Studying new wood composites through nano science and technology (NSC) will develop new compounding theory of wood, and accelerate the combination of new technology, wood science, material science and other discipline...Studying new wood composites through nano science and technology (NSC) will develop new compounding theory of wood, and accelerate the combination of new technology, wood science, material science and other disciplines. The compounding of wood and inorganic MMT on nanoscale molecular level has high potential to greatly improve the mechanical properties, fire retardance, abrasion resistance, decay resistance, dimensional stability and other properties of wood. Based on the great achievements of polymer/montmorillonite (MMT) nanocomposites, this paper reviewed nano intercalation compounding methods (i.e. in-situ intercalative polymerization and direct polymer intercalation), and discussed the structure, properties and modification of montmorillonite (MMT). According to the main chemical components and particular structure of wood, the authors discussed the liquefaction and plasticization of wood, compared the dissolvability and meltability between wood and polymer, and then systematically put forward the basic idea, technological processes and schematic diagram to prepare wood/MMT nanocomposites (WMNC). The key technology to prepare WMNC is either to introduce delaminated MMT nanolayers into wood with the help of some intermediate polymers, or to obtain liquefied wood or plasticized wood from the complicated natural composite. It is applicable and effective to realize wood/MMT nanoscale compounding with the help of proper intercalation agent and medium polymer through the proposed 搊ne-step?or 搕wo-step?impregnating processes.展开更多
For this study, an intercalation compounding method was used to prepare Chinese fir wood/Ca-montmorillonite （Ca-MMT） composite board to improve its properties such as surface mechanical properties, flame retardance ...For this study, an intercalation compounding method was used to prepare Chinese fir wood/Ca-montmorillonite （Ca-MMT） composite board to improve its properties such as surface mechanical properties, flame retardance and dimensional stability. By virtue of water-soluble phenolic resin （PF）, Chinese fir wood and Ca-MMT were mixed by pressure and vacuum impregnation. The optimum impregnation technology of Chinese fir wood/Ca-MMT composite board was obtained by using an orthogonal design and a single factor design of pressure and vacuum impregnation, using weight percent gain （WPG） as the basic index. The results are as follows： 1） On the basis of the orthogonal design and an actual experiment, the optimum preparation technology of Chinese fir wood/Ca-MMT composite board is 20% PF resin dispersion concentration （wt%）, 1.0 CEC amount of organic intercalation agent, 0.098 MPa vacuum degree, 5% concentration of Ca-MMT and 1.0 MPa pressure. 2） The WPG of the composite board samples of 450 mm length was much larger than that of the samples of 600, 750 and 900 mm length. Warm water extraction contributed little to WPG展开更多
Hybrid organic-inorganic polymer nanocomposites incorporating organically modified montmorillonite (MMT) and ultra-high molecular weight polyethylene (UHMWPE) were examined. UHMWPE/MMT hybrid nanocomposites were prepa...Hybrid organic-inorganic polymer nanocomposites incorporating organically modified montmorillonite (MMT) and ultra-high molecular weight polyethylene (UHMWPE) were examined. UHMWPE/MMT hybrid nanocomposites were prepared using gel and pressure-induced flow(PIF) processing methods at a gel weight concentration of 8% UHMWPE with various organoclay contents (0, 0.4, 0.8, 1.2, and 1.6 parts per hundred parts). The interlayer properties of the nanocomposites were studied by transmission electron microscopy (TEM) and scanning electron microscopy (SEM). The thermal and mechanical interfacial properties of the nanocomposites were investigated through thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), and the use of a universal test machine (UTM). TEM indicates that the nanocomposites are formed upon dispersion of MMT in the polymer matrix. From the DSC, TGA, and DMA results, we find that the thermal stability of the UHMWPE nanocomposites increases as the MMT content increases. The nanocomposites show higher tensile strengths than pure UHMWPE gel sheet. These findings indicate that the interfacial and mechanical properties are improved by the addition of MMT and PIF processing.展开更多
Nanocomposites were prepared by a simple technique of emulsion polymerization using VC monomer and Na + montmorillonite. The nano structure of the composites was studied with the aid of X ray diffraction and t ransmis...Nanocomposites were prepared by a simple technique of emulsion polymerization using VC monomer and Na + montmorillonite. The nano structure of the composites was studied with the aid of X ray diffraction and t ransmission electron microscopy,and the mechanical and thermal properties of th e composites were also tested. The results showed that the silicate layers were delam inated or partially exfoliated in the PVC matrix. The impact strength of the mat erial with 2 1% MMT was almost two times as high as that of pure PVC, while the tensi le strength decreased little. However, the mechanical strength of the composites began to decrease with further increasing the amount of MMT. The TGA resul ts showed that the temperature,at which a 50% weight loss of the composites occurred,was higher than that of pure PVC. The vicat softening temperatures of composites were enhanced with increasing MMT content.展开更多
