Oxygen ions(O;)were implanted into fused silica at a fixed fluence of 1×10^(17) ions/cm^(2) with different ion energies ranging from 10 ke V to 60 ke V.The surface roughness,optical properties,mechanical properti...Oxygen ions(O;)were implanted into fused silica at a fixed fluence of 1×10^(17) ions/cm^(2) with different ion energies ranging from 10 ke V to 60 ke V.The surface roughness,optical properties,mechanical properties and laser damage performance of fused silica were investigated to understand the effect of oxygen ion implantation on laser damage resistance of fused silica.The ion implantation accompanied with sputtering effect can passivate the sub-/surface defects to reduce the surface roughness and improve the surface quality slightly.The implanted oxygen ions can combine with the structural defects(ODCs and E′centers)to reduce the defect densities and compensate the loss of oxygen in fused silica surface under laser irradiation.Furthermore,oxygen ion implantation can reduce the Si-O-Si bond angle and densify the surface structure,thus introducing compressive stress in the surface to strengthen the surface of fused silica.Therefore,the laser induced damage threshold of fused silica increases and the damage growth coefficient decreases when ion energy up to30 ke V.However,at higher ion energy,the sputtering effect is weakened and implantation becomes dominant,which leads to the surface roughness increase slightly.In addition,excessive energy aggravates the breaking of Si-O bonds.At the same time,the density of structural defects increases and the compressive stress decreases.These will degrade the laser laser-damage resistance of fused silica.The results indicate that oxygen ion implantation with appropriate ion energy is helpful to improve the damage resistance capability of fused silica components.展开更多
<div style="text-align:justify;"> The effects of the main parameters of argon flux, oxygen flux and beam voltage on the surface morphology, transmittance spectrum and laser damage of the HfO<sub>...<div style="text-align:justify;"> The effects of the main parameters of argon flux, oxygen flux and beam voltage on the surface morphology, transmittance spectrum and laser damage of the HfO<sub>2</sub> single layers prepared by ion beam sputtering are studied. The HfO<sub>2</sub> amorphous single layers have porous surface morphologies. Different processes will cause differences in coatings absorption and surface morphology, which in turn will cause changes in the spectral transmittance curve. The ion beam sputtering HfO<sub>2</sub> single layers have high content of argon (4.5% - 8%). The laser damage of HfO<sub>2</sub> single layers is related to argon inclusions and non-stoichiometric defects. The changes of argon flux and beam voltage have a greater impact on argon content and O/Hf ratio. When the argon content in the coatings is lower and the O/Hf ratio is higher, the laser damage thresholds of the HfO<sub>2</sub> single layers are higher. </div>展开更多
The laser-induced damage threshold(LIDT) of optical coating is a limited factor for development of a high peak power laser. The automatic damage testing facility was built to determine the LIDT of optics at 1 064 nm a...The laser-induced damage threshold(LIDT) of optical coating is a limited factor for development of a high peak power laser. The automatic damage testing facility was built to determine the LIDT of optics at 1 064 nm and 355 nm.. The cleanning and processing procedure of the substrate and coating technique were improved, and the damage resistance of high-reflective coating at 1 064 nm was increased.展开更多
Polished fused silica samples were etched for different durations by using hydrofluoric(HF) acid solution with HF concentrations in an ultrasonic field. Surface and subsurface polishing residues and molecular structur...Polished fused silica samples were etched for different durations by using hydrofluoric(HF) acid solution with HF concentrations in an ultrasonic field. Surface and subsurface polishing residues and molecular structure parameters before and after the etching process were characterized by using a fluorescence microscope and infrared(IR) spectrometer, respectively. The laser induced damage thresholds(LIDTs) of the samples were measured by using pulsed nanosecond laser with wavelength of 355 nm. The results showed that surface and subsurface polishing residues can be effectively reduced by the acid etching process, and the LIDTs of fused silica are significantly improved. The etching effects increased with the increase of the HF concentration from 5 wt.% to 40 wt.%. The amount of polishing residues decreased with the increase of the etching duration and then kept stable. Simultaneously, with the increase of the etching time, the mechanical strength and molecular structure were improved.展开更多
The low laser induced damage threshold of the KH2PO4 crystal seriously restricts the output power of inertial confinement fusion.The micro-waviness on the KH2PO4 surface processed by single point diamond turning has a...The low laser induced damage threshold of the KH2PO4 crystal seriously restricts the output power of inertial confinement fusion.The micro-waviness on the KH2PO4 surface processed by single point diamond turning has a significant influence on the damage threshold.In this paper,the influence of micro-waviness on the damage threshold of the KH2PO4 crystal and the chief sources introducing the micro-waviness are analysed based on the combination of the Fourier modal theory and the power spectrum density method.Research results indicate that among the sub-wavinesses with different characteristic spatial frequencies there exists the most dangerous frequency which greatly reduces the damage threshold,although it may not occupy the largest proportion in the original surface.The experimental damage threshold is basically consistent with the theoretical calculation.For the processing parameters used,the leading frequency of micro-waviness which causes the damage threshold to decrease is between 350-1 μm-1 and 30-1 μm-1,especially between 90-1 μm-1 and 200-1 μm-1.Based on the classification study of the time frequencies of microwaviness,we find that the axial vibration of the spindle is the chief source introducing the micro-waviness,nearly all the leading frequencies are related to the practical spindle frequency(about 6.68 Hz,400 r/min) and a special middle frequency(between 1.029 Hz and 1.143 Hz).展开更多
