Sodium with low cost and high abundance is considered as a substitute element of lithium for batteries and supercapacitors,which need the appropriate host materials to accommodate the relatively large Na^(+) ions.Comp...Sodium with low cost and high abundance is considered as a substitute element of lithium for batteries and supercapacitors,which need the appropriate host materials to accommodate the relatively large Na^(+) ions.Compared to Li^(+) storage,Na^(+) storage makes higher demands on the structural optimization of perovskite bismuth ferrite(BiFeO_(3)).We propose a novel strategy of defect engineering on BiFeO_(3) through Na and V codoping for high-efficiency Na^(+) storage,to reveal the roles of oxygen vacancies and V ions played in the enhanced electrochemical energy storage performances of Na-ion capacitors.The formation of the oxygen vacancies in the Na and V codoped BiFeO_(3)(denoted as NV-BFO),is promoted by Na doping and suppressed by V doping,which can be demonstrated by XPS and EPR spectra.By the first-principles calculations,the oxygen vacancies and V ions in NV-BFO are confirmed to substantially lower the Na^(+)migration energy barriers through the space and electric field effects,to effectively promote the Na^(+) transport in the crystals.Electrochemical kinetic analysis of the NV-BFO//NV-BFO capacitors indicates the dominant capacitive-controlled capacity,which depends on fast Na^(+) deintercalation-intercalation process in the NV-BFO electrode.The NV-BFO//NV-BFO capacitors open up a new avenue for developing highperformance Na-ion capacitors.展开更多
The safe operating voltage and low volume variation of Li_(3)VO_(4)(LVO)make it an ideal anode material for lithium(Li)-ion batteries.However,the insufficient understanding of the inner storage mechanism hinders the d...The safe operating voltage and low volume variation of Li_(3)VO_(4)(LVO)make it an ideal anode material for lithium(Li)-ion batteries.However,the insufficient understanding of the inner storage mechanism hinders the design of LVO-based electrodes.Herein,we investigate,for the first time,the Li-ion storage activity in LVO via Cl doping.Moreover,N-doped C coating was simultaneously achieved in the Cl doping process,resulting in synergistically improved reaction kinetics.As a result,the as-prepared Cl-doped Li_(3)VO_(4) coated with N-doped C(Cl-LVO@NC)electrodes deliver a discharge capacity of 884.1 mAh/g after 200 cycles at 0.2 A/g,which is the highest among all of the LVO-based electrodes.The Cl-LVO@NC electrodes also exhibit high-capacity retention of 331.1 mAh/g at 8.0 A/g and full capacity recovery after 5 periods of rate testing over 400 cycles.After 5000 cycles at 4.0 A/g,the discharge capacity can be maintained at 423.2 mAh/g,which is superior to most LVO-based electrodes.The Li-ion storage activity in LVO via Cl doping and significant improvement in the high-rate Li-ion storage reported in this work can be used as references for the design of advanced LVO-based electrodes for high-power applications.展开更多
The activation of H_(2)O is a key step of the COS hydrolysis,which may be tuned by oxygen vacancy defects in the catalysts.Herein,we have introduced Cu into Co_(3)O_(4) to regulate the oxygen vacancy defect content of...The activation of H_(2)O is a key step of the COS hydrolysis,which may be tuned by oxygen vacancy defects in the catalysts.Herein,we have introduced Cu into Co_(3)O_(4) to regulate the oxygen vacancy defect content of the catalysts.In situ DRIFTS and XPS spectra reveal that COS and H_(2)O are adsorbed and activated by oxygen vacancy.The 10 at%Cu doped Co_(3)O_(4) sample(10Cu-Co_(3)O_(4))exhibits the optimal activity,100%of COS conversion at 70℃.The improved oxygen vacancies of CueCo_(3)O_(4) accelerate the activation of H_(2)O to form active -OH.COS binds with hydroxyl to form the intermediate HSCO^(-)_(2),and then the activated-OH on the oxygen vacancy reacts with HSCO^(-)_(2) to form HCO^(-)_(3).Meanwhile,the catalyst exhibits high catalytic stability because copper species(Cu+/Cu^(2+))redox cycle mitigate the sulfation of Co_(3)O_(4)(Co^(2+)/Co^(3+)).Our work offers a promising approach for the rational design of cobalt-related catalysts in the highly efficient hydrolysis COS process.展开更多
