Coal gangue is the main pollution source of mining areas.When coal gangue is stacked and recycled,the heavy metal elements contained in it are released by natural weathering and leaching,which causes damage to the sur...Coal gangue is the main pollution source of mining areas.When coal gangue is stacked and recycled,the heavy metal elements contained in it are released by natural weathering and leaching,which causes damage to the surrounding ecological environment.In this study,the leaching and precipitation characteristics of heavy metals in low-sulfur coal gangue under different environmental conditions were simulated by indoor dynamic leaching experiments,which provided a theoretical basis for environmental restoration of the mining area.The conclusions are as follows:higher heavy metal content in low-sulfur coal gangue is associated with greater,leaching of heavy metals;acidic conditions promote the release of heavy metals in low-sulfur coal gangue;and more precipitation is associated with better release of heavy metals from the low-sulfur coal gangue.展开更多
A new technology for microwave pretreatment of spent catalyst on Zn extraction by HCl leaching was proposed and the temperature-change curve of spent catalyst under microwave irradiation was measured.The influence of ...A new technology for microwave pretreatment of spent catalyst on Zn extraction by HCl leaching was proposed and the temperature-change curve of spent catalyst under microwave irradiation was measured.The influence of microwave pretreatment temperature and microwave irradiation time on zinc extraction was investigated and the mechanism of microwave pretreatment for spent catalyst was analyzed.The results show that microwave pretreatment can greatly enhance the leaching rate of Zn.The Zn extraction reaches 96.58%under the conditions of microwave pretreatment temperature of 950℃and the microwave irradiation time of 12 min.The blocked pores of spent catalyst can be opened through microwave pretreatment,increasing the contact area of leaching reagent and zinc.展开更多
A high-voltage pulsed discharge(HVPD)pretreatment was used to strengthen the leaching effect of Carlin-type gold ore containing arsenic.Optimal results of the pretreatment experiments were obtained at the following op...A high-voltage pulsed discharge(HVPD)pretreatment was used to strengthen the leaching effect of Carlin-type gold ore containing arsenic.Optimal results of the pretreatment experiments were obtained at the following operating conditions:a spherical gap spacing of 20 mm,pulse number of 100,and voltage of 30 kV.The leaching rate of gold was increased by 15.65%via the HVPD pretreatment.The mass fraction of–0.5+0.35 mm and–0.35+0.1 mm was increased by 10.97%and 6.83%compared to the untreated samples,respectively,and the Au grade of–0.1 mm was increased by 22.84%.However,the superiority of the HVPD pretreatment would be weakened by prolonged grinding time.Scanning electron microscopy results indicated that the pretreated products presented as a melting state and then condensation,accompanying by some pore formation.More micro-cracks were generated at the interface of the ore and the original crack were expended via pulsed discharge pretreatment,with the contact area between the leaching reagent and ore increased,the leaching reaction rate enhanced and the leaching effect strengthened.展开更多
To explore the distribution of and the mechanical properties(compressive strength)of the hardened body of alkali slag-fly ash cementitious materials,this study was conducted by using the XRD,FTIR,SEM/EDS,and other tes...To explore the distribution of and the mechanical properties(compressive strength)of the hardened body of alkali slag-fly ash cementitious materials,this study was conducted by using the XRD,FTIR,SEM/EDS,and other test methods in three conditions:airtight drying(AD),airtight immersion(AI),and airtight soaking(AS).The 1D distribution law of free of hardened body under standard curing conditions was explored.The experimental results show that under standard curing conditions,the 1D distribution of within 0d-3 d shows a∨-shaped distribution,within 3-7 d show a∧-shaped distribution,and within 7-28 d tends to be balanced.The test results of leaching rate show that the free was the most stable under AD conditions and the hardened body bound the most by XRD,FTIR and SEM/EDS.And the compressive strength of the hardened body was the highest.The compressive strength of 28th reached 95.9 MPa.The definite distribution of provides an important reference for the strength development and durability evaluation of the hardened body of alkaliexcited cementitious materials.展开更多
The chemical composition of vanadium slag significantly affects its element distribution and phase composition,which affect the subsequent calcification roasting process and vanadium recovery.In this work,seven kinds ...The chemical composition of vanadium slag significantly affects its element distribution and phase composition,which affect the subsequent calcification roasting process and vanadium recovery.In this work,seven kinds of vanadium slags derived from different regions in China were used as the raw materials to study the effects of different components on the vanadium slag’s elements distribution,phase composition,calcification roasting,and leaching rate of major elements using scanning electron microscope,X-ray diffraction analysis,and inductively coupled plasma-optical emission spectroscopy.The results show that the spinel phase is wrapped with silicate phase in all vanadium slag samples.The main elements in the spinel phase are Cr,V,and Ti from the interior to the exterior.The size of spinel phase in low chromium vanadium slag is larger than the other vanadium slags with higher chromium contents.The spinel phase of high-calcium and high-phosphorus vanadium slag is more dispersed.The strongest diffraction peak of vanadium spinel phase in the vanadium slag migrates to a higher diffraction angle,and(Fe_(0.6)Cr_(0.4))_(2)O_(3)is formed after calcification roasting as the chromium content increased.A large amount of Ca_(2)SiO_(4)is produced because excess Ca reacts with Si in high-calcium and high-phosphorus vanadium slag.The vanadium leaching rate reaches 88%in some vanadium slags.The chromium leaching rate is less than 5%in all vanadium slags.The silicon leaching rate of high-calcium and high-phosphorus vanadium slag is much higher than that of the other slags.The leaching rate of manganese is higher than 10%,and the leaching rates of iron and titanium are negligible.展开更多
基金the National Natural Science Fund Project of China(41373108)the Mining Group Project of Huaibei(K160139078)。
文摘Coal gangue is the main pollution source of mining areas.When coal gangue is stacked and recycled,the heavy metal elements contained in it are released by natural weathering and leaching,which causes damage to the surrounding ecological environment.In this study,the leaching and precipitation characteristics of heavy metals in low-sulfur coal gangue under different environmental conditions were simulated by indoor dynamic leaching experiments,which provided a theoretical basis for environmental restoration of the mining area.The conclusions are as follows:higher heavy metal content in low-sulfur coal gangue is associated with greater,leaching of heavy metals;acidic conditions promote the release of heavy metals in low-sulfur coal gangue;and more precipitation is associated with better release of heavy metals from the low-sulfur coal gangue.