Ta2O5 films are prepared by e-beam evaporation with varied deposition temperatures,annealing temperatures,and annealing times.The effects of temperature on the optical properties,chemical composition,structure,and las...Ta2O5 films are prepared by e-beam evaporation with varied deposition temperatures,annealing temperatures,and annealing times.The effects of temperature on the optical properties,chemical composition,structure,and laserinduced damage threshold(LIDT) are systematically investigated.The results show that the increase of deposition temperature decreases the film transmittance slightly,yet annealing below 923 K is beneficial for the transmittance.The XRD analysis reveals that the film is in the amorphous phase when annealed below 873 K and in thehexagonal phase when annealed at 1073 K.While an interesting near-crystalline phase is found when annealed at 923 K.The LIDT increases with the deposition temperature increasing,whereas it increases firstly and then decreases as the annealing temperature increases.In addition,the increase of the annealing time from 4 h to 12 h is favourable to improving the LIDT,which is mainly due to the improvement of the O/Ta ratio.The highest LIDT film is obtained when annealed at 923 K,owing to the lowest density of defect.展开更多
The laser damage resistances of four crystals(CaF_(2),MgF_(2),Al_(2)O_(3),and SiO_(2))and fused silica(JGS1)irradiated at 355nm(8 ns,300-on-1)are reported.The laser-induced damage threshold is measured using a tripled...The laser damage resistances of four crystals(CaF_(2),MgF_(2),Al_(2)O_(3),and SiO_(2))and fused silica(JGS1)irradiated at 355nm(8 ns,300-on-1)are reported.The laser-induced damage threshold is measured using a tripled Nd:YAG laser system.The results obtained from the pure crystals are in accordance with their specific optical,mechanical,and thermal properties.An empirical law based on the Franz–Keldysh effect can interpret the experimental results.展开更多
A non-evaporative technique is used to mitigate damage sites with lateral sizes in a range from 50 μm to 400 μm and depths smaller than 100 μm.The influence of the pulse frequency of a CO 2 laser on the mitigation ...A non-evaporative technique is used to mitigate damage sites with lateral sizes in a range from 50 μm to 400 μm and depths smaller than 100 μm.The influence of the pulse frequency of a CO 2 laser on the mitigation effect is studied.It is found that a more symmetrical and smooth mitigation crater can be obtained by increasing the laser pulse frequency form 0.1 to 20 kHz.Furthermore,the sizes of laser-affected and distorted zones decrease with the increase of the laser pulse frequency,leading to less degradation of the wave-front quality of the conditioned sample.The energy density of the CO 2 laser beam is introduced for selecting the mitigation parameters.The damage sites can be successfully mitigated by increasing the energy density in a ramped way.Finally,the laser-induced damage threshold(LIDT) of the mitigated site is tested using 355 nm laser beam with a small spot(0.23 mm 2) and a large spot(3.14 mm 2),separately.It is shown that the non-evaporative mitigation technique is a successful method to stop damage re-initiation since the average LIDTs of mitigated sites tested with small or large laser spots are higher than that of pristine material.展开更多
A numerical model based on measured fictive temperature distributions is explored to evaluate the residual stress fields of CO_(2)laser-annealed mitigated fused silica damage sites.The proposed model extracts the resi...A numerical model based on measured fictive temperature distributions is explored to evaluate the residual stress fields of CO_(2)laser-annealed mitigated fused silica damage sites.The proposed model extracts the residual strain from the differences in thermoelastic contraction of fused silica with different fictive temperatures from the initial frozen-in temperatures to ambient temperature.The residual stress fields of mitigated damage sites for the CO_(2)laser-annealed case are obtained by a finite element analysis of equilibrium equations and constitutive equations.The simulated results indicate that the proposed model can accurately evaluate the residual stress fields of laser-annealed mitigated damage sites with a complex thermal history.The calculated maximum hoop stress is in good agreement with the reported experimental result.The estimated optical retardance profiles from the calculated radial and hoop stress fields are consistent with the photoelastic measurements.These results provide sufficient evidence to demonstrate the suitability of the proposed model for describing the residual stresses of mitigated fused silica damage sites after CO_(2)laser annealing.展开更多
Laser anti-drone technology is entering the sequence of actual combat,and it is necessary to consider the vulnerability of typical functional parts of UAVs.Since the concept of"vulnerability"was proposed,a v...Laser anti-drone technology is entering the sequence of actual combat,and it is necessary to consider the vulnerability of typical functional parts of UAVs.Since the concept of"vulnerability"was proposed,a variety of analysis programs for battlefield targets to traditional weapons have been developed,but a comprehensive assessment methodology for targets'vulnerability to laser is still missing.Based on the shotline method,this paper proposes a method that equates laser beam to shotline array,an efficient vulnerability analysis program of target to laser is established by this method,and the program includes the circuit board and the wire into the vulnerability analysis category,which improves the precision of the vulnerability analysis.Taking the UAV engine part as the target of vulnerability analysis,combine with the"life-death unit method"to calculate the laser penetration rate of various materials of the UAV,and the influence of laser weapon system parameters and striking orientation on the killing probability is quantified after introducing the penetration rate into the vulnerability analysis program.The quantitative analysis method proposed in this paper has certain general expansibility,which can provide a fresh idea for the vulnerability analysis of other targets to laser.展开更多