Sn doping is an effective way to improve the response rate of Ga_(2)O_(3) film based solar-blind detectors. In this paper,Sn-doped Ga_(2)O_(3) films were prepared on a sapphire substrate by radio frequency magnetron s...Sn doping is an effective way to improve the response rate of Ga_(2)O_(3) film based solar-blind detectors. In this paper,Sn-doped Ga_(2)O_(3) films were prepared on a sapphire substrate by radio frequency magnetron sputtering. The films were characterized by X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy and ultraviolet visible spectroscopy, and the effect of annealing atmosphere on the properties of films was studied. The Ga_(2)O_(3) films changed from amorphous to β-Ga_(2)O_(3) after annealing at 900 °C. The films were composed of micro crystalline particles with a diameter of about 5–20 nm.The β-Ga_(2)O_(3) had high transmittance for wavelengths above 300 nm, and obvious absorption for solar-blind signals at 200–280 nm.The metal semiconductor metal type solar-blind detectors were prepared. The detector based on Sn-doped β-Ga_(2)O_(3) thin film annealed in N_2 has the best response performance to 254 nm light. The photo-current is 10 μA at 20 V, the dark-current is 5.76 pA,the photo dark current ratio is 1.7 × 10~6, the response rate is 12.47 A/W, the external quantum efficiency is 6.09 × 10~3%, the specific detection rate is 2.61 × 10~(12) Jones, the response time and recovery time are 378 and 90 ms, respectively.展开更多
采用高温固相法合成了La_(2)MgTiO_(6)∶Mn^(4+)、La_(2)MgTiO_(6)∶Pr^(3+)、La_(2)MgTiO_(6)∶Pr^(3+),Mn^(4+)单掺杂和双掺杂荧光粉,并通过X射线衍射、扫描电镜、荧光光谱等测试方法对荧光粉的物相结构、形貌和发光特性进行了表征及...采用高温固相法合成了La_(2)MgTiO_(6)∶Mn^(4+)、La_(2)MgTiO_(6)∶Pr^(3+)、La_(2)MgTiO_(6)∶Pr^(3+),Mn^(4+)单掺杂和双掺杂荧光粉,并通过X射线衍射、扫描电镜、荧光光谱等测试方法对荧光粉的物相结构、形貌和发光特性进行了表征及分析。结果表明:成功合成了La_(2)MgTiO_(6)∶Mn^(4+)、La_(2)MgTiO_(6)∶Pr^(3+)、La_(2)MgTiO_(6)∶Pr^(3+),Mn^(4+)荧光粉且均为纯相;样品的粒径为1~2μm;La_(2)MgTiO_(6)∶Mn^(4+)在650~750 nm的红光发射是来自Mn^(4+)的2 E 1→4 A 2跃迁,La_(2)MgTiO_(6)∶Pr^(3+)在红光区域600~660 nm具有强烈的发射,归属为Pr^(3+)的3 P 0→3 H 6和3 P 0→3 F 2跃迁。当Mn^(4+)与Pr^(3+)共同掺杂于La_(2)MgTiO_(6)时,来自Mn^(4+)、Pr^(3+)不同波段的红光发射使荧光粉的发射光谱与植物光敏色素P r与P fr吸收光谱的重叠程度大幅增加,表明Mn^(4+)、Pr^(3+)共掺有效拓宽了La_(2)MgTiO_(6)荧光粉的红光发射区域,更符合植物照明的需求,在LED植物照明领域具有更明显的潜在应用价值。展开更多
文章主要研究了Y_(2)SiO_(5):Pr^(3+)上转换纳米荧光粉对ZnO:Pr^(3+)的光催化性能的影响,通过XRD、FE-SEM、FL和UV-Vis对样品的物相、形貌、发光性能和光催化行性能进行了分析表征,实验结果表明:随着Y_(2)SiO_(5):Pr^(3+)上转换纳米荧...文章主要研究了Y_(2)SiO_(5):Pr^(3+)上转换纳米荧光粉对ZnO:Pr^(3+)的光催化性能的影响,通过XRD、FE-SEM、FL和UV-Vis对样品的物相、形貌、发光性能和光催化行性能进行了分析表征,实验结果表明:随着Y_(2)SiO_(5):Pr^(3+)上转换纳米荧光粉的加入量增加,ZnO:Pr^(3+)光催化效率逐渐提高,当加入0.2 g Y_(2)SiO_(5):Pr^(3+)时,光催化效率最高,在光照60 min后对亚甲基蓝的降解率达到了98.11%,相比未加入Y_(2)SiO_(5):Pr^(3+)时的光催化效率有显著提升。展开更多
Charging P2-Na_(2/3)Ni_(1/3)Mn_(2/3)O_(2)to 4.5 V for higher capacity is enticing.However,it leads to severe capacity fading,ascribing to the lattice oxygen evolution and the P2-O2 phase transformation.Here,the Mg Fe_...Charging P2-Na_(2/3)Ni_(1/3)Mn_(2/3)O_(2)to 4.5 V for higher capacity is enticing.However,it leads to severe capacity fading,ascribing to the lattice oxygen evolution and the P2-O2 phase transformation.Here,the Mg Fe_(2)O_(4) coating and Mg,Fe co-doping were constructed simultaneously by Mg,Fe surface treatment to suppress lattice oxygen evolution and P2-O2 phase