基金Project(2008DFA91500)supported by the China International Science and Technology Cooperation ProgramProject(2006GH01)supported by the International Collaboration Project of Yunnan Provincial Science and Technology DepartmentProject(14051157)supported by Yunnan Provincial Natural Science Foundation
文摘A new technology for microwave pretreatment of spent catalyst on Zn extraction by HCl leaching was proposed and the temperature-change curve of spent catalyst under microwave irradiation was measured.The influence of microwave pretreatment temperature and microwave irradiation time on zinc extraction was investigated and the mechanism of microwave pretreatment for spent catalyst was analyzed.The results show that microwave pretreatment can greatly enhance the leaching rate of Zn.The Zn extraction reaches 96.58%under the conditions of microwave pretreatment temperature of 950℃and the microwave irradiation time of 12 min.The blocked pores of spent catalyst can be opened through microwave pretreatment,increasing the contact area of leaching reagent and zinc.
基金This work was financially supported by the National Natural Science Foundation of China(No.51974063)the Fundamental Research Funds for the Central Universities,China(No.N180104016).
文摘A high-voltage pulsed discharge(HVPD)pretreatment was used to strengthen the leaching effect of Carlin-type gold ore containing arsenic.Optimal results of the pretreatment experiments were obtained at the following operating conditions:a spherical gap spacing of 20 mm,pulse number of 100,and voltage of 30 kV.The leaching rate of gold was increased by 15.65%via the HVPD pretreatment.The mass fraction of–0.5+0.35 mm and–0.35+0.1 mm was increased by 10.97%and 6.83%compared to the untreated samples,respectively,and the Au grade of–0.1 mm was increased by 22.84%.However,the superiority of the HVPD pretreatment would be weakened by prolonged grinding time.Scanning electron microscopy results indicated that the pretreated products presented as a melting state and then condensation,accompanying by some pore formation.More micro-cracks were generated at the interface of the ore and the original crack were expended via pulsed discharge pretreatment,with the contact area between the leaching reagent and ore increased,the leaching reaction rate enhanced and the leaching effect strengthened.
基金Funded by the Natural Sciences Foundation of China(No.51808025)the Pyramid Talent Training Project of BUCEA(No.JDYC20200329)。
文摘To explore the distribution of and the mechanical properties(compressive strength)of the hardened body of alkali slag-fly ash cementitious materials,this study was conducted by using the XRD,FTIR,SEM/EDS,and other test methods in three conditions:airtight drying(AD),airtight immersion(AI),and airtight soaking(AS).The 1D distribution law of free of hardened body under standard curing conditions was explored.The experimental results show that under standard curing conditions,the 1D distribution of within 0d-3 d shows a∨-shaped distribution,within 3-7 d show a∧-shaped distribution,and within 7-28 d tends to be balanced.The test results of leaching rate show that the free was the most stable under AD conditions and the hardened body bound the most by XRD,FTIR and SEM/EDS.And the compressive strength of the hardened body was the highest.The compressive strength of 28th reached 95.9 MPa.The definite distribution of provides an important reference for the strength development and durability evaluation of the hardened body of alkaliexcited cementitious materials.
基金financially supported by the National Natural Science Foundation of China (No. 51874077)the Opening Foundation of State Key Laboratory of Vanadium and Titanium Resources Comprehensive Utilization, China (No. 2019P4FZG00A)
文摘The chemical composition of vanadium slag significantly affects its element distribution and phase composition,which affect the subsequent calcification roasting process and vanadium recovery.In this work,seven kinds of vanadium slags derived from different regions in China were used as the raw materials to study the effects of different components on the vanadium slag’s elements distribution,phase composition,calcification roasting,and leaching rate of major elements using scanning electron microscope,X-ray diffraction analysis,and inductively coupled plasma-optical emission spectroscopy.The results show that the spinel phase is wrapped with silicate phase in all vanadium slag samples.The main elements in the spinel phase are Cr,V,and Ti from the interior to the exterior.The size of spinel phase in low chromium vanadium slag is larger than the other vanadium slags with higher chromium contents.The spinel phase of high-calcium and high-phosphorus vanadium slag is more dispersed.The strongest diffraction peak of vanadium spinel phase in the vanadium slag migrates to a higher diffraction angle,and(Fe_(0.6)Cr_(0.4))_(2)O_(3)is formed after calcification roasting as the chromium content increased.A large amount of Ca_(2)SiO_(4)is produced because excess Ca reacts with Si in high-calcium and high-phosphorus vanadium slag.The vanadium leaching rate reaches 88%in some vanadium slags.The chromium leaching rate is less than 5%in all vanadium slags.The silicon leaching rate of high-calcium and high-phosphorus vanadium slag is much higher than that of the other slags.The leaching rate of manganese is higher than 10%,and the leaching rates of iron and titanium are negligible.