In this study electrochemical performance of Al and some of its alloys （Al-Zn, Al-rvlg and Al-rvln） anodes vs MnO2 cathode were carried out in alkaline solution. The results show that the Al-Zn alloy anode has the b...In this study electrochemical performance of Al and some of its alloys （Al-Zn, Al-rvlg and Al-rvln） anodes vs MnO2 cathode were carried out in alkaline solution. The results show that the Al-Zn alloy anode has the best cell capacity among the other alloys. Cell capacity values go in the order Al-Zn〉Al-Mg〉Al〉Al-Mn. This result is probably related to the nature of passive films formed on the surface of the alloys which examined by scanning electron microscopy （SEM）. SEM morphologies of Al and its alloys showed coarse grains of passive films formed on the surface of these anode materials while Al-Mn morphology shows a needle-like structure. Electrolytic manganese dioxide （EMD） produced by electrodepositing on platinum anode from liquor resulting from reduction of low grade pyrolusite ore （β-MnO2） by sulfur slag was characterized as cathode in alkaline Zn-MnO2 batteries. Ore produced sample （EMD1） was performed well in comparison with EMD standard （EMD2） （commercial battery grade electrolytic manganese dioxide, TOSOH-Hellas GH-S）. SEM morphology of Zn anode after cell reaction was carried out and showed that Zn anode has fine grains of passive film on its surface.展开更多
Current aqueous battery electrolytes,including conve ntional hydrogel electrolytes,exhibit unsatisfactory water retention capabilities.The sustained water loss will lead to subsequent polarization and increased intern...Current aqueous battery electrolytes,including conve ntional hydrogel electrolytes,exhibit unsatisfactory water retention capabilities.The sustained water loss will lead to subsequent polarization and increased internal resistance,ultimately resulting in battery failure.Herein,a double network(DN) orga no hydrogel electrolyte based on dimethyl sulfoxide(DMSO)/H_(2)O binary solvent was proposed.Through directionally reconstructing hydrogen bonds and reducing active H_(2)O molecules,the water retention ability and cathode/anode interfaces were synergistic enhanced.As a result,the synthesized DN organohydrogel demonstrates exceptional water retention capabilities,retaining approximately 75% of its original weight even after the exposure to air for 20 days.The Zn MnO_(2) battery delivers an outstanding specific capacity of275 mA h g^(-1) at 1 C,impressive rate performance with 85 mA h g^(-1) at 30 C,and excellent cyclic stability(95% retention after 6000 cycles at 5 C).Zn‖Zn symmetric battery can cycle more than 5000 h at 1 mA cm^(-2) and 1 mA h cm^(-2) without short circuiting.This study will encourage the further development of functional organohydrogel electrolytes for advanced energy storage devices.展开更多
Alkaline zinc manganese dioxide（Zn–MnO2）batteries are widely used in everyday life. Recycling of waste alkaline Zn–MnO2 batteries has always been a hot environmental concern. In this study, a simple and costeffect...Alkaline zinc manganese dioxide（Zn–MnO2）batteries are widely used in everyday life. Recycling of waste alkaline Zn–MnO2 batteries has always been a hot environmental concern. In this study, a simple and costeffective process for synthesizing Mn3O4/carbon nanotube（CNT） nanocomposites from recycled alkaline Zn–MnO2 batteries is presented. Manganese oxide was recovered from spent Zn–MnO2 battery cathodes. The Mn3O4/CNT nanocomposites were produced by ball milling the recovered manganese oxide in a commercial multi-wall carbon nanotubes（MWCNTs） solution. Scanning electron microscopy（SEM） analysis demonstrates that the nanocomposite has a unique three-dimensional（3D） bird nest structure. Mn3O4 nanoparticles are homogeneously distributed on MWCNT framework. Mn3O4/CNT nanocomposites were evaluated as an anode material for lithium-ion batteries, exhibiting a highly reversible specific capacitance of -580 mA h·g^-1 after 100 cycles. Moreover, Mn3O4/CNT nanocomposite also shows a fairly positive onset potential of -0.15 V and quite high oxygen reducibility when considered as an electrocatalyst for oxygen reduction reaction.展开更多
文摘In this study electrochemical performance of Al and some of its alloys （Al-Zn, Al-rvlg and Al-rvln） anodes vs MnO2 cathode were carried out in alkaline solution. The results show that the Al-Zn alloy anode has the best cell capacity among the other alloys. Cell capacity values go in the order Al-Zn〉Al-Mg〉Al〉Al-Mn. This result is probably related to the nature of passive films formed on the surface of the alloys which examined by scanning electron microscopy （SEM）. SEM morphologies of Al and its alloys showed coarse grains of passive films formed on the surface of these anode materials while Al-Mn morphology shows a needle-like structure. Electrolytic manganese dioxide （EMD） produced by electrodepositing on platinum anode from liquor resulting from reduction of low grade pyrolusite ore （β-MnO2） by sulfur slag was characterized as cathode in alkaline Zn-MnO2 batteries. Ore produced sample （EMD1） was performed well in comparison with EMD standard （EMD2） （commercial battery grade electrolytic manganese dioxide, TOSOH-Hellas GH-S）. SEM morphology of Zn anode after cell reaction was carried out and showed that Zn anode has fine grains of passive film on its surface.
