In this work,various Co_(3)O_(4)-ZSM-5 catalysts were prepared by the microwave hydrothermal method(MH-Co_(3)O_(4)@ZSM-5),dynamic hydrothermal method(DH-Co_(3)O_(4)@ZSM-5),and conventio nal hydrothermal method(CH-Co_(...In this work,various Co_(3)O_(4)-ZSM-5 catalysts were prepared by the microwave hydrothermal method(MH-Co_(3)O_(4)@ZSM-5),dynamic hydrothermal method(DH-Co_(3)O_(4)@ZSM-5),and conventio nal hydrothermal method(CH-Co_(3)O_(4)/ZSM-5).Their catalytic oxidation of dichloromethane(DCM)was analyzed.Detailed characterizations such as X-ray diffractometer(XRD),scanning microscopy(SEM),X-ray photoelectron spectroscopy(XPS),Brunauer-Emmett-Teller(BET),H2 temperature-programmed reduction(H2-TPR),temperature-programmed desorption of O_(2)(O_(2)-TPD),temperature-programmed desorption of NH_(3)(NH_(3)-TPD),diffuse reflectance infrared Fourier-transform spectra with NH_(3)molecules(NH_(3)-DRIFT),and temperature-programmed surface reaction(TPSR)were performed.Results showed that with the assistance of microwave,MH-Co_(3)O_(4)@ZSM-5 formed a uniform core-shell structure,while the other two samples did not.MH-Co_(3)O_(4)@ZSM-5 possessed rich surface adsorbed oxygen species,higher ratio of Co^(3+)/Co^(2+),strong acidity,high reducibility,and oxygen mobility among the three Co_(3)O_(4)-ZSM-5 catalysts,which was beneficial for the improvement of DCM oxidation.In the oxidation of dichloromethane,MH-Co_(3)O_(4)@ZSM-5 presented the best activity and mineralization,which was consistent with the characterizations results.Meanwhile,according to the TPSR test,HCl or Cl_(2)removal from the catalyst surface was also promoted in MH-Co_(3)O_(4)@ZSM-5 by their abundant Bronsted acid sites and the promotion of Deacon reaction by Co_(3)O_(4)or the synergistic effect of Co_(3)O_(4)and ZSM-5.According to the results of in situ DRIFT studies,a possible reaction pathway of DCM oxidation was proposed over the MH-Co_(3)O_(4)@ZSM-5 catalysts.展开更多
A series of uniform single-phase spherical BaWO 4:Dy^(3+),Tm^(3+),Eu^(3+)phosphors were prepared via a microwave hydrothermal method by using trisodium citrate dehydrate as surfactant.The phase structure,morphology an...A series of uniform single-phase spherical BaWO 4:Dy^(3+),Tm^(3+),Eu^(3+)phosphors were prepared via a microwave hydrothermal method by using trisodium citrate dehydrate as surfactant.The phase structure,morphology and photoluminescence properties were measured by powder X-ray diffraction,scanning electron microscope and fluorescence spectrometer,respectively.The results show that uniform spherical microcrystals with diameters in the range of 2–4μm are obtained.And the phase and morphology of samples are not significantly changed by doping rare earth(RE^(3+))ions.Under the excitation wavelength of 356 and 365 nm,the samples BaWO 4:0.03Dy^(3+),yTm^(3+)can emit cold white light.In order to lower the correlated color temperature(CCT)to get a warm white light,the Eu^(3+)ions were doped into BaWO 4:0.03Dy^(3+),0.01Tm^(3+).Especially,under the excitation of 365 nm,BaWO 4:0.03Dy^(3+),0.01Tm^(3+),0.03Eu^(3+)phosphor shew a bright warm white light with color coordi-nate of(0.4013,0.3629)and CCT of 3288 K.Moreover,in the BaWO 4:Dy^(3+),Tm^(3+),Eu^(3+)phosphors,the energy transfer mechanism among Dy^(3+),Tm^(3+)and Eu^(3+)ions have been discussed and the change of electron structures have been calculated by first-principles calculations.The results shew that the uniform single-phase spherical BaWO 4:Dy^(3+),Tm^(3+),Eu^(3+)phosphors could be favorable candidates in warm white LEDs.展开更多
In this paper,the Pt/SnO2 nanostructures were prepared via a facile one-step microwave assisted hydrothermal route.The structure of the introduced Pt/SnO2 and its gas-sensing properties toward CO were investigated.The...In this paper,the Pt/SnO2 nanostructures were prepared via a facile one-step microwave assisted hydrothermal route.The structure of the introduced Pt/SnO2 and its gas-sensing properties toward CO were investigated.The results from the TEM test reveal that Pt grows on the SnO2 nanostructure,which was not found for bulk in this situ method,constructing Pt/SnO2.The results indicated that the sensor using 3.0 wt%Pt/SnO2 to 100 ppm carbon monoxide performed a superior sensing properties compared to 1.5 wt%and 4.5 wt%Pt/SnO2 at 225℃.The response time of 3.0 wt%sensor is 16 s to 100 ppm CO at225℃.Such enhanced gas sensing performances could be attributed to the chemical and electrical factors.In view of chemical factors,the presence of Pt facilitates the surface reaction,which will improve the gas sensing properties.With respect to the electrical factors,the Pt/SnO2 plays roles in increasing the sensor’s response due to its characteristic configuration.In addition,the one-step in situ microwave assisted process provides a promising and versatile choice for the preparation of gas sensing materials.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51708492)National Key Research and Development Plan of China(No.2016YFC0204700)+1 种基金Zhejiang Provincial"151"Talents Programthe Program for Zhejiang Leading Team of S&T Innovation(No.2013TD07)。
