Four oil absorbents based on styrene butadiene (SBR),i. e., pure SBR (PS), 4- tert-butylstyrene-SBR (PBS),EPDM-SBR network (PES) and 4-tert-butylstyrene-EPDMSBR ( PBES ), were produced from crosslinking polymerization...Four oil absorbents based on styrene butadiene (SBR),i. e., pure SBR (PS), 4- tert-butylstyrene-SBR (PBS),EPDM-SBR network (PES) and 4-tert-butylstyrene-EPDMSBR ( PBES ), were produced from crosslinking polymerization of uncured styrene butadiene rubber (SBR),4- tert-butylstyrene ( tBS ) and ethylene-propylene-diene terpolymer (EPDM). The reaction took place in toluene using benzoyl peroxide (BPO) as an initiator. Uncured SBR was used as both a pre-polymer and a crosslink agent in this work, and the crosslinked polymer was identified by IR spectroscopy. The oil absorbency of the crosslinked polymer was evaluated with the method ASTM (F726 - 81). The order of maximum oil absorbency was PBES ＞ PBS ＞PES ＞ PS. The maximum values of oil absorbency of PBES and PBS were 74.0g/g and 69.5g/g, respectively. Gel fractions and swelling kinetic constants, however, had the opposite sequences. The swelling kinetic constant of PS evaluated by an experimental equation was 49. 97 ×10-2h-1.展开更多
The properties of styrene-butadiene rubber (SBR) reinforced by modified silica was investigated according to national standards. Silica was modified by silane coupling agents KH-570, KH-590, and KH-792. The optimized ...The properties of styrene-butadiene rubber (SBR) reinforced by modified silica was investigated according to national standards. Silica was modified by silane coupling agents KH-570, KH-590, and KH-792. The optimized geome-tries of molecular modified silica reinforced SBR were obtained by using B3LYP calculation of density functional theory with the 6-31+G basis sets. The natural bond orbital analyses were carried out. The Si—O bond length of silica modified by KH-792 was the shortest and the electronegative of O was the highest. It indicated that the connection between silica and KH-792 was the tightest. Higher tensile strength and elongation of reinforced SBR was obtained by silica modified with the KH-792. It was caused by large delocalization of lone pair electrons of the two N atoms in KH-792. The S—C bond length in silica modified by KH-590 was longer than the ordinary S—C bond length. Then the sulfur free radical (·S·) was produced more easily in vulcanization. The degree of crosslink was increased by the cross-linkage of the rubber molecule and the sulfur free radical. That was why the highest stress and tear strength of reinforced SBR was produced when silane coupling agent KH-590 was used. The calculation results was in accord with experimental data.展开更多
This paper presents the influence of graphene on the vulcanization kinetics of styrene butadiene rubber(SBR) with dicumyl peroxide. A curemeter and a differential scanning calorimeter were used to investigate the cure...This paper presents the influence of graphene on the vulcanization kinetics of styrene butadiene rubber(SBR) with dicumyl peroxide. A curemeter and a differential scanning calorimeter were used to investigate the cure kinetics, from which the kinetic parameters and apparent activation energy were obtained. It turns out that with increasing graphene loading, the induction period of the vulcanization process of SBR is remarkably reduced at low graphene loading and then levels off; on the other hand, the optimum cure time shows a monotonous decrease. As a result, the vulcanization rate is suppressed at first and then accelerated, and the corresponding activation energy increases slightly at first and then decreases. Upon adding graphene, the crosslinking density of the nanocomposites increases, because graphene takes part in the vulcanization process.展开更多
A natural nanotubular material,halloysite nanotubes(HNTs),was introduced to prepare styrene-butadiene rubber/modified halloysite nanotube(SBR/m-HNT) nanocomposites.Complex of resorcinol and hexamethylenetetramine (RH)...A natural nanotubular material,halloysite nanotubes(HNTs),was introduced to prepare styrene-butadiene rubber/modified halloysite nanotube(SBR/m-HNT) nanocomposites.Complex of resorcinol and hexamethylenetetramine (RH) was used as the interfacial modifier.The structure,morphology and mechanical properties of SBR/m-HNT nanocomposites,especially the interfacial interactions,were investigated.SEM and TEM observations showed that RH can not only facilitate the dispersion and orientation of HNTs in SBR matrix ...展开更多
