A numerical analysis of mechanical behavior of aluminum alloy sheet under cyclic plastic deformation was investigated.Forming limit at fracture was derived from Cockcroft-Latham ductile damage criterion.The strain pat...A numerical analysis of mechanical behavior of aluminum alloy sheet under cyclic plastic deformation was investigated.Forming limit at fracture was derived from Cockcroft-Latham ductile damage criterion.The strain path of bending center of incremental roller hemming could be accepted as a kind of plane strain bending deformation process.Incremental rope roller hemming could be used to alleviate ductile fracture behavior by changing the stress state of the hemming-effected area.SEM observation on the fracture surface indicates that cyclic plastic deformation affects ductile fracture mechanism.展开更多
The experimental study of Bauschinger effect in Mn18Cr18N austenitic stainless steel was presented by compression-tensile cyclic loading tests with the prestrains ranging from 0.005 to 0.1,which was illustrated utiliz...The experimental study of Bauschinger effect in Mn18Cr18N austenitic stainless steel was presented by compression-tensile cyclic loading tests with the prestrains ranging from 0.005 to 0.1,which was illustrated utilizing stress-strain curves and analysed by TEM images from aspects of microstructural mechanisms.Moreover,the Bauschinger effect and its associated roundness phenomenon in reverse flow curve with respect to different cycles and cyclic strain amplitudes were evaluated in a quantitative manner.The experimental results indicate that Bauschinger effect is apparent during the test.At smaller cyclic strain amplitude,intergranular backstress is the main source of Bauschinger effect.With further increasing of cycles,dislocation density increases and dislocation movement is hindered in the reverse deformation.Therefore,Bauschinger effect is weakened to some extent.At large cyclic strain amplitude,backstress originating from the dislocation pile-up at grain boundaries and the continuous formation of deformation twins dominate the Bauschinger effect.In addition,the backstress results in the roundness of reverse curve during cyclic loading.The larger value ofΔεp*,the more obvious the roundness of the reverse curve,and the more significant the Bauschinger effect.展开更多
基金Project(2010CB731703) supported by the National Basic Research Program of China Project(0804) supported by the Shanghai Automotive Industry Corporation Foundation,ChinaProject(MSV-2010-03) supported by State Key Laboratory of Mechanical System and Vibration,Shanghai Jiao Tong University,China
文摘A numerical analysis of mechanical behavior of aluminum alloy sheet under cyclic plastic deformation was investigated.Forming limit at fracture was derived from Cockcroft-Latham ductile damage criterion.The strain path of bending center of incremental roller hemming could be accepted as a kind of plane strain bending deformation process.Incremental rope roller hemming could be used to alleviate ductile fracture behavior by changing the stress state of the hemming-effected area.SEM observation on the fracture surface indicates that cyclic plastic deformation affects ductile fracture mechanism.
基金the National Natural Science Foundation of China(No.51575372)the Science and Technology Research Plan(Industrial)Project of Shanxi Province,China(No.201603D121006-2)+1 种基金the Start-up Fund for Scientific Research of Taiyuan University of Science and Technology(No.20172011)the Fund for Shanxi Key Subjects Construction。
文摘The experimental study of Bauschinger effect in Mn18Cr18N austenitic stainless steel was presented by compression-tensile cyclic loading tests with the prestrains ranging from 0.005 to 0.1,which was illustrated utilizing stress-strain curves and analysed by TEM images from aspects of microstructural mechanisms.Moreover,the Bauschinger effect and its associated roundness phenomenon in reverse flow curve with respect to different cycles and cyclic strain amplitudes were evaluated in a quantitative manner.The experimental results indicate that Bauschinger effect is apparent during the test.At smaller cyclic strain amplitude,intergranular backstress is the main source of Bauschinger effect.With further increasing of cycles,dislocation density increases and dislocation movement is hindered in the reverse deformation.Therefore,Bauschinger effect is weakened to some extent.At large cyclic strain amplitude,backstress originating from the dislocation pile-up at grain boundaries and the continuous formation of deformation twins dominate the Bauschinger effect.In addition,the backstress results in the roundness of reverse curve during cyclic loading.The larger value ofΔεp*,the more obvious the roundness of the reverse curve,and the more significant the Bauschinger effect.