Within the past ten years,spark plasma sintering(SPS)has become an increasingly popular process for Mg manufacturing.In the SPS process,interparticle diffusion of compressed particles is rapidly achieved due to the co...Within the past ten years,spark plasma sintering(SPS)has become an increasingly popular process for Mg manufacturing.In the SPS process,interparticle diffusion of compressed particles is rapidly achieved due to the concept of Joule heating.Compared to traditional and additive manufacturing(AM)techniques,SPS gives unique control of the structural and microstructural features of Mg components.By doing so,their mechanical,tribological,and corrosion properties can be tailored.Although great advancements in this field have been made,these pieces of knowledge are scattered and have not been contextualized into a single work.The motivation of this work is to address this scientific gap and to provide a groundwork for understanding the basics of SPS manufacturing for Mg.To do so,the existing body of SPS Mg literature was first surveyed,with a focus on their structural formation and degradation mechanisms.It was found that successful Mg SPS fabrication highly depended on the processing temperature,particle size,and particle crystallinity.The addition of metal and ceramic composites also affected their microstructural features due to the Zener pinning effect.In degradative environments,their performance depends on their structural features and whether they have secondary phased composites.In industrial applications,SPS'd Mg was found to have great potential in biomedical,hydrogen storage,battery,automotive,and recycling sectors.The prospects to advance the field include using Mg as a doping agent for crystallite size refinement and using bulk metallic Mg-based glass powders for amorphous SPS components.Despite these findings,the interactions of multi-composites on the processing-structure-property relationships of SPS Mg is not well understood.In total,this work will provide a useful direction in the SPS field and serve as a milestone for future Mg-based SPS manufacturing.展开更多
In this study,a single-doped phosphors yttrium aluminum garnet(Y_(3)Al_(5)O_(12),YAG):Ce^(3+),single-doped YAG:Sc^(3+),and double-doped phosphors YAG:Ce^(3+),Sc^(3+) were prepared by spark plasma sintering(SPS)(lower ...In this study,a single-doped phosphors yttrium aluminum garnet(Y_(3)Al_(5)O_(12),YAG):Ce^(3+),single-doped YAG:Sc^(3+),and double-doped phosphors YAG:Ce^(3+),Sc^(3+) were prepared by spark plasma sintering(SPS)(lower than 1 200℃).The characteristics of synthesized phosphors were determined using scanning electron microscopy(SEM),X-ray diffraction(XRD),and fluorescence spectroscopy.During SPS,the lattice structure of YAG was maintained by the added Ce^(3+) and Sc^(3+).The emission wavelength of YAG:Ce^(3+) prepared from SPS(425-700 nm) was wider compared to that of YAG:Ce^(3+) prepared from high-temperature solid-state reaction(HSSR)(500-700 nm).The incorporation of low-dose Sc^(3+) in YAG:Ce^(3+) moved the emission peak towards the short wavelength.展开更多
W-based WTaVCr refractory high entropy alloys (RHEA) may be novel and promising candidate materials for plasma facing components in the first wall and diverter in fusion reactors. This alloy has been developed by a po...W-based WTaVCr refractory high entropy alloys (RHEA) may be novel and promising candidate materials for plasma facing components in the first wall and diverter in fusion reactors. This alloy has been developed by a powder metallurgy process combining mechanical alloying and spark plasma sintering (SPS). The SPSed samples contained two phases, in which the matrix is RHEA with a body-centered cubic structure, while the oxide phase was most likely Ta2VO6through a combined analysis of X-ray diffraction (XRD),energy-dispersive spectroscopy (EDS), and selected area electron diffraction (SAED). The higher oxygen affinity of Ta and V may explain the preferential formation of their oxide phases based on thermodynamic calculations. Electron backscatter diffraction (EBSD) revealed an average grain size of 6.2μm. WTaVCr RHEA showed a peak compressive strength of 2997 MPa at room temperature and much higher micro-and nano-hardness than W and other W-based RHEAs in the literature. Their high Rockwell hardness can be retained to at least 1000°C.展开更多
The characteristic of easy sintering of aluminum nanoparticle(ANP)limits its application in solid propellants.Coating ANP with fluoropolymer could effectively improve its combustion performance.To find out how the coa...The characteristic of easy sintering of aluminum nanoparticle(ANP)limits its application in solid propellants.Coating ANP with fluoropolymer could effectively improve its combustion performance.To find out how the coating layer inhibits sintering and promotes complete combustion of particles from an atomic view,a comparative study has been done for bare ANP and PTFE coated ANP by using reactive molecular dynamics simulations.The sintering process is quantified by shrinkage ratio and gyration radius.Our results show that,at the same heating rate and combustion temperatures,bare ANPs are sintered together after the temperature exceeds the melting point of aluminum but the decomposition of PTFE coating layer pushes particles away and increases reaction surface area by producing small Al-F clusters.The sintering of ANPs which are heated in PTFE is alleviated compared with particles heated in oxygen,but particles still sinter together due to the lack of intimate contact between PTFE and alumina surface.The effect of temperature on the combustion of PTFE coated ANPs is also studied from 1000 to3500 K.The number density analysis shows the particles will not be sintered at any temperature.Aluminum fluoride prefers diffusing to the external space and the remained particles are mainly composed of Al,C and O.Fast ignition simulations are performed by adopting micro canonical ensemble.With the expansion of aluminum core and the melting of alumina shell,bare ANPs are sintered into a liquid particle directly.For PTFE coated ANPs,the volatilization of gaseous aluminum fluoride products continually endows particles opposite momentum.展开更多