Evolution and fractal character of the phase morphology of high impact polystyrene/poly(cis-butadiene) rubber (HIPS/PcBR) blends during melting and mixing were investigated using scanning electron microscopy (SEM). Th...Evolution and fractal character of the phase morphology of high impact polystyrene/poly(cis-butadiene) rubber (HIPS/PcBR) blends during melting and mixing were investigated using scanning electron microscopy (SEM). The characteristic length L was defined as the size of particles of the dispersed phase in blends. Different fractal dimensions, Df and Dm, were introduced to study the distribution width of phase dimensions in the dimensionless region and the uniformity of the spatial distribution of particles, respectively. The results showed that the average characteristic length Lm and Df increase as the volume fraction of the dispersed phase increases, when the volume fraction of the dispersed phase is lower than 50%. In other words, the size of particles increases and their distribution in the dimensionless region becomes more uniform. Meanwhile, the uniformity of the spatial distribution becomes more perfect as the volume fraction increases. At a certain composition, Lm decreases in the initial stage of the mixing and levels off in the late stage. In the initial stage, Df becomes large rapidly with the process of blending, which means that the distribution of L in the dimensionless region becomes more uniform. Meanwhile, the spatial distribution tends to be ideal rapidly in the early stage and fluctuates in a definite range in the late stage of the mixing.展开更多
An approach for analyzing and optimizing sealing mechanism of ball valve made of nitrile butadiene rubber(NBR) with finite element method was presented. The Mooney-Rivlin hyperelastic material model was chosen to char...An approach for analyzing and optimizing sealing mechanism of ball valve made of nitrile butadiene rubber(NBR) with finite element method was presented. The Mooney-Rivlin hyperelastic material model was chosen to characterize NBR sealing, as it has been recommended in the similar applications. That is, NBR sealing was modeled as incompressible hyperelasticity, as well as the assumption of isotropic flow. The results illustrate the structural pressure and contact pressure on the contact surface, which shows that the NBR sealing mechanism is very suitable for sealing after dimension optimization.展开更多
<正>Polystyrene-styrene/butadiene diblock copolymers were synthesized via reversible addition-fragmentation chain transfer (RAFT) miniemulsion polymerization.During the polymerization process,the molecular weigh...<正>Polystyrene-styrene/butadiene diblock copolymers were synthesized via reversible addition-fragmentation chain transfer (RAFT) miniemulsion polymerization.During the polymerization process,the molecular weight distribution was narrow and the numerical molecular weight of the copolymers increased with increasing conversion of monomers,which was close to the theoretical.FT-IR and ~1H NMR results indicated that the microstructure of the polymer was mainly 1,4-trans-butadiene with small amount of 1,2-units,and composition in the copolymers was obtained.展开更多
In this paper, acrylonitrile-butadiene-styrene(ABS) nanocomposite foams are produced using carbon dioxide through the solid-state batch process. Microcellular closed-cell foams are produced with the relative density r...In this paper, acrylonitrile-butadiene-styrene(ABS) nanocomposite foams are produced using carbon dioxide through the solid-state batch process. Microcellular closed-cell foams are produced with the relative density ranging from 0.38 to 0.97. The effects of the processing conditions on the density, morphology, and flexural properties of ABS and its nanocomposite foams are studied. It is found that nanoclay particles, as nucleating sites, play an important role in reducing the size of cells and increasing their number in the unit volume of foamed polymer, as well as increasing the flexural modulus of foam through reinforcing its matrix.展开更多
The residual levels and migration behavior of volatile substances were detected using HS-GC/MS for acrylonitrile-butadiene-styrene copolymer (ABS) toys, thermoplastic elastomer toys, and rubber toys made from 1,3-buta...The residual levels and migration behavior of volatile substances were detected using HS-GC/MS for acrylonitrile-butadiene-styrene copolymer (ABS) toys, thermoplastic elastomer toys, and rubber toys made from 1,3-butadiene and styrene found on the Japanese market. The maximum residual level of these volatile substances was 2600 μg/g of styrene in ABS toys. In particular, the levels of known carcinogens 1,3-butadiene, benzene, and acrylonitrile are 5.3, 2.5 and 55 μg/g, which are much lower than the EU limit of 0.1%. Furthermore, some volatile substances migrated from ABS toys into water in amounts of 3 -40 ng/mL. Thermoplastic elastomer toys and rubber toys contained these volatile substances at significantly lower levels than ABS toys.展开更多
