Hierarchical nano-sized ZSM-5 aggregates were successfully synthesized via a seed-assisted method in the presence of cetyltrimethylammonium bromide(CTAB)through a facile one-step crystallization process.Commercial ZSM...Hierarchical nano-sized ZSM-5 aggregates were successfully synthesized via a seed-assisted method in the presence of cetyltrimethylammonium bromide(CTAB)through a facile one-step crystallization process.Commercial ZSM-5 zeolites with a SiO2/Al2O3 ratio comparable to that of ZSM-5 products were treated with alkali and used as the seed particles.The influences of crystallization conditions were investigated,and the possible synthesis mechanism was proposed.ZSM-5 zeolites with diff erent amounts of CTAB added were characterized using many techniques and evaluated in toluene alkylation with methanol.The results showed that a trace amount of CTAB signifi cantly promoted the crystallization of ZSM-5 zeolite,with the morphology changing from hexagonal-shape crystals to uniform spherical aggregates.CTAB may act as the structure-directing agent and assemble the primary crystallites to generate hierarchical ZSM-5 aggregates.The ZSM-5 zeolite with the smallest primary particles of 50-80 nm exhibited large specific surface area,abundant mesopores,and the greatest microporosity.The hierarchical nano-sized ZSM-5 aggregate showed higher toluene conversion and a longer lifetime without compromising the selectivity to xylene and p-xylene in toluene alkylation with methanol.展开更多
Core-shell structured ZSM-5@Silicalite-1 zeolite could effectively hinder the deactivation of catalyst surface. Currently, organic structure directing agents(OSDAs) are necessary in the conventional route for the synt...Core-shell structured ZSM-5@Silicalite-1 zeolite could effectively hinder the deactivation of catalyst surface. Currently, organic structure directing agents(OSDAs) are necessary in the conventional route for the synthesis of this core-shell zeolite under hydrothermal conditions, which is costly and environmental-unfriendly. In this research, a synthesis of the core-shell structured ZSM-5@Silicalite-1 zeolite with a strategy of alcohol filling and zeolite seeding without any organic template or solvent is exhibited. The obtained products are well characterized by X-ray powder diffractometer(XRD), scanning electron microscopy(SEM), transmission electron microscopy(TEM), N2 sorption isotherms, solid magic angle spinning(MAS) NMR, temperature-programmed-desorption of ammonia(NH3-TPD), and X-ray photoelectron spectroscopy(XPS) techniques, in order to confirm the core-shell structure. More importantly, the core-shell structured ZSM-5@Silicalite-1 zeolite exhibits a long lifetime and a high p-xylene selectivity in the alkylation of toluene with methanol, compared with the conventional ZSM-5 catalyst.展开更多
基金supported by the National Natural Science Foundation of China(No.21276183).
文摘Hierarchical nano-sized ZSM-5 aggregates were successfully synthesized via a seed-assisted method in the presence of cetyltrimethylammonium bromide(CTAB)through a facile one-step crystallization process.Commercial ZSM-5 zeolites with a SiO2/Al2O3 ratio comparable to that of ZSM-5 products were treated with alkali and used as the seed particles.The influences of crystallization conditions were investigated,and the possible synthesis mechanism was proposed.ZSM-5 zeolites with diff erent amounts of CTAB added were characterized using many techniques and evaluated in toluene alkylation with methanol.The results showed that a trace amount of CTAB signifi cantly promoted the crystallization of ZSM-5 zeolite,with the morphology changing from hexagonal-shape crystals to uniform spherical aggregates.CTAB may act as the structure-directing agent and assemble the primary crystallites to generate hierarchical ZSM-5 aggregates.The ZSM-5 zeolite with the smallest primary particles of 50-80 nm exhibited large specific surface area,abundant mesopores,and the greatest microporosity.The hierarchical nano-sized ZSM-5 aggregate showed higher toluene conversion and a longer lifetime without compromising the selectivity to xylene and p-xylene in toluene alkylation with methanol.
基金This work was supported by the National Key Research and Development Program of China(No.2017YFB0702803)the Fundamental Research Funds for the Central Universities,China(No.2021QNA4028)the National Natural Science Foundation of China(Nos.21802121,2217020097,21720102001).
文摘Core-shell structured ZSM-5@Silicalite-1 zeolite could effectively hinder the deactivation of catalyst surface. Currently, organic structure directing agents(OSDAs) are necessary in the conventional route for the synthesis of this core-shell zeolite under hydrothermal conditions, which is costly and environmental-unfriendly. In this research, a synthesis of the core-shell structured ZSM-5@Silicalite-1 zeolite with a strategy of alcohol filling and zeolite seeding without any organic template or solvent is exhibited. The obtained products are well characterized by X-ray powder diffractometer(XRD), scanning electron microscopy(SEM), transmission electron microscopy(TEM), N2 sorption isotherms, solid magic angle spinning(MAS) NMR, temperature-programmed-desorption of ammonia(NH3-TPD), and X-ray photoelectron spectroscopy(XPS) techniques, in order to confirm the core-shell structure. More importantly, the core-shell structured ZSM-5@Silicalite-1 zeolite exhibits a long lifetime and a high p-xylene selectivity in the alkylation of toluene with methanol, compared with the conventional ZSM-5 catalyst.