In this paper,C50 ultra-high-early-strength concrete was prepared with rapid-harden sulphoaluminate cement,alkali carbonate early strength agent,inorganic tribasic acid retarder and polycarboxylate water reducing agen...In this paper,C50 ultra-high-early-strength concrete was prepared with rapid-harden sulphoaluminate cement,alkali carbonate early strength agent,inorganic tribasic acid retarder and polycarboxylate water reducing agent. The properties testing results of C50 ultra-high-early-strength concrete indicated that the compressive strength at 12 h exceeded 37 MPa and at 3 d exceeded 59 MPa. Compared to the C50 ordinary reference concrete,the durability of C50 ultra-high-early strength concrete was investigated. The results indicated that C50 ultra-high-early-strength concrete had the same chloride ion permeability resistance,carbonization resistance and abrasion resistance to the C50 ordinary concrete. As to the sulfate resistance,the ultra-high-early-strength concrete was much better than the ordinary concrete.展开更多
基金the financial support from China Communications Construction Company Limited.
文摘In this paper,C50 ultra-high-early-strength concrete was prepared with rapid-harden sulphoaluminate cement,alkali carbonate early strength agent,inorganic tribasic acid retarder and polycarboxylate water reducing agent. The properties testing results of C50 ultra-high-early-strength concrete indicated that the compressive strength at 12 h exceeded 37 MPa and at 3 d exceeded 59 MPa. Compared to the C50 ordinary reference concrete,the durability of C50 ultra-high-early strength concrete was investigated. The results indicated that C50 ultra-high-early-strength concrete had the same chloride ion permeability resistance,carbonization resistance and abrasion resistance to the C50 ordinary concrete. As to the sulfate resistance,the ultra-high-early-strength concrete was much better than the ordinary concrete.