The laser-induced damage threshold(LIDT)of plate laser beam splitter(PLBS)coatings is closely related to the subsurface absorption defects of the substrate.Herein,a two-step deposition temperature method is proposed t...The laser-induced damage threshold(LIDT)of plate laser beam splitter(PLBS)coatings is closely related to the subsurface absorption defects of the substrate.Herein,a two-step deposition temperature method is proposed to understand the effect of substrate subsurface impurity defects on the LIDT of PLBS coatings.Firstly,BK7 substrates are heat-treated at three different temperatures.The surface morphology and subsurface impurity defect distribution of the substrate before and after the heat treatment are compared.Then,a PLBS coating consisting of alternating HfO2–Al2O3 mixture and SiO2 layers is designed to achieve a beam-splitting ratio(transmittance to reflectance,s-polarized light)of approximately 50:50 at 1053 nm and an angle of incidence of 45◦,and it is prepared under four different deposition processes.The experimental and simulation results show that the subsurface impurity defects of the substrate migrate to the surface and accumulate on the surface during the heat treatment,and become absorption defect sources or nodule defect seeds in the coating,reducing the LIDT of the coating.The higher the heat treatment temperature,the more evident the migration and accumulation of impurity defects.A lower deposition temperature(at which the coating can be fully oxidized)helps to improve the LIDT of the PLBS coating.When the deposition temperature is 140◦C,the LIDT(s-polarized light,wavelength:1064 nm,pulse width:9 ns,incident angle:45◦)of the PLBS coating is 26.2 J/cm2,which is approximately 6.7 times that of the PLBS coating deposited at 200◦C.We believe that the investigation into the laser damage mechanism of PLBS coatings will help to improve the LIDT of coatings with partial or high transmittance at laser wavelengths.展开更多
The process of thermal stress damage during 1080 nm laser ablation of single-crystal germanium was recorded in real time using a high-speed charge-coupled device.A three-dimensional finite element numerical model base...The process of thermal stress damage during 1080 nm laser ablation of single-crystal germanium was recorded in real time using a high-speed charge-coupled device.A three-dimensional finite element numerical model based on Fourier's heat conduction equation,Hooke's law and the Alexander–Hasson equation was developed to analyze the thermal stress damage mechanism involved.The damage morphology of the ablated samples was observed using an optical microscope.The results show that the cooling process has an important influence on fracture in the laser-irradiated region of single-crystal germanium.Fracture is the result of a combination of thermal stress and reduction in local yield strength.展开更多
In this study,a phase-field scheme that rigorously obeys conservation laws and irreversible thermodynamics is developed for modeling stress-corrosion coupled damage(SCCD).The coupling constitutive relationships of the...In this study,a phase-field scheme that rigorously obeys conservation laws and irreversible thermodynamics is developed for modeling stress-corrosion coupled damage(SCCD).The coupling constitutive relationships of the deformation,phase-field damage,mass transfer,and electrostatic field are derived from the entropy inequality.The SCCD localization induced by secondary phases in Mg is numerically simulated using the implicit iterative algorithm of the self-defined finite elements.The quantitative evaluation of the SCCD of a C-ring is in good agreement with the experimental results.To capture the damage localization,a micro-galvanic corrosion domain is defined,and the buffering effect on charge migration is explored.Three cases are investigated to reveal the effect of localization on corrosion acceleration and provide guidance for the design for resistance to SCCD at the crystal scale.展开更多
In a further aging society,excellent eyesight is an integral part of overall well-being and quality of life.Preserving good vision is crucial to maintaining mobility,independence,and mental health.There can be several...In a further aging society,excellent eyesight is an integral part of overall well-being and quality of life.Preserving good vision is crucial to maintaining mobility,independence,and mental health.There can be several reasons for visual impairment in elderly people,these include age-related macular degeneration,the leading cause of vision loss among older adults,cataract,glaucoma,diabetic retinopathy,retinal detachment,and others.展开更多
Stroke is a significant leading cause of death and disability in the United States(Tsao et al.,2022).Approximately 87% of strokes fall into the ischemic category,mainly caused by arterial blockage(Jayaraj et al.,2019)...Stroke is a significant leading cause of death and disability in the United States(Tsao et al.,2022).Approximately 87% of strokes fall into the ischemic category,mainly caused by arterial blockage(Jayaraj et al.,2019).Although the only FDA-approved effective medication is tissue plasminogen activator(tPA),it should be administrated within 4.5 hours of ischemic stroke.Furthermore,tPA has been an integral part of managing acute ischemic stro ke.展开更多
