Prior to heat treatment, increasing the stand-off distance between samples from 1 to 2.5 mm caused their interface to become wavy and the thickness of intermetallic layers to increase from 3.5 to 102.3 μm. The microhardness increased from HV 766 in the sample prepared at a stand-off distance of 1 mm to HV 927 in the sample prepared at a stand-off distance of 2.5 mm; in addition, the sample strength increased from 103.2 to 214.5 MPa. Heat treatment at 450°C for 6 h increased the thickness of intermetallic compound layers to 4.4 and 118.5 μm in the samples prepared at stand-off distances of 1 and 2.5 mm, respectively. These results indicated that increasing the duration and temperature of heat treatment decreased the microhardness and strength of the interface of explosively welded stainless steel 321-Al 1230 and increased the thickness of the intermetallic region.