Palm fiber (PF) reinforced acrylonitrile butadiene styrene (ABS) composite matrix was prepared by employing Injection Moulding Machine (IMM). Palm fiber was collected from ten different trees of different age group fr...Palm fiber (PF) reinforced acrylonitrile butadiene styrene (ABS) composite matrix was prepared by employing Injection Moulding Machine (IMM). Palm fiber was collected from ten different trees of different age group from Comilla region in Bangladesh. Three sets of samples were prepared for three different wt% (5%, 10% and 20%) of fiber contents. The mechanical (tensile strength, flexural stress, micro hardness, Leeb’s rebound hardness) and physical (bulk density and water absorption) properties were measured. The observed result reveals that the tensile strength (TS) and flexural stress (FS) were decreased with increasing fiber contents in the PF-ABS composites except 10% fiber content.展开更多
A new fourth-generation poly(propylene imine) dendrimer(G4-M) containing 32 triolefinic 15-membered macrocycles on the surfaces has been synthesized. The bimetallic Ru Rh dendrimer-stabilized nanoparticles(DSNs) were ...A new fourth-generation poly(propylene imine) dendrimer(G4-M) containing 32 triolefinic 15-membered macrocycles on the surfaces has been synthesized. The bimetallic Ru Rh dendrimer-stabilized nanoparticles(DSNs) were first prepared within G4-M by a co-complexation route. The new G4-M dendrimer has been characterized by 1H nuclear magnetic resonance, infrared radiation, and elemental analysis.The dendrimer-stabilized bimetallic ions and reduction courses were analyzed by UV-vis spectroscopy. Highresolution transmission electron microscopy and energy dispersive spectrometer were used to characterize the bimetallic nanoparticle size, size distribution, and particle morphology. The Ru Rh bimetallic DSNs showed high catalytic activity for the hydrogenation of nitrile-butadiene rubber.展开更多
Palygorskite (PGS) and vinyl tris-(2-methoxyethoxy) silane (KH-172) modified palygorskite (OPGS) were used to prepare acrylonitrile-butadiene-styrene (ABS)/clay composites. Thermal stability of the composites was eval...Palygorskite (PGS) and vinyl tris-(2-methoxyethoxy) silane (KH-172) modified palygorskite (OPGS) were used to prepare acrylonitrile-butadiene-styrene (ABS)/clay composites. Thermal stability of the composites was evaluated by using thermogravimetric analysis (TGA). The morphology of the fractured surface and the degree of dispersion of the clay in the ABS matrix were observed by scanning electron microscopy (SEM). X-ray diffraction (XRD) analysis results showed the variation of the crystal structure. Measurements of the tensile properties of the ABS/clay composites proved that the ABS/OPGS composited material represented the most excellent tensile property, because of good compatibility and dispersion of ABS with OPGS.展开更多
This paper mainly deals with the design and synthesis of a novel styrene-butadieneblock copolymer. When this copolymer is used in the tread portion of tyres, it can improvewet skid resistance and reduce rolling resist...This paper mainly deals with the design and synthesis of a novel styrene-butadieneblock copolymer. When this copolymer is used in the tread portion of tyres, it can improvewet skid resistance and reduce rolling resistance without sacrificing its general physical-mechanical properties. The visco-elastic curve of tire tread using the novel copolymer asits rubber portion was showed. Reactivity ratios for two monomers in the polymerizingsystem were calculated. The diagrams of differelitial, integral and finite difference calculithroughout the whole molecular chain were presented. The influence of the micro- andmacro-structure of the copolymer chain on wet skid resistance and rolling resistance展开更多
With the advent of plastics and the wide range of fillers that are available have made modifications as precise as the tailored resins themselves. To modify the properties of polymer either by using fillers or by prep...With the advent of plastics and the wide range of fillers that are available have made modifications as precise as the tailored resins themselves. To modify the properties of polymer either by using fillers or by preparation of polymer blends gives rise to new materials with tailored properties. More complex, three-component systems, obtained by the addition of polymeric modifier to polymer filled composites may be of interest. Use of Fly ash cenospheres is very attractive because it is inexpensive and its use can reduce the environmental pollution to a significant extent. In the present study, Poly (Methyl Methacrylate) (PMMA)-Fly ash cenospheres composites were prepared using extrusion followed by Injection molding. The effect of matrix modification with Methyl methacrylate– acrylonitrile -butadiene–styrene (MABS) on the performance of PMMA- Fly ash cenospheres compositions was also, studied. It was found that with the addition of Fly ash cenospheres particulate as filler in PMMA showed marginal reduction in Tensile Strength, % Elongation and Impact strength and improvement in Flexural Strength, Heat Deflection Temperature and Vicat Softening Point. Compared with PMMA-cenospheres composites, the notched Impact Strength of the PMMA/MABS/cenospheres composites showed marginal enhancement in values at higher loading of cenospheres. The optimum performances in mechanical and thermal properties were obtained when the ratio of MABS to cenospheres was 1:2.