A new type of composite filler was designed by a modified sol-gel method using fly ash(FA),Fe(NO_(3))_(3)·9H_(2)O,and Ni(NO_(3))_(2)·6H_(2)O as raw materials.The composite filler was a spherical core-shell s...A new type of composite filler was designed by a modified sol-gel method using fly ash(FA),Fe(NO_(3))_(3)·9H_(2)O,and Ni(NO_(3))_(2)·6H_(2)O as raw materials.The composite filler was a spherical core-shell structure composed of FA as the core and NiFe_(2)O_(4)as the shell.Further,the composite filler was added into the silicone rubber to fabricate the high temperature vulcanized microwave absorption materials;X-ray diffraction,fourier transform infrared spectroscopy,X-ray photoelectron spectroscopy,and scanning electron microscope confirmed that NiFe_(2)O_(4)was successfully coated on the surface of FA and formed a uniform and continuous coating layer.As expected,silicone rubber filled with the composite filler had a minimum reflection loss of-23.8 dB at 17.5 GHz with the thickness of 1.8 mm,while the effective absorption bandwidth was as high as 12 GHz.The addition of the composite filler greatly enhanced the microwave absorption properties of the system,which was resulted from multiple losses mechanism:interface polarization losses,magnetic losses,and multiple reflection losses.Also,silicone rubber filled with the composite filler exhibited excellent thermal stability,flexibility,environmental resistance,and hydrophobicity compared with traditional silicone rubber.Therefore,this work not only responds to the green chemistry to achieve efficient FA recovery,but also devises a new strategy to prepare microwave absorption materials with strong potential for civilian applications.展开更多
We improved the adhesion between silicon based insulating materials and epoxy resin composites by adding the adhesion promoter cycloborosiloxane(BSi,cyclo-1,3,3,5,7,7-hexaphenyl-1,5-diboro-3,7-disiloxane).The experime...We improved the adhesion between silicon based insulating materials and epoxy resin composites by adding the adhesion promoter cycloborosiloxane(BSi,cyclo-1,3,3,5,7,7-hexaphenyl-1,5-diboro-3,7-disiloxane).The experimental results show that the addition of BSi in the silicone rubber(SR)system significantly increases the tensile shear strength between BSi and epoxy resin(EP),reaching 309%of the original value.On this basis,the mechanism of BSi to enhance the adhesion effect was discussed.The electron deficient B in BSi attracted the electron rich N and O in EP to enhance the chemical interaction,combined with the interfacial migration behavior in the curing process,to improve the adhesion strength.This study provides the design and synthesis ideas of adhesive aids,and a reference for further exploring the interface mechanism of epoxy resin matrix composites.展开更多
By means of the wet chemical surface modification,the surface of CeO_2 was modified by vinyltrimethoxysilane (VTMS).Infrared spectroscopy was used to investigate the structure of the modified CeO_2 and the result show...By means of the wet chemical surface modification,the surface of CeO_2 was modified by vinyltrimethoxysilane (VTMS).Infrared spectroscopy was used to investigate the structure of the modified CeO_2 and the result showed that VTMS has been attached onto the surface of CeO_2.Effect of VTMS concentration on the active index of the modified CeO_2 was also studied,and the result indicated that the active index of the modified CeO_2 increases with the increase of VTMS concentration and the optimal concentration o...展开更多
To study the effects of different proportions of aluminum hydroxide and expandable graphite （EG） composites on flame retardation, sealing, mechanical, electrical and other properties of RTV- 1, aluminum hydroxide/ex...To study the effects of different proportions of aluminum hydroxide and expandable graphite （EG） composites on flame retardation, sealing, mechanical, electrical and other properties of RTV- 1, aluminum hydroxide/expandable graphite （ATH/EG） and silicone rubber composites were prepared by the compression molding method. The experimental results show that heat resistance improves with the increase of proportion of EG. Although the resistance coefficient changes, the composite materials still keep good electrical insulating property. Moreover, oxygen index and expansion index rise first then fall. When ATH/EG is 1：1, the oxygen index reaches the highest; the mechanical property of the silicone rubber is not affected under various environments such as acid, alkali, oily, artificial sea water environments, etc.展开更多