The tensile-shear interactive damage(TSID)model is a novel and powerful constitutive model for rock-like materials.This study proposes a methodology to calibrate the TSID model parameters to simulate sandstone.The bas...The tensile-shear interactive damage(TSID)model is a novel and powerful constitutive model for rock-like materials.This study proposes a methodology to calibrate the TSID model parameters to simulate sandstone.The basic parameters of sandstone are determined through a series of static and dynamic tests,including uniaxial compression,Brazilian disc,triaxial compression under varying confining pressures,hydrostatic compression,and dynamic compression and tensile tests with a split Hopkinson pressure bar.Based on the sandstone test results from this study and previous research,a step-by-step procedure for parameter calibration is outlined,which accounts for the categories of the strength surface,equation of state(EOS),strain rate effect,and damage.The calibrated parameters are verified through numerical tests that correspond to the experimental loading conditions.Consistency between numerical results and experimental data indicates the precision and reliability of the calibrated parameters.The methodology presented in this study is scientifically sound,straightforward,and essential for improving the TSID model.Furthermore,it has the potential to contribute to other rock constitutive models,particularly new user-defined models.展开更多
We report a high-average-power acousto-optic(AO)Q-switched intracavity frequency-doubled red laser based on a high-efficiency light-emitting-diode(LED)pumped two-rod Nd,Ce:YAG laser module.Under quasi-continuous wave ...We report a high-average-power acousto-optic(AO)Q-switched intracavity frequency-doubled red laser based on a high-efficiency light-emitting-diode(LED)pumped two-rod Nd,Ce:YAG laser module.Under quasi-continuous wave operation conditions,a maximum output power of 1319.08 nm wavelength was achieved at 11.26 W at a repetition rate of 100 Hz.展开更多
In the past few years,many groups have focused on the research and development of GaN-based ultraviolet laser diodes(UV LDs).Great progresses have been achieved even though many challenges exist.In this article,we ana...In the past few years,many groups have focused on the research and development of GaN-based ultraviolet laser diodes(UV LDs).Great progresses have been achieved even though many challenges exist.In this article,we analyze the challenges of developing GaN-based ultraviolet laser diodes,and the approaches to improve the performance of ultraviolet laser diode are reviewed.With these techniques,room temperature(RT)pulsed oscillation of AlGaN UVA(ultraviolet A)LD has been realized,with a lasing wavelength of 357.9 nm.Combining with the suppression of thermal effect,the high output power of 3.8 W UV LD with a lasing wavelength of 386.5 nm was also fabricated.展开更多
The 975 nm multimode diode lasers with high-order surface Bragg diffraction gratings have been simulated and calcu-lated using the 2D finite difference time domain(FDTD)algorithm and the scattering matrix method(SMM)....The 975 nm multimode diode lasers with high-order surface Bragg diffraction gratings have been simulated and calcu-lated using the 2D finite difference time domain(FDTD)algorithm and the scattering matrix method(SMM).The periods and etch depth of the grating parameters have been optimized.A board area laser diode(BA-LD)with high-order diffraction grat-ings has been designed and fabricated.At output powers up to 10.5 W,the measured spectral width of full width at half maxi-mum(FWHM)is less than 0.5 nm.The results demonstrate that the designed high-order surface gratings can effectively nar-row the spectral width of multimode semiconductor lasers at high output power.展开更多
We present a Brillouin–Raman random fiber laser(BRRFL)with full-open linear cavity structure to generate broadband Brillouin frequency comb(BFC)with double Brillouin-frequency-shift spacing.The incorporation of a reg...We present a Brillouin–Raman random fiber laser(BRRFL)with full-open linear cavity structure to generate broadband Brillouin frequency comb(BFC)with double Brillouin-frequency-shift spacing.The incorporation of a regeneration portion consisting of an erbium-doped fiber and a single-mode fiber enables the generation of broadband BFC.The dynamics of broadband BFC generation changing with the pump power(EDF and Raman)and Brillouin pump(BP)wavelength are investigated in detail,respectively.Under suitable conditions,the bidirectional BRRFL proposed can produce a flatamplitude BFC with 40.7-nm bandwidth ranging from 1531 nm to 1571.7 nm,and built-in 242-order Brillouin Stokes lines(BSLs)with double Brillouin-frequency-shift spacing.Moreover,the linewidth of single BSL is experimentally measured to be about 2.5 kHz.The broadband bidirectional narrow-linewidth BRRFL has great potential applications in optical communication,optical sensing,spectral measurement,and so on.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant No.12105037)the Key Project of National Natural Science Foundation of China-China Academy of Engineering Physics Joint Foundation(Grant No.U1830204)。
文摘Oxygen ions(O;)were implanted into fused silica at a fixed fluence of 1×10^(17) ions/cm^(2) with different ion energies ranging from 10 ke V to 60 ke V.The surface roughness,optical properties,mechanical properties and laser damage performance of fused silica were investigated to understand the effect of oxygen ion implantation on laser damage resistance of fused silica.The ion implantation accompanied with sputtering effect can passivate the sub-/surface defects to reduce the surface roughness and improve the surface quality slightly.The implanted oxygen ions can combine with the structural defects(ODCs and E′centers)to reduce the defect densities and compensate the loss of oxygen in fused silica surface under laser irradiation.Furthermore,oxygen ion implantation can reduce the Si-O-Si bond angle and densify the surface structure,thus introducing compressive stress in the surface to strengthen the surface of fused silica.Therefore,the laser induced damage threshold of fused silica increases and the damage growth coefficient decreases when ion energy up to30 ke V.However,at higher ion energy,the sputtering effect is weakened and implantation becomes dominant,which leads to the surface roughness increase slightly.In addition,excessive energy aggravates the breaking of Si-O bonds.At the same time,the density of structural defects increases and the compressive stress decreases.These will degrade the laser laser-damage resistance of fused silica.The results indicate that oxygen ion implantation with appropriate ion energy is helpful to improve the damage resistance capability of fused silica components.
