Hot isostatic pressing parameters are critical to Ti60 high temperature titanium alloy castings which have wide application perspective in aerospace.In order to obtain optimal processing parameters,the effects of hot ...Hot isostatic pressing parameters are critical to Ti60 high temperature titanium alloy castings which have wide application perspective in aerospace.In order to obtain optimal processing parameters,the effects of hot isostatic pressing parameters on defects,composition uniformity,microstructure and mechanical properties of Ti60 cast high temperature titanium alloy were investigated in detail.Results show that increasing temperature and pressure of hot isostatic pressing can reduce defects,especially,the internal defects are substantially eliminated when the temperature exceeds 920℃or the pressure exceeds 125 MPa.The higher temperature and pressure can improve the microstructure uniformity.Besides,the higher pressure can promote the composition uniformity.With the temperature increases from 880℃to 960℃,α-laths are coarsened.But with increasing pressure,the grain size of prior-βphase,the widths ofα-laths andα-colony are reduced.The tensile strength of Ti60 alloy is 949 MPa,yield strength is 827 MPa,and the elongation is 11%when the hot isostatic pressing parameters are 960℃/125 MPa/2 h,which exhibits the best match between the strength and plasticity.展开更多
Air plasma spraying process was employed to fabricate various hydroxyapatite(HA)coatings on titanium substrates.The influence of processing parameters on the phase composition and the microstructure of the obtained co...Air plasma spraying process was employed to fabricate various hydroxyapatite(HA)coatings on titanium substrates.The influence of processing parameters on the phase composition and the microstructure of the obtained coatings was investigated.The effect of heat treatment on as-sprayed coating in terms of the crystallinity and microstructure was also studied.The phase composition of coatings was analyzed by X-ray diffraction(XRD)and FTIR.The surface and cross-section morphologies and microstructure of coatings as well as the morphology of feedstock were evaluated using scanning electron microscope(SEM).The crystallization temperature of amorphous HA phase in as-sprayed coating was examined by using differential thermal analysis(DTA). The results suggest that phase composition and microstructure of as-sprayed HA coatings strongly depend on the spraying parameters,and heat treatment at 760 ℃for 2 h is one of effective means for increasing the crystallinity and improvement in microstructure of as-sprayed HA coatings.展开更多
Al-3Ti-1B master alloys were prepared at different processing parameters by the reaction of halide salts,and the grain refining response of Al-7Si alloy was investigated with Al-3Ti-B master alloy.The microstructure o...Al-3Ti-1B master alloys were prepared at different processing parameters by the reaction of halide salts,and the grain refining response of Al-7Si alloy was investigated with Al-3Ti-B master alloy.The microstructure of master alloy and its grain refining effect on Al-7Si alloy were investigated by means of OM,XRD and SEM.Experimental results show that,the size of Al3Ti particles presented in Al-3Ti-1B master alloys increases with the increase of reaction temperature and decreases with the increase of cooling rate.The grain refining efficiency of Al-3Ti-1B master alloy on Al-7Si alloy is mainly attributed to heterogeneous nucleation of Al3Ti particles,and the morphology ofα(Al)changes from coarse dendritic to fine equiaxed.As a result,Al-3Ti-1B master alloy is prepared by permanent mold,and holding at 800 ℃for 30min,which has better grain refining performance on Al-7Si alloy.展开更多
The influence of processing parameters on the coating surface roughness of LD10 aluminum alloy treated by the power source with positive and negative pulse in the alkaline electrolyte was discussed.Lots of experiments...The influence of processing parameters on the coating surface roughness of LD10 aluminum alloy treated by the power source with positive and negative pulse in the alkaline electrolyte was discussed.Lots of experiments were done with different processing parameters including the positive final voltage,the negative final voltage,the frequency,the duty ratio,the processing time and electrolyte temperature.And the surface roughness tester TR200 was used to measure the coating surface roughness.The influence of the processing time on the surface roughness is the smallest,less than 0.2μm.The surface roughness decreases gradually with the duty ratio decreasing or the frequency increasing;it decreases gradually with each of the other parameters increasing,and then increases gradually after achieving the minimum value.Appropriately by selecting processing parameters,the coating with Ra 0.6 can be obtained.展开更多
In order to improve the intrinsic brittleness of TiAl alloys,Ti_(2)AlNb alloys with outstanding ductility and toughness at room temperature,and good high-temperature performance are competitive candidates in construct...In order to improve the intrinsic brittleness of TiAl alloys,Ti_(2)AlNb alloys with outstanding ductility and toughness at room temperature,and good high-temperature performance are competitive candidates in constructing the TiAl-based laminated composites.In this work,TiAl/Ti_(2)AlNb laminated composites are successfully synthesized by vacuum hot pressing combined with the foil-foil(sheet)metallurgy.Under the pressure of 65 MPa,different holding time and temperature of hot pressing are tried and the optimized fabrication parameter is acquired as 1050℃/120 min/65 MPa.Along with the changes of processing parameters,the defect,microstructure,interface,phase transformation and the corresponding mechanical properties are detailly discussed.The results show that the TiAl/Ti_(2)AlNb laminated composite fabricated at 1050℃ for 2 h achieves a good metallurgical interface bonding.The corresponding interface microstructure is composed of region I and region II.The region I consists of O,α_(2)and B2/βphase,and region II is made up ofα2.Subsequently,the tensile tests indicate that the composite synthesized at 1050℃ for 2 h possesses a maximum strength of 812 MPa and a total elongation of 1.31%at room temperature,and a strength of 539.71 MPa and the highest total elongation of 10.34%at 750℃.The well synergistic deformation ability between the interface and the two base alloys endows the composite an excellent tensile performance.Moreover,the composite processed at 1050℃ for 2 h behaves the best fracture toughness in both arrester orientation and divider orientation with the value of 32.6 MPa.m^(1/2)and 30.1 MPa.m^(1/2),respectively.The Ti_(2)AlNb alloy in the laminated structure effectively release the stress around the crack tip and plays a role in toughening.Further,crack deflection,crack bridging,crack blunting and fragmentation also make contributions to enhance the fracture toughness of the laminated composites.展开更多