transformation of P2-Na_(2/3)Ni_(1/3)Mn_(2/3)O_(2)at deep charging.Through ex-situ X-ray diffraction(XRD)tests,we found that the Mg,Fe bulk co-doping could reduce the repulsion between transition metals and Na+/vacancies ordering,thus inhibiting the P2-O2 phase transition and significantly reducing the irreversible volume change of the material.Meanwhile,the internal electric field formed by the dielectric polarization of Mg Fe_(2)O_(4) effectively inhibits the outward migration of oxidized O^(a-)(a<2),thereby suppressing the lattice oxygen evolution at deep charging,confirmed by in situ Raman and ex situ XPS techniques.P2-Na NM@MF-3 shows enhanced high-voltage cycling performance with capacity retentions of 84.8% and 81.3%at 0.1 and 1 C after cycles.This work sheds light on regulating the surface chemistry for Na-layered oxide materials to enhance the high-voltage performance of Na-ion batteries.展开更多
The SrTiO3∶Pr3+ material,co-doped with monovalent Li+,divalent Mg2+,and trivalent Al3+ was prepared by a new sol-gel method. The phase and crystallinity of the synthesized materials were investigated by powder X-ray ...The SrTiO3∶Pr3+ material,co-doped with monovalent Li+,divalent Mg2+,and trivalent Al3+ was prepared by a new sol-gel method. The phase and crystallinity of the synthesized materials were investigated by powder X-ray diffraction(XRD) and scanning electron microcopy(SEM). Among the co-doped ion,Al3+ incorporation caused the least lattice change and had the best crystallinity. Photoluminescence spectra were taken to investigate the luminescence characteristics. We observed a red luminescence change of SrTiO3∶Pr3+ after being co-doped,and a best enhancement on the red luminescence with the trivalent Al3+ was observed. The present results indicated that the charge defect associated with Al3+ has led to charge compensation of Pr+Sr and also implied that the charge defects(usually the second dopant ions replacing the A or B sites in the lattice) which are closer to Pr+Sr contribute more to the red luminescence enhancement.展开更多
基金financial supports from National Natural Science Foundation of China(22005174 and 52271133)。
文摘Sodium with low cost and high abundance is considered as a substitute element of lithium for batteries and supercapacitors,which need the appropriate host materials to accommodate the relatively large Na^(+) ions.Compared to Li^(+) storage,Na^(+) storage makes higher demands on the structural optimization of perovskite bismuth ferrite(BiFeO_(3)).We propose a novel strategy of defect engineering on BiFeO_(3) through Na and V codoping for high-efficiency Na^(+) storage,to reveal the roles of oxygen vacancies and V ions played in the enhanced electrochemical energy storage performances of Na-ion capacitors.The formation of the oxygen vacancies in the Na and V codoped BiFeO_(3)(denoted as NV-BFO),is promoted by Na doping and suppressed by V doping,which can be demonstrated by XPS and EPR spectra.By the first-principles calculations,the oxygen vacancies and V ions in NV-BFO are confirmed to substantially lower the Na^(+)migration energy barriers through the space and electric field effects,to effectively promote the Na^(+) transport in the crystals.Electrochemical kinetic analysis of the NV-BFO//NV-BFO capacitors indicates the dominant capacitive-controlled capacity,which depends on fast Na^(+) deintercalation-intercalation process in the NV-BFO electrode.The NV-BFO//NV-BFO capacitors open up a new avenue for developing highperformance Na-ion capacitors.
基金supported by the National Natural Science Foundation of China(No.52101262)Distinguished Youth Foundation of Hubei Province(2019CFA084)+1 种基金Educational offi ce of Hubei Province(Q20201201)the 111 project(D20015).
