In order to investigate the chloride ion penetration resistance of coal gangue concrete under multi-factor comprehensive action, the non-steady-state accelerated chloride ion migration test was used to test the chlori...In order to investigate the chloride ion penetration resistance of coal gangue concrete under multi-factor comprehensive action, the non-steady-state accelerated chloride ion migration test was used to test the chloride diffusion law of coal gangue concrete specimens by crack width, curing temperature and water-cement ratio. Three groups of crack width (0 mm, 0.05 - 0.12 mm, 0.12 - 0.2 mm), three curing temperatures (high temperature 45, medium temperature 25, low temperature 10), three water cement ratios (0.3, 0.4, 0.5) were set in the experiment. The results show that when the curing temperature and water cement ratio are constant, the crack width less than 0.12 mm has little effect on the chloride content and chloride diffusion coefficient. When the crack width is larger than 0.12 mm, the chloride penetration depth increases with the crack width. The resistance to chloride ion penetration of gangue concrete is greatly influenced by the water cement ratio. The influ-ence degree of three factors on chloride ion migration coefficient of gangue concrete is as follows: water cement ratio > crack width > curing temperature.展开更多
To explore the distribution of and the mechanical properties(compressive strength)of the hardened body of alkali slag-fly ash cementitious materials,this study was conducted by using the XRD,FTIR,SEM/EDS,and other tes...To explore the distribution of and the mechanical properties(compressive strength)of the hardened body of alkali slag-fly ash cementitious materials,this study was conducted by using the XRD,FTIR,SEM/EDS,and other test methods in three conditions:airtight drying(AD),airtight immersion(AI),and airtight soaking(AS).The 1D distribution law of free of hardened body under standard curing conditions was explored.The experimental results show that under standard curing conditions,the 1D distribution of within 0d-3 d shows a∨-shaped distribution,within 3-7 d show a∧-shaped distribution,and within 7-28 d tends to be balanced.The test results of leaching rate show that the free was the most stable under AD conditions and the hardened body bound the most by XRD,FTIR and SEM/EDS.And the compressive strength of the hardened body was the highest.The compressive strength of 28th reached 95.9 MPa.The definite distribution of provides an important reference for the strength development and durability evaluation of the hardened body of alkaliexcited cementitious materials.展开更多
文摘In order to investigate the chloride ion penetration resistance of coal gangue concrete under multi-factor comprehensive action, the non-steady-state accelerated chloride ion migration test was used to test the chloride diffusion law of coal gangue concrete specimens by crack width, curing temperature and water-cement ratio. Three groups of crack width (0 mm, 0.05 - 0.12 mm, 0.12 - 0.2 mm), three curing temperatures (high temperature 45, medium temperature 25, low temperature 10), three water cement ratios (0.3, 0.4, 0.5) were set in the experiment. The results show that when the curing temperature and water cement ratio are constant, the crack width less than 0.12 mm has little effect on the chloride content and chloride diffusion coefficient. When the crack width is larger than 0.12 mm, the chloride penetration depth increases with the crack width. The resistance to chloride ion penetration of gangue concrete is greatly influenced by the water cement ratio. The influ-ence degree of three factors on chloride ion migration coefficient of gangue concrete is as follows: water cement ratio > crack width > curing temperature.
基金Funded by the Natural Sciences Foundation of China(No.51808025)the Pyramid Talent Training Project of BUCEA(No.JDYC20200329)。
文摘To explore the distribution of and the mechanical properties(compressive strength)of the hardened body of alkali slag-fly ash cementitious materials,this study was conducted by using the XRD,FTIR,SEM/EDS,and other test methods in three conditions:airtight drying(AD),airtight immersion(AI),and airtight soaking(AS).The 1D distribution law of free of hardened body under standard curing conditions was explored.The experimental results show that under standard curing conditions,the 1D distribution of within 0d-3 d shows a∨-shaped distribution,within 3-7 d show a∧-shaped distribution,and within 7-28 d tends to be balanced.The test results of leaching rate show that the free was the most stable under AD conditions and the hardened body bound the most by XRD,FTIR and SEM/EDS.And the compressive strength of the hardened body was the highest.The compressive strength of 28th reached 95.9 MPa.The definite distribution of provides an important reference for the strength development and durability evaluation of the hardened body of alkaliexcited cementitious materials.