Cr2O3 has eminent slag corrosion resistance. So, the magnesite -chrome brick is thought as an important refractory material used in RH refining furnace in the process of steel-making around the world. After chromebear...Cr2O3 has eminent slag corrosion resistance. So, the magnesite -chrome brick is thought as an important refractory material used in RH refining furnace in the process of steel-making around the world. After chromebearing sols being prepared by sol-gel method, single sol （ Cr（ OH）3） and mixed sol （ Mg（ OH）2 - Cr（ OH）3） were impregnated into magnesite - chrome bricks by vacuum impregnation. The corrosion resistance of the impregnated bricks to silicon steel slag was studied by porosimetric analysis and fractal dimension calculation. The results showed that the corrosion resistance of impregnated magnesite -chrome brick was better than that of the unimpregnated brick and the brick impregnated by MgSO4 solution, and the one which has surface-treated by Mg（ OH）2 -Cr（OH）3 sol was the best, mainly because of lower apparent porosity, smaller pores diameter and their smoother inner sarface.展开更多
Operating condition and service results of several tested bricks in slagline area of the VOD vessel are described. It has been shown that the fully co-clinkered magnesite chrome brick is superior, followed by two-stag...Operating condition and service results of several tested bricks in slagline area of the VOD vessel are described. It has been shown that the fully co-clinkered magnesite chrome brick is superior, followed by two-stage calcined magnesite-dolomite brick , prereacted magnesite-chrome brick and one-stage calcined magnesite-dolomite brick. Chemical and petrological examination were carried out by conventional analysis and optical microscope respectively. The reason of damage of the tested bricks are discussed and described as follows : (1) MgO in brick is erased and dissolved by slag to destroy structure of the direct bond ; (2) slag penetrating into the brick and then reacting with it to form various belts leading to spatting ; (3 ) reducing action of reducing agents ; (4) vaporization of some composition in the brick at high temperature under vacuum causes reducing weight and increasing porosity and (5 ) serious ma-chanic abrasion. Therefore, some opinions on increasing lining life of VOD vessels are suggested.展开更多
Wear of the spent high chrome brick in slagging gasifier was studied. The result shows that erosion and spalling are the m, ain wear mechanism of high chrome brick and the CaO content of coal slag is crucial to wear o...Wear of the spent high chrome brick in slagging gasifier was studied. The result shows that erosion and spalling are the m, ain wear mechanism of high chrome brick and the CaO content of coal slag is crucial to wear of high chrome brick.展开更多
The corrosion resistance of four kinds magnesitechrome bricks against converter salg was investigated by static crucible slag tests. The microstructures of the asdelivered and tested refractories were analyzed by mean...The corrosion resistance of four kinds magnesitechrome bricks against converter salg was investigated by static crucible slag tests. The microstructures of the asdelivered and tested refractories were analyzed by means of SEM and EDS. The results showed that： Different magnesite-chrome bricks have different slag resistances. Generally, the slag resiantance sequence is as follows： rebounded fused magnesite-chrome brick 〉 semi-reboun- ded magnesite-chrome brick 〉 direct-bonded magnesitechrome brick 〉 silicate bonded magnesite-chrome brick. Slag reacts with the periclase of magnesite-chrome refractories, which results in the dissoving of periclase in fayalite slag. However, the complex spinels have superior slag resistance.展开更多
Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and...Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and microstructure of fused rebonded magnesia - chrome brick with 26.02 massqc of Cr2O3 were researched by rotary cylinder method. The results show that ： （ 1 ） the corro- sion amolult of magnesia -chrome brick by slag without FeO is higher than that by the slag with 5% FeO, and the vorrosion amount increases when FeO content increa- ses from 5% to 15% ; （2） the test temperature is one of the important factors affecting the slag corrosion resist- ance of magnesia - chrome brick, and the corrosion of smelting reduction slag to brick increases with the temperature rising.展开更多
The penetration behavior of different kinds of coal ash slags into chrome corundum bricks was studied by cup test. As a preliminary attempt,the oxides of Fe2O3 and MgO were added into coal ash to reduce the erosion of...The penetration behavior of different kinds of coal ash slags into chrome corundum bricks was studied by cup test. As a preliminary attempt,the oxides of Fe2O3 and MgO were added into coal ash to reduce the erosion of refractories. Different cup tests were carried out to study coal slag erosion to the refractories. FactSage was used to simulate the phase diagram of the main chemical compositions in coal ash and in the refractories. Both results agreed with each other. The results show that the elements in coal slag can penetrate into bricks and the penetration deepens with the duration increasing; it is difficult for Fe but easier for Ca and Si to penetrate into bricks; different kinds of melting coal ashes penetrate into refractories differently and the penetration depth of silicon and calcium can be significantly reduced by adding oxides into coal ash.展开更多
