Pilling is a severe concern for blended fabrics. The aesthetic look and smoothness are the buyers’ prime requirements. The main focus of the study was to see the pilling behavior from various percentages of polyester...Pilling is a severe concern for blended fabrics. The aesthetic look and smoothness are the buyers’ prime requirements. The main focus of the study was to see the pilling behavior from various percentages of polyester fiber blend ratio as well as the different pilling cycles on blended fabrics. The cotton, polyester, and elastane prepared the study fabrics. These fabrics are (90% Cotton/5% Polyester/5% Elastane, 90% Cotton/6% Polyester/4% Elastane, 90% Cotton/7% Polyester/3% Elastane, 90% Cotton/8% Polyester/2% Elastane, and 90% Cotton/9% Polyester/1% Elastane, 85% Cotton/10% Polyester/5% Elastane, 85% Cotton/11% Polyester/4% Elastane, 85% Cotton/12% Polyester/3% Elastane, 85% Cotton/13% Polyester/2% Elastane, and 85% Cotton/ 14% Polyester/1% Elastane, 80% Cotton/15% Polyester/5% Elastane, 80% Cotton/16% Polyester/4% Elastane, 80% Cotton/17% Polyester/3% Elastane, 80% Cotton/18% Polyester/2% Elastane, and 80% Cotton/19% Polyester/1% Elastane). The selected polyester blend ratios were 5%, 6%, 7%, 8%, 9%, 10%, 11%, 12%, 13%, 14%, 15%, 16%, 17%, 18% and 19% respectively. The study used the Martindale pilling tester with 2000, 5000, and 7000 cycles, respectively. The evaluation followed the ISO 12945-2:2000. The study findings are that the polyester fiber blend ratio did not influence the pilling grade on blended fabrics for pilling cycles 2000, and the pilling grade remained constant at 4 - 5. The pilling grade started to deteriorate in pilling cycle 5000 for the fabrics 85%C/10%P/5%E, 85%C/11%P/4%E, 85%C/12%P/3%E, 85%C/ 13%P/2%E, 85%C/14%P/1%E showed the pilling grade 4, and the fabrics made from 80%C/15%P/5%E, 80%C/16%P/4%E, 80%C/17%P/3%E, 80%C/ 18%P/2%E, 80%C/19%P/1%E showed the pilling grade 4, 3, 3, 3, and 3 respectively. For the pilling cycles 7000, the pilling grade further deteriorated for the fabrics 80%C/15%P/5%E, 80%C/16%P/4%E, 80%C/17%P/3%E, 80%C/ 18%P/2%E, 80%C/19%P/1%E showed the pilling grade 3, 3, 2, 2, and 2 respectively. The study finds the dominance of polyester fiber throughout the experiment. The author hopes this study’s outcome will help new researchers, advanced researchers, and the textile industry’s sustainable development research and development team.展开更多
The effects of the blending ratio on the properties of Ramie/Polyester blended yarns are discussed in this paper. The experimental results show that the elongation of the yarn with the polyester content more than 40% ...The effects of the blending ratio on the properties of Ramie/Polyester blended yarns are discussed in this paper. The experimental results show that the elongation of the yarn with the polyester content more than 40% is better than that of others. There is a lowest tenacity of the yarn corresponding to the blending ratio of 50/50 or so. The other properties of the yarn, such as the evenness and hairiness, will be improved with the increasing of the polyester content.展开更多
The bursting strength is an essential quality parameter of knit fabric. The fabric structure, weight, types of fibers, and fiber blend proportion influence the bursting strength parameter. The tenacity of polyester fi...The bursting strength is an essential quality parameter of knit fabric. The fabric structure, weight, types of fibers, and fiber blend proportion influence the bursting strength parameter. The tenacity of polyester fiber is better than cotton and spandex. The study focused on predicting knit fabric bursting strength test value using different fibers (cotton, polyester, and spandex) with varying percentages of the blend ratio. This study used fifteen categories of blended fabrics. The Pearson Correlation and the hypothetical ANOVA regression analysis were conducted to do the statistical significance test. The experimental result reveals that the bursting strength test result increased with the increased percentage of polyester and suggested a suitable regression equation. The dominance of the polyester fiber was observed throughout the experiment, i.e., the higher the polyester blend proportion, the higher the bursting strength value. The inclusion of polyester in blends can reduce the cost of fabric. The developed prediction model or equation can help the fabric manufacturer make appropriate decisions regarding getting the expected bursting strength. The researcher hopes that the findings from this study will motivate new researchers, advanced researchers, and the textile manufacturing industry.展开更多
