The finite-depth concrete panels have been widely applied in the protective structures,and its impact resistance and dynamic fracture failures,especially the scabbing/perforation limits,under high velocity projectile ...The finite-depth concrete panels have been widely applied in the protective structures,and its impact resistance and dynamic fracture failures,especially the scabbing/perforation limits,under high velocity projectile impact,are mainly concerned by protective engineers,which are numerically studied based on an improved dynamic concrete model in this study.Firstly,based on the framework of the KCC(Karagozian&Case concrete)model,a dynamic concrete model is proposed which considers an independent tensile damage model and a continued transition between dynamic tensile and compressive properties.Secondly,the strength surface,equation of state and damage parameters of the proposed model are comprehensively calibrated by a triaxial compressive test with high confinement pressure,the rationality of which is further verified based on the single element tests,e.g.,uniaxial and triaxial compression as well as uniaxial,biaxial and triaxial tension.Thirdly,a series of projectile high velocity impact tests on thin and thick concrete panels are simulated,which indicates that the projectile residual velocity and dynamic fracture failures are reproduced satisfactorily,while the KCC model underestimates both the spalling and scabbing dimensions severely.Finally,based on the validated concrete model and finite element analyses approach,the validations of the existing five empirical formulae are evaluated,in terms of the depth of penetration(DOP)and scabbing/perforation limits of concrete panel.Both the Army corps of engineers(ACE)and modified National Defense Research Committee(NDRC)formulae are recommended in the design of the protective structure to avoid scabbing failure.展开更多
In this study,a novel testing method is proposed to characterize the dynamic shear property and failure mechanism of rocks by introducing the short beam compression(SBC)specimen into the split Hopkinson pressure bar(S...In this study,a novel testing method is proposed to characterize the dynamic shear property and failure mechanism of rocks by introducing the short beam compression(SBC)specimen into the split Hopkinson pressure bar(SHPB)system.Firstly,the stress distribution of SBC specimen is comprehensively analyzed by finite element method(FEM),and the results show that the optimal notch separation ratio of SBC specimen is C/H?0.2 to achieve successful dynamic simple-shear tests.Then,dynamic shear tests are conducted on sandstone using the SBC-SHPB method.Via careful pulse shaping technique,the dynamic force balance is guaranteed for SBC specimens,and the testing results show that the dynamic shear strength of sandstone is significantly rate-dependent.Combining the results of dynamic compression and tension tests,the failure envelopes of sandstone under different loading rates are obtained in the principle stress plane.It is found that the failure envelope of sandstone constantly expands outwards with increasing loading rate.Moreover,the energy partition of SBC specimen is quantified by virtue of high-speed digital image correlation(DIC)technique.The results show that the kinetic energy portion is non-negligible,and the shear fracture energy increases with increasing loading rate.In addition,the microscopic shear cracking mechanism of SBC specimen is analyzed by the thin section observation:the intra-granular(TG)fracture of minerals dominates the dynamic shear failure of sandstone,and the portion of TG fracture increases with increasing loading rate.This study provides a convenient and reliable method to investigate the dynamic shear property and failure mechanism of rocks.展开更多
The dynamic fracture behaviors of Ti-6Al-4V alloy at high strain rate loading were investigated systemically through Taylor impact test, over the range of impact velocities from 145 m/s to 306 m/s. The critical impact...The dynamic fracture behaviors of Ti-6Al-4V alloy at high strain rate loading were investigated systemically through Taylor impact test, over the range of impact velocities from 145 m/s to 306 m/s. The critical impact velocity of fracture ranges from 217 m/s to 236 m/s. Smooth surfaces and ductile dimple areas were observed on the fracture surfaces. As the impact velocity reached 260 m/s, the serious melting regions were also observed on the fracture surfaces. Self-organization of cracks emerges when the impact velocity reaches 260 m/s, while some special cracks whose ＂tips＂ are not sharp but arc and smooth, and without any evidence of deformation or adiabatic shear band were also observed on the impact end surfaces. Examination of the sections of these special cracks reveals that the cracks expand along the two maximum shear stress directions respectively, and finally intersect as a tridimensional ＂stagger ridge＂ structure.展开更多
The reflected optical caustics method is applied to study dynamic fracture problems in hardened cement paste. First both the unreinforced cement paste and the glass fibres reinforced cement paste specimens were fabric...The reflected optical caustics method is applied to study dynamic fracture problems in hardened cement paste. First both the unreinforced cement paste and the glass fibres reinforced cement paste specimens were fabricated and the reflective coating on the surface of the specimen was prepared. Secondly the crack path and the shadow spot patterns during the crack propagation process for the two specimens were recorded by using a multi-spark high speed camera.Thirdly some dynamic parameters of two cement paste specimens including crack onset time the dynamic stress intensity factor and crack growth velocity were determined and analyzed comparatively.This indicates that the glass fibres can improve the fracture resistance and delay fracture time.These results will play an important role in evaluating the dynamic fracture properties of cement paste.展开更多
