The as-cast ingot of equiatomic nickel-titanium shape memory alloy （NiTi SMA） was prepared by vacuum consumable arc melting. The tensile tests and the compressive tests with respect to as-cast NiTi SMA were performe...The as-cast ingot of equiatomic nickel-titanium shape memory alloy （NiTi SMA） was prepared by vacuum consumable arc melting. The tensile tests and the compressive tests with respect to as-cast NiTi SMA were performed to study its mechanical properties of fracture. The microanalysis of as-cast NiTi SMA as well as its fractured samples was performed so as to better understand microstructure evolution and fracture behavior of NiTi SMA. Under tensile loading, the as-cast NiTi SMA shows higher plasticity and is characterized by ductile fracture at 750℃, but it demonstrates poorer plasticity and is characterized by cleavage fracture as well as transcrystalline fracture at room temperature and -100 ℃. Under compressive loading at -100 ~C, the as-cast NiTi SMA is characterized by shear fracture where the normal to the shearing fracture surface inclines about 45° to the compressive axis, and belongs to cleavage fracture where the cracks exoand via transcrvstalline fracture.展开更多
基金Project (51071056) supported by the National Natural Science Foundation of ChinaProject (HEUCFR1132) supported by the Fundamental Research Funds for the Central Universities of China
文摘The as-cast ingot of equiatomic nickel-titanium shape memory alloy （NiTi SMA） was prepared by vacuum consumable arc melting. The tensile tests and the compressive tests with respect to as-cast NiTi SMA were performed to study its mechanical properties of fracture. The microanalysis of as-cast NiTi SMA as well as its fractured samples was performed so as to better understand microstructure evolution and fracture behavior of NiTi SMA. Under tensile loading, the as-cast NiTi SMA shows higher plasticity and is characterized by ductile fracture at 750℃, but it demonstrates poorer plasticity and is characterized by cleavage fracture as well as transcrystalline fracture at room temperature and -100 ℃. Under compressive loading at -100 ~C, the as-cast NiTi SMA is characterized by shear fracture where the normal to the shearing fracture surface inclines about 45° to the compressive axis, and belongs to cleavage fracture where the cracks exoand via transcrvstalline fracture.