High-performance thermoplastic composites have been developed as significant structural materials for cutting-edge equipment in the aerospace and defence fields.However,the internal mechanism of processing parameters ...High-performance thermoplastic composites have been developed as significant structural materials for cutting-edge equipment in the aerospace and defence fields.However,the internal mechanism of processing parameters on mechanical properties in the manufacturing process of thermoplastic composite structures is still a serious challenge.The purpose of this study is to investigate the process/crystallization/property relationships for continuous carbon fiber(CF)reinforced polyether-ether-ketone(PEEK)composites.The composite laminates are fabricated according to orthogonal experiments via the thermoforming method.The mechanical performance is investigated in terms of crystallization properties and fracture morphology characterizations.Experimental results show that the mechanical performance and crystallization properties of thermoplastic composites are significantly affected by the coupling of processing parameters.The increased molding temperature,pressure,and holding time improve the degree of fiber/matrix infiltration and affect the crystallinity and crystalline morphology of the matrix,which further influences the mechanical properties of the composites.This is reflected in the test results that crystallinity has an approximately linear effect on mode-I interlaminar fracture toughness and transverse flexural modulus.As well as the higher molding temperature can destroy the pre-existent crystals to improve the toughness of the matrix,and the well-defined crystalline structures can be observed when fabricated at higher temperatures and longer periods of holding time.展开更多
The unique properties of bulk metallic glass(BMG)render it an excellent material for bone-implant applications.BMG samples are difficult to produce directly because of the critical cooling rate of molding.Advancements...The unique properties of bulk metallic glass(BMG)render it an excellent material for bone-implant applications.BMG samples are difficult to produce directly because of the critical cooling rate of molding.Advancements in additive manufacturing technologies,such as selective laser melting(SLM),have enabled the development of BMG.The successful production of materials via SLM relies significantly on the processing parameters;meanwhile,the overall energy density affects the crystallization and,thus,the final properties.Therefore,to further determine the effects of the processing parameters,SLM is performed in this study to print Fe-based BMG with different properties three dimensionally using selected processing parameters but a constant energy density.The printed amorphous Fe-based BMG outperforms the typical 316 L stainless steel(316 L SS)in terms of mechanical properties and corrosion resistance.Moreover,observations from nanoindentation tests indicate that the hardness and elastic modulus of the Fe-based BMG can be customized explicitly by adjusting the SLM processing parameters.Indirect cytotoxicity results show that the Fe-based BMG can enhance the viability of SAOS2 cells,as compared with 316 L SS.These intriguing results show that Fe-based BMG should be investigated further for orthopedic implant applications.展开更多
Squeeze casting(SC)is an advanced net manufacturing process with many advantages for which the quality and properties of the manufactured parts depend strongly on the process parameters.Unfortunately,a universal effic...Squeeze casting(SC)is an advanced net manufacturing process with many advantages for which the quality and properties of the manufactured parts depend strongly on the process parameters.Unfortunately,a universal efficient method for the determination of optimal process parameters is still unavailable.In view of the shortcomings and development needs of the current research methods for the setting of SC process parameters,by consulting and analyzing the recent research literature on SC process parameters and using the CiteSpace literature analysis software,manual reading and statistical analysis,the current state and characteristics of the research methods used for the determination of SC process parameters are summarized.The literature data show that the number of pub-lications in the literature related to the design of SC process parameters generally trends upward albeit with signifi-cant fluctuations.Analysis of the research focus shows that both“mechanical properties”and“microstructure”are the two main subjects in the studies of SC process parameters.With regard to materials,aluminum alloys have been extensively studied.Five methods have been used to obtain SC process parameters:Physical experiments,numeri-cal simulation,modeling optimization,formula calculation,and the use of empirical values.Physical experiments are the main research methods.The main methods for designing SC process parameters are divided into three categories:Fully experimental methods,optimization methods that involve modeling based on experimental data,and theoreti-cal calculation methods that involve establishing an analytical formula.The research characteristics and shortcomings of each method were analyzed.Numerical simulations and model-based optimization have become the new required methods.Considering the development needs and data-driven trends of the SC process,suggestions for the develop-ment of SC process parameter research have been proposed.展开更多
The successful confinement of the arc by the flux band depends on the welding process parameters for achieving single-pass,multi-layer, and ultra-narrow gap welding. The sidewall fusion depth, the width of the heat-af...The successful confinement of the arc by the flux band depends on the welding process parameters for achieving single-pass,multi-layer, and ultra-narrow gap welding. The sidewall fusion depth, the width of the heat-affected zone, and the line energy are utilized as comprehensive indications of the quality of the welded joint. In order to achieve well fusion and reduce the heat input to the base metal.Three welding process characteristics were chosen as the primary determinants, including welding voltage, welding speed, and wire feeding speed. The metamodel of the welding quality index was built by the orthogonal experiments. The metamodel and NSGA-Ⅱ(Non-dominated sorting genetic algorithm Ⅱ) were combined to develop a multi-objective optimization model of ultra-narrow gap welding process parameters. The results showed that the optimized welding process parameters can increase the sidewall fusion depth, reduce the width of the heataffected zone and the line energy, and to some extent improve the overall quality of the ultra-narrow gap welding process.展开更多
Lunar surface additive manufacturing with lunar regolith is a key step in in-situ resource utilization.The powder spreading process is the key process,which has a major impact on the quality of the powder bed and the ...Lunar surface additive manufacturing with lunar regolith is a key step in in-situ resource utilization.The powder spreading process is the key process,which has a major impact on the quality of the powder bed and the precision of molded parts.In this study,the discrete element method(DEM)was adopted to simulate the powder spreading process with a roller.The three powder bed quality indicators,including the molding layer offset,voidage fraction,and surface roughness,were established.Besides,the influence of the three process parameters,which are roller’s translational speed,rotational speed,and powder spreading layer thickness on the powder bed quality indicators was also analyzed.The results show that with the reduction of the powder spreading layer thickness and the increase of the rotational speed,the offset increased significantly;when the translational speed increased,the offset first increased and then decreased,which resulted in an extreme value;with the increase of the layer thickness and the decrease of the translational speed,the values for voidage fraction and surface roughness significantly reduced.The powder bed quality indicators were adopted as the optimization objective,and the multi-objective parameter optimization was carried out.The predicted optimal powder spreading parameters and powder bed quality indicators were then obtained.Moreover,the optimal values were then verified.This study can provide informative guidance for in-situ manufacturing at the moon in future deep space exploration missions.展开更多