The paper considers application of artificial neural networks(ANNs)for fast numerical evaluation of a residual impactor velocity for a family of perforated PMMA(Polymethylmethacrylate)targets.The ANN models were train...The paper considers application of artificial neural networks(ANNs)for fast numerical evaluation of a residual impactor velocity for a family of perforated PMMA(Polymethylmethacrylate)targets.The ANN models were trained using sets of numerical results on impact of PMMA plates obtained via dynamic FEM coupled with incubation time fracture criterion.The developed approach makes it possible to evaluate the impact strength of a particular target configuration without complicated FEM calculations which require considerable computational resources.Moreover,it is shown that the ANN models are able to predict results for the configurations which cannot be processed using the developed FEM routine due to numerical instabilities and errors:the trained neural network uses information from successful computations to obtain results for the problematic cases.A simple static problem of a perforated plate deformation is discussed prior to the impact problem and preferable ANN architectures are presented for both problems.Some insight into the perforation pattern optimization using a genetic algorithm coupled with the ANN is also made and optimized perforation patterns which theoretically enhance the target impact strength are constructed.展开更多
Rock fracture mechanics and accurate characterization of rock fracture are crucial for understanding a variety of phenomena interested in geological engineering and geoscience.These phenomena range from very large-sca...Rock fracture mechanics and accurate characterization of rock fracture are crucial for understanding a variety of phenomena interested in geological engineering and geoscience.These phenomena range from very large-scale asymmetrical fault structures to the scale of engineering projects and laboratory-scale rock fracture tests.Comprehensive study can involve mechanical modeling,site or post-mortem investigations,and inspection on the point cloud of the source locations in the form of earthquake,microseismicity,or acoustic emission.This study presents a comprehensive data analysis on characterizing the forming of the asymmetrical damage zone around a laboratory mixed-mode rock fracture.We substantiate the presence of asymmetrical damage through qualitative analysis and demonstrate that measurement uncertainties cannot solely explain the observed asymmetry.The implications of this demonstration can be manifold.On a larger scale,it solidifies a mechanical model used for explaining the contribution of aseismic mechanisms to asymmetrical fault structures.On a laboratory scale,it exemplifies an alternative approach to understanding the observational difference between the source location and the in situ or post-mortem inspection on the rock fracture path.The mechanical model and the data analysis can be informative to the interpretations of other engineering practices as well,but may face different types of challenges.展开更多
An effective Dynamic Moire method was presented to determine the critical time of crack instable propagation in rock dynamic fracture. Two pieces of grating were installed near the notch of Short Rod specimen to form ...An effective Dynamic Moire method was presented to determine the critical time of crack instable propagation in rock dynamic fracture. Two pieces of grating were installed near the notch of Short Rod specimen to form the Moire fringes, then the COD versus time could be monitored from the movement of the Moire fringes, and finally the critical time could be determined from the velocity of COD. This method was also compared with another one.It could be concluded that the critical time determined by Dynamic Moire method corresponds with that of the Transmitted Wave method at the loading rates from 103 to 104 MPa·m(1/2)·S(-1).展开更多
This study presents a meso-criterion of dynamic fracture, on the basis of stress in integral form In such way the difficulty due to the singularity of stress distribution at the crack tip is overcome. A micro-paramete...This study presents a meso-criterion of dynamic fracture, on the basis of stress in integral form In such way the difficulty due to the singularity of stress distribution at the crack tip is overcome. A micro-parameter, the atom radius, is introduced into the criterion.Meanwhile a characteristic time concept is taken into account for describing the inertia effect of material. The criterion reveals The criterion reveals the effects of loading rate, defect and sample geometry,material constants including the micro-structure parameter.展开更多
The fracture behaviour and crack propagation features of coal under coupled static-dynamic loading conditions are important when evaluating the dynamic failure of coal.In this study,coupled static-dynamic loading test...The fracture behaviour and crack propagation features of coal under coupled static-dynamic loading conditions are important when evaluating the dynamic failure of coal.In this study,coupled static-dynamic loading tests are conducted on Brazilian disc(BD)coal specimens using a modified split Hopkinson pressure bar(SHPB).The effects of the static axial pre-stress and loading rate on the dynamic tensile strength and crack propagation characteristics of BD coal specimens are studied.The average dynamic indirect tensile strength of coal specimens increases first and then decreases with the static axial pre-stress increasing.When no static axial pre-stress is applied,or the static axial pre-stress is 30%of the static tensile strength,the dynamic indirect tensile strength of coal specimens shows an increase trend as the loading rate increases.When the static axial pre-stress is 60%of the static tensile strength,the dynamic indirect tensile strength shows a fluctuant trend as the loading rate increases.According to the crack propagation process of coal specimens recorded by high-speed camera,the impact velocity influences the mode of crack propagation,while the static axial pre-stress influences the direction of crack propagation.The failure of coal specimens is a coupled tensile-shear failure under high impact velocity.When there is no static axial pre-stress,tensile cracks occur in the vertical loading direction.When the static axial pre-stress is applied,the number of cracks perpendicular to the loading direction decreases,and more cracks occur in the parallel loading direction.展开更多
The characterization and testing methods of the dynamic fractureinitiation toughness of elas- tic-plastic materials under tensileimpact are studied. By using the self-designed bar-bar tensile impactappa- ratus, a nove...The characterization and testing methods of the dynamic fractureinitiation toughness of elas- tic-plastic materials under tensileimpact are studied. By using the self-designed bar-bar tensile impactappa- ratus, a novel test method for studying dynamicfracture-initiation ahs been proposed based on the one-di- mensionaltest principle. The curve of average load v. s. displacement (P-δ)is smooth until unstable crack propagation, and the kinetic energywhich does not contribute to the crack growth can be removed fromtotal work done by external-force to the specimen.展开更多