展开更多
In this paper, the effects of build parameters on the mechanical properties of 3D-printed acrylonitrile butadiene styrene (ABS) produced using fused deposition modeling (FDM) are investigated. Full factorial experimen...In this paper, the effects of build parameters on the mechanical properties of 3D-printed acrylonitrile butadiene styrene (ABS) produced using fused deposition modeling (FDM) are investigated. Full factorial experimental design incorporating a 2-level, 3-factor design with raster angle, layer thickness and interior fill style was carried out. Tensile tests were performed at four different strain rates to determine how the build parameters influence the mechanical properties of the 3-D printed ABS and to assess its strain rate sensitivity under quasi-static loading. It was found that the modulus of toughness of ABS material is most influenced by raster angle, while the interior fill style is the most dominant build parameter that dictates the specimen’s modulus of resilience, yield strength and ultimate tensile strength. At all strain rates, it is further revealed that higher mean values of yield strength, ultimate tensile strength and modulus of resilience were obtained when the interior fill style is solid as opposed to high density. This can be attributed to the denser structure and higher effective cross-sectional area in solid interior fill style in comparison with high density interior fill style. However, the influence of the layer thickness on the investigated mechanical properties was found to be inconsistent. It was noted that specimens built with both 0.254 mm layer thickness and the cross [0°/90°] raster angle had superior mechanical properties when compared to those built with the 0.3302 mm layer thickness and cross [0°/90°] raster angle. This suggests that there is a key interaction between the layer thickness and the raster angle. At any FDM build parameter, it was found that all the mechanical properties investigated in this work exhibited modest sensitivity to strain rates. This study has provided a platform for an appropriate selection of build parameters combinations and strain rates for additive manufacturing of 3D-printed ABS with improved mechanical properties.展开更多
A novel multifunctional macromolecular organolithium initiator (PD-Sn-(RLi)3) was prepared via living anionic polymerization and used for the synthesis of miktoarm star copolymers in cyclohexane. The average molecular...A novel multifunctional macromolecular organolithium initiator (PD-Sn-(RLi)3) was prepared via living anionic polymerization and used for the synthesis of miktoarm star copolymers in cyclohexane. The average molecular weight, polydispersity index, microstructure and unit composition of the miktoarm star copolymers were characterized with GPC and 1H-NMR. Performances of the miktoarm star styrene-butadiene rubbers were investigated in comparison with those of the blend rubbers such as the tin-coupled star-shaped random copolymers of styrene-butadiene rubber(S-SBR)/natural rubber(NR) blend rubber and S-SBR/Cis-1, 4-polybutadiene rubber (Cis-BR) blend rubber.展开更多
Interpenetrating polymer networks(IPNs)based on fluoroelastomer/butadiene-acrylonitrile rubber(FKM/NBR)by molten blending at a high temperature and chemical cross-linking of two components were prepared.The influence ...Interpenetrating polymer networks(IPNs)based on fluoroelastomer/butadiene-acrylonitrile rubber(FKM/NBR)by molten blending at a high temperature and chemical cross-linking of two components were prepared.The influence of the two networks component on the mechanical properties and thermostabilities was studied.The experimental results show that the mechanical properties of the IPNs are superior to those of the individual FKM and NBR networks due to forming the case of interpenetrating and intercross-linking between the two networks,the mechanical properties and thermal resistance exhibit higher values when 80/20 (w/w)FKM and NBR is blended and respectively cured simultaneously.The co-continuous morphology of the IPNs in the blends of 80/20(w/w)FKM/NBR is found by transmission electron microscopy(TEM),the differential scanning calorimetry(DSC)determination shows that the blends of 80/20(w/w)FKM/NBR have better compatibility,and the glass transition temperature of the elastomer is -21.5℃,展开更多