In this paper,work was conducted to reveal electrical tree behaviors（initiation and propagation）of silicone rubber（SIR） under an impulse voltage with high temperature.Impulse frequencies ranging from 10 Hz to 1 k ...In this paper,work was conducted to reveal electrical tree behaviors（initiation and propagation）of silicone rubber（SIR） under an impulse voltage with high temperature.Impulse frequencies ranging from 10 Hz to 1 k Hz were applied and the temperature was controlled between 30 °C and 90 °C.Experimental results show that tree initiation voltage decreases with increasing pulse frequency,and the descending amplitude is different in different frequency bands.As the pulse frequency increases,more frequent partial discharges occur in the channel,increasing the tree growth rate and the final shape intensity.As for temperature,the initiation voltage decreases and the tree shape becomes denser as the temperature gets higher.Based on differential scanning calorimetry results,we believe that partial segment relaxation of SIR at high temperature leads to a decrease in the initiation voltage.However,the tree growth rate decreases with increasing temperature.Carbonization deposition in the channel under high temperature was observed under microscope and proven by Raman analysis.Different tree growth models considering tree channel characteristics are proposed.It is believed that increasing the conductivity in the tree channel restrains the partial discharge,holding back the tree growth at high temperature.展开更多
We have shown that some phenylethynylsilicon compounds are good cure crosslinkersof heat-curable silicone rubber(HCSR). In this paper the effects of 1, 1, 3, 3-tetramethyl-1, 3-diphenylethynyldisiloxane (TMDPDS) as a ...We have shown that some phenylethynylsilicon compounds are good cure crosslinkersof heat-curable silicone rubber(HCSR). In this paper the effects of 1, 1, 3, 3-tetramethyl-1, 3-diphenylethynyldisiloxane (TMDPDS) as a crosslinker on HCSR were studied. Thevulcanizates with fine mechanical properties could be obtained with suitable amounts ofTMDPDS. Sol fractions, and crosslinking density of vulcanizates and vulcanizationretardation effect of TMDPDS on hydrosilation curing silicone rubber were also discussed.展开更多
Hydrophobic nano silica sol(HNSS)was incorporated into polyvinylmethylsiloxane to prepare reinforced high- temperature vulcanized(HTV)silicone rubber.HTV silicone rubber filled with 40 phr HNSS showed excellent mechan...Hydrophobic nano silica sol(HNSS)was incorporated into polyvinylmethylsiloxane to prepare reinforced high- temperature vulcanized(HTV)silicone rubber.HTV silicone rubber filled with 40 phr HNSS showed excellent mechanical and optical properties:the tensile strength reached 11.7 MPa and the optical transmittance was higher than 90%.Possible reasons for reinforcement and transparency were discussed on the basis of the bound rubber percentage,total crosslink density,and SEM analysis.Our work suggests that HNSS...展开更多
In this paper, the damage to methyl silicone rubber induced by irradiation with protons of 150 keV energy wasstudied. The surface morphology, tensile strength, Shore hardness, cross-linking density and glass transitio...In this paper, the damage to methyl silicone rubber induced by irradiation with protons of 150 keV energy wasstudied. The surface morphology, tensile strength, Shore hardness, cross-linking density and glass transition temperaturewere examined. Positron annihilation lifetime spectrum analysis (PALS) was perfomed to reveal the damage mechanisms ofthe rubber. The results showed that tensile strength and Shore hardness of the rubber increased first and then decreased withincreasing irradiation fluence. The PALS characteristics τ_3 and I_3, as well as the free volume V_f, decreased with increasingirradiation fluence up to 10^(15) cm^(-2), and then increased slowly. It indicates that proton irradiation causes a decrease of freevolume in the methyl silicone rubber when the fluence is less than 10^(15)cm^(-2), while the free volume increases when thefluence is greater than 10^(15)cm^(-2). The results on cross-linking density indicate that the cross-linking induced by protonirradiation is dominant at smaller proton fluences, increasing the tensile strength and Shore hardness of the rubber, while thedegradation of rubber dominates at greater fluence, leading to a decrease of tensile strength and Shore hardness.展开更多
Silicone rubber (SIR) shows superior performance when used outdoors, but its surface can be transformed from inherently hydrophobic to hydrophilic by the adsorption of contaminants. Al(OH)(3), Al2O3, quartz powder and...Silicone rubber (SIR) shows superior performance when used outdoors, but its surface can be transformed from inherently hydrophobic to hydrophilic by the adsorption of contaminants. Al(OH)(3), Al2O3, quartz powder and active carbon were selected as authentic contaminants. Hydrophobicity of the surface was determined using contact angle measurement. The results indicate that the adsorbability of the contaminants can strongly affect the hydrophobicity of contaminated SIR surface. The increasing rate of contact angle of specimens contaminated by Al(OH)(3) was much faster than that by Al2O3 and quartz due to the adsorption of migrated low molecular weight (LMW) polydimethylsiloxanes. Specimens contaminated by active carbon could achieve surface hydrophobicity within 15 min because active carbon has high adsorbability. Surfaces of contaminated ultrapure SIR, polytetrafluoroethylene (PTFE) and glass remain hydrophilic because they contain no mobile LMW components. The addition of oligomeric polydimethylsiloxanes has little effect on the hydrophobicity of contaminants covered on SIR surface.展开更多
