Preparation of natural brucite nanofibers by the dispersion method 被引量:2
1
作者 Li Xu Wen Ni +3 位作者 Wenping Li Xingde Liu Hailong Yang Xiaoguang Yang 《Journal of University of Science and Technology Beijing》 CSCD 2008年第4期489-494,共6页
The preparation of natural brucite nanofibers through dispersion by the wet process is described. The test results indicate that brucite fibers can be well dispersed by using sodium dioctyl sulfosuccinate (OT) as th... The preparation of natural brucite nanofibers through dispersion by the wet process is described. The test results indicate that brucite fibers can be well dispersed by using sodium dioctyl sulfosuccinate (OT) as the dispersant at a dispersant/fiber mass ratio of 0.15:1, dispersing for 30 min at a water/solid mass ratio of 20:1. The prepared nanofibers were characterized with X-ray diffraction (XRD), scanning electron microscope (SEM), and transmission electron microscope (TEM). It is shown that the prepared single brucite nanofiber is around 30 nm in diameter and the talus of the nonsingle brucite nanofibers is about 50-150 nm in diameter. Natural brucite mineral fibers were treated by the dispersion method to obtain nanomaterials. These fibers have significant advantages over artificial nanofibers both in yield and in cost. 展开更多
关键词 BRUCITE NANOFIBER sodium dioctyl sulfosuccinate (OT) ULTRASONIC dispersion method
下载PDF
Electroneutral Quaternization/Sulfosuccination for Alleviating the Adverse Effect of Paste Aging on the Properties of Corn Starch Film 被引量:3
2
作者 李伟 祝志峰 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2017年第2期482-490,共9页
For the purpose of alleviating the adverse effect of paste aging on the properties of corn starch film, a series of electroneutrally quaternized/sulfosuccinylated starches(EQSS) with different degrees of substitutio... For the purpose of alleviating the adverse effect of paste aging on the properties of corn starch film, a series of electroneutrally quaternized/sulfosuccinylated starches(EQSS) with different degrees of substitution(DS) were synthesized via the quaternization/sulfosuccination of acid-thinned corn starch(ATS) by varying the amounts of N-(3-chloro-2-hydroxypropl) trimethylammonium chloride, maleic anhydride, and sodium hydrogen sulfite. The influence of paste aging on the properties of starch film cast from heat-induced starch paste was investigated and the properties were explored in terms of tensile strength, elongation, work at break, degree of crystallinity, and flex-fatigue resistance. The experimental results showed that the paste ageing generated adverse influence on the elongation, work at break, and flex-fatigue resistance of starch film. Further experiments showed that electroneutral quaternization/sulfosuccination of starch were able to alleviate the negative effect of paste ageing on the elongation, work at break, and flex-fatigue resistance, thereby obviously enhancing the elongation, work at break and flex-fatigue resistance, and thus reducing the drawback of brittleness. The enhancement depended on the amounts of the substituents introduced. With the increase in DS value, the elongation and work at break as well as flex-fatigue resistance continuously rose, whereas the tensile strength gradually reduced. 展开更多
关键词 starch film ageing starch paste electroneutral quaternization/sulfosuccination tensile properties