To simplify the composite propellant formulation and address the current issue of the single-functionality present in existing additives,the multi-cyano,amine-based polybutadiene(AEHTPB-CN)was prepared based on AEHTPB...To simplify the composite propellant formulation and address the current issue of the single-functionality present in existing additives,the multi-cyano,amine-based polybutadiene(AEHTPB-CN)was prepared based on AEHTPB by adopting appropriate synthesis strategies.By replacing 10% of HTPB binder in the propellant formulation,it can effectively enhance the interfacial bond strength between the propellant binder matrix and solid fillers(AP(ammonium perchlorate)and RDX(cyclotrimethylene-trinitramine)),the mechanical properties of the HTPB/AP/RDX/Al propellant were superior to blank control propellant with an improvement of 35.4% in tensile strength,62.0% enhancement in elongation at break,and reduce the propellant burn rate by 10.7% with any energy loss.The function mechanism of AEHTPB-CN was systematically elucidated through experiments and computer simulation techniques.The results show that the tertiary amine group in AEHTPB-CN can react with AP to form ammonium ionic bonds,and the hydroxyl and cyano groups can form hydrogen bonding interactions with AP,which enables AEHTPB-CN to be firmly adsorbed on the AP surface through chemical and physical interactions.For RDX,the interfacial bonding effect of AEHTPB-CN is attributed to their ability to form C-H···N≡C weak hydrogen bonding interaction between the cyano group and RDX methylene group.展开更多
Constructing a functional hybrid coating appears to be a promising strategy for addressing the poor corrosion resistance and insufficient endothelialization of Mg-based stents.Nevertheless,the steps for preparing comp...Constructing a functional hybrid coating appears to be a promising strategy for addressing the poor corrosion resistance and insufficient endothelialization of Mg-based stents.Nevertheless,the steps for preparing composite coatings are usually complicated and time-consuming.Herein,a novel composite coating,composed of bioactive magnesium thioctic acid(MTA)layer formed by deposition and corrosion-resistant magnesium hydroxide(Mg(OH)_(2))layer grown in situ,is simply fabricated on ZE21B alloys via one-step electrodeposition.Scanning electron microscopy(SEM)shows that the electrodeposited coating has a compact and uniform structure.And the high adhesion of the MTA/Mg(OH)_(2)hybrid coating is also confirmed by the micro-scratch test.Electrochemical test,scanning kelvin probe(SKP),and hydrogen evolution measurement indicate that the hybrid coating effectively reduces the degradation rate of Mg substrates.Haemocompatibility experiment and cell culture trial detect that the composite coating is of fine biocompatibility.Finally,the preparation mechanism of MTA/Mg(OH)_(2)hybrid coatings is discussed and proposed.This coating shows a great potential application for cardiovascular stents.展开更多
Isothermal hot compression experiments were conducted on homogenized Mg-8.5Gd-4.5Y-0.8Zn-0.4Zr alloy to investigate hot deformation behavior at the temperature range of 673-773 K and the strain rate range of 0.001-1 s...Isothermal hot compression experiments were conducted on homogenized Mg-8.5Gd-4.5Y-0.8Zn-0.4Zr alloy to investigate hot deformation behavior at the temperature range of 673-773 K and the strain rate range of 0.001-1 s^(-1)by using a Gleeble-1500D thermo mechanical simulator.Metallographic characterization on samples deformed to true strain of 0.70 illustrates the occurrence of flow localization and/or microcrack at deformation conditions of 673 K/0.01 s^(-1),673 K/1 s^(-1)and 698 K/1 s^(-1),indicating that these three deformation conditions should be excluded during hot working of homogenized Mg-8.5Gd-4.5Y-0.8Zn-0.4Zr alloy.Based on the measured true stress-strain data,the strain-compensated Arrhenius constitutive model was constructed and then incorporated into UHARD subroutine of ABAQUS software to study hot deformation process of homogenized Mg-8.5Gd-4.5Y-0.8Zn-0.4Zr alloy.By comparison with measured force-displacement curves,the predicted results can describe well the rheological behavior of homogenized Mg-8.5Gd-4.5Y-0.8Zn-0.4Zr alloy,verifying the validity of finite element simulation of hot compression process with this complicated constitutive model.Numerical results demonstrate that the distribution of values of material parameters(α,n,Q and ln A)within deformed sample is inhomogeneous.This issue is directly correlated to the uneven distribution of equivalent plastic strain due to the friction effect.Moreover,at a given temperature the increase of strain rate would result in the decrease of equivalent plastic strain within the central region of deformed sample,which hinders the occurrence of dynamic recrystallization(DRX).展开更多
Main performance of the cement grouting materials made up by Portland cement(PC) and sulphoaluminate cement(SAC) was investigated in this program, a kind of expanding agent(EA) which was mainly constituted by metakaol...Main performance of the cement grouting materials made up by Portland cement(PC) and sulphoaluminate cement(SAC) was investigated in this program, a kind of expanding agent(EA) which was mainly constituted by metakaolin and alunite was utilized for the compensation of the shrinkage, the hydration products and micro structure of the grouting materials were researched by X-ray diffraction(XRD) and scanning electron microscopy(SEM). The results showed that a high expansion rate of the grouting materials could be reached as the expanding agent mixed in 6% of PC mass; the addition of SAC in the S2(PC:SAC:EA=34:6:2.25) brought a further improvement of the expansion rate of the grouting materials, the analysis of XRD and SEM showed that due to the reaction of expanding agent and SAC in the grouting materials, more ettringite crystal was generated, which resulted in a higher early strength, the addition of SAC played an expansion and strength reinforcement role in the grouting materials.展开更多