A cold method was used to prepare coated sand for application in the selective laser sintering(SLS)process.Tensile strength,loss on ignition,gas evolution,and accuracy of the SLS samples were tested and analyzed,and t...A cold method was used to prepare coated sand for application in the selective laser sintering(SLS)process.Tensile strength,loss on ignition,gas evolution,and accuracy of the SLS samples were tested and analyzed,and the baking process was thoroughly investigated.Compared with coated sand prepared by the hot method,the cold method yields a more uniform and complete resin film on the sand's surface,resulting in enhanced tensile strength and accuracy.Additionally,the cold method requires a lower binder content to meet the same strength requirements,thereby minimizing gas evolution,reducing porosity defects,and ultimately improving casting quality.The coated sand samples prepared through the cold method exhibit superior accuracy,with a size error of within±0.4 mm.In contrast,the coated sand samples prepared by the hot method display a lower accuracy,with an average negative error of 2.1993 mm.The highest tensile strength could be attained by controlling the baking temperature within a suitable range(180-190°C),which can effectively reduce the generation of gas,thus contributing to improved overall performance.展开更多
Garnet-type Li_7La_(3)Zr_(2)O_(12)(LLZO) has high ionic conductivity and good compatibility with lithium metal.High-temperature processing has been proven an effective method to decrease the interface resistance of ca...Garnet-type Li_7La_(3)Zr_(2)O_(12)(LLZO) has high ionic conductivity and good compatibility with lithium metal.High-temperature processing has been proven an effective method to decrease the interface resistance of cathodeILLZO.However,its application is still hindered by the interlayer co-diffusion with the cathode and high sintering temperature(>1200℃).In this work,a new garnet-type composite solid-state electrolyte(SSE) Li_(6.54)La_(2.96)Ba_(0.04)Zr_(1.5)Nb_(0.5)O_(12)-LiCoO_(2)(LLBZNO-LCO) is firstly proposed to improve the chemical stability and electrochemical properties of garnet with high-temperature processing.Small doses of LCO(3%) can significantly decrease the LCOISSE interface resistance from 121.2 to 10.1 Ω cm~2,while the sintering temperature of garnet-type LLBZNO decreases from 1230 to 1000℃.The all-solid-state battery based on the sintered LLBZNO-LCO SSE exhibits excellent cycling stability.Our approach achieves an enhanced LCOISSE interface and an improved sintering activity of garnet SSE,which provides a new strategy for optimizing the comprehensive performance of garnet SSE.展开更多
Ceramic cores are the key intermediate components of hollow blades for aero-engine.Conventional processes,such as hot-press molding and gel film casting,face difficulties in fabricating complex-structured ceramic core...Ceramic cores are the key intermediate components of hollow blades for aero-engine.Conventional processes,such as hot-press molding and gel film casting,face difficulties in fabricating complex-structured ceramic cores due to the complexity of moulds and long process cycles.Stereolithography 3D printing provides a new idea for the fabrication of complex-structured ceramic cores.The effect of sintering temperature on open porosity,bulk density,weight loss rate,shrinkage rate,flexural strength and microstructure of the Al_(2)O_(3)-based ceramic core doped with 10vol.%polysilazane(PSZ)was studied.The sintering mechanism of PSZ-reinforced ceramic cores was analyzed.Results show that the optimum sintering temperature of PSZ-reinforced ceramic cores is 1,450°C.At this temperature,the open porosity of the ceramic core is 36.60%,bulk density is 2.33 g·cm^(-3),weight loss rate is 22.11%,shrinkage rate along the X,Y,Z directions is 5.72%,5.01%,9.61%,respectively;the flexural strength is 28.794 MPa at 25°C and 13.649 MPa at 1,500°C.Properties of 3D printing PSZ-reinforced ceramic cores can meet the casting requirement of superalloy hollow blades,which is expected to promote the industrial application of 3D printing complex structure ceramic cores.展开更多
How to increase strength without sacrificing ductility has been developed as a key goal in the manufacture of high-performance metals or alloys. Herein, the double-nanophase intragranular yttrium oxide dispersion stre...How to increase strength without sacrificing ductility has been developed as a key goal in the manufacture of high-performance metals or alloys. Herein, the double-nanophase intragranular yttrium oxide dispersion strengthened iron alloy with high strength and appreciable ductility was fabricated by solution combustion route and subsequent spark plasma sintering, and the influences of yttrium oxide content and sintering temperature on microstructures and mechanical properties were investigated. The results show at the same sintering temperature,with the increase of yttrium oxide content, the relative density of the sintered alloy decreases and the strength increases. For Fe–2wt%Y_(2)O_(3)alloy, as the sintering temperature increases gradually, the compressive strength decreases, while the strain-to-failure increases. The Fe–2wt%Y_(2)O_(3)alloy with 15.5 nm Y_(2)O_(3)particles uniformly distributed into the 147.5 nm iron grain interior sintered at 650℃ presents a high ultimate compressive strength of 1.86 GPa and large strain-to-failure of 29%. The grain boundary strengthening and intragranular second-phase particle dispersion strengthening are the main dominant mechanisms to enhance the mechanical properties of the alloy.展开更多
Iron ore sintering is a pre-treatment technology by which orefines are converted into porous and permeable sin-ters,which are the used in blast furnaces.This process can be adversely affected by air leakage phenomena ...Iron ore sintering is a pre-treatment technology by which orefines are converted into porous and permeable sin-ters,which are the used in blast furnaces.This process can be adversely affected by air leakage phenomena of various types.As experimental measurements are relatively difficult and often scarcely reliable,here a theoretical model based on typicalfluid-dynamic concepts and relationships is elaborated.Through the analysis of two extreme cases,namely,those in which leakage is due to a small hole or a full rupture,a generalized hole-bed mod-el is introduced,which for thefirst time also includes a complete bed permeability equation and can deal with different leakage position conditions.The results show that the model can evaluate the influence of leakage on the system at one time and be used to calculate theflowrate and pressure drop.Notably,the obtained results are within a 15%deviation with respect to available experiment values,used for comparison.展开更多