This investigation presents thermoplastic elastomers (TPEs) based on poly (styrene-butadiene-styrene) (SBS) and thermoplastic polyurethane (TPU) materials were prepared with varying compositions. A series of works wer...This investigation presents thermoplastic elastomers (TPEs) based on poly (styrene-butadiene-styrene) (SBS) and thermoplastic polyurethane (TPU) materials were prepared with varying compositions. A series of works were conducted on the relationships between rheological, optical properties, morphology, mechanical properties, abrasion resistance and thermostability given. The results showed that the shear viscosity of SBS not obvious effect with TPU content. The optical properties of the SBS/TPU blend that its uniform transparency. The morphology characteristics indicating the phase diversion and the variation in the size of the SBS domains from large to small as the TPU contents increased, with heterogeneous domain dispersions. Additionally, the mechanical properties, abrasion resistance and thermal resistance are improved as the amount of added TPU is increased, suggesting that the blending of SBS with TPU is consistent with the compound rule.展开更多
文摘Four oil absorbents based on styrene butadiene (SBR),i. e., pure SBR (PS), 4- tert-butylstyrene-SBR (PBS),EPDM-SBR network (PES) and 4-tert-butylstyrene-EPDMSBR ( PBES ), were produced from crosslinking polymerization of uncured styrene butadiene rubber (SBR),4- tert-butylstyrene ( tBS ) and ethylene-propylene-diene terpolymer (EPDM). The reaction took place in toluene using benzoyl peroxide (BPO) as an initiator. Uncured SBR was used as both a pre-polymer and a crosslink agent in this work, and the crosslinked polymer was identified by IR spectroscopy. The oil absorbency of the crosslinked polymer was evaluated with the method ASTM (F726 - 81). The order of maximum oil absorbency was PBES ＞ PBS ＞PES ＞ PS. The maximum values of oil absorbency of PBES and PBS were 74.0g/g and 69.5g/g, respectively. Gel fractions and swelling kinetic constants, however, had the opposite sequences. The swelling kinetic constant of PS evaluated by an experimental equation was 49. 97 ×10-2h-1.
文摘The properties of styrene-butadiene rubber (SBR) reinforced by modified silica was investigated according to national standards. Silica was modified by silane coupling agents KH-570, KH-590, and KH-792. The optimized geome-tries of molecular modified silica reinforced SBR were obtained by using B3LYP calculation of density functional theory with the 6-31+G basis sets. The natural bond orbital analyses were carried out. The Si—O bond length of silica modified by KH-792 was the shortest and the electronegative of O was the highest. It indicated that the connection between silica and KH-792 was the tightest. Higher tensile strength and elongation of reinforced SBR was obtained by silica modified with the KH-792. It was caused by large delocalization of lone pair electrons of the two N atoms in KH-792. The S—C bond length in silica modified by KH-590 was longer than the ordinary S—C bond length. Then the sulfur free radical (·S·) was produced more easily in vulcanization. The degree of crosslink was increased by the cross-linkage of the rubber molecule and the sulfur free radical. That was why the highest stress and tear strength of reinforced SBR was produced when silane coupling agent KH-590 was used. The calculation results was in accord with experimental data.
基金financially supported by the National Natural Science Foundation of China(No.51203096)the Ph.D.Programs Foundation of Ministry of Education of China(No.20100181120020)Sichuan University
文摘This paper presents the influence of graphene on the vulcanization kinetics of styrene butadiene rubber(SBR) with dicumyl peroxide. A curemeter and a differential scanning calorimeter were used to investigate the cure kinetics, from which the kinetic parameters and apparent activation energy were obtained. It turns out that with increasing graphene loading, the induction period of the vulcanization process of SBR is remarkably reduced at low graphene loading and then levels off; on the other hand, the optimum cure time shows a monotonous decrease. As a result, the vulcanization rate is suppressed at first and then accelerated, and the corresponding activation energy increases slightly at first and then decreases. Upon adding graphene, the crosslinking density of the nanocomposites increases, because graphene takes part in the vulcanization process.