文摘<div style="text-align:justify;"> The effects of the main parameters of argon flux, oxygen flux and beam voltage on the surface morphology, transmittance spectrum and laser damage of the HfO<sub>2</sub> single layers prepared by ion beam sputtering are studied. The HfO<sub>2</sub> amorphous single layers have porous surface morphologies. Different processes will cause differences in coatings absorption and surface morphology, which in turn will cause changes in the spectral transmittance curve. The ion beam sputtering HfO<sub>2</sub> single layers have high content of argon (4.5% - 8%). The laser damage of HfO<sub>2</sub> single layers is related to argon inclusions and non-stoichiometric defects. The changes of argon flux and beam voltage have a greater impact on argon content and O/Hf ratio. When the argon content in the coatings is lower and the O/Hf ratio is higher, the laser damage thresholds of the HfO<sub>2</sub> single layers are higher. </div>
文摘The laser-induced damage threshold(LIDT) of optical coating is a limited factor for development of a high peak power laser. The automatic damage testing facility was built to determine the LIDT of optics at 1 064 nm and 355 nm.. The cleanning and processing procedure of the substrate and coating technique were improved, and the damage resistance of high-reflective coating at 1 064 nm was increased.
基金Project supported by the China Postdoctoral Science Foundation(Grant No.2016M592709)the National Natural Science Foundation of China(Grant No.51535003)
文摘Polished fused silica samples were etched for different durations by using hydrofluoric(HF) acid solution with HF concentrations in an ultrasonic field. Surface and subsurface polishing residues and molecular structure parameters before and after the etching process were characterized by using a fluorescence microscope and infrared(IR) spectrometer, respectively. The laser induced damage thresholds(LIDTs) of the samples were measured by using pulsed nanosecond laser with wavelength of 355 nm. The results showed that surface and subsurface polishing residues can be effectively reduced by the acid etching process, and the LIDTs of fused silica are significantly improved. The etching effects increased with the increase of the HF concentration from 5 wt.% to 40 wt.%. The amount of polishing residues decreased with the increase of the etching duration and then kept stable. Simultaneously, with the increase of the etching time, the mechanical strength and molecular structure were improved.
基金Project supported by the National Natural Science Foundation of China (Grant No. 50875066)
文摘The low laser induced damage threshold of the KH2PO4 crystal seriously restricts the output power of inertial confinement fusion.The micro-waviness on the KH2PO4 surface processed by single point diamond turning has a significant influence on the damage threshold.In this paper,the influence of micro-waviness on the damage threshold of the KH2PO4 crystal and the chief sources introducing the micro-waviness are analysed based on the combination of the Fourier modal theory and the power spectrum density method.Research results indicate that among the sub-wavinesses with different characteristic spatial frequencies there exists the most dangerous frequency which greatly reduces the damage threshold,although it may not occupy the largest proportion in the original surface.The experimental damage threshold is basically consistent with the theoretical calculation.For the processing parameters used,the leading frequency of micro-waviness which causes the damage threshold to decrease is between 350-1 μm-1 and 30-1 μm-1,especially between 90-1 μm-1 and 200-1 μm-1.Based on the classification study of the time frequencies of microwaviness,we find that the axial vibration of the spindle is the chief source introducing the micro-waviness,nearly all the leading frequencies are related to the practical spindle frequency(about 6.68 Hz,400 r/min) and a special middle frequency(between 1.029 Hz and 1.143 Hz).