Aluminum alloy thin-walled structures are widely used in the automotive industry due to their advantages related to light weight and crashworthiness.They can be produced at room temperature by the electrohydraulic for...Aluminum alloy thin-walled structures are widely used in the automotive industry due to their advantages related to light weight and crashworthiness.They can be produced at room temperature by the electrohydraulic forming process.In the present study,the influence of the related parameters on the forming quality of a 6063 aluminum alloy sinusoidal corrugation tube has been assessed.In particular,the orthogonal experimental design(OED)and central composite design(CCD)methods have been used.Through the range analysis and variance analysis of the experimental data,the influence degree of wire diameter(WD)and discharge energy(DE)on the forming quality was determined.Multiple regression analysis was performed using the response surface methodology.A prediction model for the attaching-die state coefficient was established accordingly.The following optimal arrangement of parameters was obtained(WD=0.759 mm,DE=2.926 kJ).The attaching-die state coefficient reached the peak value of 0.001.Better optimized wire diameter and discharge energy for a better attaching-die state could be screened by CCD compared with OED.The response surface method in CCD was more suitable for the design and optimization of the considered process parameters.展开更多
In order to obtain better quality cookies, food 3D printing technology was employed to prepare cookies. The texture, color, deformation, moisture content, and temperature of the cookie as evaluation indicators, the in...In order to obtain better quality cookies, food 3D printing technology was employed to prepare cookies. The texture, color, deformation, moisture content, and temperature of the cookie as evaluation indicators, the influences of baking process parameters, such as baking time, surface heating temperature and bottom heating temperature, on the quality of the cookie were studied to optimize the baking process parameters. The results showed that the baking process parameters had obvious effects on the texture, color, deformation, moisture content, and temperature of the cookie. All of the roasting surface heating temperature, bottom heating temperature and baking time had positive influences on the hardness, crunchiness, crispiness, and the total color difference(ΔE) of the cookie. When the heating temperatures of the surfac and bottom increased, the diameter and thickness deformation rate of the cookie increased. However,with the extension of baking time, the diameter and thickness deformation rate of the cookie first increased and then decreased. With the surface heating temperature of 180 ℃, the bottom heating temperature of 150 ℃, and baking time of 15 min, the cookie was crisp and moderate with moderate deformation and uniform color. There was no burnt phenomenon with the desired quality. Research results provided a theoretical basis for cookie manufactory based on food 3D printing technology.展开更多
Many studies have investigated the selective laser melting(SLM)of AlSi10Mg and AlSi7Mg alloys,but there are still lack of researches focused on Al-Si-Mg alloys specifically tailored for SLM.In this work,a novel high M...Many studies have investigated the selective laser melting(SLM)of AlSi10Mg and AlSi7Mg alloys,but there are still lack of researches focused on Al-Si-Mg alloys specifically tailored for SLM.In this work,a novel high Mg-content AlSi8Mg3 alloy was specifically designed for SLM.The results showed that this new alloy exhibited excellent SLM processability with a lowest porosity of 0.07%.Massive lattice distortion led to a high Vickers hardness in samples fabricated at a high laser power due to the precipitation of Mg_(2)Si nanoparticles from theα-Al matrix induced by high-intensity intrinsic heat treatment during SLM.The maximum microhardness and compressive yield strength of the alloy reached HV(211±4)and(526±12)MPa,respectively.After aging treatment at 150℃,the maximum microhardness and compressive yield strength of the samples were further improved to HV(221±4)and(577±5)MPa,respectively.These values are higher than those of most known aluminum alloys fabricated by SLM.This paper provides a new idea for optimizing the mechanical properties of Al-Si-Mg alloys fabricated using SLM.展开更多
The large warping deformation at platform of turbine blade directly affects the forming precision. In the present research, equivalent warping deformation was firstly presented to describe the extent of deformation at...The large warping deformation at platform of turbine blade directly affects the forming precision. In the present research, equivalent warping deformation was firstly presented to describe the extent of deformation at platform. To optimize the process parameters during investment casting to minimize the warping deformation of the platform, based on simulation with Pro CAST, the single factor method, orthogonal test, neural network and genetic algorithm were subsequently used to analyze the influence of pouring temperature, shell mold preheating temperature, furnace temperature and withdrawal velocity on dimensional accuracy of the platform of superalloyDD6 turbine blade. The accuracy of investment casting simulation was verified by measurement of platform at blade casting. The simulation results with the optimal process parameters illustrate that the equivalent warping deformation was dramatically reduced by 21.8% from 0.232295 mm to 0.181698 mm.展开更多
A certain amount of Ti was added to the plasma cladding Fe-Cr-C coating in the early stage in order to improve the quality and properties of the coating.Ti-Fe-Cr-C composite powder was prepared by precursor carbonizat...A certain amount of Ti was added to the plasma cladding Fe-Cr-C coating in the early stage in order to improve the quality and properties of the coating.Ti-Fe-Cr-C composite powder was prepared by precursor carbonization-composition process.In situ synthesized TiC-Fe-Cr coatings were fabricated on substrate of Q235 steel by plasma cladding process with the composite powder.Microstructures of the coatings with different process parameters,including cladding current,cladding speed,number of overlapping cladding layers,were analyzed by scanning electron microscope.The results show that the structure of the TiC-Fe-Cr coating is greatly affected by the cladding current,the cladding speed and the overlapping cladding process.In this test,when the cladding current of 300 A and the cladding process parameter of the cladding speed of 50 mm/min are clad with three layers,a well-formed and well-structured TiC-Fe-Cr coating can be obtained in this test.TiC-Fe-Cr coating has good wear resistance and good load characteristics under dry sliding wear test conditions.展开更多