The natural attapulgite(NAPT)was disaggregated by high-pressure homogenization technology combined with extrusion process to prepare the attapulgite with disaggregated rod crystal bundles(DAPT)and large specific surfa...The natural attapulgite(NAPT)was disaggregated by high-pressure homogenization technology combined with extrusion process to prepare the attapulgite with disaggregated rod crystal bundles(DAPT)and large specific surface area of 133.7 m^(2)/g.NAPT and DAPT were incorporated into the silicone rubber to obtain the composite NAPTSR and DAPT-SR by mechanical blending method,respectively.After thermal oxidative ageing at 300℃ for 0.5 h,temperature for the 5%weight loss increased greatly from 385℃ of the neat silicone rubber to 396-399℃ with addition of NAPT and DAPT.NAPT and DAPT enhanced the interaction between the filler nanoparticles and rubber matrix thus inhibited the nanoparticle agglomeration.The conservation rate of the side methyl group in NAPT-SR and DAPT-SR was greatly improved after ageing.Therefore,the thermal oxidative degradation and ageing performance of the silicone rubber composites was significantly reinforced.Moreover,DAPT could greatly restrain the growth of nanoparticles after ageing.Therefore,DAPT-SR showed the better retention of tensile strength(40.6%),elongation at break(34.9%)and tear strength(30.1%)compared with the corresponding mechanical properties of the neat silicone rubber(10.6%,7.4%,and 5.0%)after ageing.展开更多
The damage effects and mechanisms of proton irradiation with 50-200 keV energy to space-grade methyl silicone rubber was performed using a ground-based simulator for space irradiation environment. The changes in surfa...The damage effects and mechanisms of proton irradiation with 50-200 keV energy to space-grade methyl silicone rubber was performed using a ground-based simulator for space irradiation environment. The changes in surface morphology, mechanicai properties, cross-linking density, glass temperature, infrared attenuated total reflection spectrum, mass spectrum and pyrolysis gas chromatography-mass spectrum indicated that, under lower energy, the proton irradiation would induce cross-linking effect, resulting in an increase in tensile strengths and hardness of the methyl silicon rubber. However, after the irradiation of protons for more than 150 keV, the irradiation induced degradation, which decreased the tensile strengths and hardness, became a dominant effect. A macromolecular network destruction modei for the silicone rubber radiated vvith the protons was proposed.展开更多
A novel EVA/unmodified nano-magnesium hydroxide （NMH）/silicone rubber ternary nanocomposite was prepared by using a special compound flame retardant of NMH and silicone rubber （CFR）. The flammability of the ternar...A novel EVA/unmodified nano-magnesium hydroxide （NMH）/silicone rubber ternary nanocomposite was prepared by using a special compound flame retardant of NMH and silicone rubber （CFR）. The flammability of the ternary composite was studied by cone calorimeter test （CCT）. Synergistic effect on flame retardancy was found between silicone rubber and NMH. EVA/CFR ternary nanocomposite showed the lowest peak heat release rate （PHRR） and mass loss rate （MLR） among the samples of virgin EVA, EVA composites. The synergistic flame retardancy of silicone rubber and NMH in EVA system is attributed to the enhanced char layers in the condensed phase that prevents the heat and mass transfer in the fire.展开更多
The dynamic stiffness and the specific damping energy, as well as the vibration response characteristics of a silicone rubber isolator were researched. The results of the vibration test showed that the silicone rubber...The dynamic stiffness and the specific damping energy, as well as the vibration response characteristics of a silicone rubber isolator were researched. The results of the vibration test showed that the silicone rubber isolator was excellent in the performance of vibration control. The dynamic stiffness and the damping characteristics were non-linear. From the comparison between experimental results and simulation analysis, the displacement transmissibility characteristics of the isolator were obtained. As a result, the dynamic characteristics of the isolator could be accurately described by the quadratic type non-linear terms at small amolitude.展开更多