基金Project supported by the National Natural Science Foundation of China (Grant Nos. 61107080 and 50921002)the Natural Science Foundation of Jiangsu Province,China (Grant No. BK2011223)+2 种基金the Specialized Research Fund for the Doctoral Program of Higher Education of China (New Teachers) (Grant No.20110095120018)the China Postdoctoral Science Foundation (Grant No. 20110491472)the Fundamental Research Funds for the Central Universities,China (Grant No. 2012QNA03)
文摘Ta2O5 films are prepared by e-beam evaporation with varied deposition temperatures,annealing temperatures,and annealing times.The effects of temperature on the optical properties,chemical composition,structure,and laserinduced damage threshold(LIDT) are systematically investigated.The results show that the increase of deposition temperature decreases the film transmittance slightly,yet annealing below 923 K is beneficial for the transmittance.The XRD analysis reveals that the film is in the amorphous phase when annealed below 873 K and in thehexagonal phase when annealed at 1073 K.While an interesting near-crystalline phase is found when annealed at 923 K.The LIDT increases with the deposition temperature increasing,whereas it increases firstly and then decreases as the annealing temperature increases.In addition,the increase of the annealing time from 4 h to 12 h is favourable to improving the LIDT,which is mainly due to the improvement of the O/Ta ratio.The highest LIDT film is obtained when annealed at 923 K,owing to the lowest density of defect.
基金Supported by the National Natural Science Foundation of China under Grant No 11104293.
文摘The laser damage resistances of four crystals(CaF_(2),MgF_(2),Al_(2)O_(3),and SiO_(2))and fused silica(JGS1)irradiated at 355nm(8 ns,300-on-1)are reported.The laser-induced damage threshold is measured using a tripled Nd:YAG laser system.The results obtained from the pure crystals are in accordance with their specific optical,mechanical,and thermal properties.An empirical law based on the Franz–Keldysh effect can interpret the experimental results.
基金Project supported by the National High Technology Research and Development Program of China(Grant No.2008AA8040508)Foundation for Young Scholars of University of Electronic Science and Technology of China(Grant No.L08010401JX0806)+2 种基金the Joint Fund of the National Natural Science Foundation of China and the China Academy of Engineering Physics(Grant No.11076008)the Fundamental Research Funds for the Central Universities of China(Grant No.ZYGX2011J043)the Sichuan Provincial Young Scientists Foundation,China(Grant No.2010JQ0006)
文摘A non-evaporative technique is used to mitigate damage sites with lateral sizes in a range from 50 μm to 400 μm and depths smaller than 100 μm.The influence of the pulse frequency of a CO 2 laser on the mitigation effect is studied.It is found that a more symmetrical and smooth mitigation crater can be obtained by increasing the laser pulse frequency form 0.1 to 20 kHz.Furthermore,the sizes of laser-affected and distorted zones decrease with the increase of the laser pulse frequency,leading to less degradation of the wave-front quality of the conditioned sample.The energy density of the CO 2 laser beam is introduced for selecting the mitigation parameters.The damage sites can be successfully mitigated by increasing the energy density in a ramped way.Finally,the laser-induced damage threshold(LIDT) of the mitigated site is tested using 355 nm laser beam with a small spot(0.23 mm 2) and a large spot(3.14 mm 2),separately.It is shown that the non-evaporative mitigation technique is a successful method to stop damage re-initiation since the average LIDTs of mitigated sites tested with small or large laser spots are higher than that of pristine material.
基金Project supported by the National Natural Science Foundation of China(Grant No.62275235).
文摘A numerical model based on measured fictive temperature distributions is explored to evaluate the residual stress fields of CO_(2)laser-annealed mitigated fused silica damage sites.The proposed model extracts the residual strain from the differences in thermoelastic contraction of fused silica with different fictive temperatures from the initial frozen-in temperatures to ambient temperature.The residual stress fields of mitigated damage sites for the CO_(2)laser-annealed case are obtained by a finite element analysis of equilibrium equations and constitutive equations.The simulated results indicate that the proposed model can accurately evaluate the residual stress fields of laser-annealed mitigated damage sites with a complex thermal history.The calculated maximum hoop stress is in good agreement with the reported experimental result.The estimated optical retardance profiles from the calculated radial and hoop stress fields are consistent with the photoelastic measurements.These results provide sufficient evidence to demonstrate the suitability of the proposed model for describing the residual stresses of mitigated fused silica damage sites after CO_(2)laser annealing.
基金National Natural Science Foundation of China(Grant Nos.62005276,62175234)the Scientific and Technological Development Program of Jilin,China(Grant No.20230508111RC)to provide fund for this research。
文摘Laser anti-drone technology is entering the sequence of actual combat,and it is necessary to consider the vulnerability of typical functional parts of UAVs.Since the concept of"vulnerability"was proposed,a variety of analysis programs for battlefield targets to traditional weapons have been developed,but a comprehensive assessment methodology for targets'vulnerability to laser is still missing.Based on the shotline method,this paper proposes a method that equates laser beam to shotline array,an efficient vulnerability analysis program of target to laser is established by this method,and the program includes the circuit board and the wire into the vulnerability analysis category,which improves the precision of the vulnerability analysis.Taking the UAV engine part as the target of vulnerability analysis,combine with the"life-death unit method"to calculate the laser penetration rate of various materials of the UAV,and the influence of laser weapon system parameters and striking orientation on the killing probability is quantified after introducing the penetration rate into the vulnerability analysis program.The quantitative analysis method proposed in this paper has certain general expansibility,which can provide a fresh idea for the vulnerability analysis of other targets to laser.