Cryogenic rolling experiments have been conducted on the AZ31 magnesium(Mg)alloy sheet with bimodal non-basal texture,which is fabricated via the newly developed equal channel angular rolling and continuous bending pr...Cryogenic rolling experiments have been conducted on the AZ31 magnesium(Mg)alloy sheet with bimodal non-basal texture,which is fabricated via the newly developed equal channel angular rolling and continuous bending process with subsequent annealing(ECAR-CB-A)process.Results demonstrate that this sheet shows no edge cracks until the accumulated thickness reduction reaches about 18.5%,which is about 105.6%larger than that of the sheet with traditional basal texture.Characterization experiments including optical microstructure(OM),X-ray diffractometer(XRD),and electron backscatter diffraction(EBSD)measurements are then performed to explore the microstructure characteristics,texture evolution and deformation mechanisms during cryogenic rolling.Experimental observations confirm the occurrence of abundant{10–12}extension twins(ETs),twin-twin interactions among{10–12}ET variants and{10–12}-{10–12}double twins(DTs).The twinning behaviors as for{10–12}ETs are responsible for the concentration of c-axes of grains towards normal direction(ND)and the formation of transverse direction(TD)-component texture at the beginning of cryogenic rolling.The twinning behaviors with respect to{10–12}-{10–12}DTs are responsible for the disappearance of TD-component texture at the later stage of cryogenic rolling.The involved deformation mechanisms can be summarized as follows:Firstly{10–12}ETs dominate the plastic deformation.Subsequently,dislocation slip,especially basal<a>slip,starts to sustain more plastic strain,while{10–12}ETs occur more frequently and enlarge continuously,resulting in the formation of twin-twin interaction among{10–12}ET variants.With the increasing rolling passes,{10–12}-{10–12}DTs incorporate in the plastic deformation and dislocation slip serves as the major one to sustain plastic strain.The activities of basal<a>slip,{10–12}ETs and{10–12}-{10–12}DTs benefit in accommodating the plastic strain in sheet thickness,which contributes to the improved rolling formability in AZ31 Mg alloy sheet with bimodal non-basal texture during cryogenic rolling.展开更多
In this paper,the occurrence and development mechanism of strain on the cross-section during the wood drying is explored.Therefore,strain regularity on the cross-section of 50 mm thickness elm(Ulmus rubra)board at the...In this paper,the occurrence and development mechanism of strain on the cross-section during the wood drying is explored.Therefore,strain regularity on the cross-section of 50 mm thickness elm(Ulmus rubra)board at the temperature of 40℃and 80℃is detected via digital image correlation technology.Hence,the difference between tangential and radial strain at surface and core layers was denoted.The results showed that strain distribution in the width direction of the board is uneven.Moreover,a large drying shrinkage strain occurs at the near-core layer,while the maximum strain difference reaches 4.08%.Hence,the surface of the board is cracked along the thickness direction.The radial strain of the board is higher than the tangential strain in the early stage of drying,while these strains are reversed in the later stage of drying.The temperature is related to the difference between the tangential and radial strains of the elm board.These differences at the core layer are larger than those of the surface layer.The conducted research results provide a theoretical basis for process optimization.展开更多
Flow softening behavior of a homogenized Mg-7Gd-4Y-1Nd-0.5Zr alloy under compression to a final strain of∼1.8 at elevated temperatures of 450∼550℃ and a constant strain rate of 2s^(−1) has been investigated by opti...Flow softening behavior of a homogenized Mg-7Gd-4Y-1Nd-0.5Zr alloy under compression to a final strain of∼1.8 at elevated temperatures of 450∼550℃ and a constant strain rate of 2s^(−1) has been investigated by optical microscopy,scanning electron microscopy,electron back-scattered diffraction and transmission electron microscopy.The results show that true stress first rises to the peak point and then drops to the bottom value and increases again with further increasing strain at each temperature.Twinning dynamic recrystallization(DRX)and continuous DRX contribute to the formation of new fine grains at temperatures 450∼475℃ when the restoration is caused by both DRX and texture change due to extension twinning,resulting in the larger softening degrees compared with the softening effects owing to continuous DRX and discontinuous DRX at 500∼550℃ when twinning activation is suppressed.500℃ is the transition temperature denoting a significant decline in the contribution of twinning and TDRX to the strain with increasing temperature.The cuboid-shape phase exists in both homogenized and compressed samples,while the compositions are varied.展开更多
Rechargeable zinc-ion batteries with mild aqueous electrolytes are one of the most promising systems for large-scale energy storage as a result of their inherent safety,low cost,environmental-friendliness,and acceptab...Rechargeable zinc-ion batteries with mild aqueous electrolytes are one of the most promising systems for large-scale energy storage as a result of their inherent safety,low cost,environmental-friendliness,and acceptable energy density.However,zinc metal anodes always suffer from unwanted dendrite growth,leading to low Coulombic efficiency and poor cycle stability and during the repeated plating/stripping processes,which substantially restrict their further development and application.To solve these critical issues,a lot of research works have been dedicated to overcoming the drawbacks associated with zinc metal anodes.In this overview,the working mechanisms and existing issues of the zinc metal anodes are first briefly outlined.Moreover,we look into the ongoing processes of the different strategies for achieving highly stable and dendrite-free zinc metal anodes,including crystal engineering,structural engineering,coating engineering,electrolyte engineering,and separator engineering.Finally,some challenges being faced and prospects in this field are provided,together with guiding significant research directions in the future.展开更多
This study aims to develop highly hygroscopic bio-based co-polyamides(CPs)by melt co-polycondensation of polyamide(PA)56 salt and PA66 salt with varying molar fractions.The functional groups and the chemical structure...This study aims to develop highly hygroscopic bio-based co-polyamides(CPs)by melt co-polycondensation of polyamide(PA)56 salt and PA66 salt with varying molar fractions.The functional groups and the chemical structure of the prepared samples were determined by Fourier transform infrared(FTIR)spectroscopy and proton nuclear magnetic resonance(^(1)H-NMR)spectroscopy.The relative viscosity was determined with an Ubbelohde viscometer.The melting behavior and the thermal stability of CPs were investigated by differential scanning calorimetry(DSC)and thermogravimetric analysis(TGA).Furthermore,the water absorption behavior of CP hot-pressed film was studied.The results reveal that the melting point,the crystallization temperature and the crystallinity of CPs firstly decrease and then increase with the molar fraction of PA66 in CPs.The copolymerization of PA56 with PA66 leads to an obvious increase in water absorption.The CPs with PA66 molar fraction of 50%possess a high saturated water absorption rate of 17.6%,compared to 11.6%for pure PA56 and 7.8%for pure PA66.展开更多