基金supported by the Natural Science Foundation of Hubei Province (2007ABA372)the New Century Excellent Talents in University (NCET-06-0676)
文摘Cr2O3 has eminent slag corrosion resistance. So, the magnesite -chrome brick is thought as an important refractory material used in RH refining furnace in the process of steel-making around the world. After chromebearing sols being prepared by sol-gel method, single sol （ Cr（ OH）3） and mixed sol （ Mg（ OH）2 - Cr（ OH）3） were impregnated into magnesite - chrome bricks by vacuum impregnation. The corrosion resistance of the impregnated bricks to silicon steel slag was studied by porosimetric analysis and fractal dimension calculation. The results showed that the corrosion resistance of impregnated magnesite -chrome brick was better than that of the unimpregnated brick and the brick impregnated by MgSO4 solution, and the one which has surface-treated by Mg（ OH）2 -Cr（OH）3 sol was the best, mainly because of lower apparent porosity, smaller pores diameter and their smoother inner sarface.
文摘Operating condition and service results of several tested bricks in slagline area of the VOD vessel are described. It has been shown that the fully co-clinkered magnesite chrome brick is superior, followed by two-stage calcined magnesite-dolomite brick , prereacted magnesite-chrome brick and one-stage calcined magnesite-dolomite brick. Chemical and petrological examination were carried out by conventional analysis and optical microscope respectively. The reason of damage of the tested bricks are discussed and described as follows : (1) MgO in brick is erased and dissolved by slag to destroy structure of the direct bond ; (2) slag penetrating into the brick and then reacting with it to form various belts leading to spatting ; (3 ) reducing action of reducing agents ; (4) vaporization of some composition in the brick at high temperature under vacuum causes reducing weight and increasing porosity and (5 ) serious ma-chanic abrasion. Therefore, some opinions on increasing lining life of VOD vessels are suggested.
文摘Wear of the spent high chrome brick in slagging gasifier was studied. The result shows that erosion and spalling are the m, ain wear mechanism of high chrome brick and the CaO content of coal slag is crucial to wear of high chrome brick.
文摘The corrosion resistance of four kinds magnesitechrome bricks against converter salg was investigated by static crucible slag tests. The microstructures of the asdelivered and tested refractories were analyzed by means of SEM and EDS. The results showed that： Different magnesite-chrome bricks have different slag resistances. Generally, the slag resiantance sequence is as follows： rebounded fused magnesite-chrome brick 〉 semi-reboun- ded magnesite-chrome brick 〉 direct-bonded magnesitechrome brick 〉 silicate bonded magnesite-chrome brick. Slag reacts with the periclase of magnesite-chrome refractories, which results in the dissoving of periclase in fayalite slag. However, the complex spinels have superior slag resistance.
文摘Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and microstructure of fused rebonded magnesia - chrome brick with 26.02 massqc of Cr2O3 were researched by rotary cylinder method. The results show that ： （ 1 ） the corro- sion amolult of magnesia -chrome brick by slag without FeO is higher than that by the slag with 5% FeO, and the vorrosion amount increases when FeO content increa- ses from 5% to 15% ; （2） the test temperature is one of the important factors affecting the slag corrosion resist- ance of magnesia - chrome brick, and the corrosion of smelting reduction slag to brick increases with the temperature rising.
文摘The penetration behavior of different kinds of coal ash slags into chrome corundum bricks was studied by cup test. As a preliminary attempt,the oxides of Fe2O3 and MgO were added into coal ash to reduce the erosion of refractories. Different cup tests were carried out to study coal slag erosion to the refractories. FactSage was used to simulate the phase diagram of the main chemical compositions in coal ash and in the refractories. Both results agreed with each other. The results show that the elements in coal slag can penetrate into bricks and the penetration deepens with the duration increasing; it is difficult for Fe but easier for Ca and Si to penetrate into bricks; different kinds of melting coal ashes penetrate into refractories differently and the penetration depth of silicon and calcium can be significantly reduced by adding oxides into coal ash.