The quality standards for Fructus Comi have been established based on the effects of the manufacturing processes.Three critical process parameters(CPPs)of extraction,filtration,and concentration to prepare Fructus Com...The quality standards for Fructus Comi have been established based on the effects of the manufacturing processes.Three critical process parameters(CPPs)of extraction,filtration,and concentration to prepare Fructus Comi concentrate were identified by Plackett-Burman design with a single batch of Fructus Corni,which were heating medium temperature,extraction time,and water addition.Morroniside yield,loganin yield,and dry matter yield were process critical quality attributes(CQAs).CPPs arranged with a Box-Behnken design were applied to treat different batches of Fructus Comi After constructing a model that included CPPs,material propertie s,and process CQAs,loganin content was found to be the critical material attribute(CMA).The design space was calculated with a probability method.According to the limits of process CQAs,the minimum content of loganin in Fructus Corni was calculated with an error propagation method,which was 6.92 mg·g^(-1).When the content of loganin in Fructus Corni reaches up to 6.92 mg·g^(-1),the material is considered high-quality and is most suitable for the process.High-quality material can be used for production of Fructus Comi concentrate.This method can also be used to set material quality standards for other Chinese medicines.展开更多
As a typical laser additive manufacturing technology,laser powder bed fusion(LPBF)has achieved demonstration applications in aerospace,biomedical and other fields.However,how to select process parameters quickly and r...As a typical laser additive manufacturing technology,laser powder bed fusion(LPBF)has achieved demonstration applications in aerospace,biomedical and other fields.However,how to select process parameters quickly and reasonably is still themain concern of LPBF production.In order to quantitatively analyze the influence of different process parameters(laser power,scanning speed,hatch space and layer thickness)on the LPBF process,the multilayer and multi-path forming process of LPBF was predicted based on the open-source discrete element method framework Yade and the open-source finite volume method framework OpenFOAM.Based on the design of experiments method,a four-factor three-level orthogonal test scheme was designed,and the porosity and surface roughness data of each calculation scheme were extracted.By analyzing the orthogonal test data,it was found that as the laser power increased,the porosity decreased,and as the scanning speed,hatch space,and layer thickness increased,the porosity increased.In addition,the influence of laser power and scanning speed on surface roughness showed a trend of decreasing first and then increasing,while the influence of scanning distance and layer thickness on surface roughness showed amonotonous increasing trend.The order of the influence of each process parameter on porosity was:scanning speed>laying thickness>laser power>hatch space,and the order of the influence of each process parameter on surface roughness was:hatch space>layer thickness>laser power>scanning speed.So the porosity of the part is most sensitive to scanning speed,and the surface roughness is the most sensitive to hatch space.The above conclusions are expected to provide process control basis for actual LPBF production of the 316L stainless steel alloy.展开更多
The relationships between the surface quality of a single crystal copper ingot and the process parameters of heated mould continuous casting method were studied experimentally using our own design of horizontal heated...The relationships between the surface quality of a single crystal copper ingot and the process parameters of heated mould continuous casting method were studied experimentally using our own design of horizontal heated mould continuous casting apparatus, and the mechanism by which process parameters affect the surface quality of a single crystal copper ingot is analyzed in the present paper. The results show that the process parameters affect the surface quality of a pure copper ingot by affecting the position of the liquid-solid interface in the mould. The position of the liquid-solid interface in the mould must be controlled carefully within an appropriate range, which is determined through a series of experiments, in order to gain a single crystal copper ingot with good surface quality.展开更多
In this study,friction stir lap welding(FSLW)was performed for the welding test of 6061 aluminium alloy and T2 pure copper.The effect of process parameters containing rotation rate and travel speed on interfacial micr...In this study,friction stir lap welding(FSLW)was performed for the welding test of 6061 aluminium alloy and T2 pure copper.The effect of process parameters containing rotation rate and travel speed on interfacial microstructure evolution and mechanical properties of Al/Cu dissimilar joints were explored.The experiments were carried out under the rotation rates of 600,900 and 1200 r/min and with the travel speeds of 30,70 and 100 mm/min.The characteristic of interface transition zones(ITZs)and the species of intermetallic compounds(IMCs)were investigated.The Al/Cu interface showed a layered structure composed of Al-Cu IMCs,which will affect the mechanical property.The layer consisting of Al2Cu was formed at lower heat input,and as heat input increased the Al4Cu9 phase started to form.Excessive heat input will increase the thickness of the interface and raise the brittleness of the joints.The thickness of the IMCs layers changed from0.89μm to 3.96μm as the heat input increased.The maximum value of tensile shear loading of 4.65 kN was obtained at the rotation rate of900 r/min and travel speed of 100 mm/min with the interface thickness of 2.89μm.The fracture mode of the joints was a mix of ductile and brittle fracture.展开更多
Here we develop a two-dimensional numerical model of wire and arc additive manufacturing(WAAM)to determine the relationship between process parameters and deposition geometry,and to reveal the influence mechanism of p...Here we develop a two-dimensional numerical model of wire and arc additive manufacturing(WAAM)to determine the relationship between process parameters and deposition geometry,and to reveal the influence mechanism of process parameters on deposition geometry.From the predictive results,a higher wire feed rate matched with a higher current could generate a larger and hotter droplet,and thus transfer more thermal and kinetic energy into melt pool,which results in a wider and lower deposited layer with deeper penetration.Moreover,a higher preheat temperature could enlarge melt pool volume and thus enhance heat and mass convection along both axial and radial directions,which gives rise to a wider and higher deposited layer with deeper penetration.These findings offer theoretical guidelines for the acquirement of acceptable deposition shape and optimal deposition quality through adjusting process parameters in fabricating WAAM components.展开更多
基金financially supported by the National Key Research and Development Program of China(Grant No.2020YFB2008300)。
文摘Hot isostatic pressing parameters are critical to Ti60 high temperature titanium alloy castings which have wide application perspective in aerospace.In order to obtain optimal processing parameters,the effects of hot isostatic pressing parameters on defects,composition uniformity,microstructure and mechanical properties of Ti60 cast high temperature titanium alloy were investigated in detail.Results show that increasing temperature and pressure of hot isostatic pressing can reduce defects,especially,the internal defects are substantially eliminated when the temperature exceeds 920℃or the pressure exceeds 125 MPa.The higher temperature and pressure can improve the microstructure uniformity.Besides,the higher pressure can promote the composition uniformity.With the temperature increases from 880℃to 960℃,α-laths are coarsened.But with increasing pressure,the grain size of prior-βphase,the widths ofα-laths andα-colony are reduced.The tensile strength of Ti60 alloy is 949 MPa,yield strength is 827 MPa,and the elongation is 11%when the hot isostatic pressing parameters are 960℃/125 MPa/2 h,which exhibits the best match between the strength and plasticity.
