The poor bonding performance between aqueous adhesives represented by melamine-urea formaldehyde(MUF)resins and reed straw hinders their applications in the field of non-wood-based panels.Multi-hydroxyl polymers are h...The poor bonding performance between aqueous adhesives represented by melamine-urea formaldehyde(MUF)resins and reed straw hinders their applications in the field of non-wood-based panels.Multi-hydroxyl polymers are highly reactive and are often used as crosslinkers.This study fabricated a resin with a strengthened crosslinked structure by combining a multi-hydroxyl polymer and MUF resin prepolymer.The reed particleboard was prepared by using this resin as an adhesive and reed stalk as the matrix.The results show that neighboring molecules combined to form C–O–C bonds that strengthened the cross-linked structure of the resin.In addition,the viscosity of the resin was increased,and a continuous adhesive layer on the surface of reed particles was formed,which slowed the penetration of reed particles.The adhesive layer significantly improved the mechanical properties of the reed particleboard.The maximum modulus of rupture(MOR),modulus of elasticity(MOE),and internal bonding strength(IB)of the reed particleboard were 33.53,4126,and 0.79 MPa,respectively.The IB of the board was 3.3 times higher than that of the reed particleboard prepared with a conventional MUF resin.Reed straw is a non-wood biomass material that has the advantage of sustainable development and may replace woodbased materials to produce particleboard.This resin-prepared reed particleboard is expected to be used in areas such as custom furniture and engineering materials.展开更多
基金supported by the Hunan Province Science and Technology Major Project[2021NK1050]Strategic Research and Consulting Project of the Chinese Academy of Engineering:Research on Green and Low-Carbon Technology Innovation Strategy of Wood-Based Panel Industry[2022-XY-62]+1 种基金Changsha Science and Technology Project[kq2004096]Hunan Provincial Technical Innovation Platform and Talent Program in Science and Technology[2016TP1013].
文摘The poor bonding performance between aqueous adhesives represented by melamine-urea formaldehyde(MUF)resins and reed straw hinders their applications in the field of non-wood-based panels.Multi-hydroxyl polymers are highly reactive and are often used as crosslinkers.This study fabricated a resin with a strengthened crosslinked structure by combining a multi-hydroxyl polymer and MUF resin prepolymer.The reed particleboard was prepared by using this resin as an adhesive and reed stalk as the matrix.The results show that neighboring molecules combined to form C–O–C bonds that strengthened the cross-linked structure of the resin.In addition,the viscosity of the resin was increased,and a continuous adhesive layer on the surface of reed particles was formed,which slowed the penetration of reed particles.The adhesive layer significantly improved the mechanical properties of the reed particleboard.The maximum modulus of rupture(MOR),modulus of elasticity(MOE),and internal bonding strength(IB)of the reed particleboard were 33.53,4126,and 0.79 MPa,respectively.The IB of the board was 3.3 times higher than that of the reed particleboard prepared with a conventional MUF resin.Reed straw is a non-wood biomass material that has the advantage of sustainable development and may replace woodbased materials to produce particleboard.This resin-prepared reed particleboard is expected to be used in areas such as custom furniture and engineering materials.