An atmospheric-pressure plasma jet array specially designed for HTV silicone rubber treatment is reported in this paper. Stable plasma containing highly energetic active particles was uniformly generated in the plasma...An atmospheric-pressure plasma jet array specially designed for HTV silicone rubber treatment is reported in this paper. Stable plasma containing highly energetic active particles was uniformly generated in the plasma jet array. The discharge pattern was affected by the applied voltage. The divergence phenomenon was observed at low gas flow rate and abated when the flow rate increased.Temperature of the plasma plume is close to room temperature which makes it feasible for temperature-sensitive material treatment. Hydrophobicity of contaminated HTV silicone rubber was significantly improved after quick exposure of the plasma jet array, and the effective treatment area reached 120 mm？×？50 mm（length？×？width）. Reactive particles in the plasma accelerate accumulation of the hydrophobic molecules, namely low molecular weight silicone chains, on the contaminated surface, which result in a hydrophobicity improvement of the HTV silicone rubber.展开更多
All antifouling paints in use today are effective because toxic ingredients based on heavy metals are included in their formulation, the environmental effects of organotins in seawater have been a topic of much intere...All antifouling paints in use today are effective because toxic ingredients based on heavy metals are included in their formulation, the environmental effects of organotins in seawater have been a topic of much interest and concern in recent years. This study has found that the material of rich silicone rubber on coating surface based on the low discursive component of surface energy makes barnacle settling on them unable to attach permanently and is removed by moving water. The material Permits only small amounts of fouling to attach, such as algae, Ciona intestinalis, because the high polar interaction of coating surface may absorb water to form water film in sea, and cause very low adhesion of the fouling spotes.展开更多
The hydrophobicity of polluted silicone rubber was improved rapidly under plasma jet treatment.It is an important phenomenon of the interaction between the plasma jet and the porous surface,and shows a wide applicatio...The hydrophobicity of polluted silicone rubber was improved rapidly under plasma jet treatment.It is an important phenomenon of the interaction between the plasma jet and the porous surface,and shows a wide application prospect in the power system.In this process,the spatial characteristics and dose of plasma jet are very important.Therefore,the variation of hydrophobicity of polluted silicone rubber under plasma jet treatment was studied,and the spatial characteristics and dose of plasma jet on polluted silicone rubber were also investigated in the work.The results show that the surface property(hydrophilic or hydrophobic)depended on the dose of plasma applied to the surface.The effective treated area was a circle,and the contact angles changed along the radial direction of the circle.This was attributable to the diffusion of plasma bullets on the surface and the distribution of plasma species.The plasma dose could be characterized by the energy density of the plasma applied on the surface.With the increase of plasma dose,the surface contact angles first increased rapidly and then decreased gradually.展开更多
In the present work, tracking phenomenon in Silicone rubber material has beenstudied under AC and DC voltage, with ammonium chloride as a contaminant. It is observed that thetracking is more severe under the DC voltag...In the present work, tracking phenomenon in Silicone rubber material has beenstudied under AC and DC voltage, with ammonium chloride as a contaminant. It is observed that thetracking is more severe under the DC voltages. The tracking time is less under negative DC comparedto the positive DC voltage. The tracking mechanism is explained in detail. The leakage currentduring the tracking studies was as measured and the moving average technique was adopted tounderstand the trend in current flow. The leakage current magnitude is high with thermally agedspecimens compared to the virgin specimen, irrespective of the type of applied voltage. It isrealized that the tracking time and the leakage current magnitude shows an inverse relationship.展开更多
Allyl terminated polyether was used to improve the hydrophilicity of addition-cured room temperature vulcanization silicone rubber. With the increasing of the polyether, both the hydrophilicity and water absorbed of t...Allyl terminated polyether was used to improve the hydrophilicity of addition-cured room temperature vulcanization silicone rubber. With the increasing of the polyether, both the hydrophilicity and water absorbed of the vulcanizates were increased. The mechanical properties were also improved by adding the polyether. The result showed that 1.5wt% of the polyether provided the silicone rubber with proper hydrophilicity.展开更多