文摘The safe operating voltage and low volume variation of Li_(3)VO_(4)(LVO)make it an ideal anode material for lithium(Li)-ion batteries.However,the insufficient understanding of the inner storage mechanism hinders the design of LVO-based electrodes.Herein,we investigate,for the first time,the Li-ion storage activity in LVO via Cl doping.Moreover,N-doped C coating was simultaneously achieved in the Cl doping process,resulting in synergistically improved reaction kinetics.As a result,the as-prepared Cl-doped Li_(3)VO_(4) coated with N-doped C(Cl-LVO@NC)electrodes deliver a discharge capacity of 884.1 mAh/g after 200 cycles at 0.2 A/g,which is the highest among all of the LVO-based electrodes.The Cl-LVO@NC electrodes also exhibit high-capacity retention of 331.1 mAh/g at 8.0 A/g and full capacity recovery after 5 periods of rate testing over 400 cycles.After 5000 cycles at 4.0 A/g,the discharge capacity can be maintained at 423.2 mAh/g,which is superior to most LVO-based electrodes.The Li-ion storage activity in LVO via Cl doping and significant improvement in the high-rate Li-ion storage reported in this work can be used as references for the design of advanced LVO-based electrodes for high-power applications.
基金the National Natural Science Foundation of China (92034301,22078063 and 22022804)Major Program of Qingyuan Innovation Laboratory (00121003)the Natural Science Foundation of Fujian Province (2020H6007)。
文摘The activation of H_(2)O is a key step of the COS hydrolysis,which may be tuned by oxygen vacancy defects in the catalysts.Herein,we have introduced Cu into Co_(3)O_(4) to regulate the oxygen vacancy defect content of the catalysts.In situ DRIFTS and XPS spectra reveal that COS and H_(2)O are adsorbed and activated by oxygen vacancy.The 10 at%Cu doped Co_(3)O_(4) sample(10Cu-Co_(3)O_(4))exhibits the optimal activity,100%of COS conversion at 70℃.The improved oxygen vacancies of CueCo_(3)O_(4) accelerate the activation of H_(2)O to form active -OH.COS binds with hydroxyl to form the intermediate HSCO^(-)_(2),and then the activated-OH on the oxygen vacancy reacts with HSCO^(-)_(2) to form HCO^(-)_(3).Meanwhile,the catalyst exhibits high catalytic stability because copper species(Cu+/Cu^(2+))redox cycle mitigate the sulfation of Co_(3)O_(4)(Co^(2+)/Co^(3+)).Our work offers a promising approach for the rational design of cobalt-related catalysts in the highly efficient hydrolysis COS process.
基金supported by the National Natural Science Foundation of China (Grant No. 62204203)the Shaanxi Natural Science Basic Research Program (Grant No. 2022JQ-701)。
文摘Sn doping is an effective way to improve the response rate of Ga_(2)O_(3) film based solar-blind detectors. In this paper,Sn-doped Ga_(2)O_(3) films were prepared on a sapphire substrate by radio frequency magnetron sputtering. The films were characterized by X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy and ultraviolet visible spectroscopy, and the effect of annealing atmosphere on the properties of films was studied. The Ga_(2)O_(3) films changed from amorphous to β-Ga_(2)O_(3) after annealing at 900 °C. The films were composed of micro crystalline particles with a diameter of about 5–20 nm.The β-Ga_(2)O_(3) had high transmittance for wavelengths above 300 nm, and obvious absorption for solar-blind signals at 200–280 nm.The metal semiconductor metal type solar-blind detectors were prepared. The detector based on Sn-doped β-Ga_(2)O_(3) thin film annealed in N_2 has the best response performance to 254 nm light. The photo-current is 10 μA at 20 V, the dark-current is 5.76 pA,the photo dark current ratio is 1.7 × 10~6, the response rate is 12.47 A/W, the external quantum efficiency is 6.09 × 10~3%, the specific detection rate is 2.61 × 10~(12) Jones, the response time and recovery time are 378 and 90 ms, respectively.