基金This study was supported by the National Natural Science Foundation of China(61975215)Youth Innovation Promotion Association of the Chinese Academy of Sciences,Strategic Priority Research Program of the Chinese Academy of Sciences(XDA25020206)the Science and Technology Planning Project of Shanghai Municipal Science&Technology Commission(21DZ1100400).
文摘The laser-induced damage threshold(LIDT)of plate laser beam splitter(PLBS)coatings is closely related to the subsurface absorption defects of the substrate.Herein,a two-step deposition temperature method is proposed to understand the effect of substrate subsurface impurity defects on the LIDT of PLBS coatings.Firstly,BK7 substrates are heat-treated at three different temperatures.The surface morphology and subsurface impurity defect distribution of the substrate before and after the heat treatment are compared.Then,a PLBS coating consisting of alternating HfO2–Al2O3 mixture and SiO2 layers is designed to achieve a beam-splitting ratio(transmittance to reflectance,s-polarized light)of approximately 50:50 at 1053 nm and an angle of incidence of 45◦,and it is prepared under four different deposition processes.The experimental and simulation results show that the subsurface impurity defects of the substrate migrate to the surface and accumulate on the surface during the heat treatment,and become absorption defect sources or nodule defect seeds in the coating,reducing the LIDT of the coating.The higher the heat treatment temperature,the more evident the migration and accumulation of impurity defects.A lower deposition temperature(at which the coating can be fully oxidized)helps to improve the LIDT of the PLBS coating.When the deposition temperature is 140◦C,the LIDT(s-polarized light,wavelength:1064 nm,pulse width:9 ns,incident angle:45◦)of the PLBS coating is 26.2 J/cm2,which is approximately 6.7 times that of the PLBS coating deposited at 200◦C.We believe that the investigation into the laser damage mechanism of PLBS coatings will help to improve the LIDT of coatings with partial or high transmittance at laser wavelengths.
文摘The process of thermal stress damage during 1080 nm laser ablation of single-crystal germanium was recorded in real time using a high-speed charge-coupled device.A three-dimensional finite element numerical model based on Fourier's heat conduction equation,Hooke's law and the Alexander–Hasson equation was developed to analyze the thermal stress damage mechanism involved.The damage morphology of the ablated samples was observed using an optical microscope.The results show that the cooling process has an important influence on fracture in the laser-irradiated region of single-crystal germanium.Fracture is the result of a combination of thermal stress and reduction in local yield strength.
基金the National Natural Science Foundation of China(Nos.11872216 and 12272192)the Natural Science Foundation of Zhejiang Province(No.LY22A020002)+2 种基金the Natural Science Foundation of Ningbo City(No.202003N4083)the Scientific Research Foundation of Graduate School of Ningbo UniversityNingbo Science and Technology Major Project(No.2022Z002)。
文摘In this study,a phase-field scheme that rigorously obeys conservation laws and irreversible thermodynamics is developed for modeling stress-corrosion coupled damage(SCCD).The coupling constitutive relationships of the deformation,phase-field damage,mass transfer,and electrostatic field are derived from the entropy inequality.The SCCD localization induced by secondary phases in Mg is numerically simulated using the implicit iterative algorithm of the self-defined finite elements.The quantitative evaluation of the SCCD of a C-ring is in good agreement with the experimental results.To capture the damage localization,a micro-galvanic corrosion domain is defined,and the buffering effect on charge migration is explored.Three cases are investigated to reveal the effect of localization on corrosion acceleration and provide guidance for the design for resistance to SCCD at the crystal scale.
基金supported by FoRUM(Ruhr-University Bochum,Germany,to SCJ)the Deutsche Forschungsgemeinschaft(DFG,Germany,RE-4543/1-1,to SR).
文摘In a further aging society,excellent eyesight is an integral part of overall well-being and quality of life.Preserving good vision is crucial to maintaining mobility,independence,and mental health.There can be several reasons for visual impairment in elderly people,these include age-related macular degeneration,the leading cause of vision loss among older adults,cataract,glaucoma,diabetic retinopathy,retinal detachment,and others.
基金supported by the UTHSC Bridge funding award (E073005058 Bridge Support-2022)the National Institute of Health (R01-NS09 7800 and R56 NS127924-01) to TI。
文摘Stroke is a significant leading cause of death and disability in the United States(Tsao et al.,2022).Approximately 87% of strokes fall into the ischemic category,mainly caused by arterial blockage(Jayaraj et al.,2019).Although the only FDA-approved effective medication is tissue plasminogen activator(tPA),it should be administrated within 4.5 hours of ischemic stroke.Furthermore,tPA has been an integral part of managing acute ischemic stro ke.