The technology for spraying a sintering bed and thus improving sinter quality indicators while reducing the emission of flue gas pollutants has recently become an important research topic.The impacts on sinter quality...The technology for spraying a sintering bed and thus improving sinter quality indicators while reducing the emission of flue gas pollutants has recently become an important research topic.The impacts on sinter quality and emissions when spraying the sintering surface with different amounts and flow rates of steam were investigated in this study.The sinter quality indicators were most effectively improved by spraying 180 g of steam flow continuously at a rate of 0.02 m^(3)/min for 15 min after ignition for 8 min.The optimal effect on emission reduction was obtained by spraying 90 g of steam flow continuously at a rate of 0.01 m^(3)/min for 15 min after ignition for 8 min.展开更多
Boron carbide(B_(4)C)has excellent high-temperature oxidation resistance,high hardness,low relative density,high melting point and excellent abrasive resistance,which is widely used in fields such as refractories,wear...Boron carbide(B_(4)C)has excellent high-temperature oxidation resistance,high hardness,low relative density,high melting point and excellent abrasive resistance,which is widely used in fields such as refractories,wear-resistant materials and lightweight protective materials.The research progress and application of B_(4)C materials in China and overseas in recent years were summarized.The influences of sintering processes(pressureless sintering,hot-pressing sintering,hot isostatic pressing sintering,spark plasma sintering and microwave sintering)and sintering additives(simple substances,oxides and carbides)on the B_(4)C densification were analyzed.The development of B_(4)C materials was prospected.展开更多
92WC-8Co powder mixture with superfine-tungsten carbide was respectively sintered by spark plasma sintering(SPS)and sintering isostatic pressure (SIP). Complete dense samples with 200 nm WC grains and 94.2HRA hardness...92WC-8Co powder mixture with superfine-tungsten carbide was respectively sintered by spark plasma sintering(SPS)and sintering isostatic pressure (SIP). Complete dense samples with 200 nm WC grains and 94.2HRA hardness were prepared by spark plasma sintering at 1 150 ℃ and under 4.5 kN for 5 minutes. SIP was carried out at 1 400 ℃ for 30 minutes with a result of 300-400 nm WC grains and 93 HRA hardness. The results show that sintering temperature is greatly decreased by SPS, sintering time is largely shortened and WC grain growth is effectively retarded. Micropores and drawbacks in superfine-cemented carbide made by SPS are greatly declined, which is very useful to improving mechanical properties.展开更多
Varistor ceramics of ZnO Bi 2O 3 TiO 2 Sb 2O 3 system have been fabricated by introducing pre fabricated ZnO seed grains with different size distributions respectively. The results show that the varistor properties we...Varistor ceramics of ZnO Bi 2O 3 TiO 2 Sb 2O 3 system have been fabricated by introducing pre fabricated ZnO seed grains with different size distributions respectively. The results show that the varistor properties were significantly influenced by the size of introduced seed grains, and introducing larger seed grains is more advantageous to the modification of microstructure and the improvement of varistor properties. The varistor properties were considerably improved with a moderately increased sintering temperature or time, whereas degraded apparently when the sintering temperature or time was excessively increased. Compared with the sintering time, the sintering temperature plays a more critical role in determining the varistor properties. By introducing pre fabricated ZnO seed grains into the original powders, low voltage ZnO varistor ceramics possessing the desired electrical properties have been produced with a sintering temperature of about 1 210 ℃ and a sintering temperature of 2~2.5 h. [展开更多
It was reported that TiB2 gains grew fast during sintering was a main cause for its properties degrading. In this paper the HP-sintering mechanics of TiB2 was studied and the results show that grains grow very fast wh...It was reported that TiB2 gains grew fast during sintering was a main cause for its properties degrading. In this paper the HP-sintering mechanics of TiB2 was studied and the results show that grains grow very fast when the sintering temperature is near 1800℃ . From the sintering dynamics, it can be concluded that grain fast growing results in boundary-transporting processing, during which grain boundary work as fast tunnel for material transporting.展开更多
A one-step sintering process of bauxite raw material from direct mining was completed, and the kinetics of this process was analyzed thoroughly. The results show that the sintering kinetics of bauxite raw material exh...A one-step sintering process of bauxite raw material from direct mining was completed, and the kinetics of this process was analyzed thoroughly. The results show that the sintering kinetics of bauxite raw material exhibits the liquid-phase sintering behavior. A small portion of impurities existed in the raw material act as a liquid phase. After X-ray diffraction analyses, scanning electron microscopy observations, and kinetics calculations, sintering temperature and heating duration were determined as the two major factors contributing to the sintering process and densification of bauxite ore. An elevated heating temperature and longer duration favor the densification process. The major obstacle for the densification of bauxite material is attributed to the formation of the enclosed blowhole during liquid-phase sintering.展开更多
Si2N2O ceramics were prepared using amorphous Si3N4 as the raw material and Li2CO3 as the sintering additive through vacuum multi-stage sintering.The influence of the Li2CO3 addition(0%,1%,2%,3%,and 5%,by mass)on the ...Si2N2O ceramics were prepared using amorphous Si3N4 as the raw material and Li2CO3 as the sintering additive through vacuum multi-stage sintering.The influence of the Li2CO3 addition(0%,1%,2%,3%,and 5%,by mass)on the phase composition,the microstructure,the porosity,the mechanical properties,the dielectric constant and the tangent of the dielectric loss angle of the porous Si2N2O ceramics was investigated.The results reveal that a suitable addition of Li2CO3 can promote the generation of Si2N2O but excessive or inadequate Li2CO3 causes decomposition of Si2N2O ceramics.The prepared porous Si2N2O ceramics have good mechanical properties,good thermal shock resistance,and low dielectric properties,which have excellent potential for application in microwave sintering furnaces.展开更多