文摘采用高温固相法合成了La_(2)MgTiO_(6)∶Mn^(4+)、La_(2)MgTiO_(6)∶Pr^(3+)、La_(2)MgTiO_(6)∶Pr^(3+),Mn^(4+)单掺杂和双掺杂荧光粉,并通过X射线衍射、扫描电镜、荧光光谱等测试方法对荧光粉的物相结构、形貌和发光特性进行了表征及分析。结果表明:成功合成了La_(2)MgTiO_(6)∶Mn^(4+)、La_(2)MgTiO_(6)∶Pr^(3+)、La_(2)MgTiO_(6)∶Pr^(3+),Mn^(4+)荧光粉且均为纯相;样品的粒径为1~2μm;La_(2)MgTiO_(6)∶Mn^(4+)在650~750 nm的红光发射是来自Mn^(4+)的2 E 1→4 A 2跃迁,La_(2)MgTiO_(6)∶Pr^(3+)在红光区域600~660 nm具有强烈的发射,归属为Pr^(3+)的3 P 0→3 H 6和3 P 0→3 F 2跃迁。当Mn^(4+)与Pr^(3+)共同掺杂于La_(2)MgTiO_(6)时,来自Mn^(4+)、Pr^(3+)不同波段的红光发射使荧光粉的发射光谱与植物光敏色素P r与P fr吸收光谱的重叠程度大幅增加,表明Mn^(4+)、Pr^(3+)共掺有效拓宽了La_(2)MgTiO_(6)荧光粉的红光发射区域,更符合植物照明的需求,在LED植物照明领域具有更明显的潜在应用价值。
文摘文章主要研究了Y_(2)SiO_(5):Pr^(3+)上转换纳米荧光粉对ZnO:Pr^(3+)的光催化性能的影响,通过XRD、FE-SEM、FL和UV-Vis对样品的物相、形貌、发光性能和光催化行性能进行了分析表征,实验结果表明:随着Y_(2)SiO_(5):Pr^(3+)上转换纳米荧光粉的加入量增加,ZnO:Pr^(3+)光催化效率逐渐提高,当加入0.2 g Y_(2)SiO_(5):Pr^(3+)时,光催化效率最高,在光照60 min后对亚甲基蓝的降解率达到了98.11%,相比未加入Y_(2)SiO_(5):Pr^(3+)时的光催化效率有显著提升。
基金supported by the Special Project for the Central Government to Guide Local Technological Development (GUIKE ZY20198008)the Guangxi Technology Base and talent Subject (GUIKE AD20238012,AD20297086)+5 种基金the Natural Science Foundation of Guangxi Province (2021GXNSFDA075012)the National Natural Science Foundation of China (51902108,52104298,22169004)the National Natural Science Foundation of China (U20A20249)the Regional Innovation and Development Joint Fundthe Guangxi Innovation Driven Development Subject (GUIKE AA19182020,19254004)the Special Fund for Guangxi Distinguished Expert。
文摘Charging P2-Na_(2/3)Ni_(1/3)Mn_(2/3)O_(2)to 4.5 V for higher capacity is enticing.However,it leads to severe capacity fading,ascribing to the lattice oxygen evolution and the P2-O2 phase transformation.Here,the Mg Fe_(2)O_(4) coating and Mg,Fe co-doping were constructed simultaneously by Mg,Fe surface treatment to suppress lattice oxygen evolution and P2-O2 phase transformation of P2-Na_(2/3)Ni_(1/3)Mn_(2/3)O_(2)at deep charging.Through ex-situ X-ray diffraction(XRD)tests,we found that the Mg,Fe bulk co-doping could reduce the repulsion between transition metals and Na+/vacancies ordering,thus inhibiting the P2-O2 phase transition and significantly reducing the irreversible volume change of the material.Meanwhile,the internal electric field formed by the dielectric polarization of Mg Fe_(2)O_(4) effectively inhibits the outward migration of oxidized O^(a-)(a<2),thereby suppressing the lattice oxygen evolution at deep charging,confirmed by in situ Raman and ex situ XPS techniques.P2-Na NM@MF-3 shows enhanced high-voltage cycling performance with capacity retentions of 84.8% and 81.3%at 0.1 and 1 C after cycles.This work sheds light on regulating the surface chemistry for Na-layered oxide materials to enhance the high-voltage performance of Na-ion batteries.
基金The Natural Science Foundation of Shaan'xi Province(2005F06)
文摘The SrTiO3∶Pr3+ material,co-doped with monovalent Li+,divalent Mg2+,and trivalent Al3+ was prepared by a new sol-gel method. The phase and crystallinity of the synthesized materials were investigated by powder X-ray diffraction(XRD) and scanning electron microcopy(SEM). Among the co-doped ion,Al3+ incorporation caused the least lattice change and had the best crystallinity. Photoluminescence spectra were taken to investigate the luminescence characteristics. We observed a red luminescence change of SrTiO3∶Pr3+ after being co-doped,and a best enhancement on the red luminescence with the trivalent Al3+ was observed. The present results indicated that the charge defect associated with Al3+ has led to charge compensation of Pr+Sr and also implied that the charge defects(usually the second dopant ions replacing the A or B sites in the lattice) which are closer to Pr+Sr contribute more to the red luminescence enhancement.