Ultrafine oxide dispersion strengthening(ODS)-Mo and ODS-W alloy powders containing different types of oxide nanoparticles were successfully synthesized by spraying method(solid−liquid mixing method)combined with the ...Ultrafine oxide dispersion strengthening(ODS)-Mo and ODS-W alloy powders containing different types of oxide nanoparticles were successfully synthesized by spraying method(solid−liquid mixing method)combined with the reductions with carbon black and hydrogen in sequence.It is concluded that the solution concentration and type of rare earth oxide have no effect on the grain size of ODS-Mo alloy powder,but have obvious effect on that of ODS-W alloy powder.The higher the concentration of rare earth solution is,the smaller the average grain size of ODS-W alloy powder is.Furthermore,compared with doping with CeO_(2),the grain sizes of reduction products of La_(2)O_(3) and Y_(2)O_(3) doped WO_(3) are relatively larger.Compared with the undoped case,there is almost no change for grain size of ODS-Mo alloy powder,while the grain size of ODS-W alloy powder becomes much larger.This is probably due to the appearance of the composite oxide(such as La_(2)WO_(6))formed by the reaction between tungsten oxide and rare earth oxides,which promotes the heterogeneous nucleation and growth of tungsten grains during the reduction process of ODS-W,while there is no complex oxide composed of molybdenum and rare earth oxides in the reduction process of ODS-Mo.展开更多
基金financial support from the National Natural Science Foundation of China (No.51734002)。
文摘Ultrafine oxide dispersion strengthening(ODS)-Mo and ODS-W alloy powders containing different types of oxide nanoparticles were successfully synthesized by spraying method(solid−liquid mixing method)combined with the reductions with carbon black and hydrogen in sequence.It is concluded that the solution concentration and type of rare earth oxide have no effect on the grain size of ODS-Mo alloy powder,but have obvious effect on that of ODS-W alloy powder.The higher the concentration of rare earth solution is,the smaller the average grain size of ODS-W alloy powder is.Furthermore,compared with doping with CeO_(2),the grain sizes of reduction products of La_(2)O_(3) and Y_(2)O_(3) doped WO_(3) are relatively larger.Compared with the undoped case,there is almost no change for grain size of ODS-Mo alloy powder,while the grain size of ODS-W alloy powder becomes much larger.This is probably due to the appearance of the composite oxide(such as La_(2)WO_(6))formed by the reaction between tungsten oxide and rare earth oxides,which promotes the heterogeneous nucleation and growth of tungsten grains during the reduction process of ODS-W,while there is no complex oxide composed of molybdenum and rare earth oxides in the reduction process of ODS-Mo.