Experiments on simultaneous absorption of SO_2 and NO_X from sintering flue gas via a composite absorbent NaClO_2/NaClO were carried out. The effects of various operating parameters such as NaClO_2 concentration(ms), ...Experiments on simultaneous absorption of SO_2 and NO_X from sintering flue gas via a composite absorbent NaClO_2/NaClO were carried out. The effects of various operating parameters such as NaClO_2 concentration(ms), NaClO concentration(mp), molar ratio of NaClO_2/NaClO(M), solution temperature(TR), initial solution pH, gas flow(Vg) and inlet concentration of SO_2(CS) and NO(CN) on the removal efficiencies of SO_2 and NO were discussed. The optimal experimental conditions were determined to be initial solution pH = 6, TR=55 °C and M = 1.3 under which the average efficiencies of desulfurization and denitrification could reach99.7% and 90.8%, respectively. Moreover, according to the analysis of reaction products, it was found that adding NaClO to NaClO_2 aqueous solution is favorable for the generation of ClO_2 and Cl_2 which have significant effect on desulfurization and denitrification. Finally, engineering experiments were performed and obtained good results demonstrating that this method is practicable and promising.展开更多
Baozhu sand particles with size between 75 μm and 150 μm were coated by resin with the ratio of 1.5 wt.% of sands. Laser sintering experiments were carried out to investigate the effects of laser energy density(E = ...Baozhu sand particles with size between 75 μm and 150 μm were coated by resin with the ratio of 1.5 wt.% of sands. Laser sintering experiments were carried out to investigate the effects of laser energy density(E = P/v), with different laser power(P) and scanning velocity(v), on the dimensional accuracy and tensile strength of sintered parts. The experimental results indicate that with the constant scanning velocity, the tensile strength of sintered samples increases with an increase in laser energy density; while the dimensional accuracy apparently decreases when the laser energy density is larger than 0.032 J·mm-2. When the laser energy density is 0.024 J·mm-2, the tensile strength shows no obvious change; but when the laser energy density is larger than 0.024 J·mm-2, the sample strength is featured by the initial increase and subsequent decrease with simultaneous increase of both laser power and scanning velocity. In this study, the optimal energy density range for laser sintering is 0.024-0.032 J·mm-2. Moreover, samples with the best tensile strength and dimensional accuracy can be obtained when P = 30-40 W and v = 1.5-2.0 m·s-1. Using the optimized laser energy density, laser power and scanning speed, a complex coated sand mould with clear contour and excellent forming accuracy has been successfully fabricated.展开更多
By desilication treatment,the Al2O3/SiO2 molar ratio of coal fly ash could be improved to the range of 1.63-2.0.The desilicated coal fly ash(DSCFA)was enriched in alumina extraction.A processing technology was develop...By desilication treatment,the Al2O3/SiO2 molar ratio of coal fly ash could be improved to the range of 1.63-2.0.The desilicated coal fly ash(DSCFA)was enriched in alumina extraction.A processing technology was developed for alumina extraction from the DSCFA with the lime sintering process.Ca/(SiO2+TiO2)molar ratio,and NaO/Al2O3 molar ratio,sintering time,and temperature were the most significant parameters impacting on the aluminum extraction efficiency.The optima aluminum extraction efficiency was obtained under conditions of Ca/(SiO2+TiO2)molar ratio of 2.0,NaO/Al2O3 molar ratio of 0.98,and sintering at 1 200 ℃for 60 min.Astandard industrial dissolution method was used under conditions of caustic ratio(αk=n(NaO)/n(Al2O3)of 2.0,Al2O3 concentration of 50 g/L,sodium hydroxide concentration(Nk)of 60.78 g/L,Na2CO3 concentration of 10 g/L,temperature of 85℃, and dissolution duration of 10 min.The final aluminum extraction efficiency was 90%.展开更多
Yttria stabilized zirconia (YSZ) has widely been used as electrolyte in solid oxide fuel cell (SOFC). The microstructure of YSZ related to the fabrication process was discussed in the paper. With YSZ nano-powders abou...Yttria stabilized zirconia (YSZ) has widely been used as electrolyte in solid oxide fuel cell (SOFC). The microstructure of YSZ related to the fabrication process was discussed in the paper. With YSZ nano-powders about 40-100 nm as raw material, the YSZ adobe was manufactured by tape calendering process. The named three-step sintering process was performed at 1000 ℃ for 2 h, then raised the temperature with normal rate and as soon as up to 1400 ℃, the furnace was controlled at 1250-1300 ℃ for 10-20 h. The high dense YSZs with the relative density of 96%-99% were obtained; the grain size of YSZ could be reduced to 0.5-3 μm. The above result is benefited to co-fired in the electrode-supported SOFCs.展开更多
文摘Within the past ten years,spark plasma sintering(SPS)has become an increasingly popular process for Mg manufacturing.In the SPS process,interparticle diffusion of compressed particles is rapidly achieved due to the concept of Joule heating.Compared to traditional and additive manufacturing(AM)techniques,SPS gives unique control of the structural and microstructural features of Mg components.By doing so,their mechanical,tribological,and corrosion properties can be tailored.Although great advancements in this field have been made,these pieces of knowledge are scattered and have not been contextualized into a single work.The motivation of this work is to address this scientific gap and to provide a groundwork for understanding the basics of SPS manufacturing for Mg.To do so,the existing body of SPS Mg literature was first surveyed,with a focus on their structural formation and degradation mechanisms.It was found that successful Mg SPS fabrication highly depended on the processing temperature,particle size,and particle crystallinity.The addition of metal and ceramic composites also affected their microstructural features due to the Zener pinning effect.In degradative environments,their performance depends on their structural features and whether they have secondary phased composites.In industrial applications,SPS'd Mg was found to have great potential in biomedical,hydrogen storage,battery,automotive,and recycling sectors.The prospects to advance the field include using Mg as a doping agent for crystallite size refinement and using bulk metallic Mg-based glass powders for amorphous SPS components.Despite these findings,the interactions of multi-composites on the processing-structure-property relationships of SPS Mg is not well understood.In total,this work will provide a useful direction in the SPS field and serve as a milestone for future Mg-based SPS manufacturing.
