The modification methods of pozzolan slurry combined with sodium silicate and silicon-based additive were respectively adopted to treat recycled coarse brick-mixed aggregate(RCBA)in this study.The compressive strength...The modification methods of pozzolan slurry combined with sodium silicate and silicon-based additive were respectively adopted to treat recycled coarse brick-mixed aggregate(RCBA)in this study.The compressive strength and chloride permeability resistance of recycled aggregate concrete(RAC)before and after modification treatment were tested,and the microstructure of RAC was analyzed by mercury intrusion porosimetry(MIP)and scanning electron microscopy(SEM).The results show that the physical properties of RCBA strengthened by modification treatment are improved,and the compressive strength and chloride permeability resistance of treated RAC are also significantly improved.The modification treatment optimizes the pore size distribution of RAC,which increases the number of gel pores and transition pores,and decreases the number of capillary pores and macro pores.The surface fractal dimension shows a significant correlation with chloride diffusion coefficient,indicating that the variation of chloride permeability of treated RAC is consistent with the microstructure evolution.展开更多
In order to increase use ratio of steel slag solid waste,the concrete containing steel slag powder and zeolite powder as admixtures was prepared by using the orthogonal test method.The effects of water-binder ratio,s...In order to increase use ratio of steel slag solid waste,the concrete containing steel slag powder and zeolite powder as admixtures was prepared by using the orthogonal test method.The effects of water-binder ratio,sand ratio,steel slag powder content and zeolite powder on working properties,mechanical strength and chloride ion permeability of the concrete was studied.It was found that the early strength of the concrete had a decrease with the mixing of steel slag and zeolite powders,but its later strength approached to pure concrete.Moreover,the physical filling and pozzolanic activity of the admixtures increased the density of the concrete,resulting in the improvement of the durability of the concrete by the migration speed of Cl−reducing.The optimum mix ratio of C40 steel slag powder-zeolite powder concrete is obtained,and which had the slump of 220 mm,the 3 d,7 d and 28 d compressive strengths of 27.8 MPa,37.5 MPa and 48.4 MPa,the 6 h electric flux of 950 C and the diffusion coefficient of 1.65×10−12 m2/s.展开更多
基金Funded by the National Natural Science Foundation of China(No.52078050)the Natural Science Basic Research Plan in Shaanxi Province of China(No.2020JZ-22)。
文摘The modification methods of pozzolan slurry combined with sodium silicate and silicon-based additive were respectively adopted to treat recycled coarse brick-mixed aggregate(RCBA)in this study.The compressive strength and chloride permeability resistance of recycled aggregate concrete(RAC)before and after modification treatment were tested,and the microstructure of RAC was analyzed by mercury intrusion porosimetry(MIP)and scanning electron microscopy(SEM).The results show that the physical properties of RCBA strengthened by modification treatment are improved,and the compressive strength and chloride permeability resistance of treated RAC are also significantly improved.The modification treatment optimizes the pore size distribution of RAC,which increases the number of gel pores and transition pores,and decreases the number of capillary pores and macro pores.The surface fractal dimension shows a significant correlation with chloride diffusion coefficient,indicating that the variation of chloride permeability of treated RAC is consistent with the microstructure evolution.
基金This work was supported by the Gui Ke Neng(19-J-21-7 and 19-J-21-12).
文摘In order to increase use ratio of steel slag solid waste,the concrete containing steel slag powder and zeolite powder as admixtures was prepared by using the orthogonal test method.The effects of water-binder ratio,sand ratio,steel slag powder content and zeolite powder on working properties,mechanical strength and chloride ion permeability of the concrete was studied.It was found that the early strength of the concrete had a decrease with the mixing of steel slag and zeolite powders,but its later strength approached to pure concrete.Moreover,the physical filling and pozzolanic activity of the admixtures increased the density of the concrete,resulting in the improvement of the durability of the concrete by the migration speed of Cl−reducing.The optimum mix ratio of C40 steel slag powder-zeolite powder concrete is obtained,and which had the slump of 220 mm,the 3 d,7 d and 28 d compressive strengths of 27.8 MPa,37.5 MPa and 48.4 MPa,the 6 h electric flux of 950 C and the diffusion coefficient of 1.65×10−12 m2/s.