文摘Air plasma spraying process was employed to fabricate various hydroxyapatite(HA)coatings on titanium substrates.The influence of processing parameters on the phase composition and the microstructure of the obtained coatings was investigated.The effect of heat treatment on as-sprayed coating in terms of the crystallinity and microstructure was also studied.The phase composition of coatings was analyzed by X-ray diffraction(XRD)and FTIR.The surface and cross-section morphologies and microstructure of coatings as well as the morphology of feedstock were evaluated using scanning electron microscope(SEM).The crystallization temperature of amorphous HA phase in as-sprayed coating was examined by using differential thermal analysis(DTA). The results suggest that phase composition and microstructure of as-sprayed HA coatings strongly depend on the spraying parameters,and heat treatment at 760 ℃for 2 h is one of effective means for increasing the crystallinity and improvement in microstructure of as-sprayed HA coatings.
文摘Al-3Ti-1B master alloys were prepared at different processing parameters by the reaction of halide salts,and the grain refining response of Al-7Si alloy was investigated with Al-3Ti-B master alloy.The microstructure of master alloy and its grain refining effect on Al-7Si alloy were investigated by means of OM,XRD and SEM.Experimental results show that,the size of Al3Ti particles presented in Al-3Ti-1B master alloys increases with the increase of reaction temperature and decreases with the increase of cooling rate.The grain refining efficiency of Al-3Ti-1B master alloy on Al-7Si alloy is mainly attributed to heterogeneous nucleation of Al3Ti particles,and the morphology ofα(Al)changes from coarse dendritic to fine equiaxed.As a result,Al-3Ti-1B master alloy is prepared by permanent mold,and holding at 800 ℃for 30min,which has better grain refining performance on Al-7Si alloy.
基金The work was supported by the Innovation Fund for Small Technology-based Firms for Harbin DS Numerical Control Equipment Co.,Ltd.Samples,the micro-arcoxidation equipment and chemicals were provided by thecompany。
文摘The influence of processing parameters on the coating surface roughness of LD10 aluminum alloy treated by the power source with positive and negative pulse in the alkaline electrolyte was discussed.Lots of experiments were done with different processing parameters including the positive final voltage,the negative final voltage,the frequency,the duty ratio,the processing time and electrolyte temperature.And the surface roughness tester TR200 was used to measure the coating surface roughness.The influence of the processing time on the surface roughness is the smallest,less than 0.2μm.The surface roughness decreases gradually with the duty ratio decreasing or the frequency increasing;it decreases gradually with each of the other parameters increasing,and then increases gradually after achieving the minimum value.Appropriately by selecting processing parameters,the coating with Ra 0.6 can be obtained.
基金supported by Major Special Science and Technology Project of Yunnan Province 202002AB080001-3the National Natural Science Foundation of China(no.51704088)Fundamental Research and Development Program of China(Grant no.JCKY2017205B032)。
文摘In order to improve the intrinsic brittleness of TiAl alloys,Ti_(2)AlNb alloys with outstanding ductility and toughness at room temperature,and good high-temperature performance are competitive candidates in constructing the TiAl-based laminated composites.In this work,TiAl/Ti_(2)AlNb laminated composites are successfully synthesized by vacuum hot pressing combined with the foil-foil(sheet)metallurgy.Under the pressure of 65 MPa,different holding time and temperature of hot pressing are tried and the optimized fabrication parameter is acquired as 1050℃/120 min/65 MPa.Along with the changes of processing parameters,the defect,microstructure,interface,phase transformation and the corresponding mechanical properties are detailly discussed.The results show that the TiAl/Ti_(2)AlNb laminated composite fabricated at 1050℃ for 2 h achieves a good metallurgical interface bonding.The corresponding interface microstructure is composed of region I and region II.The region I consists of O,α_(2)and B2/βphase,and region II is made up ofα2.Subsequently,the tensile tests indicate that the composite synthesized at 1050℃ for 2 h possesses a maximum strength of 812 MPa and a total elongation of 1.31%at room temperature,and a strength of 539.71 MPa and the highest total elongation of 10.34%at 750℃.The well synergistic deformation ability between the interface and the two base alloys endows the composite an excellent tensile performance.Moreover,the composite processed at 1050℃ for 2 h behaves the best fracture toughness in both arrester orientation and divider orientation with the value of 32.6 MPa.m^(1/2)and 30.1 MPa.m^(1/2),respectively.The Ti_(2)AlNb alloy in the laminated structure effectively release the stress around the crack tip and plays a role in toughening.Further,crack deflection,crack bridging,crack blunting and fragmentation also make contributions to enhance the fracture toughness of the laminated composites.
