The microstmcture evolution of plastic-bonded explosives （PBXs） after thermal stimulus plays a key role in PBX performance. In this paper, the nanoscale pores of thermal-treated octahydro-1,3,5,7-tetranitro-1,3,5,7 ...The microstmcture evolution of plastic-bonded explosives （PBXs） after thermal stimulus plays a key role in PBX performance. In this paper, the nanoscale pores of thermal-treated octahydro-1,3,5,7-tetranitro-1,3,5,7 tetrazocine （HMX）- based PBXs with different HMX particle sizes [approximately 40 （FLIP） and 100 μm （LHP）] were measured using small- angle X-ray scattering （SAXS）. No obvious pore variations were found in the LHP samples heated at 160 ℃ for 6 h, whereas the amount of pores of FHP decreased when subjected to 160 ℃ for 6 h. At 180 ℃, the average pore radii of FHP and LHP decreased from approximately 45 nm to 25 nm, and the total pore volume increased distinctively because of phase transformation. The LHP sample reached a high level of pore content after being held at 180 ℃ for 1 h, whereas FHP required 3 h. Both FHP and LHP had relatively high pore volumes when subjected to 200 ℃ for 1 and 3 h.展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.11205137,11079043,and 11302199)
文摘The microstmcture evolution of plastic-bonded explosives （PBXs） after thermal stimulus plays a key role in PBX performance. In this paper, the nanoscale pores of thermal-treated octahydro-1,3,5,7-tetranitro-1,3,5,7 tetrazocine （HMX）- based PBXs with different HMX particle sizes [approximately 40 （FLIP） and 100 μm （LHP）] were measured using small- angle X-ray scattering （SAXS）. No obvious pore variations were found in the LHP samples heated at 160 ℃ for 6 h, whereas the amount of pores of FHP decreased when subjected to 160 ℃ for 6 h. At 180 ℃, the average pore radii of FHP and LHP decreased from approximately 45 nm to 25 nm, and the total pore volume increased distinctively because of phase transformation. The LHP sample reached a high level of pore content after being held at 180 ℃ for 1 h, whereas FHP required 3 h. Both FHP and LHP had relatively high pore volumes when subjected to 200 ℃ for 1 and 3 h.