基金Funded by the Primary Research and Development Plan of Jiangsu Province(No.BE2016175)。
文摘In this study,a single-doped phosphors yttrium aluminum garnet(Y_(3)Al_(5)O_(12),YAG):Ce^(3+),single-doped YAG:Sc^(3+),and double-doped phosphors YAG:Ce^(3+),Sc^(3+) were prepared by spark plasma sintering(SPS)(lower than 1 200℃).The characteristics of synthesized phosphors were determined using scanning electron microscopy(SEM),X-ray diffraction(XRD),and fluorescence spectroscopy.During SPS,the lattice structure of YAG was maintained by the added Ce^(3+) and Sc^(3+).The emission wavelength of YAG:Ce^(3+) prepared from SPS(425-700 nm) was wider compared to that of YAG:Ce^(3+) prepared from high-temperature solid-state reaction(HSSR)(500-700 nm).The incorporation of low-dose Sc^(3+) in YAG:Ce^(3+) moved the emission peak towards the short wavelength.
基金supported by the National Science Foundation under Grant No.CMMI-1762190The research was performed in part in the Nebraska Nanoscale Facility:National Nanotechnology Coordinated Infrastructure and the Nebraska Center for Materials and Nanoscience (and/or NERCF),which are supported by the National Science Foundation under Award ECCS:2025298+1 种基金the Nebraska Research Initiativesupported by the U.S.Department of Energy,Office of Nuclear Energy under DOE Idaho Operations Office Contract DE-AC07-051D14517 as part of a Nuclear Science User Facilities experiment。
文摘W-based WTaVCr refractory high entropy alloys (RHEA) may be novel and promising candidate materials for plasma facing components in the first wall and diverter in fusion reactors. This alloy has been developed by a powder metallurgy process combining mechanical alloying and spark plasma sintering (SPS). The SPSed samples contained two phases, in which the matrix is RHEA with a body-centered cubic structure, while the oxide phase was most likely Ta2VO6through a combined analysis of X-ray diffraction (XRD),energy-dispersive spectroscopy (EDS), and selected area electron diffraction (SAED). The higher oxygen affinity of Ta and V may explain the preferential formation of their oxide phases based on thermodynamic calculations. Electron backscatter diffraction (EBSD) revealed an average grain size of 6.2μm. WTaVCr RHEA showed a peak compressive strength of 2997 MPa at room temperature and much higher micro-and nano-hardness than W and other W-based RHEAs in the literature. Their high Rockwell hardness can be retained to at least 1000°C.
基金supported by the fellowship of China Postdoctoral Science Foundation(Grant No.2021TQ0267)。
文摘The characteristic of easy sintering of aluminum nanoparticle(ANP)limits its application in solid propellants.Coating ANP with fluoropolymer could effectively improve its combustion performance.To find out how the coating layer inhibits sintering and promotes complete combustion of particles from an atomic view,a comparative study has been done for bare ANP and PTFE coated ANP by using reactive molecular dynamics simulations.The sintering process is quantified by shrinkage ratio and gyration radius.Our results show that,at the same heating rate and combustion temperatures,bare ANPs are sintered together after the temperature exceeds the melting point of aluminum but the decomposition of PTFE coating layer pushes particles away and increases reaction surface area by producing small Al-F clusters.The sintering of ANPs which are heated in PTFE is alleviated compared with particles heated in oxygen,but particles still sinter together due to the lack of intimate contact between PTFE and alumina surface.The effect of temperature on the combustion of PTFE coated ANPs is also studied from 1000 to3500 K.The number density analysis shows the particles will not be sintered at any temperature.Aluminum fluoride prefers diffusing to the external space and the remained particles are mainly composed of Al,C and O.Fast ignition simulations are performed by adopting micro canonical ensemble.With the expansion of aluminum core and the melting of alumina shell,bare ANPs are sintered into a liquid particle directly.For PTFE coated ANPs,the volatilization of gaseous aluminum fluoride products continually endows particles opposite momentum.