Yarn quality characteristics are affected by processing parameters. A 36 tex rotor spun yarn of 50/50 Basofil/ cotton （B/C） blended yarn was spun, and the spinning process optimised for rotor speed, opening roller s...Yarn quality characteristics are affected by processing parameters. A 36 tex rotor spun yarn of 50/50 Basofil/ cotton （B/C） blended yarn was spun, and the spinning process optimised for rotor speed, opening roller speed and twist factor. Selected yarn characteristics were studied during the optimization process. During the optimizations process yarn elongation and hairiness reduced with increase in rotor speed. Tenacity increased with increase of rotor speed. The increase in TF caused tenacity and CV of count to increase up to a peak and then started to decrease with further increase of TF.While TF caused an increase in yarn hairiness, elongation decreased to a minimum level and then started to increase with further increase of TF. CV of count and hairiness increased with increase in opening roller speed, but tenacity and elongation decreased with increase in opening roller speed. The optimization process yielded the optimum levels for rotor speed, opening roller speed and twist factor （TF） as 45,000 rpm, 6,500 rpm and 450 respectively. As per uster Standards the optimum yam showed good results for CV of count, CV of tenacity and thin places/km.展开更多
Nowadays,more and more natural or functional fibers are being investigated due to their utilization in thermal underwear.Kapok fiber is one of the natural cellulosic fibers whose source is the kapok plant. It has holl...Nowadays,more and more natural or functional fibers are being investigated due to their utilization in thermal underwear.Kapok fiber is one of the natural cellulosic fibers whose source is the kapok plant. It has hollow body and sealed tail,which exhibits desirable features required for functional textiles of this nature. In this study,cotton / kapok( 80 /20 by mass) blended yarn with two types of yarn size 18. 5 and 14. 8 tex,respectively are knitted into plain stitches. The fabrics are undergone with an optimal preparation plan according to orthogonal design. Then,after dyeing and softening,fabric properties including thermal and water-vapour resistances, wicking property, pilling behaviour, and surface morphology,are tested and scrutinized for their candidacy for thermal underwear. The results showed that cotton / kapok blended fabrics have good thermal resistance which is significantly higher than those of cotton / modal blended fabrics,and the same water vapour resistance compared with cotton / modal blended fabrics which are normally used as underwear. Cotton / modal blended knitted fabrics has better pilling grade than cotton / kapok blended fabrics. Meanwhile, the cotton / kapok blends fabrics have good wicking property. Collectively,it was concluded that cotton / kapok blended fabric was appropriate for thermal underwear. However,the main limitation of these fabrics is their pilling properties.展开更多
文摘Pilling is a severe concern for blended fabrics. The aesthetic look and smoothness are the buyers’ prime requirements. The main focus of the study was to see the pilling behavior from various percentages of polyester fiber blend ratio as well as the different pilling cycles on blended fabrics. The cotton, polyester, and elastane prepared the study fabrics. These fabrics are (90% Cotton/5% Polyester/5% Elastane, 90% Cotton/6% Polyester/4% Elastane, 90% Cotton/7% Polyester/3% Elastane, 90% Cotton/8% Polyester/2% Elastane, and 90% Cotton/9% Polyester/1% Elastane, 85% Cotton/10% Polyester/5% Elastane, 85% Cotton/11% Polyester/4% Elastane, 85% Cotton/12% Polyester/3% Elastane, 85% Cotton/13% Polyester/2% Elastane, and 85% Cotton/ 14% Polyester/1% Elastane, 80% Cotton/15% Polyester/5% Elastane, 80% Cotton/16% Polyester/4% Elastane, 80% Cotton/17% Polyester/3% Elastane, 80% Cotton/18% Polyester/2% Elastane, and 80% Cotton/19% Polyester/1% Elastane). The selected polyester blend ratios were 5%, 6%, 7%, 8%, 9%, 10%, 11%, 12%, 13%, 14%, 15%, 16%, 17%, 18% and 19% respectively. The study used the Martindale pilling tester with 2000, 5000, and 7000 cycles, respectively. The evaluation followed the ISO 12945-2:2000. The study findings are that the polyester fiber blend ratio did not influence the pilling grade on blended fabrics for pilling cycles 2000, and the pilling grade remained constant at 4 - 5. The pilling grade started to deteriorate in pilling cycle 5000 for the fabrics 85%C/10%P/5%E, 85%C/11%P/4%E, 85%C/12%P/3%E, 85%C/ 13%P/2%E, 85%C/14%P/1%E showed the pilling grade 4, and the fabrics made from 80%C/15%P/5%E, 80%C/16%P/4%E, 80%C/17%P/3%E, 80%C/ 18%P/2%E, 80%C/19%P/1%E showed the pilling grade 4, 3, 3, 3, and 3 respectively. For the pilling cycles 7000, the pilling grade further deteriorated for the fabrics 80%C/15%P/5%E, 80%C/16%P/4%E, 80%C/17%P/3%E, 80%C/ 18%P/2%E, 80%C/19%P/1%E showed the pilling grade 3, 3, 2, 2, and 2 respectively. The study finds the dominance of polyester fiber throughout the experiment. The author hopes this study’s outcome will help new researchers, advanced researchers, and the textile industry’s sustainable development research and development team.