基金financial support of the National Natural Science Foundation of China(NO.11902255,U1837601 and 52090051).
文摘High-performance thermoplastic composites have been developed as significant structural materials for cutting-edge equipment in the aerospace and defence fields.However,the internal mechanism of processing parameters on mechanical properties in the manufacturing process of thermoplastic composite structures is still a serious challenge.The purpose of this study is to investigate the process/crystallization/property relationships for continuous carbon fiber(CF)reinforced polyether-ether-ketone(PEEK)composites.The composite laminates are fabricated according to orthogonal experiments via the thermoforming method.The mechanical performance is investigated in terms of crystallization properties and fracture morphology characterizations.Experimental results show that the mechanical performance and crystallization properties of thermoplastic composites are significantly affected by the coupling of processing parameters.The increased molding temperature,pressure,and holding time improve the degree of fiber/matrix infiltration and affect the crystallinity and crystalline morphology of the matrix,which further influences the mechanical properties of the composites.This is reflected in the test results that crystallinity has an approximately linear effect on mode-I interlaminar fracture toughness and transverse flexural modulus.As well as the higher molding temperature can destroy the pre-existent crystals to improve the toughness of the matrix,and the well-defined crystalline structures can be observed when fabricated at higher temperatures and longer periods of holding time.
基金National Natural Science Foundation of China(Grant Nos.51875379,52105342)China Scholarship Council via a research collaboration with National University of Singapore Additive Manufacturing Centre.
文摘The unique properties of bulk metallic glass(BMG)render it an excellent material for bone-implant applications.BMG samples are difficult to produce directly because of the critical cooling rate of molding.Advancements in additive manufacturing technologies,such as selective laser melting(SLM),have enabled the development of BMG.The successful production of materials via SLM relies significantly on the processing parameters;meanwhile,the overall energy density affects the crystallization and,thus,the final properties.Therefore,to further determine the effects of the processing parameters,SLM is performed in this study to print Fe-based BMG with different properties three dimensionally using selected processing parameters but a constant energy density.The printed amorphous Fe-based BMG outperforms the typical 316 L stainless steel(316 L SS)in terms of mechanical properties and corrosion resistance.Moreover,observations from nanoindentation tests indicate that the hardness and elastic modulus of the Fe-based BMG can be customized explicitly by adjusting the SLM processing parameters.Indirect cytotoxicity results show that the Fe-based BMG can enhance the viability of SAOS2 cells,as compared with 316 L SS.These intriguing results show that Fe-based BMG should be investigated further for orthopedic implant applications.
基金Supported by National Natural Science Foundation of China(Grant Nos.51965006 and 51875209)Guangxi Natural Science Foundation of China(Grant No.2018GXNSFAA050111)+1 种基金Innovation Project of Guangxi Graduate Education of China(Grant No.YCSW2019035)Open Fund of National Engineering Research Center of Near-Shape Forming for Metallic Materials of China(Grant No.2019001).
文摘Squeeze casting(SC)is an advanced net manufacturing process with many advantages for which the quality and properties of the manufactured parts depend strongly on the process parameters.Unfortunately,a universal efficient method for the determination of optimal process parameters is still unavailable.In view of the shortcomings and development needs of the current research methods for the setting of SC process parameters,by consulting and analyzing the recent research literature on SC process parameters and using the CiteSpace literature analysis software,manual reading and statistical analysis,the current state and characteristics of the research methods used for the determination of SC process parameters are summarized.The literature data show that the number of pub-lications in the literature related to the design of SC process parameters generally trends upward albeit with signifi-cant fluctuations.Analysis of the research focus shows that both“mechanical properties”and“microstructure”are the two main subjects in the studies of SC process parameters.With regard to materials,aluminum alloys have been extensively studied.Five methods have been used to obtain SC process parameters:Physical experiments,numeri-cal simulation,modeling optimization,formula calculation,and the use of empirical values.Physical experiments are the main research methods.The main methods for designing SC process parameters are divided into three categories:Fully experimental methods,optimization methods that involve modeling based on experimental data,and theoreti-cal calculation methods that involve establishing an analytical formula.The research characteristics and shortcomings of each method were analyzed.Numerical simulations and model-based optimization have become the new required methods.Considering the development needs and data-driven trends of the SC process,suggestions for the develop-ment of SC process parameter research have been proposed.
基金Project was supported by National Natural Science Foundation of China(Grant No.62173170).
文摘The successful confinement of the arc by the flux band depends on the welding process parameters for achieving single-pass,multi-layer, and ultra-narrow gap welding. The sidewall fusion depth, the width of the heat-affected zone, and the line energy are utilized as comprehensive indications of the quality of the welded joint. In order to achieve well fusion and reduce the heat input to the base metal.Three welding process characteristics were chosen as the primary determinants, including welding voltage, welding speed, and wire feeding speed. The metamodel of the welding quality index was built by the orthogonal experiments. The metamodel and NSGA-Ⅱ(Non-dominated sorting genetic algorithm Ⅱ) were combined to develop a multi-objective optimization model of ultra-narrow gap welding process parameters. The results showed that the optimized welding process parameters can increase the sidewall fusion depth, reduce the width of the heataffected zone and the line energy, and to some extent improve the overall quality of the ultra-narrow gap welding process.