基金This work was financially supported by the Joint Funds of the National Natural Science Foundation of China(Grant No.U1808216)the Shanxi Provincial Key Research and Development Project(2022ZDYF072).
文摘A cold method was used to prepare coated sand for application in the selective laser sintering(SLS)process.Tensile strength,loss on ignition,gas evolution,and accuracy of the SLS samples were tested and analyzed,and the baking process was thoroughly investigated.Compared with coated sand prepared by the hot method,the cold method yields a more uniform and complete resin film on the sand's surface,resulting in enhanced tensile strength and accuracy.Additionally,the cold method requires a lower binder content to meet the same strength requirements,thereby minimizing gas evolution,reducing porosity defects,and ultimately improving casting quality.The coated sand samples prepared through the cold method exhibit superior accuracy,with a size error of within±0.4 mm.In contrast,the coated sand samples prepared by the hot method display a lower accuracy,with an average negative error of 2.1993 mm.The highest tensile strength could be attained by controlling the baking temperature within a suitable range(180-190°C),which can effectively reduce the generation of gas,thus contributing to improved overall performance.
基金financially supported by the National Natural Science Foundation of China (52102323, 51972298)the China Postdoctoral Science Foundation (2021M703055)+1 种基金the National Key R&D Program of China (2021YFB4001401)the Key Research Program of the Chinese Academy of Sciences (ZDRWCN-2021-3-1)。
文摘Garnet-type Li_7La_(3)Zr_(2)O_(12)(LLZO) has high ionic conductivity and good compatibility with lithium metal.High-temperature processing has been proven an effective method to decrease the interface resistance of cathodeILLZO.However,its application is still hindered by the interlayer co-diffusion with the cathode and high sintering temperature(>1200℃).In this work,a new garnet-type composite solid-state electrolyte(SSE) Li_(6.54)La_(2.96)Ba_(0.04)Zr_(1.5)Nb_(0.5)O_(12)-LiCoO_(2)(LLBZNO-LCO) is firstly proposed to improve the chemical stability and electrochemical properties of garnet with high-temperature processing.Small doses of LCO(3%) can significantly decrease the LCOISSE interface resistance from 121.2 to 10.1 Ω cm~2,while the sintering temperature of garnet-type LLBZNO decreases from 1230 to 1000℃.The all-solid-state battery based on the sintered LLBZNO-LCO SSE exhibits excellent cycling stability.Our approach achieves an enhanced LCOISSE interface and an improved sintering activity of garnet SSE,which provides a new strategy for optimizing the comprehensive performance of garnet SSE.
基金This work was financially supported by the National Natural Science Foundation of China(No.U22A20129)National Science and Technology Major Project(No.2017-VI-0002-0072)+2 种基金National Key Research and Development Program of China(No.2018YFB1106600)Fundamental Research Funds for the Central Universities(WK5290000003)Students'Innovation and Entrepreneurship Foundation of USTC(Nos.CY2022G10 and CY2022C24).
文摘Ceramic cores are the key intermediate components of hollow blades for aero-engine.Conventional processes,such as hot-press molding and gel film casting,face difficulties in fabricating complex-structured ceramic cores due to the complexity of moulds and long process cycles.Stereolithography 3D printing provides a new idea for the fabrication of complex-structured ceramic cores.The effect of sintering temperature on open porosity,bulk density,weight loss rate,shrinkage rate,flexural strength and microstructure of the Al_(2)O_(3)-based ceramic core doped with 10vol.%polysilazane(PSZ)was studied.The sintering mechanism of PSZ-reinforced ceramic cores was analyzed.Results show that the optimum sintering temperature of PSZ-reinforced ceramic cores is 1,450°C.At this temperature,the open porosity of the ceramic core is 36.60%,bulk density is 2.33 g·cm^(-3),weight loss rate is 22.11%,shrinkage rate along the X,Y,Z directions is 5.72%,5.01%,9.61%,respectively;the flexural strength is 28.794 MPa at 25°C and 13.649 MPa at 1,500°C.Properties of 3D printing PSZ-reinforced ceramic cores can meet the casting requirement of superalloy hollow blades,which is expected to promote the industrial application of 3D printing complex structure ceramic cores.
基金financially supported by the Guangdong Basic and Applied Basic Research Foundation,China (No.2021A1515110202)the Natural Science Foundation Program of Beijing,China (Nos.2224104,2202031,2174079+6 种基金2162027)the National Natural Science Foundation Program of China (Nos.52131307,52130407,52071013,52104359,51774035,and 52174344)the Scientific and Technological Innovation Foundation of Foshan,China (No.BK21BE007)the National Key Research and Development Program of China (Nos.2021YFB3701900,2022YFB3705400,and 2022YFB3708800)the Beijing Municipal Science & Technology Commission,Administrative Commission of Zhongguancun Science Park,China (No.Z221100005822001)the S&T Program of Hebei,China(No.20311001D)the Fundamental Research Funds for the Central Universities (Nos.FRF-IDRY-20-022,FRF-TP-20-032A2,FRF-TP-20-100A1Z,and FRF-IDRY-22-030)。
文摘How to increase strength without sacrificing ductility has been developed as a key goal in the manufacture of high-performance metals or alloys. Herein, the double-nanophase intragranular yttrium oxide dispersion strengthened iron alloy with high strength and appreciable ductility was fabricated by solution combustion route and subsequent spark plasma sintering, and the influences of yttrium oxide content and sintering temperature on microstructures and mechanical properties were investigated. The results show at the same sintering temperature,with the increase of yttrium oxide content, the relative density of the sintered alloy decreases and the strength increases. For Fe–2wt%Y_(2)O_(3)alloy, as the sintering temperature increases gradually, the compressive strength decreases, while the strain-to-failure increases. The Fe–2wt%Y_(2)O_(3)alloy with 15.5 nm Y_(2)O_(3)particles uniformly distributed into the 147.5 nm iron grain interior sintered at 650℃ presents a high ultimate compressive strength of 1.86 GPa and large strain-to-failure of 29%. The grain boundary strengthening and intragranular second-phase particle dispersion strengthening are the main dominant mechanisms to enhance the mechanical properties of the alloy.