基金funded by the National Natural Science Foundation of China(Grant No.12272247)National Key Project(Grant No.GJXM92579)Major Research and Development Project of Metallurgical Corporation of China Ltd.in the Non-Steel Field(Grant No.2021-5).
文摘The tensile-shear interactive damage(TSID)model is a novel and powerful constitutive model for rock-like materials.This study proposes a methodology to calibrate the TSID model parameters to simulate sandstone.The basic parameters of sandstone are determined through a series of static and dynamic tests,including uniaxial compression,Brazilian disc,triaxial compression under varying confining pressures,hydrostatic compression,and dynamic compression and tensile tests with a split Hopkinson pressure bar.Based on the sandstone test results from this study and previous research,a step-by-step procedure for parameter calibration is outlined,which accounts for the categories of the strength surface,equation of state(EOS),strain rate effect,and damage.The calibrated parameters are verified through numerical tests that correspond to the experimental loading conditions.Consistency between numerical results and experimental data indicates the precision and reliability of the calibrated parameters.The methodology presented in this study is scientifically sound,straightforward,and essential for improving the TSID model.Furthermore,it has the potential to contribute to other rock constitutive models,particularly new user-defined models.
基金Nanjing University of Posts and Telecommunications Foundation(Grant Nos.JUH219002 and JUH219007)Key Laboratory of Functional Crystals and Laser Technology,TIPC,CAS Foundation(Grant No.FCLT 202201)。
文摘We report a high-average-power acousto-optic(AO)Q-switched intracavity frequency-doubled red laser based on a high-efficiency light-emitting-diode(LED)pumped two-rod Nd,Ce:YAG laser module.Under quasi-continuous wave operation conditions,a maximum output power of 1319.08 nm wavelength was achieved at 11.26 W at a repetition rate of 100 Hz.
基金This work was supported by the National Key R&D Program of China(2022YFB3605104)National Natural Science Foundation of China(62250038,61904172,61974162,62034008,62074142,and 62074140)+1 种基金Strategic Priority Research Program of Chinese Academy of Sciences(XDB43030101)Shanxi-Zheda Institute of Advanced Materials and Chemical Engineering(2022SX-TD016).
文摘In the past few years,many groups have focused on the research and development of GaN-based ultraviolet laser diodes(UV LDs).Great progresses have been achieved even though many challenges exist.In this article,we analyze the challenges of developing GaN-based ultraviolet laser diodes,and the approaches to improve the performance of ultraviolet laser diode are reviewed.With these techniques,room temperature(RT)pulsed oscillation of AlGaN UVA(ultraviolet A)LD has been realized,with a lasing wavelength of 357.9 nm.Combining with the suppression of thermal effect,the high output power of 3.8 W UV LD with a lasing wavelength of 386.5 nm was also fabricated.
基金supported by the National Key R&D Program of China,No.2022YFB4601201.
文摘The 975 nm multimode diode lasers with high-order surface Bragg diffraction gratings have been simulated and calcu-lated using the 2D finite difference time domain(FDTD)algorithm and the scattering matrix method(SMM).The periods and etch depth of the grating parameters have been optimized.A board area laser diode(BA-LD)with high-order diffraction grat-ings has been designed and fabricated.At output powers up to 10.5 W,the measured spectral width of full width at half maxi-mum(FWHM)is less than 0.5 nm.The results demonstrate that the designed high-order surface gratings can effectively nar-row the spectral width of multimode semiconductor lasers at high output power.
基金Project supported by the National Natural Science Foundation of China (Grant Nos. 62175116 and 91950105)the 1311 Talent Plan of Nanjing University of Posts and Telecommunications, Chinathe Postgraduate Research & Practice Innovation Program, Jiangsu Province, China (Grant No. SJCX21_0276)
文摘We present a Brillouin–Raman random fiber laser(BRRFL)with full-open linear cavity structure to generate broadband Brillouin frequency comb(BFC)with double Brillouin-frequency-shift spacing.The incorporation of a regeneration portion consisting of an erbium-doped fiber and a single-mode fiber enables the generation of broadband BFC.The dynamics of broadband BFC generation changing with the pump power(EDF and Raman)and Brillouin pump(BP)wavelength are investigated in detail,respectively.Under suitable conditions,the bidirectional BRRFL proposed can produce a flatamplitude BFC with 40.7-nm bandwidth ranging from 1531 nm to 1571.7 nm,and built-in 242-order Brillouin Stokes lines(BSLs)with double Brillouin-frequency-shift spacing.Moreover,the linewidth of single BSL is experimentally measured to be about 2.5 kHz.The broadband bidirectional narrow-linewidth BRRFL has great potential applications in optical communication,optical sensing,spectral measurement,and so on.