Self-vulcanizing blends of phenol hydroxy silicone rubber (PHSR) and fluoroelastomer (FPM) were prepared. Vulcanized rubbers with lower glass transition temperature (T(g)) were successfully obtained. The results of dy...Self-vulcanizing blends of phenol hydroxy silicone rubber (PHSR) and fluoroelastomer (FPM) were prepared. Vulcanized rubbers with lower glass transition temperature (T(g)) were successfully obtained. The results of dynamic mechanical analysis (DMA) show that the vulcanized FPM/PHSR (10 phr) blend has only one T(g) temperature, demonstrating the well compatibility between FPM and PHSR. The thermogravimetric analysis (TGA) demonstrates that the PHSR do little damage to the thermal stability of FPM. The vulcanization characteristics of the FPM/PHSR blends were analyzed by using oscillating disc rheometer (ODR). The results show that FPM/PHSR blends have smaller S(min) values and longer scorch time than that of FPM with the same level of bisphenol AF curing agent. It means that FPM/PHSR blends have better processability and curing security. Better mechanical properties can be gained for FPM/PHSR blends at appropriate level of PHSR.展开更多
Peroxide-cured high-temperature vulcanized （HTV） silicone rubber was prepared by using allyl-capped carbosilane dendrimers, in which the core molecule is Si（CHaCH=CH2）4, as the cross-linker. It showed that this ki...Peroxide-cured high-temperature vulcanized （HTV） silicone rubber was prepared by using allyl-capped carbosilane dendrimers, in which the core molecule is Si（CHaCH=CH2）4, as the cross-linker. It showed that this kind of allyl-capped carbosilane dendrimer improved the mechanical properties of silicone rubber.展开更多
文摘A new type of composite filler was designed by a modified sol-gel method using fly ash(FA),Fe(NO_(3))_(3)·9H_(2)O,and Ni(NO_(3))_(2)·6H_(2)O as raw materials.The composite filler was a spherical core-shell structure composed of FA as the core and NiFe_(2)O_(4)as the shell.Further,the composite filler was added into the silicone rubber to fabricate the high temperature vulcanized microwave absorption materials;X-ray diffraction,fourier transform infrared spectroscopy,X-ray photoelectron spectroscopy,and scanning electron microscope confirmed that NiFe_(2)O_(4)was successfully coated on the surface of FA and formed a uniform and continuous coating layer.As expected,silicone rubber filled with the composite filler had a minimum reflection loss of-23.8 dB at 17.5 GHz with the thickness of 1.8 mm,while the effective absorption bandwidth was as high as 12 GHz.The addition of the composite filler greatly enhanced the microwave absorption properties of the system,which was resulted from multiple losses mechanism:interface polarization losses,magnetic losses,and multiple reflection losses.Also,silicone rubber filled with the composite filler exhibited excellent thermal stability,flexibility,environmental resistance,and hydrophobicity compared with traditional silicone rubber.Therefore,this work not only responds to the green chemistry to achieve efficient FA recovery,but also devises a new strategy to prepare microwave absorption materials with strong potential for civilian applications.
基金the Core Research Facilities of College of Chemistry and Molecular Sciences and Wuhan University Test Center and Open Fund of Hubei Key Laboratory of Aerospace Power Advanced Technologythe Open Fund of Hubei Key Laboratory of Aerospace Power Advanced Technologythe Special Fund for Industrial and informatization Industry Foundation Reconstruction and High Quality Development of Manufacturing Industry(No.TC220H068)。
文摘We improved the adhesion between silicon based insulating materials and epoxy resin composites by adding the adhesion promoter cycloborosiloxane(BSi,cyclo-1,3,3,5,7,7-hexaphenyl-1,5-diboro-3,7-disiloxane).The experimental results show that the addition of BSi in the silicone rubber(SR)system significantly increases the tensile shear strength between BSi and epoxy resin(EP),reaching 309%of the original value.On this basis,the mechanism of BSi to enhance the adhesion effect was discussed.The electron deficient B in BSi attracted the electron rich N and O in EP to enhance the chemical interaction,combined with the interfacial migration behavior in the curing process,to improve the adhesion strength.This study provides the design and synthesis ideas of adhesive aids,and a reference for further exploring the interface mechanism of epoxy resin matrix composites.
基金the Science and Technology Department of Zhejiang Province(No.2006C21072)
文摘By means of the wet chemical surface modification,the surface of CeO_2 was modified by vinyltrimethoxysilane (VTMS).Infrared spectroscopy was used to investigate the structure of the modified CeO_2 and the result showed that VTMS has been attached onto the surface of CeO_2.Effect of VTMS concentration on the active index of the modified CeO_2 was also studied,and the result indicated that the active index of the modified CeO_2 increases with the increase of VTMS concentration and the optimal concentration o...