In this paper,the dynamic propagation problem of a mixed-mode crack was studied by means of the experimental method of caustics.The initial curve and caustic equations were derived un- der the mixed-mode dynamic condi...In this paper,the dynamic propagation problem of a mixed-mode crack was studied by means of the experimental method of caustics.The initial curve and caustic equations were derived un- der the mixed-mode dynamic condition.A multi-point measurement method for determining the dy- namic stress intensity factors,K_Ⅰ~d and K_Ⅱ~d,and the position of the crack tip was developed.Several other methods were adopted to check this method,and showed that it has a good precision.Finally, the dynamic propagating process of a mixed-mode crack in a three-point bending beam specimen was investigated with our method.展开更多
To investigate the influence of loading rate and high temperature on the dynamic fracture toughness of rock,dynamic fracture tests were carried out on notched semi-circular bend specimens under four temperature condit...To investigate the influence of loading rate and high temperature on the dynamic fracture toughness of rock,dynamic fracture tests were carried out on notched semi-circular bend specimens under four temperature conditions based on the split Hopkinson pressure bar system.Experimental and analytical methods were applied to investigating the effect of temperature gradient on the stress waves.A high-speed camera was used to check the fracture characteristics of the specimens.The results demonstrate that the temperature gradient on the bars will not significantly distort the shape of the stress wave.The dynamic force balance is achieved even when the specimens are at a temperature of 400°C.The dynamic fracture toughness linearly develops with the increase of loading rate within the temperature range of 25-400°C,and high temperature has a strengthening effect on the dynamic fracture toughness.展开更多
Cyclic freezing-thawing can lead to fracture development in coal,affecting its mechanical and consumer properties.To study crack formations in coal,an ultrasonic sounding method using shear polarized waves was propose...Cyclic freezing-thawing can lead to fracture development in coal,affecting its mechanical and consumer properties.To study crack formations in coal,an ultrasonic sounding method using shear polarized waves was proposed.Samples of three coal types(anthracite,lignite and hard coal)were tested.The research results show that,in contrast to the shear wave velocity,the shear wave amplitude is extremely sensitive to the formation of new cracks at the early stages of cyclic freezing-thawing.Tests also show an inverse correlation between coal compressive strength and its tendency to form cracks under temperature impacts;shear wave attenuation increases more sharply in high-rank coals after the first freezing cycle.Spectral analysis of the received signals also confirmed significant crack formation in anthracite after the first freeze-thaw cycle.The initial anisotropy was determined,and its decrease with an increase in the number of freeze-thaw cycles was shown.The data obtained forms an experimental basis for the development of new approaches to preserve coal consumer properties during storage and transportation under severe natural and climatic conditions.展开更多
Fractional differential constitutive relationships are introduced to depict the history of dynamic stress inten- sity factors （DSIFs） for a semi-infinite crack in infinite viscoelastic material subjected to anti-pla...Fractional differential constitutive relationships are introduced to depict the history of dynamic stress inten- sity factors （DSIFs） for a semi-infinite crack in infinite viscoelastic material subjected to anti-plane shear impact load. The basic equations which govern the anti-plane deformation behavior are converted to a fractional wave-like equation. By utilizing Laplace and Fourier integral transforms, the fractional wave-like equation is cast into an ordinary differential equation （ODE）. The unknown function in the solution of ODE is obtained by applying Fourier transform directly to the boundary conditions of fractional wave-like equation in Laplace domain instead of solving dual integral equations. Analytical solutions of DSIFs in Laplace domain are derived by Wiener-Hopf technique and the numerical solutions of DSIFs in time domain are obtained by Talbot algorithm. The effects of four parameters α, β, b1, b2 of the fractional dif- ferential constitutive model on DSIFs are discussed. The numerical results show that the present fractional differential constitutive model can well describe the behavior of DSIFs of anti-plane fracture in viscoelastic materials, and the model is also compatible with solutions of DSIFs of anti-plane fracture in elastic materials.展开更多
A novel method was proposed for the evaluation of Mode I dynamic fracture toughness （DFT） under plane stress and small scale yielding conditions for welded joints of stainless steel （SS）, 0Cr18Ni10Ti. In a hybrid ...A novel method was proposed for the evaluation of Mode I dynamic fracture toughness （DFT） under plane stress and small scale yielding conditions for welded joints of stainless steel （SS）, 0Cr18Ni10Ti. In a hybrid experimental-numerical approach, the experiments were carried out on the Hopkinson pressure bar apparatus, and three dimensional （3D） transient numerical simulations were performed by a finite element （FE） computer program. Macroscopical plastic deformation was observed at the loading and supporting points, on the specimens, after the test, which could cause a large error if omitted in the numerical simulation. Therefore, elustic-viscoplustic analysis was performed on the specimen by adopting the Johnson-Cook （J-C） model to describe the rate-dependent plastic flow behavior of the material. The material heterogeneity in the mismatched welded joints, induced by the difference in the base metal （BM） and the weld metal （WM） in yield stress, has also been taken into consideration by using the J-C models separately. Good accordance was obtained between the experimental and the computational results by the present approach. The relationship between plane stress DFT and loading rate was also obtained on the order of 108 MPa.m^1/2.s^-1.展开更多