基金supported by the National Natural Science Foundation of China(Nos.50573021 and 50603005)
文摘A natural nanotubular material,halloysite nanotubes(HNTs),was introduced to prepare styrene-butadiene rubber/modified halloysite nanotube(SBR/m-HNT) nanocomposites.Complex of resorcinol and hexamethylenetetramine (RH) was used as the interfacial modifier.The structure,morphology and mechanical properties of SBR/m-HNT nanocomposites,especially the interfacial interactions,were investigated.SEM and TEM observations showed that RH can not only facilitate the dispersion and orientation of HNTs in SBR matrix ...
基金This work was supported by the National Natural Science Foundation of China (No. 50390090).
文摘Evolution and fractal character of the phase morphology of high impact polystyrene/poly(cis-butadiene) rubber (HIPS/PcBR) blends during melting and mixing were investigated using scanning electron microscopy (SEM). The characteristic length L was defined as the size of particles of the dispersed phase in blends. Different fractal dimensions, Df and Dm, were introduced to study the distribution width of phase dimensions in the dimensionless region and the uniformity of the spatial distribution of particles, respectively. The results showed that the average characteristic length Lm and Df increase as the volume fraction of the dispersed phase increases, when the volume fraction of the dispersed phase is lower than 50%. In other words, the size of particles increases and their distribution in the dimensionless region becomes more uniform. Meanwhile, the uniformity of the spatial distribution becomes more perfect as the volume fraction increases. At a certain composition, Lm decreases in the initial stage of the mixing and levels off in the late stage. In the initial stage, Df becomes large rapidly with the process of blending, which means that the distribution of L in the dimensionless region becomes more uniform. Meanwhile, the spatial distribution tends to be ideal rapidly in the early stage and fluctuates in a definite range in the late stage of the mixing.
基金supported by Technical Center for High-Performance Valves from the Regional Innovation Center (RIC) Program of the Ministry of Knowledge Economy (MKE),Korea
文摘An approach for analyzing and optimizing sealing mechanism of ball valve made of nitrile butadiene rubber(NBR) with finite element method was presented. The Mooney-Rivlin hyperelastic material model was chosen to characterize NBR sealing, as it has been recommended in the similar applications. That is, NBR sealing was modeled as incompressible hyperelasticity, as well as the assumption of isotropic flow. The results illustrate the structural pressure and contact pressure on the contact surface, which shows that the NBR sealing mechanism is very suitable for sealing after dimension optimization.
基金supported by Major Program of National Natural Science Foundation of China(No. 20836007)National Natural Science Foundation of China(No.20806067).
文摘<正>Polystyrene-styrene/butadiene diblock copolymers were synthesized via reversible addition-fragmentation chain transfer (RAFT) miniemulsion polymerization.During the polymerization process,the molecular weight distribution was narrow and the numerical molecular weight of the copolymers increased with increasing conversion of monomers,which was close to the theoretical.FT-IR and ~1H NMR results indicated that the microstructure of the polymer was mainly 1,4-trans-butadiene with small amount of 1,2-units,and composition in the copolymers was obtained.
文摘In this paper, acrylonitrile-butadiene-styrene(ABS) nanocomposite foams are produced using carbon dioxide through the solid-state batch process. Microcellular closed-cell foams are produced with the relative density ranging from 0.38 to 0.97. The effects of the processing conditions on the density, morphology, and flexural properties of ABS and its nanocomposite foams are studied. It is found that nanoclay particles, as nucleating sites, play an important role in reducing the size of cells and increasing their number in the unit volume of foamed polymer, as well as increasing the flexural modulus of foam through reinforcing its matrix.
文摘The residual levels and migration behavior of volatile substances were detected using HS-GC/MS for acrylonitrile-butadiene-styrene copolymer (ABS) toys, thermoplastic elastomer toys, and rubber toys made from 1,3-butadiene and styrene found on the Japanese market. The maximum residual level of these volatile substances was 2600 μg/g of styrene in ABS toys. In particular, the levels of known carcinogens 1,3-butadiene, benzene, and acrylonitrile are 5.3, 2.5 and 55 μg/g, which are much lower than the EU limit of 0.1%. Furthermore, some volatile substances migrated from ABS toys into water in amounts of 3 -40 ng/mL. Thermoplastic elastomer toys and rubber toys contained these volatile substances at significantly lower levels than ABS toys.