基金Supported by the National Natural Science Foundation of China (Grant No. 30271055)
文摘Studying new wood composites through nano science and technology (NSC) will develop new compounding theory of wood, and accelerate the combination of new technology, wood science, material science and other disciplines. The compounding of wood and inorganic MMT on nanoscale molecular level has high potential to greatly improve the mechanical properties, fire retardance, abrasion resistance, decay resistance, dimensional stability and other properties of wood. Based on the great achievements of polymer/montmorillonite (MMT) nanocomposites, this paper reviewed nano intercalation compounding methods (i.e. in-situ intercalative polymerization and direct polymer intercalation), and discussed the structure, properties and modification of montmorillonite (MMT). According to the main chemical components and particular structure of wood, the authors discussed the liquefaction and plasticization of wood, compared the dissolvability and meltability between wood and polymer, and then systematically put forward the basic idea, technological processes and schematic diagram to prepare wood/MMT nanocomposites (WMNC). The key technology to prepare WMNC is either to introduce delaminated MMT nanolayers into wood with the help of some intermediate polymers, or to obtain liquefied wood or plasticized wood from the complicated natural composite. It is applicable and effective to realize wood/MMT nanoscale compounding with the help of proper intercalation agent and medium polymer through the proposed 搊ne-step?or 搕wo-step?impregnating processes.
基金the National Natural Science Foundation of China (Grant No.30271055)
文摘For this study, an intercalation compounding method was used to prepare Chinese fir wood/Ca-montmorillonite （Ca-MMT） composite board to improve its properties such as surface mechanical properties, flame retardance and dimensional stability. By virtue of water-soluble phenolic resin （PF）, Chinese fir wood and Ca-MMT were mixed by pressure and vacuum impregnation. The optimum impregnation technology of Chinese fir wood/Ca-MMT composite board was obtained by using an orthogonal design and a single factor design of pressure and vacuum impregnation, using weight percent gain （WPG） as the basic index. The results are as follows： 1） On the basis of the orthogonal design and an actual experiment, the optimum preparation technology of Chinese fir wood/Ca-MMT composite board is 20% PF resin dispersion concentration （wt%）, 1.0 CEC amount of organic intercalation agent, 0.098 MPa vacuum degree, 5% concentration of Ca-MMT and 1.0 MPa pressure. 2） The WPG of the composite board samples of 450 mm length was much larger than that of the samples of 600, 750 and 900 mm length. Warm water extraction contributed little to WPG
基金National Natural Science Foundations of China (No. 50833002, No. 20774018)
文摘Hybrid organic-inorganic polymer nanocomposites incorporating organically modified montmorillonite (MMT) and ultra-high molecular weight polyethylene (UHMWPE) were examined. UHMWPE/MMT hybrid nanocomposites were prepared using gel and pressure-induced flow(PIF) processing methods at a gel weight concentration of 8% UHMWPE with various organoclay contents (0, 0.4, 0.8, 1.2, and 1.6 parts per hundred parts). The interlayer properties of the nanocomposites were studied by transmission electron microscopy (TEM) and scanning electron microscopy (SEM). The thermal and mechanical interfacial properties of the nanocomposites were investigated through thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), and the use of a universal test machine (UTM). TEM indicates that the nanocomposites are formed upon dispersion of MMT in the polymer matrix. From the DSC, TGA, and DMA results, we find that the thermal stability of the UHMWPE nanocomposites increases as the MMT content increases. The nanocomposites show higher tensile strengths than pure UHMWPE gel sheet. These findings indicate that the interfacial and mechanical properties are improved by the addition of MMT and PIF processing.
文摘Nanocomposites were prepared by a simple technique of emulsion polymerization using VC monomer and Na + montmorillonite. The nano structure of the composites was studied with the aid of X ray diffraction and t ransmission electron microscopy,and the mechanical and thermal properties of th e composites were also tested. The results showed that the silicate layers were delam inated or partially exfoliated in the PVC matrix. The impact strength of the mat erial with 2 1% MMT was almost two times as high as that of pure PVC, while the tensi le strength decreased little. However, the mechanical strength of the composites began to decrease with further increasing the amount of MMT. The TGA resul ts showed that the temperature,at which a 50% weight loss of the composites occurred,was higher than that of pure PVC. The vicat softening temperatures of composites were enhanced with increasing MMT content.