The difference of conductivity between primary iron-rich phases and aluminum melt has been used to separate them by electromagnetic force (EMF) which is induced by imposing a direct electric current and a steady magne...The difference of conductivity between primary iron-rich phases and aluminum melt has been used to separate them by electromagnetic force (EMF) which is induced by imposing a direct electric current and a steady magnetic field in molten Al-Si alloy. Theoretical analysis and experiments on self-designed electromagnetic separation indicates that primary needle-like β phases are difficult to separate; while primary α iron-rich phases can be separated by electromagnetic separation. Primary iron-rich phases have been removed from the melt successfully when the molten metal flows horizontally through separation channel. The iron content is reduced from 1.13% to 0.41%.展开更多
Modifying effect and mechanism of trace rare earth on Fe(Si) rich impurity phases in commercial purity aluminum were studied with the aids of SEM, EDAX, TEM, etc. It is found that Ce rich mixed rare earth (RE) is an...Modifying effect and mechanism of trace rare earth on Fe(Si) rich impurity phases in commercial purity aluminum were studied with the aids of SEM, EDAX, TEM, etc. It is found that Ce rich mixed rare earth (RE) is an effective modifying agent, which makes the coarse Fe rich impurity phases transform into complex compounds of tiny, sphere/short stick form, thus improving mechanical properties of this material; its modifying mechanism is in that RE gathering in front of solid/liquid interface enters into the impurity phases, forming complex (AlFeSiRE) compounds; or is adsorbed in the impurity phases surface, impeding the growth of impurity phases; however, excessive RE will result in the increasing of RE compounds (secondary phases), and plasticity reduction of this material. Therefore, its addition amount should be less than 0 07% (mass fraction).展开更多
文摘The difference of conductivity between primary iron-rich phases and aluminum melt has been used to separate them by electromagnetic force (EMF) which is induced by imposing a direct electric current and a steady magnetic field in molten Al-Si alloy. Theoretical analysis and experiments on self-designed electromagnetic separation indicates that primary needle-like β phases are difficult to separate; while primary α iron-rich phases can be separated by electromagnetic separation. Primary iron-rich phases have been removed from the melt successfully when the molten metal flows horizontally through separation channel. The iron content is reduced from 1.13% to 0.41%.
文摘Modifying effect and mechanism of trace rare earth on Fe(Si) rich impurity phases in commercial purity aluminum were studied with the aids of SEM, EDAX, TEM, etc. It is found that Ce rich mixed rare earth (RE) is an effective modifying agent, which makes the coarse Fe rich impurity phases transform into complex compounds of tiny, sphere/short stick form, thus improving mechanical properties of this material; its modifying mechanism is in that RE gathering in front of solid/liquid interface enters into the impurity phases, forming complex (AlFeSiRE) compounds; or is adsorbed in the impurity phases surface, impeding the growth of impurity phases; however, excessive RE will result in the increasing of RE compounds (secondary phases), and plasticity reduction of this material. Therefore, its addition amount should be less than 0 07% (mass fraction).