Using non-toxic,low-volatile glyoxal to completely replace formaldehyde for preparing urea-glyoxal(UG)resin adhesive is a hot research topic that could be of great interest for the wood industry.However,urea-glyoxal(U...Using non-toxic,low-volatile glyoxal to completely replace formaldehyde for preparing urea-glyoxal(UG)resin adhesive is a hot research topic that could be of great interest for the wood industry.However,urea-glyoxal(UG)resins prepared by just using glyoxal instead of formaldehyde usually yields a lower degree of polymerization.This results in a poorer bonding performance and water resistance of UG resins.A good solution is to pre-react urea to preform polyurea molecules presenting already a certain degree of polymerization,and then to condense these with glyoxal to obtain a novel UG resin.Therefore,in this present work,the urea was reacted with hexamethylene diamine to form a polyurea named HU,and then this was used to react it with different amounts of glyoxal to synthesize hexamethylenediamine-urea-glyoxal(HUG)polycondensation resins,and to use this for bonding plywood.The results show that the glyoxal can well react with HU polyuria via addition and schiff base reaction,and also the HUG resin exhibits excellent bonding strength and water resistance.The shear strength of the plywood bonded with this HUG at 160°C hot press temperature as high as 1.93 MPa,2.16 MPa and 1.61 MPa,respectively,which meets the requirement of the China national standard GB/T 9846-2015(≥0.7 MPa),and can be a good choice as a wood adhesive for industrial application.展开更多
LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2(NCM) cathode material containing copper was prepared by co-precipitation method.The material was characterized by X-ray photoelectron spectroscopy(XPS) and galvanostatic cycling.XPS data ...LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2(NCM) cathode material containing copper was prepared by co-precipitation method.The material was characterized by X-ray photoelectron spectroscopy(XPS) and galvanostatic cycling.XPS data indicate that surface compositions of the samples containing copper are different from the bare NCM.Copper on surface of particles was enriched,while nickel and lithium content was reduced.The electrochemical performance of NCM was affected by the change of surface compositions.Cycling performance charged to the cutoff voltage of 4.6 V was improved by introducing copper into the material.The effects of copper content on electrochemical behaviors of NCM at 4.5 V were discussed.展开更多
La-doped Li2Mo0.9La0.2O4 was synthesized as an active anode material via the sol-gel process. The structural and morphological characteristics of the target product and the precursor were analyzed by XRD, SEM, and TG-...La-doped Li2Mo0.9La0.2O4 was synthesized as an active anode material via the sol-gel process. The structural and morphological characteristics of the target product and the precursor were analyzed by XRD, SEM, and TG-DTA. Crystal started to format at 300°C and the optimum crystal structure was obtained at 700°C. By detecting battery performance, the charged and discharged platform was over 3.6 V; the anode exhibited a discharge capacity decay of 2% from its initial ca-pacity (165 mA?h/g) after 20 cycles. Therefore, it was a perfect anode material.展开更多
Two kinds of Al based functionally gradient composite tubes reinforced by primary Si particles alone and primary Si/in situ Mg2Si particles jointly were successfully prepared by centrifugal casting,and their structura...Two kinds of Al based functionally gradient composite tubes reinforced by primary Si particles alone and primary Si/in situ Mg2Si particles jointly were successfully prepared by centrifugal casting,and their structural and mechanical characters were compared.It is found that the composite reinforced with primary Si particles takes a characteristic of particles distribution both in the inner and outer layers.However,composite reinforced with primary Si/Mg2Si particles jointly takes a characteristic of particles distribution only in the inner layer and shows a sudden change of particles distribution across the section of inner and outer layers.The hardness and wear resistance of Al-19Si-5Mg tube in the inner layer are greatly higher than that in the other layers of Al-19Si-5Mg tube and Al-19Si tube.Theoretical analysis reveals that the existence of Mg2Si particles is the key factor to form this sudden change of gradient distribution of two kinds of particles.Because Mg2Si particles with a lower density have a higher centripetal moving velocity than primary Si particles,in a field of centrifugal force,they would collide with primary Si particles and then impel the later to move together forward to the inner layer of the tube.展开更多
The extract of green peel of Juglans mandshurica Maxim was extracted by common method for studying its insecticidal activities and analyzing the active components. Results showed that the alcohol extract and the chlor...The extract of green peel of Juglans mandshurica Maxim was extracted by common method for studying its insecticidal activities and analyzing the active components. Results showed that the alcohol extract and the chloroform part of extract (separated with chloroform from alcohol extract) form green peel of J. mandshurica have insecticidal activities in contact toxicity and stomach toxicity against larvae of Lymantria dispar L.. After application of the extracts for five days, the corrected mortality of larvae of Lymantria dispar for both extracts was more than 50% in contact toxicity and stomach toxicity at the concentration of ≥ 5 g·L^(-1). The insecticidal activity for both alcohol extract and chloroform part of extract is more effect in contact toxicity than in stomach toxicity, but no significant difference in the insecticidal activities was found between alcohol extract and chloroform part of extract. The active components in the chloroform part of extract from green peel of J. mandshurica were analyzed by GC-MS. The analyzed results showed that the active components in the chloroform part of extract are: (1) juglone (5-hydroxy-1,4-naphthaoquinone), the relative content 27.11%, (2) 1,5-Naphthalenediol, the relative content 9.52%, (3) 7-Methoxy-1-tetralone, the relative content 6.81%, (4) Benzofuran, 2,3-dihydro-, the relative content 6.76%, (5) 4-Hydroxy-2-methoxycinnamaldehyde, the relative content 3.99%, (6) 2-Methoxy-4-vinylphenol, the relative content 3.05%.展开更多
High performance cement based composite materials was prepared by adding epoxy emulsion. The epoxy emulsion was synthesized with epoxy phosphoric acid ester and poly-glycol in laboratory. This epoxy emulsion has advan...High performance cement based composite materials was prepared by adding epoxy emulsion. The epoxy emulsion was synthesized with epoxy phosphoric acid ester and poly-glycol in laboratory. This epoxy emulsion has advantages over other emulsion, such as dehydrated slightly, and well film formation abilities. The mechanical properties, corruptness resistance and structure of ep-oxy emulsion modified cement mortars were studied. Experimental results show that the mechanical properties of modified cement mortars are slightly increased with increasing epoxy emulsion content, especially the flexure strength. The corruptness resistance of all modified mortars is better than the unmodified mortar. The polymer film forms the bridge phases between the matrix and the aggregate regions, and forms a three-dimension structure in the cement hydration system , which improves the mechanical properties of modified mortars.展开更多
