Fused salt accelerated hot corrosion is quite common in gas turbines, fossil fuelled devices, waste inclinators, pyrochemical systems, etc. Presence of fused salt on metal surface dissolves their existing oxide layer....Fused salt accelerated hot corrosion is quite common in gas turbines, fossil fuelled devices, waste inclinators, pyrochemical systems, etc. Presence of fused salt on metal surface dissolves their existing oxide layer. This results in an increase in oxidation rate of the metal. Since, zirconia coating is well recognized for corrosion protection under high temperature oxidative environment, we have developed zirconia coating on 9Cr1Mo ferritic steel and their oxidation performance was evaluated in LiCl-NaCl and Na2SO4-K2SO4 salts deposit system in air atmosphere at 650?C and 850?C, respectively. Before coating development, zirconium based sol was synthesized using zirconium (IV) propoxide as a precursor. Oxidation test results indicated that the zirconia coated specimens shows more than two times higher corrosion resistance in LiCl-NaCl and three time higher corrosion resistance in Na2SO4-K2SO4 salt deposit, respectively.展开更多
The solidification characteristics and microstructure evolution in grey cast iron were investigated through Jmat-Pro simulations and quenching performed during directional solidification. The phase transition sequence...The solidification characteristics and microstructure evolution in grey cast iron were investigated through Jmat-Pro simulations and quenching performed during directional solidification. The phase transition sequence of grey cast iron was determined as L → L + γ→ L + γ + G →γ + G → P(α + Fe_3C) + α + G. The graphite can be formed in three ways: directly nucleated from liquid through the eutectic reaction(L →γ + G), independently precipitated from the oversaturated γ phase(γ→γ + G), and produced via the eutectoid transformation(γ→ G + α). The area fraction and length of graphite as well as the primary dendrite spacing decrease with increasing cooling rate. Type-A graphite is formed at a low cooling rate, whereas a high cooling rate results in the precipitation of type-D graphite. After analyzing the graphite precipitation in the as-cast and transition regions separately solidified with and without inoculation, we concluded that, induced by the inoculant addition, the location of graphite precipitation changes from mainly the γ interdendritic region to the entire γ matrix. It suggests that inoculation mainly acts on graphite precipitation in the γ matrix, not in the liquid or at the solid–liquid front.展开更多
文摘Fused salt accelerated hot corrosion is quite common in gas turbines, fossil fuelled devices, waste inclinators, pyrochemical systems, etc. Presence of fused salt on metal surface dissolves their existing oxide layer. This results in an increase in oxidation rate of the metal. Since, zirconia coating is well recognized for corrosion protection under high temperature oxidative environment, we have developed zirconia coating on 9Cr1Mo ferritic steel and their oxidation performance was evaluated in LiCl-NaCl and Na2SO4-K2SO4 salts deposit system in air atmosphere at 650?C and 850?C, respectively. Before coating development, zirconium based sol was synthesized using zirconium (IV) propoxide as a precursor. Oxidation test results indicated that the zirconia coated specimens shows more than two times higher corrosion resistance in LiCl-NaCl and three time higher corrosion resistance in Na2SO4-K2SO4 salt deposit, respectively.
基金The financial support provided by Ford Motor Company (University Research Program)
文摘The solidification characteristics and microstructure evolution in grey cast iron were investigated through Jmat-Pro simulations and quenching performed during directional solidification. The phase transition sequence of grey cast iron was determined as L → L + γ→ L + γ + G →γ + G → P(α + Fe_3C) + α + G. The graphite can be formed in three ways: directly nucleated from liquid through the eutectic reaction(L →γ + G), independently precipitated from the oversaturated γ phase(γ→γ + G), and produced via the eutectoid transformation(γ→ G + α). The area fraction and length of graphite as well as the primary dendrite spacing decrease with increasing cooling rate. Type-A graphite is formed at a low cooling rate, whereas a high cooling rate results in the precipitation of type-D graphite. After analyzing the graphite precipitation in the as-cast and transition regions separately solidified with and without inoculation, we concluded that, induced by the inoculant addition, the location of graphite precipitation changes from mainly the γ interdendritic region to the entire γ matrix. It suggests that inoculation mainly acts on graphite precipitation in the γ matrix, not in the liquid or at the solid–liquid front.