文摘In this work,various Co_(3)O_(4)-ZSM-5 catalysts were prepared by the microwave hydrothermal method(MH-Co_(3)O_(4)@ZSM-5),dynamic hydrothermal method(DH-Co_(3)O_(4)@ZSM-5),and conventio nal hydrothermal method(CH-Co_(3)O_(4)/ZSM-5).Their catalytic oxidation of dichloromethane(DCM)was analyzed.Detailed characterizations such as X-ray diffractometer(XRD),scanning microscopy(SEM),X-ray photoelectron spectroscopy(XPS),Brunauer-Emmett-Teller(BET),H2 temperature-programmed reduction(H2-TPR),temperature-programmed desorption of O_(2)(O_(2)-TPD),temperature-programmed desorption of NH_(3)(NH_(3)-TPD),diffuse reflectance infrared Fourier-transform spectra with NH_(3)molecules(NH_(3)-DRIFT),and temperature-programmed surface reaction(TPSR)were performed.Results showed that with the assistance of microwave,MH-Co_(3)O_(4)@ZSM-5 formed a uniform core-shell structure,while the other two samples did not.MH-Co_(3)O_(4)@ZSM-5 possessed rich surface adsorbed oxygen species,higher ratio of Co^(3+)/Co^(2+),strong acidity,high reducibility,and oxygen mobility among the three Co_(3)O_(4)-ZSM-5 catalysts,which was beneficial for the improvement of DCM oxidation.In the oxidation of dichloromethane,MH-Co_(3)O_(4)@ZSM-5 presented the best activity and mineralization,which was consistent with the characterizations results.Meanwhile,according to the TPSR test,HCl or Cl_(2)removal from the catalyst surface was also promoted in MH-Co_(3)O_(4)@ZSM-5 by their abundant Bronsted acid sites and the promotion of Deacon reaction by Co_(3)O_(4)or the synergistic effect of Co_(3)O_(4)and ZSM-5.According to the results of in situ DRIFT studies,a possible reaction pathway of DCM oxidation was proposed over the MH-Co_(3)O_(4)@ZSM-5 catalysts.
基金This work was supported by Priority Academic Program Development(PAPD)of Jiangsu Higher Education Institutions.
文摘A series of uniform single-phase spherical BaWO 4:Dy^(3+),Tm^(3+),Eu^(3+)phosphors were prepared via a microwave hydrothermal method by using trisodium citrate dehydrate as surfactant.The phase structure,morphology and photoluminescence properties were measured by powder X-ray diffraction,scanning electron microscope and fluorescence spectrometer,respectively.The results show that uniform spherical microcrystals with diameters in the range of 2–4μm are obtained.And the phase and morphology of samples are not significantly changed by doping rare earth(RE^(3+))ions.Under the excitation wavelength of 356 and 365 nm,the samples BaWO 4:0.03Dy^(3+),yTm^(3+)can emit cold white light.In order to lower the correlated color temperature(CCT)to get a warm white light,the Eu^(3+)ions were doped into BaWO 4:0.03Dy^(3+),0.01Tm^(3+).Especially,under the excitation of 365 nm,BaWO 4:0.03Dy^(3+),0.01Tm^(3+),0.03Eu^(3+)phosphor shew a bright warm white light with color coordi-nate of(0.4013,0.3629)and CCT of 3288 K.Moreover,in the BaWO 4:Dy^(3+),Tm^(3+),Eu^(3+)phosphors,the energy transfer mechanism among Dy^(3+),Tm^(3+)and Eu^(3+)ions have been discussed and the change of electron structures have been calculated by first-principles calculations.The results shew that the uniform single-phase spherical BaWO 4:Dy^(3+),Tm^(3+),Eu^(3+)phosphors could be favorable candidates in warm white LEDs.
基金supported by the National Natural Science Foundation of China (No.61803172)the Start-up Research Foundation of Hainan University (No.KYQD(ZR)1910)。
文摘In this paper,the Pt/SnO2 nanostructures were prepared via a facile one-step microwave assisted hydrothermal route.The structure of the introduced Pt/SnO2 and its gas-sensing properties toward CO were investigated.The results from the TEM test reveal that Pt grows on the SnO2 nanostructure,which was not found for bulk in this situ method,constructing Pt/SnO2.The results indicated that the sensor using 3.0 wt%Pt/SnO2 to 100 ppm carbon monoxide performed a superior sensing properties compared to 1.5 wt%and 4.5 wt%Pt/SnO2 at 225℃.The response time of 3.0 wt%sensor is 16 s to 100 ppm CO at225℃.Such enhanced gas sensing performances could be attributed to the chemical and electrical factors.In view of chemical factors,the presence of Pt facilitates the surface reaction,which will improve the gas sensing properties.With respect to the electrical factors,the Pt/SnO2 plays roles in increasing the sensor’s response due to its characteristic configuration.In addition,the one-step in situ microwave assisted process provides a promising and versatile choice for the preparation of gas sensing materials.