The properties of styrene-butadiene rubber (SBR) reinforced by modified silica was investigated according to national standards. Silica was modified by silane coupling agents KH-570, KH-590, and KH-792. The optimized ...The properties of styrene-butadiene rubber (SBR) reinforced by modified silica was investigated according to national standards. Silica was modified by silane coupling agents KH-570, KH-590, and KH-792. The optimized geome-tries of molecular modified silica reinforced SBR were obtained by using B3LYP calculation of density functional theory with the 6-31+G basis sets. The natural bond orbital analyses were carried out. The Si—O bond length of silica modified by KH-792 was the shortest and the electronegative of O was the highest. It indicated that the connection between silica and KH-792 was the tightest. Higher tensile strength and elongation of reinforced SBR was obtained by silica modified with the KH-792. It was caused by large delocalization of lone pair electrons of the two N atoms in KH-792. The S—C bond length in silica modified by KH-590 was longer than the ordinary S—C bond length. Then the sulfur free radical (·S·) was produced more easily in vulcanization. The degree of crosslink was increased by the cross-linkage of the rubber molecule and the sulfur free radical. That was why the highest stress and tear strength of reinforced SBR was produced when silane coupling agent KH-590 was used. The calculation results was in accord with experimental data.展开更多
A sensitive, fast and low-cost molecular imprinted polymeric sensor for quantitative determination of parathion was prepared with chitosan(CS) as function matrix and parathion(PT) as template molecule via constant pot...A sensitive, fast and low-cost molecular imprinted polymeric sensor for quantitative determination of parathion was prepared with chitosan(CS) as function matrix and parathion(PT) as template molecule via constant potential electrochemical deposition. Sensitive response was obtained with a detection limit of 1.0×10–7 mol/L and an excellent recognition for PT was achieved due to the good memory capacity of the sensor. The developed sensor exhibited good fabrication reproducibility and acceptable stability, which provided a new promising tool for pesticide analysis.展开更多
In recent years, due to their high photo-to-electric power conversion efficiency(PCE)(up to 23%(certified)) and low cost, perovskite solar cells(PSCs) have attracted a great deal of attention in photovoltaics field. T...In recent years, due to their high photo-to-electric power conversion efficiency(PCE)(up to 23%(certified)) and low cost, perovskite solar cells(PSCs) have attracted a great deal of attention in photovoltaics field. The high PCE can be attributed to the excellent physical properties of organic–inorganic hybrid perovskite materials, such as a long charge diffusion length and a high absorption coefficient in the visible range. There are different diffusion lengths of holes in electrons in a PSC device, and thus the electron transporting layer(ETL) plays a critical role in the performance of PSCs. An alternative for TiO2, to the most common ETL material is SnO2, which has similar physical properties to TiO2 but with much higher electron mobility, which is beneficial for electron extraction. In addition, there are many facile methods to fabricate SnO2 nanomaterials with low cost and low energy consumption. In this review paper, we focus on recent developments in SnO2 as the ETL of PSCs. The fabrication methods of SnO2 materials are briefly introduced. The influence of multiple Sn O2 types in the ETL on the performance of PSCs is then reviewed. Different methods for improving the PCE and long-term stability of PSCs based on SnO2 ETL are also summarized. The review provides a systematic and comprehensive understanding of the influence of different Sn O2 ETL types on PSC performance and potentially motivates further development of PSCs with an extension to SnO2-based PSCs.展开更多
A preferable honeycomb ceramics of Al2TiO5-TiO2-SiO2 doped by CeO2 and Er2O3 with high performance was prepared by means of extrusion molding and the effects of CeO2 and Er2O3 on the mechanical strength, thermal stabi...A preferable honeycomb ceramics of Al2TiO5-TiO2-SiO2 doped by CeO2 and Er2O3 with high performance was prepared by means of extrusion molding and the effects of CeO2 and Er2O3 on the mechanical strength, thermal stability, and sintering temperature of ATS ceramics were mainly investigated. The experimental results and the microscopic analysis by scanning electron microscope, X-ray powder diffraction, and TG-DSC showed that adding CeO2 and Er2O3 into ATS could prohibit the growth of their crystal grains and make their size uniform, which finally decrease its sintering temperature, and also enhance its mechanical performance as well as thermal stability. After the reforming, ATS doped by 0.5%CeO2+0.5%Er2O3 was sintered at 1250 ℃, its bending strength reached to 177.4 MPa and thermal expansion coefficient was 3.8×10-6/℃ at 25～1000 ℃, which provided a promising basis of making monolithic honeycomb catalyst of deNOx.展开更多
文摘To simplify the composite propellant formulation and address the current issue of the single-functionality present in existing additives,the multi-cyano,amine-based polybutadiene(AEHTPB-CN)was prepared based on AEHTPB by adopting appropriate synthesis strategies.By replacing 10% of HTPB binder in the propellant formulation,it can effectively enhance the interfacial bond strength between the propellant binder matrix and solid fillers(AP(ammonium perchlorate)and RDX(cyclotrimethylene-trinitramine)),the mechanical properties of the HTPB/AP/RDX/Al propellant were superior to blank control propellant with an improvement of 35.4% in tensile strength,62.0% enhancement in elongation at break,and reduce the propellant burn rate by 10.7% with any energy loss.The function mechanism of AEHTPB-CN was systematically elucidated through experiments and computer simulation techniques.The results show that the tertiary amine group in AEHTPB-CN can react with AP to form ammonium ionic bonds,and the hydroxyl and cyano groups can form hydrogen bonding interactions with AP,which enables AEHTPB-CN to be firmly adsorbed on the AP surface through chemical and physical interactions.For RDX,the interfacial bonding effect of AEHTPB-CN is attributed to their ability to form C-H···N≡C weak hydrogen bonding interaction between the cyano group and RDX methylene group.