文摘To study the effects of different proportions of aluminum hydroxide and expandable graphite （EG） composites on flame retardation, sealing, mechanical, electrical and other properties of RTV- 1, aluminum hydroxide/expandable graphite （ATH/EG） and silicone rubber composites were prepared by the compression molding method. The experimental results show that heat resistance improves with the increase of proportion of EG. Although the resistance coefficient changes, the composite materials still keep good electrical insulating property. Moreover, oxygen index and expansion index rise first then fall. When ATH/EG is 1：1, the oxygen index reaches the highest; the mechanical property of the silicone rubber is not affected under various environments such as acid, alkali, oily, artificial sea water environments, etc.
基金supported in part by National Basic Research Program of China(973 Project)(No.2014CB239501)National Natural Science Foundation of China(Nos.51707100,51377089)+1 种基金State Key Laboratory of Electrical Insulation and Power Equipment(No.EIPE16208)China Postdoctoral Science Foundation(No.2016M591176)
文摘In this paper,work was conducted to reveal electrical tree behaviors（initiation and propagation）of silicone rubber（SIR） under an impulse voltage with high temperature.Impulse frequencies ranging from 10 Hz to 1 k Hz were applied and the temperature was controlled between 30 °C and 90 °C.Experimental results show that tree initiation voltage decreases with increasing pulse frequency,and the descending amplitude is different in different frequency bands.As the pulse frequency increases,more frequent partial discharges occur in the channel,increasing the tree growth rate and the final shape intensity.As for temperature,the initiation voltage decreases and the tree shape becomes denser as the temperature gets higher.Based on differential scanning calorimetry results,we believe that partial segment relaxation of SIR at high temperature leads to a decrease in the initiation voltage.However,the tree growth rate decreases with increasing temperature.Carbonization deposition in the channel under high temperature was observed under microscope and proven by Raman analysis.Different tree growth models considering tree channel characteristics are proposed.It is believed that increasing the conductivity in the tree channel restrains the partial discharge,holding back the tree growth at high temperature.
文摘We have shown that some phenylethynylsilicon compounds are good cure crosslinkersof heat-curable silicone rubber(HCSR). In this paper the effects of 1, 1, 3, 3-tetramethyl-1, 3-diphenylethynyldisiloxane (TMDPDS) as a crosslinker on HCSR were studied. Thevulcanizates with fine mechanical properties could be obtained with suitable amounts ofTMDPDS. Sol fractions, and crosslinking density of vulcanizates and vulcanizationretardation effect of TMDPDS on hydrosilation curing silicone rubber were also discussed.
基金the National Natural Science Foundation of China(Nos.50533050,20490220 and 20404008)the Special Funds for Major State Basic Research Projects of China(No.2003CB615600)
文摘Hydrophobic nano silica sol(HNSS)was incorporated into polyvinylmethylsiloxane to prepare reinforced high- temperature vulcanized(HTV)silicone rubber.HTV silicone rubber filled with 40 phr HNSS showed excellent mechanical and optical properties:the tensile strength reached 11.7 MPa and the optical transmittance was higher than 90%.Possible reasons for reinforcement and transparency were discussed on the basis of the bound rubber percentage,total crosslink density,and SEM analysis.Our work suggests that HNSS...
文摘In this paper, the damage to methyl silicone rubber induced by irradiation with protons of 150 keV energy wasstudied. The surface morphology, tensile strength, Shore hardness, cross-linking density and glass transition temperaturewere examined. Positron annihilation lifetime spectrum analysis (PALS) was perfomed to reveal the damage mechanisms ofthe rubber. The results showed that tensile strength and Shore hardness of the rubber increased first and then decreased withincreasing irradiation fluence. The PALS characteristics τ_3 and I_3, as well as the free volume V_f, decreased with increasingirradiation fluence up to 10^(15) cm^(-2), and then increased slowly. It indicates that proton irradiation causes a decrease of freevolume in the methyl silicone rubber when the fluence is less than 10^(15)cm^(-2), while the free volume increases when thefluence is greater than 10^(15)cm^(-2). The results on cross-linking density indicate that the cross-linking induced by protonirradiation is dominant at smaller proton fluences, increasing the tensile strength and Shore hardness of the rubber, while thedegradation of rubber dominates at greater fluence, leading to a decrease of tensile strength and Shore hardness.
