Transparent conducting aluminum doped tin oxide thin films were prepared by sol-gel dip coating method with differ-ent Al concentrations and characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), UV-...Transparent conducting aluminum doped tin oxide thin films were prepared by sol-gel dip coating method with differ-ent Al concentrations and characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), UV-Vis spectrophotometry and photoconductivity study. The variation observed in the properties of the measured films agrees with a difference in the film's thickness, which decreases when Al concentration augments. X-ray diffraction analysis reveals that all films are polycrystal-line with tetragonal structure, (110) plane being the strongest diffraction peak. The crystallite size calculated by the Debye Scher-rer’s formula decreases from 11.92 to 8.54 nm when Al concentration increases from 0 to 5 wt.%. AFM images showed grains uni-formly distributed in the deposited films. An average transmittance greater than 80% was measured for the films and an en-ergy gap value of about 3.9 eV was deduced from the optical analysis. Finally, the photosensitivity properties like current-voltage characteristics, ION/IOFF ratio, growth and decay time are studied and reported. Also, we have calculated the trap depth energy using the decay portion of the rise and decay curve photocurrent.展开更多
基金support of the laboratory of active components and materials,Oum El Bouaghi University.
文摘Transparent conducting aluminum doped tin oxide thin films were prepared by sol-gel dip coating method with differ-ent Al concentrations and characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), UV-Vis spectrophotometry and photoconductivity study. The variation observed in the properties of the measured films agrees with a difference in the film's thickness, which decreases when Al concentration augments. X-ray diffraction analysis reveals that all films are polycrystal-line with tetragonal structure, (110) plane being the strongest diffraction peak. The crystallite size calculated by the Debye Scher-rer’s formula decreases from 11.92 to 8.54 nm when Al concentration increases from 0 to 5 wt.%. AFM images showed grains uni-formly distributed in the deposited films. An average transmittance greater than 80% was measured for the films and an en-ergy gap value of about 3.9 eV was deduced from the optical analysis. Finally, the photosensitivity properties like current-voltage characteristics, ION/IOFF ratio, growth and decay time are studied and reported. Also, we have calculated the trap depth energy using the decay portion of the rise and decay curve photocurrent.