基金the National Key Research and Development Program of China(2018YFC1106703)the National Natural Science Foundation of China(No.U1804251)。
文摘Constructing a functional hybrid coating appears to be a promising strategy for addressing the poor corrosion resistance and insufficient endothelialization of Mg-based stents.Nevertheless,the steps for preparing composite coatings are usually complicated and time-consuming.Herein,a novel composite coating,composed of bioactive magnesium thioctic acid(MTA)layer formed by deposition and corrosion-resistant magnesium hydroxide(Mg(OH)_(2))layer grown in situ,is simply fabricated on ZE21B alloys via one-step electrodeposition.Scanning electron microscopy(SEM)shows that the electrodeposited coating has a compact and uniform structure.And the high adhesion of the MTA/Mg(OH)_(2)hybrid coating is also confirmed by the micro-scratch test.Electrochemical test,scanning kelvin probe(SKP),and hydrogen evolution measurement indicate that the hybrid coating effectively reduces the degradation rate of Mg substrates.Haemocompatibility experiment and cell culture trial detect that the composite coating is of fine biocompatibility.Finally,the preparation mechanism of MTA/Mg(OH)_(2)hybrid coatings is discussed and proposed.This coating shows a great potential application for cardiovascular stents.
基金supported by the National Natural Science Foundation of China(Grant Nos.51805064,51701034)the Scientific and Technological Research Program of Chongqing Municipal Education Commission(Grant Nos.KJQN201801137,KJ1600922)+1 种基金the Basic and Advanced Research Project of Chongqing Science and Technology Commission(Grant Nos.cstc2017jcyj AX0062,cstc2018jcyj AX0035)the Chongqing University Key Laboratory of Micro/Nano Materials Engineering and Technology(Grant Nos.KFJJ2003)
文摘Isothermal hot compression experiments were conducted on homogenized Mg-8.5Gd-4.5Y-0.8Zn-0.4Zr alloy to investigate hot deformation behavior at the temperature range of 673-773 K and the strain rate range of 0.001-1 s^(-1)by using a Gleeble-1500D thermo mechanical simulator.Metallographic characterization on samples deformed to true strain of 0.70 illustrates the occurrence of flow localization and/or microcrack at deformation conditions of 673 K/0.01 s^(-1),673 K/1 s^(-1)and 698 K/1 s^(-1),indicating that these three deformation conditions should be excluded during hot working of homogenized Mg-8.5Gd-4.5Y-0.8Zn-0.4Zr alloy.Based on the measured true stress-strain data,the strain-compensated Arrhenius constitutive model was constructed and then incorporated into UHARD subroutine of ABAQUS software to study hot deformation process of homogenized Mg-8.5Gd-4.5Y-0.8Zn-0.4Zr alloy.By comparison with measured force-displacement curves,the predicted results can describe well the rheological behavior of homogenized Mg-8.5Gd-4.5Y-0.8Zn-0.4Zr alloy,verifying the validity of finite element simulation of hot compression process with this complicated constitutive model.Numerical results demonstrate that the distribution of values of material parameters(α,n,Q and ln A)within deformed sample is inhomogeneous.This issue is directly correlated to the uneven distribution of equivalent plastic strain due to the friction effect.Moreover,at a given temperature the increase of strain rate would result in the decrease of equivalent plastic strain within the central region of deformed sample,which hinders the occurrence of dynamic recrystallization(DRX).
基金Funded by the National Key Technology R&D Program in the12th Five Year Plan of China(No.2011BAE14B06)the National High Technology ResearchDevelopment Program of China(No.2015AA034701)
文摘Main performance of the cement grouting materials made up by Portland cement(PC) and sulphoaluminate cement(SAC) was investigated in this program, a kind of expanding agent(EA) which was mainly constituted by metakaolin and alunite was utilized for the compensation of the shrinkage, the hydration products and micro structure of the grouting materials were researched by X-ray diffraction(XRD) and scanning electron microscopy(SEM). The results showed that a high expansion rate of the grouting materials could be reached as the expanding agent mixed in 6% of PC mass; the addition of SAC in the S2(PC:SAC:EA=34:6:2.25) brought a further improvement of the expansion rate of the grouting materials, the analysis of XRD and SEM showed that due to the reaction of expanding agent and SAC in the grouting materials, more ettringite crystal was generated, which resulted in a higher early strength, the addition of SAC played an expansion and strength reinforcement role in the grouting materials.
