With the growing interest in utilizing Mg and austenitic stainless steel(ASS)in the automotive sector,joining them together in three-sheet configuration is inevitable.However,achieving this task presents considerable ...With the growing interest in utilizing Mg and austenitic stainless steel(ASS)in the automotive sector,joining them together in three-sheet configuration is inevitable.However,achieving this task presents considerable challenges due to the large differences in their physical,metallurgical and mechanical properties.To overcome these challenges,the feasibility of using weld-bonding to join Mg alloy/ASS/ASS was investigated.The nugget formation,interface characteristics,microstructure and mechanical properties of the joints were investigated.The results show that the connection between the Mg alloy and upper ASS was achieved through the combined effect of the cured adhesive and weld-brazing in the weld zone.On the other hand,a metallurgical bond was formed at the ASS/ASS interface.The Mg nugget microstructure exhibited fine columar grains composed predominantly of primaryα-Mg grains along with a eutectic mixture ofα-Mg andβ-Mg17Al12.The nugget formed at the ASS/ASS interface consisted largely of columnar grains of austenite,with some equiaxed dendritic grains formed at the centerline of the joint.The weld-bonded joints exhibited an average peak load and energy absorption of about 8.5 kN and 17 J,respectively(the conventional RSW joints failed with minimal or no load application).The failure mode of the joints changed with increasing welding current from interfacial failure via the Mg nugget/upper ASS interface to partial interfacial failure(part of the Mg nugget was pulled out of the Mg sheet).Both failure modes were accompanied by cohesive failure in the adhesive zone.展开更多
Resistance spot welding and hybrid weld bonding have wide applications in the body work construction within the automobile industry. The integrity of the spot welds and applied adhesives determines the body assembly r...Resistance spot welding and hybrid weld bonding have wide applications in the body work construction within the automobile industry. The integrity of the spot welds and applied adhesives determines the body assembly rigidity and dynamic performance. Incorporating contact nonlinearity and geometric nonlinearity, finite element analysis (FEA) have been carried out to investigate the structural stiffness and strength of both spot-welded and weld-bonded assemblies. Topology optimization has been performed to reveal the distributions of material effectiveness in the overlap regions and suggest a feasible method for removing underutilized material for weight reduction. Design optimization has been conducted with an aim to reduce the maximum von Mises stress in the assembly to minimum by choosing optimum values for a set of design variables, including the weld spacing, weld diameter and overlap width.展开更多
基金Supported by National Natural Science Foundation of China (Grant No.52075378)Prince Sattam Bin Abdulaziz University of Saudi Arabia (Grant No.PSAU/2024/R/1445)。
文摘With the growing interest in utilizing Mg and austenitic stainless steel(ASS)in the automotive sector,joining them together in three-sheet configuration is inevitable.However,achieving this task presents considerable challenges due to the large differences in their physical,metallurgical and mechanical properties.To overcome these challenges,the feasibility of using weld-bonding to join Mg alloy/ASS/ASS was investigated.The nugget formation,interface characteristics,microstructure and mechanical properties of the joints were investigated.The results show that the connection between the Mg alloy and upper ASS was achieved through the combined effect of the cured adhesive and weld-brazing in the weld zone.On the other hand,a metallurgical bond was formed at the ASS/ASS interface.The Mg nugget microstructure exhibited fine columar grains composed predominantly of primaryα-Mg grains along with a eutectic mixture ofα-Mg andβ-Mg17Al12.The nugget formed at the ASS/ASS interface consisted largely of columnar grains of austenite,with some equiaxed dendritic grains formed at the centerline of the joint.The weld-bonded joints exhibited an average peak load and energy absorption of about 8.5 kN and 17 J,respectively(the conventional RSW joints failed with minimal or no load application).The failure mode of the joints changed with increasing welding current from interfacial failure via the Mg nugget/upper ASS interface to partial interfacial failure(part of the Mg nugget was pulled out of the Mg sheet).Both failure modes were accompanied by cohesive failure in the adhesive zone.
文摘Resistance spot welding and hybrid weld bonding have wide applications in the body work construction within the automobile industry. The integrity of the spot welds and applied adhesives determines the body assembly rigidity and dynamic performance. Incorporating contact nonlinearity and geometric nonlinearity, finite element analysis (FEA) have been carried out to investigate the structural stiffness and strength of both spot-welded and weld-bonded assemblies. Topology optimization has been performed to reveal the distributions of material effectiveness in the overlap regions and suggest a feasible method for removing underutilized material for weight reduction. Design optimization has been conducted with an aim to reduce the maximum von Mises stress in the assembly to minimum by choosing optimum values for a set of design variables, including the weld spacing, weld diameter and overlap width.