文摘Silicone rubber (SIR) shows superior performance when used outdoors, but its surface can be transformed from inherently hydrophobic to hydrophilic by the adsorption of contaminants. Al(OH)(3), Al2O3, quartz powder and active carbon were selected as authentic contaminants. Hydrophobicity of the surface was determined using contact angle measurement. The results indicate that the adsorbability of the contaminants can strongly affect the hydrophobicity of contaminated SIR surface. The increasing rate of contact angle of specimens contaminated by Al(OH)(3) was much faster than that by Al2O3 and quartz due to the adsorption of migrated low molecular weight (LMW) polydimethylsiloxanes. Specimens contaminated by active carbon could achieve surface hydrophobicity within 15 min because active carbon has high adsorbability. Surfaces of contaminated ultrapure SIR, polytetrafluoroethylene (PTFE) and glass remain hydrophilic because they contain no mobile LMW components. The addition of oligomeric polydimethylsiloxanes has little effect on the hydrophobicity of contaminants covered on SIR surface.
基金supported by the Key Special Program on the S&T for the Pollution Control and Treatment of Water Bodies (No.2017ZX07603-003)。
文摘The natural attapulgite(NAPT)was disaggregated by high-pressure homogenization technology combined with extrusion process to prepare the attapulgite with disaggregated rod crystal bundles(DAPT)and large specific surface area of 133.7 m^(2)/g.NAPT and DAPT were incorporated into the silicone rubber to obtain the composite NAPTSR and DAPT-SR by mechanical blending method,respectively.After thermal oxidative ageing at 300℃ for 0.5 h,temperature for the 5%weight loss increased greatly from 385℃ of the neat silicone rubber to 396-399℃ with addition of NAPT and DAPT.NAPT and DAPT enhanced the interaction between the filler nanoparticles and rubber matrix thus inhibited the nanoparticle agglomeration.The conservation rate of the side methyl group in NAPT-SR and DAPT-SR was greatly improved after ageing.Therefore,the thermal oxidative degradation and ageing performance of the silicone rubber composites was significantly reinforced.Moreover,DAPT could greatly restrain the growth of nanoparticles after ageing.Therefore,DAPT-SR showed the better retention of tensile strength(40.6%),elongation at break(34.9%)and tear strength(30.1%)compared with the corresponding mechanical properties of the neat silicone rubber(10.6%,7.4%,and 5.0%)after ageing.
文摘The damage effects and mechanisms of proton irradiation with 50-200 keV energy to space-grade methyl silicone rubber was performed using a ground-based simulator for space irradiation environment. The changes in surface morphology, mechanicai properties, cross-linking density, glass temperature, infrared attenuated total reflection spectrum, mass spectrum and pyrolysis gas chromatography-mass spectrum indicated that, under lower energy, the proton irradiation would induce cross-linking effect, resulting in an increase in tensile strengths and hardness of the methyl silicon rubber. However, after the irradiation of protons for more than 150 keV, the irradiation induced degradation, which decreased the tensile strengths and hardness, became a dominant effect. A macromolecular network destruction modei for the silicone rubber radiated vvith the protons was proposed.
基金This work was subsidized by the Special Funds for Major State Basic Research Projects(No.2005CB623800).
文摘A novel EVA/unmodified nano-magnesium hydroxide （NMH）/silicone rubber ternary nanocomposite was prepared by using a special compound flame retardant of NMH and silicone rubber （CFR）. The flammability of the ternary composite was studied by cone calorimeter test （CCT）. Synergistic effect on flame retardancy was found between silicone rubber and NMH. EVA/CFR ternary nanocomposite showed the lowest peak heat release rate （PHRR） and mass loss rate （MLR） among the samples of virgin EVA, EVA composites. The synergistic flame retardancy of silicone rubber and NMH in EVA system is attributed to the enhanced char layers in the condensed phase that prevents the heat and mass transfer in the fire.
文摘The dynamic stiffness and the specific damping energy, as well as the vibration response characteristics of a silicone rubber isolator were researched. The results of the vibration test showed that the silicone rubber isolator was excellent in the performance of vibration control. The dynamic stiffness and the damping characteristics were non-linear. From the comparison between experimental results and simulation analysis, the displacement transmissibility characteristics of the isolator were obtained. As a result, the dynamic characteristics of the isolator could be accurately described by the quadratic type non-linear terms at small amolitude.
