A red-emitting phosphor Ca_(2.91)Si_(2)O_(7):0.09Eu^(3+) with partial Al^(3+)/P^(5+) substitution on Si^(4+) was synthesized via a simple solid-state method,and the effects of the introduction of the M^(3+/5+)(M=Al,P)...A red-emitting phosphor Ca_(2.91)Si_(2)O_(7):0.09Eu^(3+) with partial Al^(3+)/P^(5+) substitution on Si^(4+) was synthesized via a simple solid-state method,and the effects of the introduction of the M^(3+/5+)(M=Al,P)ions on the crystal structure and photoluminescence performance of Ca_(2.91)Si_(2−x)M_(x)O_(7):0.09Eu^(3+) phosphors were investigated.The X-ray diffraction(XRD),energy-dispersive X-ray spectroscopy(EDS),and X-ray photoelectron spectroscopy(XPS)results revealed that the structure of Ca_(3)Si_(2)O_(7) remained the same after the introduction of Al^(3+) and P^(5+) ions.The characteristic emission of Eu^(3+)-doped Ca_(3)Si_(2−x)M_(x)O_(7) phosphors exhibited two main peaks at 617 nm(red)and 593 nm(orange)under excitation at 394 nm,which originated from the^(5)D_(0)→^(7)F_(2)and^(5)D_(0)→^(7)F_(1) electron transitions of Eu^(3+) ions.After the partial substitution of Al^(3+) and P^(5+),the red emission intensities of the Ca_(2.91)Si_(2)O_(7):0.09Eu^(3+) phosphors were significantly enhanced by 1.88-and 1.42-fold,respectively,which is attributed to the crystal-field effect around Eu^(3+).Meanwhile,the luminescence intensities of the Ca_(2.91)Si_(1.96)Al_(0.04)O_(7):0.09Eu^(3+) and Ca_(2.91)Si_(1.94)P_(0.06)O_(7):0.09Eu^(3+) phosphors at 210℃ were 79.36%and 77.53%of those at 30°C,respectively,indicating their excellent thermal stability.Moreover,the as-prepared Ca_(2.91)Si_(1.96)Al_(0.04)O_(7):0.09Eu^(3+)and Ca_(2.91)Si_(1.94)P_(0.06)O_(7):0.09Eu^(3+) red-emitting phosphors were combined with a near-ultraviolet chip of 395 nm to fabricate red-light-emitting diode(LED)and white(w)-LED devices with excellent chromaticity features.In summary,Al^(3+)/P^(5+)-substituted Ca_(2.91)Si_(2)O_(7):0.09Eu^(3+) can serve as red-emitting phosphors for applications in w-LEDs.展开更多
基金This work was financially supported by the Department of Science and Technology of Sichuan Province(No.2020YJ0157).
文摘A red-emitting phosphor Ca_(2.91)Si_(2)O_(7):0.09Eu^(3+) with partial Al^(3+)/P^(5+) substitution on Si^(4+) was synthesized via a simple solid-state method,and the effects of the introduction of the M^(3+/5+)(M=Al,P)ions on the crystal structure and photoluminescence performance of Ca_(2.91)Si_(2−x)M_(x)O_(7):0.09Eu^(3+) phosphors were investigated.The X-ray diffraction(XRD),energy-dispersive X-ray spectroscopy(EDS),and X-ray photoelectron spectroscopy(XPS)results revealed that the structure of Ca_(3)Si_(2)O_(7) remained the same after the introduction of Al^(3+) and P^(5+) ions.The characteristic emission of Eu^(3+)-doped Ca_(3)Si_(2−x)M_(x)O_(7) phosphors exhibited two main peaks at 617 nm(red)and 593 nm(orange)under excitation at 394 nm,which originated from the^(5)D_(0)→^(7)F_(2)and^(5)D_(0)→^(7)F_(1) electron transitions of Eu^(3+) ions.After the partial substitution of Al^(3+) and P^(5+),the red emission intensities of the Ca_(2.91)Si_(2)O_(7):0.09Eu^(3+) phosphors were significantly enhanced by 1.88-and 1.42-fold,respectively,which is attributed to the crystal-field effect around Eu^(3+).Meanwhile,the luminescence intensities of the Ca_(2.91)Si_(1.96)Al_(0.04)O_(7):0.09Eu^(3+) and Ca_(2.91)Si_(1.94)P_(0.06)O_(7):0.09Eu^(3+) phosphors at 210℃ were 79.36%and 77.53%of those at 30°C,respectively,indicating their excellent thermal stability.Moreover,the as-prepared Ca_(2.91)Si_(1.96)Al_(0.04)O_(7):0.09Eu^(3+)and Ca_(2.91)Si_(1.94)P_(0.06)O_(7):0.09Eu^(3+) red-emitting phosphors were combined with a near-ultraviolet chip of 395 nm to fabricate red-light-emitting diode(LED)and white(w)-LED devices with excellent chromaticity features.In summary,Al^(3+)/P^(5+)-substituted Ca_(2.91)Si_(2)O_(7):0.09Eu^(3+) can serve as red-emitting phosphors for applications in w-LEDs.