LaNiC2 was synthesized by a solvothermal route in a stainless steel autoclave at 600℃. In this process, nickel chloride, lanthanum chloride and toluene were used as raw materials, and metallic Na and Li alloy were us...LaNiC2 was synthesized by a solvothermal route in a stainless steel autoclave at 600℃. In this process, nickel chloride, lanthanum chloride and toluene were used as raw materials, and metallic Na and Li alloy were used as reductant. The products were characterized with an X-ray diffractometer （XRD） and a scanning electron microscope （SEM）. The LaNiC2 products consisted of a great deal of micro-rods. The micro-rods had diameters ranging from hundreds of nanometers to several micrometers and lengths ranging from several micrometers to tens of micrometers.展开更多
The metastable phase 3c-Fe7S8 with the hexagonal platelet morphology has been prepared by using solvothermal route. The product was characterized by means of X-ray powder diffraction (XRD) and transmission electron mi...The metastable phase 3c-Fe7S8 with the hexagonal platelet morphology has been prepared by using solvothermal route. The product was characterized by means of X-ray powder diffraction (XRD) and transmission electron microscopy (TEM) and X-ray photoelectron spectra (XPS). The experiment results show that the as-prepared Fe7S8 is a metastable phase with the hexagonal platelet morphology.展开更多
{001}facets dominated single crystalline anatase TiO_(2) nanosheet array(TNSA)was synthe-sized through an optimized organic solvothermal route on uorine-doped tin oxide substrate.The field emission scanning electron m...{001}facets dominated single crystalline anatase TiO_(2) nanosheet array(TNSA)was synthe-sized through an optimized organic solvothermal route on uorine-doped tin oxide substrate.The field emission scanning electron microscopy images and X-ray diffraction patterns re-vealed that the{001}synthesized facets dominated TNSA exhibited much higher orientation than that synthesized by hydrothermal route.The TNSAs were loaded with Pt nanoparti-cles in uniformly size by using a photodecomposition method,which were further con rmed by high resolution transmission electron microscopy(HRTEM).The HRTEM images also revealed that Pt nanoparticles preferred to deposit on{001}facets.With loading of Pt nanoparticles,the optical absorbance was significantly enhanced,while the photolumines-cence(PL)was inhibited.The photocatalytic activity of TNSA was signi cantly improved by Pt loading and reached the maximum with optimal amount of Pt loading.The optimal amount of Pt on{001}facets is far less than that on TiO_(2) nanoparticles,which may be attributed to the specific atom structure of reactive{001}facets.展开更多
基金the Science and Technology Project of Guangdong Province(2KM02304G and 2005A11001001)Qian Bai Shi Project of Guangdong Province(Q02059)International Cooperation Project of Hubei Province(2006CA014)
文摘LaNiC2 was synthesized by a solvothermal route in a stainless steel autoclave at 600℃. In this process, nickel chloride, lanthanum chloride and toluene were used as raw materials, and metallic Na and Li alloy were used as reductant. The products were characterized with an X-ray diffractometer （XRD） and a scanning electron microscope （SEM）. The LaNiC2 products consisted of a great deal of micro-rods. The micro-rods had diameters ranging from hundreds of nanometers to several micrometers and lengths ranging from several micrometers to tens of micrometers.
基金This work was supported by the National Natural Science Foundation of China.
文摘The metastable phase 3c-Fe7S8 with the hexagonal platelet morphology has been prepared by using solvothermal route. The product was characterized by means of X-ray powder diffraction (XRD) and transmission electron microscopy (TEM) and X-ray photoelectron spectra (XPS). The experiment results show that the as-prepared Fe7S8 is a metastable phase with the hexagonal platelet morphology.
基金This work is supported by the National Basic Research Program of China(No.2012CB9222000).
文摘{001}facets dominated single crystalline anatase TiO_(2) nanosheet array(TNSA)was synthe-sized through an optimized organic solvothermal route on uorine-doped tin oxide substrate.The field emission scanning electron microscopy images and X-ray diffraction patterns re-vealed that the{001}synthesized facets dominated TNSA exhibited much higher orientation than that synthesized by hydrothermal route.The TNSAs were loaded with Pt nanoparti-cles in uniformly size by using a photodecomposition method,which were further con rmed by high resolution transmission electron microscopy(HRTEM).The HRTEM images also revealed that Pt nanoparticles preferred to deposit on{001}facets.With loading of Pt nanoparticles,the optical absorbance was significantly enhanced,while the photolumines-cence(PL)was inhibited.The photocatalytic activity of TNSA was signi cantly improved by Pt loading and reached the maximum with optimal amount of Pt loading.The optimal amount of Pt on{001}facets is far less than that on TiO_(2) nanoparticles,which may be attributed to the specific atom structure of reactive{001}facets.