基金Joint Funds of the National Natural Science Foundation of China (U22A20140)University of Jinan Disciplinary Cross-Convergence Construction Project 2023 (XKJC-202309, XKJC-202307)+4 种基金Jinan City-School Integration Development Strategy Project (JNSX2023015)Independent Cultivation Program of Innovation Team of Ji’nan City (202333042)Youth Innovation Group Plan of Shandong Province (2022KJ095)Shenzhen Stable Support Plan Program for Higher Education Institutions Research Program (20220816131408001)Shenzhen Science and Technology Program (JCYJ20230807091802006)。
文摘Current aqueous battery electrolytes,including conve ntional hydrogel electrolytes,exhibit unsatisfactory water retention capabilities.The sustained water loss will lead to subsequent polarization and increased internal resistance,ultimately resulting in battery failure.Herein,a double network(DN) orga no hydrogel electrolyte based on dimethyl sulfoxide(DMSO)/H_(2)O binary solvent was proposed.Through directionally reconstructing hydrogen bonds and reducing active H_(2)O molecules,the water retention ability and cathode/anode interfaces were synergistic enhanced.As a result,the synthesized DN organohydrogel demonstrates exceptional water retention capabilities,retaining approximately 75% of its original weight even after the exposure to air for 20 days.The Zn MnO_(2) battery delivers an outstanding specific capacity of275 mA h g^(-1) at 1 C,impressive rate performance with 85 mA h g^(-1) at 30 C,and excellent cyclic stability(95% retention after 6000 cycles at 5 C).Zn‖Zn symmetric battery can cycle more than 5000 h at 1 mA cm^(-2) and 1 mA h cm^(-2) without short circuiting.This study will encourage the further development of functional organohydrogel electrolytes for advanced energy storage devices.
基金financially supported by the National Natural Science Foundation of China(Nos.21671096 and 21603094)the Shenzhen Peacock Plan(No.KQCX2014052215 0815065)+1 种基金the Natural Science Foundation of Shenzhen(Nos.JCYJ20150630145302231 and JCYJ20150331101823677)the Science and Technology Innovation Foundation for the Undergraduates of South University of Science and Technology of China(Nos.2016S10,2016S20,2015x19 and 2015x12)
文摘Alkaline zinc manganese dioxide（Zn–MnO2）batteries are widely used in everyday life. Recycling of waste alkaline Zn–MnO2 batteries has always been a hot environmental concern. In this study, a simple and costeffective process for synthesizing Mn3O4/carbon nanotube（CNT） nanocomposites from recycled alkaline Zn–MnO2 batteries is presented. Manganese oxide was recovered from spent Zn–MnO2 battery cathodes. The Mn3O4/CNT nanocomposites were produced by ball milling the recovered manganese oxide in a commercial multi-wall carbon nanotubes（MWCNTs） solution. Scanning electron microscopy（SEM） analysis demonstrates that the nanocomposite has a unique three-dimensional（3D） bird nest structure. Mn3O4 nanoparticles are homogeneously distributed on MWCNT framework. Mn3O4/CNT nanocomposites were evaluated as an anode material for lithium-ion batteries, exhibiting a highly reversible specific capacitance of -580 mA h·g^-1 after 100 cycles. Moreover, Mn3O4/CNT nanocomposite also shows a fairly positive onset potential of -0.15 V and quite high oxygen reducibility when considered as an electrocatalyst for oxygen reduction reaction.