Accurate 3-D fracture network model for rock mass in dam foundation is of vital importance for stability,grouting and seepage analysis of dam foundation.With the aim of reducing deviation between fracture network mode...Accurate 3-D fracture network model for rock mass in dam foundation is of vital importance for stability,grouting and seepage analysis of dam foundation.With the aim of reducing deviation between fracture network model and measured data,a 3-D fracture network dynamic modeling method based on error analysis was proposed.Firstly,errors of four fracture volume density estimation methods(proposed by ODA,KULATILAKE,MAULDON,and SONG)and that of four fracture size estimation methods(proposed by EINSTEIN,SONG and TONON)were respectively compared,and the optimal methods were determined.Additionally,error index representing the deviation between fracture network model and measured data was established with integrated use of fractal dimension and relative absolute error(RAE).On this basis,the downhill simplex method was used to build the dynamic modeling method,which takes the minimum of error index as objective function and dynamically adjusts the fracture density and size parameters to correct the error index.Finally,the 3-D fracture network model could be obtained which meets the requirements.The proposed method was applied for 3-D fractures simulation in Miao Wei hydropower project in China for feasibility verification and the error index reduced from 2.618 to 0.337.展开更多
An elusive phenomenon is observed in previous investigations on dynamic fracture that the dynamic fracture toughness （DFT） of high strength metals always increases with the loading rate on the order of TPa.m1/2.s-1....An elusive phenomenon is observed in previous investigations on dynamic fracture that the dynamic fracture toughness （DFT） of high strength metals always increases with the loading rate on the order of TPa.m1/2.s-1. For the purpose of verification, variation of DFT with the loading rate for two high strength steels commonly used in the aviation industry, 30CrMnSiA and 40Cr, is studied in this work. Results of the experiments are compared, which were conducted on the modified split Hopkinson pressure bar （SHPB） apparatus, with striker velocities ranging from 9.2 to 24.1 m/s and a constant value of 16.3 m/s for 30CrMnSiA and 40Cr, respectively. It is observed that for 30CrMnSiA, the crack tip loading rate increases with the increase of the striker velocity, while the fracture initiation time and the DFT simultaneously decrease. However, in the tests of 40Cr, there is also an increasing tendency of DFT, similar to other reports. Through an in-depth investigation on the relationship between the dynamic stress intensity factor （DSIF） and the loading rate, it is concluded that the generally increasing tendency in previous studies could be false, which is induced from a limited striker velocity domain and the errors existing in the experimental and numerical processes. To disclose the real dependency of DFT on the loading rate, experimentsneed to be performed in a comparatively large striker velocity range.展开更多
A novel approach is proposed in determining dy- namic fracture toughness （DFT） of high strength steel, using the split Hopkinson tension bar （SHTB） apparatus, com- bined with a hybrid experimental-numerical method...A novel approach is proposed in determining dy- namic fracture toughness （DFT） of high strength steel, using the split Hopkinson tension bar （SHTB） apparatus, com- bined with a hybrid experimental-numerical method. The center-cracked tension specimen is connected between the bars with a specially designed fixture device. The fracture initiation time is measured by the strain gage method, and dynamic stress intensity factors （DSIF） are obtained with the aid of 3D finite element analysis （FEA）. In this approach, the dimensions of the specimen are not restricted by the connec- tion strength or the stress-state equilibrium conditions, and hence plane strain state can be attained conveniently at the crack tip. Through comparison between the obtained results and those in open publication, it is concluded that the ex- perimental data are valid, and the method proposed here is reliable. The validity of the obtained DFT is checked with the ASTM criteria, and fracture surfaces are examined at the end of paper.展开更多
The prediction of dynamic crack propagation in brittle materials is still an important issue in many engineering fields. The remeshing technique based on scaled boundary finite element method(SBFEM) is extended to pre...The prediction of dynamic crack propagation in brittle materials is still an important issue in many engineering fields. The remeshing technique based on scaled boundary finite element method(SBFEM) is extended to predict the dynamic crack propagation in brittle materials. The structure is firstly divided into a number of superelements, only the boundaries of which need to be discretized with line elements. In the SBFEM formulation, the stiffness and mass matrices of the super-elements can be coupled seamlessly with standard finite elements, thus the advantages of versatility and flexibility of the FEM are well maintained. The transient response of the structure can be calculated directly in the time domain using a standard time-integration scheme. Then the dynamic stress intensity factor(DSIF) during crack propagation can be solved analytically due to the semi-analytical nature of SBFEM. Only the fine mesh discretization for the crack-tip super-element is needed to ensure the required accuracy for the determination of stress intensity factor(SIF). According to the predicted crack-tip position, a simple remeshing algorithm with the minimum mesh changes is suggested to simulate the dynamic crack propagation. Numerical examples indicate that the proposed method can be effectively used to deal with the dynamic crack propagation in a finite sized rectangular plate including a central crack. Comparison is made with the results available in the literature, which shows good agreement between each other.展开更多