基金supported by the National Natural Science Foundation of China(Grant Nos.51805064,51822509)the Qingnian project of science and technology research program of Chongqing Education Commission of China(Grant No.KJQN202101141).
文摘Cryogenic rolling experiments have been conducted on the AZ31 magnesium(Mg)alloy sheet with bimodal non-basal texture,which is fabricated via the newly developed equal channel angular rolling and continuous bending process with subsequent annealing(ECAR-CB-A)process.Results demonstrate that this sheet shows no edge cracks until the accumulated thickness reduction reaches about 18.5%,which is about 105.6%larger than that of the sheet with traditional basal texture.Characterization experiments including optical microstructure(OM),X-ray diffractometer(XRD),and electron backscatter diffraction(EBSD)measurements are then performed to explore the microstructure characteristics,texture evolution and deformation mechanisms during cryogenic rolling.Experimental observations confirm the occurrence of abundant{10–12}extension twins(ETs),twin-twin interactions among{10–12}ET variants and{10–12}-{10–12}double twins(DTs).The twinning behaviors as for{10–12}ETs are responsible for the concentration of c-axes of grains towards normal direction(ND)and the formation of transverse direction(TD)-component texture at the beginning of cryogenic rolling.The twinning behaviors with respect to{10–12}-{10–12}DTs are responsible for the disappearance of TD-component texture at the later stage of cryogenic rolling.The involved deformation mechanisms can be summarized as follows:Firstly{10–12}ETs dominate the plastic deformation.Subsequently,dislocation slip,especially basal<a>slip,starts to sustain more plastic strain,while{10–12}ETs occur more frequently and enlarge continuously,resulting in the formation of twin-twin interaction among{10–12}ET variants.With the increasing rolling passes,{10–12}-{10–12}DTs incorporate in the plastic deformation and dislocation slip serves as the major one to sustain plastic strain.The activities of basal<a>slip,{10–12}ETs and{10–12}-{10–12}DTs benefit in accommodating the plastic strain in sheet thickness,which contributes to the improved rolling formability in AZ31 Mg alloy sheet with bimodal non-basal texture during cryogenic rolling.
基金supported by the National Natural Science Foundation of China(No.31901242)Heilongjiang Science Foundation Project(No.LH2020C038)National Undergraduate Training Programs for Innovations(No.202110225074)。
文摘In this paper,the occurrence and development mechanism of strain on the cross-section during the wood drying is explored.Therefore,strain regularity on the cross-section of 50 mm thickness elm(Ulmus rubra)board at the temperature of 40℃and 80℃is detected via digital image correlation technology.Hence,the difference between tangential and radial strain at surface and core layers was denoted.The results showed that strain distribution in the width direction of the board is uneven.Moreover,a large drying shrinkage strain occurs at the near-core layer,while the maximum strain difference reaches 4.08%.Hence,the surface of the board is cracked along the thickness direction.The radial strain of the board is higher than the tangential strain in the early stage of drying,while these strains are reversed in the later stage of drying.The temperature is related to the difference between the tangential and radial strains of the elm board.These differences at the core layer are larger than those of the surface layer.The conducted research results provide a theoretical basis for process optimization.
基金This work was supported by the Changsha University Talent Introduction Project(50800-92808)the Excellent youth project of Hunan Provincial Department of Education(19B055,18B418,19C0156)the Natural Science Foundation of Hunan Province of China(2020JJ4645).
文摘Flow softening behavior of a homogenized Mg-7Gd-4Y-1Nd-0.5Zr alloy under compression to a final strain of∼1.8 at elevated temperatures of 450∼550℃ and a constant strain rate of 2s^(−1) has been investigated by optical microscopy,scanning electron microscopy,electron back-scattered diffraction and transmission electron microscopy.The results show that true stress first rises to the peak point and then drops to the bottom value and increases again with further increasing strain at each temperature.Twinning dynamic recrystallization(DRX)and continuous DRX contribute to the formation of new fine grains at temperatures 450∼475℃ when the restoration is caused by both DRX and texture change due to extension twinning,resulting in the larger softening degrees compared with the softening effects owing to continuous DRX and discontinuous DRX at 500∼550℃ when twinning activation is suppressed.500℃ is the transition temperature denoting a significant decline in the contribution of twinning and TDRX to the strain with increasing temperature.The cuboid-shape phase exists in both homogenized and compressed samples,while the compositions are varied.
基金supported by the National Natural Science Foundation of China(U1802256,21975283,21773118,21875107)the Key Research and Development Program in Jiangsu Province(BE2018122)+2 种基金the Natural Science Foundation of Jiangsu Province(BK20191343)the Fundamental Research Funds for the Central Universities(2022QN1088)the General Research Project of Jiangsu Key Laboratory of Coal-based Greenhouse Gas Control and Utilization(2022KF03).
文摘Rechargeable zinc-ion batteries with mild aqueous electrolytes are one of the most promising systems for large-scale energy storage as a result of their inherent safety,low cost,environmental-friendliness,and acceptable energy density.However,zinc metal anodes always suffer from unwanted dendrite growth,leading to low Coulombic efficiency and poor cycle stability and during the repeated plating/stripping processes,which substantially restrict their further development and application.To solve these critical issues,a lot of research works have been dedicated to overcoming the drawbacks associated with zinc metal anodes.In this overview,the working mechanisms and existing issues of the zinc metal anodes are first briefly outlined.Moreover,we look into the ongoing processes of the different strategies for achieving highly stable and dendrite-free zinc metal anodes,including crystal engineering,structural engineering,coating engineering,electrolyte engineering,and separator engineering.Finally,some challenges being faced and prospects in this field are provided,together with guiding significant research directions in the future.