文摘Iron ore sintering is a pre-treatment technology by which orefines are converted into porous and permeable sin-ters,which are the used in blast furnaces.This process can be adversely affected by air leakage phenomena of various types.As experimental measurements are relatively difficult and often scarcely reliable,here a theoretical model based on typicalfluid-dynamic concepts and relationships is elaborated.Through the analysis of two extreme cases,namely,those in which leakage is due to a small hole or a full rupture,a generalized hole-bed mod-el is introduced,which for thefirst time also includes a complete bed permeability equation and can deal with different leakage position conditions.The results show that the model can evaluate the influence of leakage on the system at one time and be used to calculate theflowrate and pressure drop.Notably,the obtained results are within a 15%deviation with respect to available experiment values,used for comparison.
文摘The technology for spraying a sintering bed and thus improving sinter quality indicators while reducing the emission of flue gas pollutants has recently become an important research topic.The impacts on sinter quality and emissions when spraying the sintering surface with different amounts and flow rates of steam were investigated in this study.The sinter quality indicators were most effectively improved by spraying 180 g of steam flow continuously at a rate of 0.02 m^(3)/min for 15 min after ignition for 8 min.The optimal effect on emission reduction was obtained by spraying 90 g of steam flow continuously at a rate of 0.01 m^(3)/min for 15 min after ignition for 8 min.
文摘Boron carbide(B_(4)C)has excellent high-temperature oxidation resistance,high hardness,low relative density,high melting point and excellent abrasive resistance,which is widely used in fields such as refractories,wear-resistant materials and lightweight protective materials.The research progress and application of B_(4)C materials in China and overseas in recent years were summarized.The influences of sintering processes(pressureless sintering,hot-pressing sintering,hot isostatic pressing sintering,spark plasma sintering and microwave sintering)and sintering additives(simple substances,oxides and carbides)on the B_(4)C densification were analyzed.The development of B_(4)C materials was prospected.
基金Funded by the Science Foundation of Shanghai , China ( No.0152nm046)
文摘92WC-8Co powder mixture with superfine-tungsten carbide was respectively sintered by spark plasma sintering(SPS)and sintering isostatic pressure (SIP). Complete dense samples with 200 nm WC grains and 94.2HRA hardness were prepared by spark plasma sintering at 1 150 ℃ and under 4.5 kN for 5 minutes. SIP was carried out at 1 400 ℃ for 30 minutes with a result of 300-400 nm WC grains and 93 HRA hardness. The results show that sintering temperature is greatly decreased by SPS, sintering time is largely shortened and WC grain growth is effectively retarded. Micropores and drawbacks in superfine-cemented carbide made by SPS are greatly declined, which is very useful to improving mechanical properties.
文摘Varistor ceramics of ZnO Bi 2O 3 TiO 2 Sb 2O 3 system have been fabricated by introducing pre fabricated ZnO seed grains with different size distributions respectively. The results show that the varistor properties were significantly influenced by the size of introduced seed grains, and introducing larger seed grains is more advantageous to the modification of microstructure and the improvement of varistor properties. The varistor properties were considerably improved with a moderately increased sintering temperature or time, whereas degraded apparently when the sintering temperature or time was excessively increased. Compared with the sintering time, the sintering temperature plays a more critical role in determining the varistor properties. By introducing pre fabricated ZnO seed grains into the original powders, low voltage ZnO varistor ceramics possessing the desired electrical properties have been produced with a sintering temperature of about 1 210 ℃ and a sintering temperature of 2~2.5 h. [
基金Supported by National Excellent Young Scientist Fund (59925207)and National Natural Science Fundation(59802008)
文摘It was reported that TiB2 gains grew fast during sintering was a main cause for its properties degrading. In this paper the HP-sintering mechanics of TiB2 was studied and the results show that grains grow very fast when the sintering temperature is near 1800℃ . From the sintering dynamics, it can be concluded that grain fast growing results in boundary-transporting processing, during which grain boundary work as fast tunnel for material transporting.
基金financially supported by the National Natural Science Foundation of China (No. 51402016)the Fundamental Research Funds for the Central Universities (No. FRF-TP-15-008A2)
文摘A one-step sintering process of bauxite raw material from direct mining was completed, and the kinetics of this process was analyzed thoroughly. The results show that the sintering kinetics of bauxite raw material exhibits the liquid-phase sintering behavior. A small portion of impurities existed in the raw material act as a liquid phase. After X-ray diffraction analyses, scanning electron microscopy observations, and kinetics calculations, sintering temperature and heating duration were determined as the two major factors contributing to the sintering process and densification of bauxite ore. An elevated heating temperature and longer duration favor the densification process. The major obstacle for the densification of bauxite material is attributed to the formation of the enclosed blowhole during liquid-phase sintering.