To study the influence of construction interfaces on dynamic characteristics of roller compacted concrete dams(RCCDs),mechanical properties of construction interfaces are firstly analyzed. Then, the viscous-spring art...To study the influence of construction interfaces on dynamic characteristics of roller compacted concrete dams(RCCDs),mechanical properties of construction interfaces are firstly analyzed. Then, the viscous-spring artificial boundary(VSAB) is adopted to simulate the radiation damping of their infinite foundations, and based on the Marc software, a simplified seismic motion input method is presented by the equivalent nodal loads. Finally, based on the practical engineering of a RCC gravity dam, effects of radiation damping and construction interfaces on the dynamic characteristics of dams are investigated in detail. Analysis results show that dynamic response of the RCC gravity dam significantly reduces about 25% when the radiation damping of infinite foundation is considered. Hot interfaces and the normal cold interfaces have little influence on the dynamic response of the RCC gravity dam.However, nonlinear fracture along the cold interfaces at the dam heel will occur under the designed earthquake if the cold interfaces are combined poorly. Therefore, to avoid the fractures along the construction interfaces under the potential super earthquakes,combination quality of the RCC layers should be significantly ensured.展开更多
基金supported by the National Natural Science Foundation of China(Grant No.52208500)。
文摘The finite-depth concrete panels have been widely applied in the protective structures,and its impact resistance and dynamic fracture failures,especially the scabbing/perforation limits,under high velocity projectile impact,are mainly concerned by protective engineers,which are numerically studied based on an improved dynamic concrete model in this study.Firstly,based on the framework of the KCC(Karagozian&Case concrete)model,a dynamic concrete model is proposed which considers an independent tensile damage model and a continued transition between dynamic tensile and compressive properties.Secondly,the strength surface,equation of state and damage parameters of the proposed model are comprehensively calibrated by a triaxial compressive test with high confinement pressure,the rationality of which is further verified based on the single element tests,e.g.,uniaxial and triaxial compression as well as uniaxial,biaxial and triaxial tension.Thirdly,a series of projectile high velocity impact tests on thin and thick concrete panels are simulated,which indicates that the projectile residual velocity and dynamic fracture failures are reproduced satisfactorily,while the KCC model underestimates both the spalling and scabbing dimensions severely.Finally,based on the validated concrete model and finite element analyses approach,the validations of the existing five empirical formulae are evaluated,in terms of the depth of penetration(DOP)and scabbing/perforation limits of concrete panel.Both the Army corps of engineers(ACE)and modified National Defense Research Committee(NDRC)formulae are recommended in the design of the protective structure to avoid scabbing failure.
基金The authors thank the financial support from the National Natural Science Foundation of China(Grant.Nos.52039007 and 52225904)the Youth Science and Technology Innovation Research Team Fund of Sichuan Province(Grant.No.2020JDTD0001).
文摘In this study,a novel testing method is proposed to characterize the dynamic shear property and failure mechanism of rocks by introducing the short beam compression(SBC)specimen into the split Hopkinson pressure bar(SHPB)system.Firstly,the stress distribution of SBC specimen is comprehensively analyzed by finite element method(FEM),and the results show that the optimal notch separation ratio of SBC specimen is C/H?0.2 to achieve successful dynamic simple-shear tests.Then,dynamic shear tests are conducted on sandstone using the SBC-SHPB method.Via careful pulse shaping technique,the dynamic force balance is guaranteed for SBC specimens,and the testing results show that the dynamic shear strength of sandstone is significantly rate-dependent.Combining the results of dynamic compression and tension tests,the failure envelopes of sandstone under different loading rates are obtained in the principle stress plane.It is found that the failure envelope of sandstone constantly expands outwards with increasing loading rate.Moreover,the energy partition of SBC specimen is quantified by virtue of high-speed digital image correlation(DIC)technique.The results show that the kinetic energy portion is non-negligible,and the shear fracture energy increases with increasing loading rate.In addition,the microscopic shear cracking mechanism of SBC specimen is analyzed by the thin section observation:the intra-granular(TG)fracture of minerals dominates the dynamic shear failure of sandstone,and the portion of TG fracture increases with increasing loading rate.This study provides a convenient and reliable method to investigate the dynamic shear property and failure mechanism of rocks.
基金Project (51001014) supported by the Young Scientists Fund of the National Natural Science Foundation of China
文摘The dynamic fracture behaviors of Ti-6Al-4V alloy at high strain rate loading were investigated systemically through Taylor impact test, over the range of impact velocities from 145 m/s to 306 m/s. The critical impact velocity of fracture ranges from 217 m/s to 236 m/s. Smooth surfaces and ductile dimple areas were observed on the fracture surfaces. As the impact velocity reached 260 m/s, the serious melting regions were also observed on the fracture surfaces. Self-organization of cracks emerges when the impact velocity reaches 260 m/s, while some special cracks whose ＂tips＂ are not sharp but arc and smooth, and without any evidence of deformation or adiabatic shear band were also observed on the impact end surfaces. Examination of the sections of these special cracks reveals that the cracks expand along the two maximum shear stress directions respectively, and finally intersect as a tridimensional ＂stagger ridge＂ structure.
基金The Ph.D.Programs Foundation of Ministry of Education of China(No.20120023120020)the National Natural Science Foundation of China(No.51404273)
文摘The reflected optical caustics method is applied to study dynamic fracture problems in hardened cement paste. First both the unreinforced cement paste and the glass fibres reinforced cement paste specimens were fabricated and the reflective coating on the surface of the specimen was prepared. Secondly the crack path and the shadow spot patterns during the crack propagation process for the two specimens were recorded by using a multi-spark high speed camera.Thirdly some dynamic parameters of two cement paste specimens including crack onset time the dynamic stress intensity factor and crack growth velocity were determined and analyzed comparatively.This indicates that the glass fibres can improve the fracture resistance and delay fracture time.These results will play an important role in evaluating the dynamic fracture properties of cement paste.
基金Russian Science Foundation[grant number 22-71-10019].