基金supported in part by National Natural Science Foundation of China (Grant No. 51677105)Key project of Shenzhen Technology Innovation Plan (JSGG20170412151407005)
文摘An atmospheric-pressure plasma jet array specially designed for HTV silicone rubber treatment is reported in this paper. Stable plasma containing highly energetic active particles was uniformly generated in the plasma jet array. The discharge pattern was affected by the applied voltage. The divergence phenomenon was observed at low gas flow rate and abated when the flow rate increased.Temperature of the plasma plume is close to room temperature which makes it feasible for temperature-sensitive material treatment. Hydrophobicity of contaminated HTV silicone rubber was significantly improved after quick exposure of the plasma jet array, and the effective treatment area reached 120 mm？×？50 mm（length？×？width）. Reactive particles in the plasma accelerate accumulation of the hydrophobic molecules, namely low molecular weight silicone chains, on the contaminated surface, which result in a hydrophobicity improvement of the HTV silicone rubber.
文摘All antifouling paints in use today are effective because toxic ingredients based on heavy metals are included in their formulation, the environmental effects of organotins in seawater have been a topic of much interest and concern in recent years. This study has found that the material of rich silicone rubber on coating surface based on the low discursive component of surface energy makes barnacle settling on them unable to attach permanently and is removed by moving water. The material Permits only small amounts of fouling to attach, such as algae, Ciona intestinalis, because the high polar interaction of coating surface may absorb water to form water film in sea, and cause very low adhesion of the fouling spotes.
基金supported by the Intergovernmental International Cooperation in Science and Technology Innovation Program(No.2019YFE0115600)National Natural Science Foundation of China(No.52177152)Science,Technology and Innovation Commission of Shenzhen Municipality(No.JCYJ20180508152057527)。
文摘The hydrophobicity of polluted silicone rubber was improved rapidly under plasma jet treatment.It is an important phenomenon of the interaction between the plasma jet and the porous surface,and shows a wide application prospect in the power system.In this process,the spatial characteristics and dose of plasma jet are very important.Therefore,the variation of hydrophobicity of polluted silicone rubber under plasma jet treatment was studied,and the spatial characteristics and dose of plasma jet on polluted silicone rubber were also investigated in the work.The results show that the surface property(hydrophilic or hydrophobic)depended on the dose of plasma applied to the surface.The effective treated area was a circle,and the contact angles changed along the radial direction of the circle.This was attributable to the diffusion of plasma bullets on the surface and the distribution of plasma species.The plasma dose could be characterized by the energy density of the plasma applied on the surface.With the increase of plasma dose,the surface contact angles first increased rapidly and then decreased gradually.
文摘In the present work, tracking phenomenon in Silicone rubber material has beenstudied under AC and DC voltage, with ammonium chloride as a contaminant. It is observed that thetracking is more severe under the DC voltages. The tracking time is less under negative DC comparedto the positive DC voltage. The tracking mechanism is explained in detail. The leakage currentduring the tracking studies was as measured and the moving average technique was adopted tounderstand the trend in current flow. The leakage current magnitude is high with thermally agedspecimens compared to the virgin specimen, irrespective of the type of applied voltage. It isrealized that the tracking time and the leakage current magnitude shows an inverse relationship.
文摘Allyl terminated polyether was used to improve the hydrophilicity of addition-cured room temperature vulcanization silicone rubber. With the increasing of the polyether, both the hydrophilicity and water absorbed of the vulcanizates were increased. The mechanical properties were also improved by adding the polyether. The result showed that 1.5wt% of the polyether provided the silicone rubber with proper hydrophilicity.
基金supported by the National Natural Science Foundation of China(No.50873036).
文摘Self-vulcanizing blends of phenol hydroxy silicone rubber (PHSR) and fluoroelastomer (FPM) were prepared. Vulcanized rubbers with lower glass transition temperature (T(g)) were successfully obtained. The results of dynamic mechanical analysis (DMA) show that the vulcanized FPM/PHSR (10 phr) blend has only one T(g) temperature, demonstrating the well compatibility between FPM and PHSR. The thermogravimetric analysis (TGA) demonstrates that the PHSR do little damage to the thermal stability of FPM. The vulcanization characteristics of the FPM/PHSR blends were analyzed by using oscillating disc rheometer (ODR). The results show that FPM/PHSR blends have smaller S(min) values and longer scorch time than that of FPM with the same level of bisphenol AF curing agent. It means that FPM/PHSR blends have better processability and curing security. Better mechanical properties can be gained for FPM/PHSR blends at appropriate level of PHSR.
文摘Peroxide-cured high-temperature vulcanized （HTV） silicone rubber was prepared by using allyl-capped carbosilane dendrimers, in which the core molecule is Si（CHaCH=CH2）4, as the cross-linker. It showed that this kind of allyl-capped carbosilane dendrimer improved the mechanical properties of silicone rubber.