文摘Palm fiber (PF) reinforced acrylonitrile butadiene styrene (ABS) composite matrix was prepared by employing Injection Moulding Machine (IMM). Palm fiber was collected from ten different trees of different age group from Comilla region in Bangladesh. Three sets of samples were prepared for three different wt% (5%, 10% and 20%) of fiber contents. The mechanical (tensile strength, flexural stress, micro hardness, Leeb’s rebound hardness) and physical (bulk density and water absorption) properties were measured. The observed result reveals that the tensile strength (TS) and flexural stress (FS) were decreased with increasing fiber contents in the PF-ABS composites except 10% fiber content.
基金supported financially by the National Natural Science Foundation of China (Project No.51273071)
文摘A new fourth-generation poly(propylene imine) dendrimer(G4-M) containing 32 triolefinic 15-membered macrocycles on the surfaces has been synthesized. The bimetallic Ru Rh dendrimer-stabilized nanoparticles(DSNs) were first prepared within G4-M by a co-complexation route. The new G4-M dendrimer has been characterized by 1H nuclear magnetic resonance, infrared radiation, and elemental analysis.The dendrimer-stabilized bimetallic ions and reduction courses were analyzed by UV-vis spectroscopy. Highresolution transmission electron microscopy and energy dispersive spectrometer were used to characterize the bimetallic nanoparticle size, size distribution, and particle morphology. The Ru Rh bimetallic DSNs showed high catalytic activity for the hydrogenation of nitrile-butadiene rubber.
基金Funded by the National Natural Science Foundation of China (Nos.20674063 and 20774074)the Specialized Research Fund for the Doctoral Program of Higher Education (20050736001)
文摘Palygorskite (PGS) and vinyl tris-(2-methoxyethoxy) silane (KH-172) modified palygorskite (OPGS) were used to prepare acrylonitrile-butadiene-styrene (ABS)/clay composites. Thermal stability of the composites was evaluated by using thermogravimetric analysis (TGA). The morphology of the fractured surface and the degree of dispersion of the clay in the ABS matrix were observed by scanning electron microscopy (SEM). X-ray diffraction (XRD) analysis results showed the variation of the crystal structure. Measurements of the tensile properties of the ABS/clay composites proved that the ABS/OPGS composited material represented the most excellent tensile property, because of good compatibility and dispersion of ABS with OPGS.
文摘This paper mainly deals with the design and synthesis of a novel styrene-butadieneblock copolymer. When this copolymer is used in the tread portion of tyres, it can improvewet skid resistance and reduce rolling resistance without sacrificing its general physical-mechanical properties. The visco-elastic curve of tire tread using the novel copolymer asits rubber portion was showed. Reactivity ratios for two monomers in the polymerizingsystem were calculated. The diagrams of differelitial, integral and finite difference calculithroughout the whole molecular chain were presented. The influence of the micro- andmacro-structure of the copolymer chain on wet skid resistance and rolling resistance
文摘With the advent of plastics and the wide range of fillers that are available have made modifications as precise as the tailored resins themselves. To modify the properties of polymer either by using fillers or by preparation of polymer blends gives rise to new materials with tailored properties. More complex, three-component systems, obtained by the addition of polymeric modifier to polymer filled composites may be of interest. Use of Fly ash cenospheres is very attractive because it is inexpensive and its use can reduce the environmental pollution to a significant extent. In the present study, Poly (Methyl Methacrylate) (PMMA)-Fly ash cenospheres composites were prepared using extrusion followed by Injection molding. The effect of matrix modification with Methyl methacrylate– acrylonitrile -butadiene–styrene (MABS) on the performance of PMMA- Fly ash cenospheres compositions was also, studied. It was found that with the addition of Fly ash cenospheres particulate as filler in PMMA showed marginal reduction in Tensile Strength, % Elongation and Impact strength and improvement in Flexural Strength, Heat Deflection Temperature and Vicat Softening Point. Compared with PMMA-cenospheres composites, the notched Impact Strength of the PMMA/MABS/cenospheres composites showed marginal enhancement in values at higher loading of cenospheres. The optimum performances in mechanical and thermal properties were obtained when the ratio of MABS to cenospheres was 1:2.
