The morphologies of intermetallic phases(IMCs)during directional solidification of the Sn-Cu(L+Cu_(3)Sn→Cu_(6)Sn_(5))and Sn-Co(L+CoSn→CoSn_(2))peritectic systems were analyzed.The primary Cu_(3)Sn and peritectic Cu_...The morphologies of intermetallic phases(IMCs)during directional solidification of the Sn-Cu(L+Cu_(3)Sn→Cu_(6)Sn_(5))and Sn-Co(L+CoSn→CoSn_(2))peritectic systems were analyzed.The primary Cu_(3)Sn and peritectic Cu_(6)Sn_(5)phases in Sn-Cu alloy are IMCs whose solubility ranges are narrow,while both the primary CoSn and peritectic CoSn_(2)phases in Sn-Co alloy are IMCs whose solubility ranges are nil in equilibrium condition.The experimental results before acid corrosion shows that the dendritic morphology of both the Cu_(6)Sn_(5)and CoSn_(2)phases can be observed.The investigation on the local dendritic morphology after deep acid corrosion shows that these dendrites are composed of small sub-structures with faceted feature.Faceted growth of the primary Cu_(3)Sn and CoSn phases is also confirmed,and a faceted to non-faceted transition in their morphologies is observed with increasing growth velocities.Further analysis shows that the dendritic morphology is formed in the solidified phases whose solubility range is larger during peritectic solidification.展开更多
基金the support of the National Natural Science Foundation of China (Grant No. 51871118)the Fast Support Project (Grant No. JZX7Y20210162400301)the fund of State Key Laboratory of Special Rare Metal Materials (Grant No. SKL2020K003)
文摘The morphologies of intermetallic phases(IMCs)during directional solidification of the Sn-Cu(L+Cu_(3)Sn→Cu_(6)Sn_(5))and Sn-Co(L+CoSn→CoSn_(2))peritectic systems were analyzed.The primary Cu_(3)Sn and peritectic Cu_(6)Sn_(5)phases in Sn-Cu alloy are IMCs whose solubility ranges are narrow,while both the primary CoSn and peritectic CoSn_(2)phases in Sn-Co alloy are IMCs whose solubility ranges are nil in equilibrium condition.The experimental results before acid corrosion shows that the dendritic morphology of both the Cu_(6)Sn_(5)and CoSn_(2)phases can be observed.The investigation on the local dendritic morphology after deep acid corrosion shows that these dendrites are composed of small sub-structures with faceted feature.Faceted growth of the primary Cu_(3)Sn and CoSn phases is also confirmed,and a faceted to non-faceted transition in their morphologies is observed with increasing growth velocities.Further analysis shows that the dendritic morphology is formed in the solidified phases whose solubility range is larger during peritectic solidification.