文摘The paper considers application of artificial neural networks(ANNs)for fast numerical evaluation of a residual impactor velocity for a family of perforated PMMA(Polymethylmethacrylate)targets.The ANN models were trained using sets of numerical results on impact of PMMA plates obtained via dynamic FEM coupled with incubation time fracture criterion.The developed approach makes it possible to evaluate the impact strength of a particular target configuration without complicated FEM calculations which require considerable computational resources.Moreover,it is shown that the ANN models are able to predict results for the configurations which cannot be processed using the developed FEM routine due to numerical instabilities and errors:the trained neural network uses information from successful computations to obtain results for the problematic cases.A simple static problem of a perforated plate deformation is discussed prior to the impact problem and preferable ANN architectures are presented for both problems.Some insight into the perforation pattern optimization using a genetic algorithm coupled with the ANN is also made and optimized perforation patterns which theoretically enhance the target impact strength are constructed.
文摘Rock fracture mechanics and accurate characterization of rock fracture are crucial for understanding a variety of phenomena interested in geological engineering and geoscience.These phenomena range from very large-scale asymmetrical fault structures to the scale of engineering projects and laboratory-scale rock fracture tests.Comprehensive study can involve mechanical modeling,site or post-mortem investigations,and inspection on the point cloud of the source locations in the form of earthquake,microseismicity,or acoustic emission.This study presents a comprehensive data analysis on characterizing the forming of the asymmetrical damage zone around a laboratory mixed-mode rock fracture.We substantiate the presence of asymmetrical damage through qualitative analysis and demonstrate that measurement uncertainties cannot solely explain the observed asymmetry.The implications of this demonstration can be manifold.On a larger scale,it solidifies a mechanical model used for explaining the contribution of aseismic mechanisms to asymmetrical fault structures.On a laboratory scale,it exemplifies an alternative approach to understanding the observational difference between the source location and the in situ or post-mortem inspection on the rock fracture path.The mechanical model and the data analysis can be informative to the interpretations of other engineering practices as well,but may face different types of challenges.
文摘An effective Dynamic Moire method was presented to determine the critical time of crack instable propagation in rock dynamic fracture. Two pieces of grating were installed near the notch of Short Rod specimen to form the Moire fringes, then the COD versus time could be monitored from the movement of the Moire fringes, and finally the critical time could be determined from the velocity of COD. This method was also compared with another one.It could be concluded that the critical time determined by Dynamic Moire method corresponds with that of the Transmitted Wave method at the loading rates from 103 to 104 MPa·m(1/2)·S(-1).
文摘This study presents a meso-criterion of dynamic fracture, on the basis of stress in integral form In such way the difficulty due to the singularity of stress distribution at the crack tip is overcome. A micro-parameter, the atom radius, is introduced into the criterion.Meanwhile a characteristic time concept is taken into account for describing the inertia effect of material. The criterion reveals The criterion reveals the effects of loading rate, defect and sample geometry,material constants including the micro-structure parameter.
基金supported by the National Natural Science Foundation of China(No.51804309)the Yue Qi Young Scholar Project(2019QN02)+5 种基金Distinguished Scholar Project(2017JCB02)from China University of Mining and Technology-Beijing,Open Fund of State Key Laboratory of Water Resource Protection and Utilization in Coal Mining(Grant No.SHJT-17-42.10)National Natural Science Foundation of China(No.U1910206)the fund of Beijing Outstanding Young Scientist Program(BJJWZYJH01201911413037)the State Key Laboratory of Coal Resources and Safe Mining(Nos.SKLCRSM16KFB07,SKLCRSM16DCB01 and SKLCRSM17DC11)Young Elite Scientists Sponsorship Program by CAST(2017QNRC001)the key project of Key Laboratory of Coal Mine Safety and High Efficiency Mining Co-established by the Province and the Ministry(Anhui University of Science and Technology)(No.JYBSYS2018201).
文摘The fracture behaviour and crack propagation features of coal under coupled static-dynamic loading conditions are important when evaluating the dynamic failure of coal.In this study,coupled static-dynamic loading tests are conducted on Brazilian disc(BD)coal specimens using a modified split Hopkinson pressure bar(SHPB).The effects of the static axial pre-stress and loading rate on the dynamic tensile strength and crack propagation characteristics of BD coal specimens are studied.The average dynamic indirect tensile strength of coal specimens increases first and then decreases with the static axial pre-stress increasing.When no static axial pre-stress is applied,or the static axial pre-stress is 30%of the static tensile strength,the dynamic indirect tensile strength of coal specimens shows an increase trend as the loading rate increases.When the static axial pre-stress is 60%of the static tensile strength,the dynamic indirect tensile strength shows a fluctuant trend as the loading rate increases.According to the crack propagation process of coal specimens recorded by high-speed camera,the impact velocity influences the mode of crack propagation,while the static axial pre-stress influences the direction of crack propagation.The failure of coal specimens is a coupled tensile-shear failure under high impact velocity.When there is no static axial pre-stress,tensile cracks occur in the vertical loading direction.When the static axial pre-stress is applied,the number of cracks perpendicular to the loading direction decreases,and more cracks occur in the parallel loading direction.
文摘The characterization and testing methods of the dynamic fractureinitiation toughness of elas- tic-plastic materials under tensileimpact are studied. By using the self-designed bar-bar tensile impactappa- ratus, a novel test method for studying dynamicfracture-initiation ahs been proposed based on the one-di- mensionaltest principle. The curve of average load v. s. displacement (P-δ)is smooth until unstable crack propagation, and the kinetic energywhich does not contribute to the crack growth can be removed fromtotal work done by external-force to the specimen.