基金The authors would like to thank the National Key R&D Program of China(2017YFB0304000)National Natural Science Foundation of China(51932008,51772277)Central China Thousand Talents Project(2042005100111).
文摘Si2N2O ceramics were prepared using amorphous Si3N4 as the raw material and Li2CO3 as the sintering additive through vacuum multi-stage sintering.The influence of the Li2CO3 addition(0%,1%,2%,3%,and 5%,by mass)on the phase composition,the microstructure,the porosity,the mechanical properties,the dielectric constant and the tangent of the dielectric loss angle of the porous Si2N2O ceramics was investigated.The results reveal that a suitable addition of Li2CO3 can promote the generation of Si2N2O but excessive or inadequate Li2CO3 causes decomposition of Si2N2O ceramics.The prepared porous Si2N2O ceramics have good mechanical properties,good thermal shock resistance,and low dielectric properties,which have excellent potential for application in microwave sintering furnaces.
基金Supported by the National Science Foundation of China for Distinguished Young Scholars(No.51325601)Major Program of National Science Foundation of China(No.51390492)Joint Funds of National Science Foundation of China(No.U1560205)
文摘Experiments on simultaneous absorption of SO_2 and NO_X from sintering flue gas via a composite absorbent NaClO_2/NaClO were carried out. The effects of various operating parameters such as NaClO_2 concentration(ms), NaClO concentration(mp), molar ratio of NaClO_2/NaClO(M), solution temperature(TR), initial solution pH, gas flow(Vg) and inlet concentration of SO_2(CS) and NO(CN) on the removal efficiencies of SO_2 and NO were discussed. The optimal experimental conditions were determined to be initial solution pH = 6, TR=55 °C and M = 1.3 under which the average efficiencies of desulfurization and denitrification could reach99.7% and 90.8%, respectively. Moreover, according to the analysis of reaction products, it was found that adding NaClO to NaClO_2 aqueous solution is favorable for the generation of ClO_2 and Cl_2 which have significant effect on desulfurization and denitrification. Finally, engineering experiments were performed and obtained good results demonstrating that this method is practicable and promising.
基金financially supported by the National Defence Key Discipline Laboratory of Light Alloy Processing Science and Technology,Aeronautical Science Foundation of China(Grant No.2011ZE56007)the Natural Science Foundation of Jiangxi Province(Grant No.2010GZC0159)the High Technology Landing Program of Jiangxi University(Grant No.DB201303014)
文摘Baozhu sand particles with size between 75 μm and 150 μm were coated by resin with the ratio of 1.5 wt.% of sands. Laser sintering experiments were carried out to investigate the effects of laser energy density(E = P/v), with different laser power(P) and scanning velocity(v), on the dimensional accuracy and tensile strength of sintered parts. The experimental results indicate that with the constant scanning velocity, the tensile strength of sintered samples increases with an increase in laser energy density; while the dimensional accuracy apparently decreases when the laser energy density is larger than 0.032 J·mm-2. When the laser energy density is 0.024 J·mm-2, the tensile strength shows no obvious change; but when the laser energy density is larger than 0.024 J·mm-2, the sample strength is featured by the initial increase and subsequent decrease with simultaneous increase of both laser power and scanning velocity. In this study, the optimal energy density range for laser sintering is 0.024-0.032 J·mm-2. Moreover, samples with the best tensile strength and dimensional accuracy can be obtained when P = 30-40 W and v = 1.5-2.0 m·s-1. Using the optimized laser energy density, laser power and scanning speed, a complex coated sand mould with clear contour and excellent forming accuracy has been successfully fabricated.
基金Project(YFZX(0804))supported by Science Foundation of the Pingshuo Coal Industry Company,China
文摘By desilication treatment,the Al2O3/SiO2 molar ratio of coal fly ash could be improved to the range of 1.63-2.0.The desilicated coal fly ash(DSCFA)was enriched in alumina extraction.A processing technology was developed for alumina extraction from the DSCFA with the lime sintering process.Ca/(SiO2+TiO2)molar ratio,and NaO/Al2O3 molar ratio,sintering time,and temperature were the most significant parameters impacting on the aluminum extraction efficiency.The optima aluminum extraction efficiency was obtained under conditions of Ca/(SiO2+TiO2)molar ratio of 2.0,NaO/Al2O3 molar ratio of 0.98,and sintering at 1 200 ℃for 60 min.Astandard industrial dissolution method was used under conditions of caustic ratio(αk=n(NaO)/n(Al2O3)of 2.0,Al2O3 concentration of 50 g/L,sodium hydroxide concentration(Nk)of 60.78 g/L,Na2CO3 concentration of 10 g/L,temperature of 85℃, and dissolution duration of 10 min.The final aluminum extraction efficiency was 90%.
基金The project was financiallysupportedby Ministry of Education,China(No.106087)and 863 Program of National High Technology Research Development Project,China(2005AA501050).
文摘Yttria stabilized zirconia (YSZ) has widely been used as electrolyte in solid oxide fuel cell (SOFC). The microstructure of YSZ related to the fabrication process was discussed in the paper. With YSZ nano-powders about 40-100 nm as raw material, the YSZ adobe was manufactured by tape calendering process. The named three-step sintering process was performed at 1000 ℃ for 2 h, then raised the temperature with normal rate and as soon as up to 1400 ℃, the furnace was controlled at 1250-1300 ℃ for 10-20 h. The high dense YSZs with the relative density of 96%-99% were obtained; the grain size of YSZ could be reduced to 0.5-3 μm. The above result is benefited to co-fired in the electrode-supported SOFCs.