文摘The effects of the blending ratio on the properties of Ramie/Polyester blended yarns are discussed in this paper. The experimental results show that the elongation of the yarn with the polyester content more than 40% is better than that of others. There is a lowest tenacity of the yarn corresponding to the blending ratio of 50/50 or so. The other properties of the yarn, such as the evenness and hairiness, will be improved with the increasing of the polyester content.
文摘The bursting strength is an essential quality parameter of knit fabric. The fabric structure, weight, types of fibers, and fiber blend proportion influence the bursting strength parameter. The tenacity of polyester fiber is better than cotton and spandex. The study focused on predicting knit fabric bursting strength test value using different fibers (cotton, polyester, and spandex) with varying percentages of the blend ratio. This study used fifteen categories of blended fabrics. The Pearson Correlation and the hypothetical ANOVA regression analysis were conducted to do the statistical significance test. The experimental result reveals that the bursting strength test result increased with the increased percentage of polyester and suggested a suitable regression equation. The dominance of the polyester fiber was observed throughout the experiment, i.e., the higher the polyester blend proportion, the higher the bursting strength value. The inclusion of polyester in blends can reduce the cost of fabric. The developed prediction model or equation can help the fabric manufacturer make appropriate decisions regarding getting the expected bursting strength. The researcher hopes that the findings from this study will motivate new researchers, advanced researchers, and the textile manufacturing industry.
文摘Yarn quality characteristics are affected by processing parameters. A 36 tex rotor spun yarn of 50/50 Basofil/ cotton （B/C） blended yarn was spun, and the spinning process optimised for rotor speed, opening roller speed and twist factor. Selected yarn characteristics were studied during the optimization process. During the optimizations process yarn elongation and hairiness reduced with increase in rotor speed. Tenacity increased with increase of rotor speed. The increase in TF caused tenacity and CV of count to increase up to a peak and then started to decrease with further increase of TF.While TF caused an increase in yarn hairiness, elongation decreased to a minimum level and then started to increase with further increase of TF. CV of count and hairiness increased with increase in opening roller speed, but tenacity and elongation decreased with increase in opening roller speed. The optimization process yielded the optimum levels for rotor speed, opening roller speed and twist factor （TF） as 45,000 rpm, 6,500 rpm and 450 respectively. As per uster Standards the optimum yam showed good results for CV of count, CV of tenacity and thin places/km.
基金Technical Standards for the Development of Kinitted Jinlong Underw ear Factory of Guangdong Province,China(No.HX201303000008)
文摘Nowadays,more and more natural or functional fibers are being investigated due to their utilization in thermal underwear.Kapok fiber is one of the natural cellulosic fibers whose source is the kapok plant. It has hollow body and sealed tail,which exhibits desirable features required for functional textiles of this nature. In this study,cotton / kapok( 80 /20 by mass) blended yarn with two types of yarn size 18. 5 and 14. 8 tex,respectively are knitted into plain stitches. The fabrics are undergone with an optimal preparation plan according to orthogonal design. Then,after dyeing and softening,fabric properties including thermal and water-vapour resistances, wicking property, pilling behaviour, and surface morphology,are tested and scrutinized for their candidacy for thermal underwear. The results showed that cotton / kapok blended fabrics have good thermal resistance which is significantly higher than those of cotton / modal blended fabrics,and the same water vapour resistance compared with cotton / modal blended fabrics which are normally used as underwear. Cotton / modal blended knitted fabrics has better pilling grade than cotton / kapok blended fabrics. Meanwhile, the cotton / kapok blends fabrics have good wicking property. Collectively,it was concluded that cotton / kapok blended fabric was appropriate for thermal underwear. However,the main limitation of these fabrics is their pilling properties.