文摘In this paper,the dynamic propagation problem of a mixed-mode crack was studied by means of the experimental method of caustics.The initial curve and caustic equations were derived un- der the mixed-mode dynamic condition.A multi-point measurement method for determining the dy- namic stress intensity factors,K_Ⅰ~d and K_Ⅱ~d,and the position of the crack tip was developed.Several other methods were adopted to check this method,and showed that it has a good precision.Finally, the dynamic propagating process of a mixed-mode crack in a three-point bending beam specimen was investigated with our method.
基金support from the National Natural Science Foundation of China(No.41972283)。
文摘To investigate the influence of loading rate and high temperature on the dynamic fracture toughness of rock,dynamic fracture tests were carried out on notched semi-circular bend specimens under four temperature conditions based on the split Hopkinson pressure bar system.Experimental and analytical methods were applied to investigating the effect of temperature gradient on the stress waves.A high-speed camera was used to check the fracture characteristics of the specimens.The results demonstrate that the temperature gradient on the bars will not significantly distort the shape of the stress wave.The dynamic force balance is achieved even when the specimens are at a temperature of 400°C.The dynamic fracture toughness linearly develops with the increase of loading rate within the temperature range of 25-400°C,and high temperature has a strengthening effect on the dynamic fracture toughness.
基金Russian Foundation for Basic Research,grant number 18-05-70002.
文摘Cyclic freezing-thawing can lead to fracture development in coal,affecting its mechanical and consumer properties.To study crack formations in coal,an ultrasonic sounding method using shear polarized waves was proposed.Samples of three coal types(anthracite,lignite and hard coal)were tested.The research results show that,in contrast to the shear wave velocity,the shear wave amplitude is extremely sensitive to the formation of new cracks at the early stages of cyclic freezing-thawing.Tests also show an inverse correlation between coal compressive strength and its tendency to form cracks under temperature impacts;shear wave attenuation increases more sharply in high-rank coals after the first freezing cycle.Spectral analysis of the received signals also confirmed significant crack formation in anthracite after the first freeze-thaw cycle.The initial anisotropy was determined,and its decrease with an increase in the number of freeze-thaw cycles was shown.The data obtained forms an experimental basis for the development of new approaches to preserve coal consumer properties during storage and transportation under severe natural and climatic conditions.
基金supported by the National Natural Science Foundation of China(11072060)the Priority Academic Program Development of Jiangsu Higher Education Institutions
文摘Fractional differential constitutive relationships are introduced to depict the history of dynamic stress inten- sity factors （DSIFs） for a semi-infinite crack in infinite viscoelastic material subjected to anti-plane shear impact load. The basic equations which govern the anti-plane deformation behavior are converted to a fractional wave-like equation. By utilizing Laplace and Fourier integral transforms, the fractional wave-like equation is cast into an ordinary differential equation （ODE）. The unknown function in the solution of ODE is obtained by applying Fourier transform directly to the boundary conditions of fractional wave-like equation in Laplace domain instead of solving dual integral equations. Analytical solutions of DSIFs in Laplace domain are derived by Wiener-Hopf technique and the numerical solutions of DSIFs in time domain are obtained by Talbot algorithm. The effects of four parameters α, β, b1, b2 of the fractional dif- ferential constitutive model on DSIFs are discussed. The numerical results show that the present fractional differential constitutive model can well describe the behavior of DSIFs of anti-plane fracture in viscoelastic materials, and the model is also compatible with solutions of DSIFs of anti-plane fracture in elastic materials.
基金111 project(No.B07050)the National Natural Science Foundation of China(No.90405016).
文摘A novel method was proposed for the evaluation of Mode I dynamic fracture toughness （DFT） under plane stress and small scale yielding conditions for welded joints of stainless steel （SS）, 0Cr18Ni10Ti. In a hybrid experimental-numerical approach, the experiments were carried out on the Hopkinson pressure bar apparatus, and three dimensional （3D） transient numerical simulations were performed by a finite element （FE） computer program. Macroscopical plastic deformation was observed at the loading and supporting points, on the specimens, after the test, which could cause a large error if omitted in the numerical simulation. Therefore, elustic-viscoplustic analysis was performed on the specimen by adopting the Johnson-Cook （J-C） model to describe the rate-dependent plastic flow behavior of the material. The material heterogeneity in the mismatched welded joints, induced by the difference in the base metal （BM） and the weld metal （WM） in yield stress, has also been taken into consideration by using the J-C models separately. Good accordance was obtained between the experimental and the computational results by the present approach. The relationship between plane stress DFT and loading rate was also obtained on the order of 108 MPa.m^1/2.s^-1.
基金Project(51321065)supported by the Innovative Research Groups of the National Natural Science Foundation of ChinaProject(2013CB035904)supported by the National Basic Research Program of China(973 Program)Project(51439005)supported by the National Natural Science Foundation of China
文摘Accurate 3-D fracture network model for rock mass in dam foundation is of vital importance for stability,grouting and seepage analysis of dam foundation.With the aim of reducing deviation between fracture network model and measured data,a 3-D fracture network dynamic modeling method based on error analysis was proposed.Firstly,errors of four fracture volume density estimation methods(proposed by ODA,KULATILAKE,MAULDON,and SONG)and that of four fracture size estimation methods(proposed by EINSTEIN,SONG and TONON)were respectively compared,and the optimal methods were determined.Additionally,error index representing the deviation between fracture network model and measured data was established with integrated use of fractal dimension and relative absolute error(RAE).On this basis,the downhill simplex method was used to build the dynamic modeling method,which takes the minimum of error index as objective function and dynamically adjusts the fracture density and size parameters to correct the error index.Finally,the 3-D fracture network model could be obtained which meets the requirements.The proposed method was applied for 3-D fractures simulation in Miao Wei hydropower project in China for feasibility verification and the error index reduced from 2.618 to 0.337.