基金National Key Research and Development Program of China(No.2017YFB0309400).
文摘This study aims to develop highly hygroscopic bio-based co-polyamides(CPs)by melt co-polycondensation of polyamide(PA)56 salt and PA66 salt with varying molar fractions.The functional groups and the chemical structure of the prepared samples were determined by Fourier transform infrared(FTIR)spectroscopy and proton nuclear magnetic resonance(^(1)H-NMR)spectroscopy.The relative viscosity was determined with an Ubbelohde viscometer.The melting behavior and the thermal stability of CPs were investigated by differential scanning calorimetry(DSC)and thermogravimetric analysis(TGA).Furthermore,the water absorption behavior of CP hot-pressed film was studied.The results reveal that the melting point,the crystallization temperature and the crystallinity of CPs firstly decrease and then increase with the molar fraction of PA66 in CPs.The copolymerization of PA56 with PA66 leads to an obvious increase in water absorption.The CPs with PA66 molar fraction of 50%possess a high saturated water absorption rate of 17.6%,compared to 11.6%for pure PA56 and 7.8%for pure PA66.
基金supported by the Yunnan Provincial Natural Science Foundation (202201AU070222,202201AT070045,202101BD070001-074)Scientific Research Fund Project of Yunnan Provincial Department of Education (2022J0490)financed by the 111 Project (D21027).
文摘Using non-toxic,low-volatile glyoxal to completely replace formaldehyde for preparing urea-glyoxal(UG)resin adhesive is a hot research topic that could be of great interest for the wood industry.However,urea-glyoxal(UG)resins prepared by just using glyoxal instead of formaldehyde usually yields a lower degree of polymerization.This results in a poorer bonding performance and water resistance of UG resins.A good solution is to pre-react urea to preform polyurea molecules presenting already a certain degree of polymerization,and then to condense these with glyoxal to obtain a novel UG resin.Therefore,in this present work,the urea was reacted with hexamethylene diamine to form a polyurea named HU,and then this was used to react it with different amounts of glyoxal to synthesize hexamethylenediamine-urea-glyoxal(HUG)polycondensation resins,and to use this for bonding plywood.The results show that the glyoxal can well react with HU polyuria via addition and schiff base reaction,and also the HUG resin exhibits excellent bonding strength and water resistance.The shear strength of the plywood bonded with this HUG at 160°C hot press temperature as high as 1.93 MPa,2.16 MPa and 1.61 MPa,respectively,which meets the requirement of the China national standard GB/T 9846-2015(≥0.7 MPa),and can be a good choice as a wood adhesive for industrial application.
基金supported by the National Natural Science Foundation of China (No. 20863008)University Project(No.KKZ4200730010) of Kunming University of Science and Technology
文摘LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2(NCM) cathode material containing copper was prepared by co-precipitation method.The material was characterized by X-ray photoelectron spectroscopy(XPS) and galvanostatic cycling.XPS data indicate that surface compositions of the samples containing copper are different from the bare NCM.Copper on surface of particles was enriched,while nickel and lithium content was reduced.The electrochemical performance of NCM was affected by the change of surface compositions.Cycling performance charged to the cutoff voltage of 4.6 V was improved by introducing copper into the material.The effects of copper content on electrochemical behaviors of NCM at 4.5 V were discussed.
文摘La-doped Li2Mo0.9La0.2O4 was synthesized as an active anode material via the sol-gel process. The structural and morphological characteristics of the target product and the precursor were analyzed by XRD, SEM, and TG-DTA. Crystal started to format at 300°C and the optimum crystal structure was obtained at 700°C. By detecting battery performance, the charged and discharged platform was over 3.6 V; the anode exhibited a discharge capacity decay of 2% from its initial ca-pacity (165 mA?h/g) after 20 cycles. Therefore, it was a perfect anode material.
基金Project(2008BB4177) supported by the Natural Science Foundation of Chongqing,China
文摘Two kinds of Al based functionally gradient composite tubes reinforced by primary Si particles alone and primary Si/in situ Mg2Si particles jointly were successfully prepared by centrifugal casting,and their structural and mechanical characters were compared.It is found that the composite reinforced with primary Si particles takes a characteristic of particles distribution both in the inner and outer layers.However,composite reinforced with primary Si/Mg2Si particles jointly takes a characteristic of particles distribution only in the inner layer and shows a sudden change of particles distribution across the section of inner and outer layers.The hardness and wear resistance of Al-19Si-5Mg tube in the inner layer are greatly higher than that in the other layers of Al-19Si-5Mg tube and Al-19Si tube.Theoretical analysis reveals that the existence of Mg2Si particles is the key factor to form this sudden change of gradient distribution of two kinds of particles.Because Mg2Si particles with a lower density have a higher centripetal moving velocity than primary Si particles,in a field of centrifugal force,they would collide with primary Si particles and then impel the later to move together forward to the inner layer of the tube.