文摘Lunar surface additive manufacturing with lunar regolith is a key step in in-situ resource utilization.The powder spreading process is the key process,which has a major impact on the quality of the powder bed and the precision of molded parts.In this study,the discrete element method(DEM)was adopted to simulate the powder spreading process with a roller.The three powder bed quality indicators,including the molding layer offset,voidage fraction,and surface roughness,were established.Besides,the influence of the three process parameters,which are roller’s translational speed,rotational speed,and powder spreading layer thickness on the powder bed quality indicators was also analyzed.The results show that with the reduction of the powder spreading layer thickness and the increase of the rotational speed,the offset increased significantly;when the translational speed increased,the offset first increased and then decreased,which resulted in an extreme value;with the increase of the layer thickness and the decrease of the translational speed,the values for voidage fraction and surface roughness significantly reduced.The powder bed quality indicators were adopted as the optimization objective,and the multi-objective parameter optimization was carried out.The predicted optimal powder spreading parameters and powder bed quality indicators were then obtained.Moreover,the optimal values were then verified.This study can provide informative guidance for in-situ manufacturing at the moon in future deep space exploration missions.
基金supported by National Natural Science Foundation of China(Grant Nos.51975202(Junjia Cui received the grant)and 52175315(Guangyao Li received the grant)).
文摘Aluminum alloy thin-walled structures are widely used in the automotive industry due to their advantages related to light weight and crashworthiness.They can be produced at room temperature by the electrohydraulic forming process.In the present study,the influence of the related parameters on the forming quality of a 6063 aluminum alloy sinusoidal corrugation tube has been assessed.In particular,the orthogonal experimental design(OED)and central composite design(CCD)methods have been used.Through the range analysis and variance analysis of the experimental data,the influence degree of wire diameter(WD)and discharge energy(DE)on the forming quality was determined.Multiple regression analysis was performed using the response surface methodology.A prediction model for the attaching-die state coefficient was established accordingly.The following optimal arrangement of parameters was obtained(WD=0.759 mm,DE=2.926 kJ).The attaching-die state coefficient reached the peak value of 0.001.Better optimized wire diameter and discharge energy for a better attaching-die state could be screened by CCD compared with OED.The response surface method in CCD was more suitable for the design and optimization of the considered process parameters.
基金Supported by Heilongjiang Provincial Fruit Tree Modernization Agro-industrial Technology Collaborative Innovation and Promotion System Project(2019-13)。
文摘In order to obtain better quality cookies, food 3D printing technology was employed to prepare cookies. The texture, color, deformation, moisture content, and temperature of the cookie as evaluation indicators, the influences of baking process parameters, such as baking time, surface heating temperature and bottom heating temperature, on the quality of the cookie were studied to optimize the baking process parameters. The results showed that the baking process parameters had obvious effects on the texture, color, deformation, moisture content, and temperature of the cookie. All of the roasting surface heating temperature, bottom heating temperature and baking time had positive influences on the hardness, crunchiness, crispiness, and the total color difference(ΔE) of the cookie. When the heating temperatures of the surfac and bottom increased, the diameter and thickness deformation rate of the cookie increased. However,with the extension of baking time, the diameter and thickness deformation rate of the cookie first increased and then decreased. With the surface heating temperature of 180 ℃, the bottom heating temperature of 150 ℃, and baking time of 15 min, the cookie was crisp and moderate with moderate deformation and uniform color. There was no burnt phenomenon with the desired quality. Research results provided a theoretical basis for cookie manufactory based on food 3D printing technology.
基金financially supported by the the National Natural Science Foundation of China(Nos.51801079 and 52001140)the Natural Science Foundation for Young Scientists of Jiangsu,China(Nos.BK20180985 and BK20180987)the Open Foundation of Zhenjiang Key Laboratory for High Technology Research on Marine Functional Films(No.ZHZ2019001)。
文摘Many studies have investigated the selective laser melting(SLM)of AlSi10Mg and AlSi7Mg alloys,but there are still lack of researches focused on Al-Si-Mg alloys specifically tailored for SLM.In this work,a novel high Mg-content AlSi8Mg3 alloy was specifically designed for SLM.The results showed that this new alloy exhibited excellent SLM processability with a lowest porosity of 0.07%.Massive lattice distortion led to a high Vickers hardness in samples fabricated at a high laser power due to the precipitation of Mg_(2)Si nanoparticles from theα-Al matrix induced by high-intensity intrinsic heat treatment during SLM.The maximum microhardness and compressive yield strength of the alloy reached HV(211±4)and(526±12)MPa,respectively.After aging treatment at 150℃,the maximum microhardness and compressive yield strength of the samples were further improved to HV(221±4)and(577±5)MPa,respectively.These values are higher than those of most known aluminum alloys fabricated by SLM.This paper provides a new idea for optimizing the mechanical properties of Al-Si-Mg alloys fabricated using SLM.
基金financially supported by the National Natural Science Foundation of China(No.51371152)
文摘The large warping deformation at platform of turbine blade directly affects the forming precision. In the present research, equivalent warping deformation was firstly presented to describe the extent of deformation at platform. To optimize the process parameters during investment casting to minimize the warping deformation of the platform, based on simulation with Pro CAST, the single factor method, orthogonal test, neural network and genetic algorithm were subsequently used to analyze the influence of pouring temperature, shell mold preheating temperature, furnace temperature and withdrawal velocity on dimensional accuracy of the platform of superalloyDD6 turbine blade. The accuracy of investment casting simulation was verified by measurement of platform at blade casting. The simulation results with the optimal process parameters illustrate that the equivalent warping deformation was dramatically reduced by 21.8% from 0.232295 mm to 0.181698 mm.
基金National Natural Science Foundation of China (Grant No. 51905382)the Cooperation in Production and Education by Ministry of Education (Grant No. 201802252016)Weifang University Distinguished Professor Support Programme
文摘A certain amount of Ti was added to the plasma cladding Fe-Cr-C coating in the early stage in order to improve the quality and properties of the coating.Ti-Fe-Cr-C composite powder was prepared by precursor carbonization-composition process.In situ synthesized TiC-Fe-Cr coatings were fabricated on substrate of Q235 steel by plasma cladding process with the composite powder.Microstructures of the coatings with different process parameters,including cladding current,cladding speed,number of overlapping cladding layers,were analyzed by scanning electron microscope.The results show that the structure of the TiC-Fe-Cr coating is greatly affected by the cladding current,the cladding speed and the overlapping cladding process.In this test,when the cladding current of 300 A and the cladding process parameter of the cladding speed of 50 mm/min are clad with three layers,a well-formed and well-structured TiC-Fe-Cr coating can be obtained in this test.TiC-Fe-Cr coating has good wear resistance and good load characteristics under dry sliding wear test conditions.