基金supported by the 111 Project (B07050)the National Natural Science Foundation of China (10932008)
文摘An elusive phenomenon is observed in previous investigations on dynamic fracture that the dynamic fracture toughness （DFT） of high strength metals always increases with the loading rate on the order of TPa.m1/2.s-1. For the purpose of verification, variation of DFT with the loading rate for two high strength steels commonly used in the aviation industry, 30CrMnSiA and 40Cr, is studied in this work. Results of the experiments are compared, which were conducted on the modified split Hopkinson pressure bar （SHPB） apparatus, with striker velocities ranging from 9.2 to 24.1 m/s and a constant value of 16.3 m/s for 30CrMnSiA and 40Cr, respectively. It is observed that for 30CrMnSiA, the crack tip loading rate increases with the increase of the striker velocity, while the fracture initiation time and the DFT simultaneously decrease. However, in the tests of 40Cr, there is also an increasing tendency of DFT, similar to other reports. Through an in-depth investigation on the relationship between the dynamic stress intensity factor （DSIF） and the loading rate, it is concluded that the generally increasing tendency in previous studies could be false, which is induced from a limited striker velocity domain and the errors existing in the experimental and numerical processes. To disclose the real dependency of DFT on the loading rate, experimentsneed to be performed in a comparatively large striker velocity range.
基金supported by the 111 Project (B07050)the National Natural Science Foundation of China (10932008)
文摘A novel approach is proposed in determining dy- namic fracture toughness （DFT） of high strength steel, using the split Hopkinson tension bar （SHTB） apparatus, com- bined with a hybrid experimental-numerical method. The center-cracked tension specimen is connected between the bars with a specially designed fixture device. The fracture initiation time is measured by the strain gage method, and dynamic stress intensity factors （DSIF） are obtained with the aid of 3D finite element analysis （FEA）. In this approach, the dimensions of the specimen are not restricted by the connec- tion strength or the stress-state equilibrium conditions, and hence plane strain state can be attained conveniently at the crack tip. Through comparison between the obtained results and those in open publication, it is concluded that the ex- perimental data are valid, and the method proposed here is reliable. The validity of the obtained DFT is checked with the ASTM criteria, and fracture surfaces are examined at the end of paper.
基金Supported by the Key Program of National Natural Science Foundation of China(No.51138001)the Science Fund for Creative Research Groups of National Natural Science Foundation of China(No.51121005)+2 种基金the Fundamental Research Funds for the Central Universities(DUT13LK16)the Young Scientists Fund of National Natural Science Foundation of China(No.51109134)China Postdoctoral Science Foundation(No.2011M500814)
文摘The prediction of dynamic crack propagation in brittle materials is still an important issue in many engineering fields. The remeshing technique based on scaled boundary finite element method(SBFEM) is extended to predict the dynamic crack propagation in brittle materials. The structure is firstly divided into a number of superelements, only the boundaries of which need to be discretized with line elements. In the SBFEM formulation, the stiffness and mass matrices of the super-elements can be coupled seamlessly with standard finite elements, thus the advantages of versatility and flexibility of the FEM are well maintained. The transient response of the structure can be calculated directly in the time domain using a standard time-integration scheme. Then the dynamic stress intensity factor(DSIF) during crack propagation can be solved analytically due to the semi-analytical nature of SBFEM. Only the fine mesh discretization for the crack-tip super-element is needed to ensure the required accuracy for the determination of stress intensity factor(SIF). According to the predicted crack-tip position, a simple remeshing algorithm with the minimum mesh changes is suggested to simulate the dynamic crack propagation. Numerical examples indicate that the proposed method can be effectively used to deal with the dynamic crack propagation in a finite sized rectangular plate including a central crack. Comparison is made with the results available in the literature, which shows good agreement between each other.
基金Projects(20120094110005,20120094130003)supported by the Research Fund for the Doctoral Program of Higher Education of ChinaProjects(51379068,51139001,51279052,51209077,51179066)supported by the National Natural Science Foundation of China+1 种基金Project(NCET-11-0628)supported by the Program for New Century Excellent Talents in University,ChinaProjects(201201038,201101013)supported by the Public Welfare Industry Research Special Fund Project of Ministry of Water Resources of China
文摘To study the influence of construction interfaces on dynamic characteristics of roller compacted concrete dams(RCCDs),mechanical properties of construction interfaces are firstly analyzed. Then, the viscous-spring artificial boundary(VSAB) is adopted to simulate the radiation damping of their infinite foundations, and based on the Marc software, a simplified seismic motion input method is presented by the equivalent nodal loads. Finally, based on the practical engineering of a RCC gravity dam, effects of radiation damping and construction interfaces on the dynamic characteristics of dams are investigated in detail. Analysis results show that dynamic response of the RCC gravity dam significantly reduces about 25% when the radiation damping of infinite foundation is considered. Hot interfaces and the normal cold interfaces have little influence on the dynamic response of the RCC gravity dam.However, nonlinear fracture along the cold interfaces at the dam heel will occur under the designed earthquake if the cold interfaces are combined poorly. Therefore, to avoid the fractures along the construction interfaces under the potential super earthquakes,combination quality of the RCC layers should be significantly ensured.