基金This study was supported by Heilongjiang Natural Science Foundation (C2004-28)
文摘The extract of green peel of Juglans mandshurica Maxim was extracted by common method for studying its insecticidal activities and analyzing the active components. Results showed that the alcohol extract and the chloroform part of extract (separated with chloroform from alcohol extract) form green peel of J. mandshurica have insecticidal activities in contact toxicity and stomach toxicity against larvae of Lymantria dispar L.. After application of the extracts for five days, the corrected mortality of larvae of Lymantria dispar for both extracts was more than 50% in contact toxicity and stomach toxicity at the concentration of ≥ 5 g·L^(-1). The insecticidal activity for both alcohol extract and chloroform part of extract is more effect in contact toxicity than in stomach toxicity, but no significant difference in the insecticidal activities was found between alcohol extract and chloroform part of extract. The active components in the chloroform part of extract from green peel of J. mandshurica were analyzed by GC-MS. The analyzed results showed that the active components in the chloroform part of extract are: (1) juglone (5-hydroxy-1,4-naphthaoquinone), the relative content 27.11%, (2) 1,5-Naphthalenediol, the relative content 9.52%, (3) 7-Methoxy-1-tetralone, the relative content 6.81%, (4) Benzofuran, 2,3-dihydro-, the relative content 6.76%, (5) 4-Hydroxy-2-methoxycinnamaldehyde, the relative content 3.99%, (6) 2-Methoxy-4-vinylphenol, the relative content 3.05%.
文摘High performance cement based composite materials was prepared by adding epoxy emulsion. The epoxy emulsion was synthesized with epoxy phosphoric acid ester and poly-glycol in laboratory. This epoxy emulsion has advantages over other emulsion, such as dehydrated slightly, and well film formation abilities. The mechanical properties, corruptness resistance and structure of ep-oxy emulsion modified cement mortars were studied. Experimental results show that the mechanical properties of modified cement mortars are slightly increased with increasing epoxy emulsion content, especially the flexure strength. The corruptness resistance of all modified mortars is better than the unmodified mortar. The polymer film forms the bridge phases between the matrix and the aggregate regions, and forms a three-dimension structure in the cement hydration system , which improves the mechanical properties of modified mortars.
文摘The properties of styrene-butadiene rubber (SBR) reinforced by modified silica was investigated according to national standards. Silica was modified by silane coupling agents KH-570, KH-590, and KH-792. The optimized geome-tries of molecular modified silica reinforced SBR were obtained by using B3LYP calculation of density functional theory with the 6-31+G basis sets. The natural bond orbital analyses were carried out. The Si—O bond length of silica modified by KH-792 was the shortest and the electronegative of O was the highest. It indicated that the connection between silica and KH-792 was the tightest. Higher tensile strength and elongation of reinforced SBR was obtained by silica modified with the KH-792. It was caused by large delocalization of lone pair electrons of the two N atoms in KH-792. The S—C bond length in silica modified by KH-590 was longer than the ordinary S—C bond length. Then the sulfur free radical (·S·) was produced more easily in vulcanization. The degree of crosslink was increased by the cross-linkage of the rubber molecule and the sulfur free radical. That was why the highest stress and tear strength of reinforced SBR was produced when silane coupling agent KH-590 was used. The calculation results was in accord with experimental data.
基金Supported by the National Natural Science Foundation of China(Nos20575023, 20955001)the Key Project of International Cooperation Foundation of Fujian Province, China(No2006I0021)the Natural Science Foundation of Fujian Province, China(NosD0710017, D0810016 and U0850008)
文摘A sensitive, fast and low-cost molecular imprinted polymeric sensor for quantitative determination of parathion was prepared with chitosan(CS) as function matrix and parathion(PT) as template molecule via constant potential electrochemical deposition. Sensitive response was obtained with a detection limit of 1.0×10–7 mol/L and an excellent recognition for PT was achieved due to the good memory capacity of the sensor. The developed sensor exhibited good fabrication reproducibility and acceptable stability, which provided a new promising tool for pesticide analysis.
基金supported by the National Natural Science Foundation of China(NSFC 61574009 and 11574014)
文摘In recent years, due to their high photo-to-electric power conversion efficiency(PCE)(up to 23%(certified)) and low cost, perovskite solar cells(PSCs) have attracted a great deal of attention in photovoltaics field. The high PCE can be attributed to the excellent physical properties of organic–inorganic hybrid perovskite materials, such as a long charge diffusion length and a high absorption coefficient in the visible range. There are different diffusion lengths of holes in electrons in a PSC device, and thus the electron transporting layer(ETL) plays a critical role in the performance of PSCs. An alternative for TiO2, to the most common ETL material is SnO2, which has similar physical properties to TiO2 but with much higher electron mobility, which is beneficial for electron extraction. In addition, there are many facile methods to fabricate SnO2 nanomaterials with low cost and low energy consumption. In this review paper, we focus on recent developments in SnO2 as the ETL of PSCs. The fabrication methods of SnO2 materials are briefly introduced. The influence of multiple Sn O2 types in the ETL on the performance of PSCs is then reviewed. Different methods for improving the PCE and long-term stability of PSCs based on SnO2 ETL are also summarized. The review provides a systematic and comprehensive understanding of the influence of different Sn O2 ETL types on PSC performance and potentially motivates further development of PSCs with an extension to SnO2-based PSCs.
基金Project supported by National High Technology Research and Development Program of China (863 Program,2006AA02Z211)Nation-al Natural Science Foundation of China (20376034)Natural Science Foundation of Jiangsu Province (BK2006181)
文摘A preferable honeycomb ceramics of Al2TiO5-TiO2-SiO2 doped by CeO2 and Er2O3 with high performance was prepared by means of extrusion molding and the effects of CeO2 and Er2O3 on the mechanical strength, thermal stability, and sintering temperature of ATS ceramics were mainly investigated. The experimental results and the microscopic analysis by scanning electron microscope, X-ray powder diffraction, and TG-DSC showed that adding CeO2 and Er2O3 into ATS could prohibit the growth of their crystal grains and make their size uniform, which finally decrease its sintering temperature, and also enhance its mechanical performance as well as thermal stability. After the reforming, ATS doped by 0.5%CeO2+0.5%Er2O3 was sintered at 1250 ℃, its bending strength reached to 177.4 MPa and thermal expansion coefficient was 3.8×10-6/℃ at 25～1000 ℃, which provided a promising basis of making monolithic honeycomb catalyst of deNOx.