文摘In this paper, the effects of build parameters on the mechanical properties of 3D-printed acrylonitrile butadiene styrene (ABS) produced using fused deposition modeling (FDM) are investigated. Full factorial experimental design incorporating a 2-level, 3-factor design with raster angle, layer thickness and interior fill style was carried out. Tensile tests were performed at four different strain rates to determine how the build parameters influence the mechanical properties of the 3-D printed ABS and to assess its strain rate sensitivity under quasi-static loading. It was found that the modulus of toughness of ABS material is most influenced by raster angle, while the interior fill style is the most dominant build parameter that dictates the specimen’s modulus of resilience, yield strength and ultimate tensile strength. At all strain rates, it is further revealed that higher mean values of yield strength, ultimate tensile strength and modulus of resilience were obtained when the interior fill style is solid as opposed to high density. This can be attributed to the denser structure and higher effective cross-sectional area in solid interior fill style in comparison with high density interior fill style. However, the influence of the layer thickness on the investigated mechanical properties was found to be inconsistent. It was noted that specimens built with both 0.254 mm layer thickness and the cross [0°/90°] raster angle had superior mechanical properties when compared to those built with the 0.3302 mm layer thickness and cross [0°/90°] raster angle. This suggests that there is a key interaction between the layer thickness and the raster angle. At any FDM build parameter, it was found that all the mechanical properties investigated in this work exhibited modest sensitivity to strain rates. This study has provided a platform for an appropriate selection of build parameters combinations and strain rates for additive manufacturing of 3D-printed ABS with improved mechanical properties.
基金Supported by the National Natural Science Foundation of China(50573005)
文摘A novel multifunctional macromolecular organolithium initiator (PD-Sn-(RLi)3) was prepared via living anionic polymerization and used for the synthesis of miktoarm star copolymers in cyclohexane. The average molecular weight, polydispersity index, microstructure and unit composition of the miktoarm star copolymers were characterized with GPC and 1H-NMR. Performances of the miktoarm star styrene-butadiene rubbers were investigated in comparison with those of the blend rubbers such as the tin-coupled star-shaped random copolymers of styrene-butadiene rubber(S-SBR)/natural rubber(NR) blend rubber and S-SBR/Cis-1, 4-polybutadiene rubber (Cis-BR) blend rubber.
文摘Interpenetrating polymer networks(IPNs)based on fluoroelastomer/butadiene-acrylonitrile rubber(FKM/NBR)by molten blending at a high temperature and chemical cross-linking of two components were prepared.The influence of the two networks component on the mechanical properties and thermostabilities was studied.The experimental results show that the mechanical properties of the IPNs are superior to those of the individual FKM and NBR networks due to forming the case of interpenetrating and intercross-linking between the two networks,the mechanical properties and thermal resistance exhibit higher values when 80/20 (w/w)FKM and NBR is blended and respectively cured simultaneously.The co-continuous morphology of the IPNs in the blends of 80/20(w/w)FKM/NBR is found by transmission electron microscopy(TEM),the differential scanning calorimetry(DSC)determination shows that the blends of 80/20(w/w)FKM/NBR have better compatibility,and the glass transition temperature of the elastomer is -21.5℃,
文摘This investigation presents thermoplastic elastomers (TPEs) based on poly (styrene-butadiene-styrene) (SBS) and thermoplastic polyurethane (TPU) materials were prepared with varying compositions. A series of works were conducted on the relationships between rheological, optical properties, morphology, mechanical properties, abrasion resistance and thermostability given. The results showed that the shear viscosity of SBS not obvious effect with TPU content. The optical properties of the SBS/TPU blend that its uniform transparency. The morphology characteristics indicating the phase diversion and the variation in the size of the SBS domains from large to small as the TPU contents increased, with heterogeneous domain dispersions. Additionally, the mechanical properties, abrasion resistance and thermal resistance are improved as the amount of added TPU is increased, suggesting that the blending of SBS with TPU is consistent with the compound rule.