基金Supported by the Open Fund of Key Laboratory of Modern Chinese Medicine Preparations,Ministry of Education,Jiangxi University of Traditional Chinese Medicine and First-class Discipline Construction Project of Jiangxi Province(JXSYLXK-ZHYAO009,JXSYLXK-ZHYAO010)。
文摘The quality standards for Fructus Comi have been established based on the effects of the manufacturing processes.Three critical process parameters(CPPs)of extraction,filtration,and concentration to prepare Fructus Comi concentrate were identified by Plackett-Burman design with a single batch of Fructus Corni,which were heating medium temperature,extraction time,and water addition.Morroniside yield,loganin yield,and dry matter yield were process critical quality attributes(CQAs).CPPs arranged with a Box-Behnken design were applied to treat different batches of Fructus Comi After constructing a model that included CPPs,material propertie s,and process CQAs,loganin content was found to be the critical material attribute(CMA).The design space was calculated with a probability method.According to the limits of process CQAs,the minimum content of loganin in Fructus Corni was calculated with an error propagation method,which was 6.92 mg·g^(-1).When the content of loganin in Fructus Corni reaches up to 6.92 mg·g^(-1),the material is considered high-quality and is most suitable for the process.High-quality material can be used for production of Fructus Comi concentrate.This method can also be used to set material quality standards for other Chinese medicines.
基金supported by the Natural Science Foundation of Guangdong Province(No.2019A1515012040).
文摘As a typical laser additive manufacturing technology,laser powder bed fusion(LPBF)has achieved demonstration applications in aerospace,biomedical and other fields.However,how to select process parameters quickly and reasonably is still themain concern of LPBF production.In order to quantitatively analyze the influence of different process parameters(laser power,scanning speed,hatch space and layer thickness)on the LPBF process,the multilayer and multi-path forming process of LPBF was predicted based on the open-source discrete element method framework Yade and the open-source finite volume method framework OpenFOAM.Based on the design of experiments method,a four-factor three-level orthogonal test scheme was designed,and the porosity and surface roughness data of each calculation scheme were extracted.By analyzing the orthogonal test data,it was found that as the laser power increased,the porosity decreased,and as the scanning speed,hatch space,and layer thickness increased,the porosity increased.In addition,the influence of laser power and scanning speed on surface roughness showed a trend of decreasing first and then increasing,while the influence of scanning distance and layer thickness on surface roughness showed amonotonous increasing trend.The order of the influence of each process parameter on porosity was:scanning speed>laying thickness>laser power>hatch space,and the order of the influence of each process parameter on surface roughness was:hatch space>layer thickness>laser power>scanning speed.So the porosity of the part is most sensitive to scanning speed,and the surface roughness is the most sensitive to hatch space.The above conclusions are expected to provide process control basis for actual LPBF production of the 316L stainless steel alloy.
文摘The relationships between the surface quality of a single crystal copper ingot and the process parameters of heated mould continuous casting method were studied experimentally using our own design of horizontal heated mould continuous casting apparatus, and the mechanism by which process parameters affect the surface quality of a single crystal copper ingot is analyzed in the present paper. The results show that the process parameters affect the surface quality of a pure copper ingot by affecting the position of the liquid-solid interface in the mould. The position of the liquid-solid interface in the mould must be controlled carefully within an appropriate range, which is determined through a series of experiments, in order to gain a single crystal copper ingot with good surface quality.
基金supported by the Key project of Education Department of Hebei Province(Grant No.ZD2019102)。
文摘In this study,friction stir lap welding(FSLW)was performed for the welding test of 6061 aluminium alloy and T2 pure copper.The effect of process parameters containing rotation rate and travel speed on interfacial microstructure evolution and mechanical properties of Al/Cu dissimilar joints were explored.The experiments were carried out under the rotation rates of 600,900 and 1200 r/min and with the travel speeds of 30,70 and 100 mm/min.The characteristic of interface transition zones(ITZs)and the species of intermetallic compounds(IMCs)were investigated.The Al/Cu interface showed a layered structure composed of Al-Cu IMCs,which will affect the mechanical property.The layer consisting of Al2Cu was formed at lower heat input,and as heat input increased the Al4Cu9 phase started to form.Excessive heat input will increase the thickness of the interface and raise the brittleness of the joints.The thickness of the IMCs layers changed from0.89μm to 3.96μm as the heat input increased.The maximum value of tensile shear loading of 4.65 kN was obtained at the rotation rate of900 r/min and travel speed of 100 mm/min with the interface thickness of 2.89μm.The fracture mode of the joints was a mix of ductile and brittle fracture.
基金supported by National Natural Science Foundation of China(Nos.52077172,U1966602)Shaanxi Province‘Sanqin scholar-s’Innovation Team Project(Key technology of advanced DC power equipment and its industrialization demonstration innovation team of Xi’an Jiaotong University)。
文摘Here we develop a two-dimensional numerical model of wire and arc additive manufacturing(WAAM)to determine the relationship between process parameters and deposition geometry,and to reveal the influence mechanism of process parameters on deposition geometry.From the predictive results,a higher wire feed rate matched with a higher current could generate a larger and hotter droplet,and thus transfer more thermal and kinetic energy into melt pool,which results in a wider and lower deposited layer with deeper penetration.Moreover,a higher preheat temperature could enlarge melt pool volume and thus enhance heat and mass convection along both axial and radial directions,which gives rise to a wider and higher deposited layer with deeper penetration.These findings offer theoretical guidelines for the acquirement of acceptable deposition shape and optimal deposition quality through adjusting process parameters in fabricating WAAM components.