Nowadays,having an effective technique in preparing semi-solid slurries for rheocasting process seems to be an essential requirement.In this study,semi-solid slurry of A356 aluminum alloy was prepared by three-phase a...Nowadays,having an effective technique in preparing semi-solid slurries for rheocasting process seems to be an essential requirement.In this study,semi-solid slurry of A356 aluminum alloy was prepared by three-phase annular electromagnetic stirring(A-EMS)technique under different conditions.The effects of stirring current,pouring temperature and stirring time on microstructural evolution,mean particle size,shape factor and solid fraction were investigated.The rheocasting process was carried out by using a drop weight setup and to inject the prepared semi-solid slurry in optimal conditions into the step-die cavity.The filling behavior and mechanical properties of parts were studied.Microstructural evolution showed that the best semi-solid slurry which had fine spherical particles with the average size of~27μm and a shape factor of~0.8 was achieved at the stirring current of 70 A,melt pouring temperature of 670℃,and stirring time of 30 s.Under these conditions,the step-die cavity was completely filled at die preheating temperature of 470℃.The hardness increases by decreasing step thickness as well as die preheating temperature.Moreover,the tensile properties are improved at lower die preheating temperatures.The fracture surface,which consists of a complex topography,indicates a typical ductile fracture.展开更多
Estimation of the rock mass modulus of deformation(Em)is one of the most important design parameters in designing many structures in and on rock.This parameter can be obtained by in situ tests,empirical relations betw...Estimation of the rock mass modulus of deformation(Em)is one of the most important design parameters in designing many structures in and on rock.This parameter can be obtained by in situ tests,empirical relations between deformation modulus and rock mass classifcation,and estimating from laboratory tests results.In this paper,a back analysis calculation is performed to present an equation for estimation of the rock mass modulus of deformation using genetic programming(GP)and numerical modeling.A database of 40,960 datasets,including vertical stress(rz),horizontal to vertical stresses ratio(k),Poisson’s ratio(m),radius of circular tunnel(r)and wall displacement of circular tunnel on the horizontal diameter(d)for input parameters and modulus of deformation for output,was established.The selected parameters are easy to determine and rock mass modulus of deformation can be obtained from instrumentation data of any size circular galleries.The resulting RMSE of 0.86 and correlation coeffcient of97%of the proposed equation demonstrated the capability of the computer program(CP)generated by GP.展开更多
The nanocrystalline Fe-Ni-Cr coatings were electrodeposited by using the pulse current technique.The SEM results showed that the coatings had a mixed morphology of small nodules and fine cauliflower structures at low ...The nanocrystalline Fe-Ni-Cr coatings were electrodeposited by using the pulse current technique.The SEM results showed that the coatings had a mixed morphology of small nodules and fine cauliflower structures at low current densities.Also,the Cr content was increased at expense of Fe and Ni contents at high current densities.XRD patterns confirmed that the pulse current density had a positive effect on the grain refinement.The results of vibrating sample magnetometer(VSM)measurements demonstrated that by increasing the current density,the saturation magnetization was decreased and the coercivity was increased due to the enhancement of Cr content and the reduction of the grain size.The friction coefficient and wear rate values were decreased by increasing the pulse current density.Also,both the adhesive and abrasive wear mechanisms were observed on the worn surfaces.The abrasive grooves and the amount of wear debris were decreased by increasing the pulse current density.展开更多
A new non-isothermal method of kinetic analysis was employed to investigate the thermal decomposition kinetic modeling of the basic carbonate cobalt nanosheets（n-BCoC） synthesized from spent lithium-ion batteries（L...A new non-isothermal method of kinetic analysis was employed to investigate the thermal decomposition kinetic modeling of the basic carbonate cobalt nanosheets（n-BCoC） synthesized from spent lithium-ion batteries（LIBs）. Fraser–Suzuki function was applied to deconvoluting overlapping complex processes from the overall differential thermal curves obtained under the linear heating rate conditions, followed by the kinetic analysis of the discrete processes using a new kinetic analysis method. Results showed that the decomposition of n-BCo C in air occurred through two consecutive reactions in the 136-270 ℃ temperature intervals. Decomposition started by hydroxide component（Co（OH）2） decomposition until to 65% and simultaneously carbonate phase decarbonation began. The process was continued by CO2 evolution and finally carbonate cobalt nanosheets have been produced. The reaction mechanism of the whole process can be kinetically characterized by two successive reactions： a phase boundary contracting reaction followed by an Avrami-Erofeev equation. Mechanistic information obtained by the kinetic study was in good agreement with FT-IR（Fourier transform infrared spectroscopy） and SEM（scanning electron microscopy） results.展开更多
In this paper, recovery of silver from anode slime of Sarcheshmeh copper complex in lran and subsequent synthesis of silver nanoparticles from leaching solution is investigated. Sarcheshmeh anode slime is mainly consi...In this paper, recovery of silver from anode slime of Sarcheshmeh copper complex in lran and subsequent synthesis of silver nanoparticles from leaching solution is investigated. Sarcheshmeh anode slime is mainly consisted ofCu, Ag, Pb and Se. Amount of Ag in the considered anode slime was 5.4% （by weight）. The goal was to recover as much as possible Ag from anode slime at atmospheric pressure to synthesize Ag nanoparticles. Therefore, acid leaching was used for this purpose. The anode slime was leached with sulfuric and nitric acid from room to 90 ~C at different acid concentrations and the run which yielded the most recovery of Ag was selected for Ag nanoparticles synthesis. At this condition, Cu, Pb and Se are lea- ched as well as Ag. To separate Ag from leach solution HCI was added and silver was precipitated as AgCl which were then dissolved by ammonia solution. The Ag nanoparticles are synthesized from this solution by chemical reduction method by aid of sodium borohydride in the presence of PVP and PEG as stabilizers. The synthesized Ag nanoparticles showed a peak of 394 nm in UV-vis spectrum and TEM images showed a rather uniform Ag nanoparticles of 12 nm.展开更多
基金Central Applied Research Laboratory(CARL)Center of Materials ResearchDepartment of Materials Science and Metallurgy,Shahid Bahonar University of Kerman(SBUK)for support of this work。
文摘Nowadays,having an effective technique in preparing semi-solid slurries for rheocasting process seems to be an essential requirement.In this study,semi-solid slurry of A356 aluminum alloy was prepared by three-phase annular electromagnetic stirring(A-EMS)technique under different conditions.The effects of stirring current,pouring temperature and stirring time on microstructural evolution,mean particle size,shape factor and solid fraction were investigated.The rheocasting process was carried out by using a drop weight setup and to inject the prepared semi-solid slurry in optimal conditions into the step-die cavity.The filling behavior and mechanical properties of parts were studied.Microstructural evolution showed that the best semi-solid slurry which had fine spherical particles with the average size of~27μm and a shape factor of~0.8 was achieved at the stirring current of 70 A,melt pouring temperature of 670℃,and stirring time of 30 s.Under these conditions,the step-die cavity was completely filled at die preheating temperature of 470℃.The hardness increases by decreasing step thickness as well as die preheating temperature.Moreover,the tensile properties are improved at lower die preheating temperatures.The fracture surface,which consists of a complex topography,indicates a typical ductile fracture.
文摘Estimation of the rock mass modulus of deformation(Em)is one of the most important design parameters in designing many structures in and on rock.This parameter can be obtained by in situ tests,empirical relations between deformation modulus and rock mass classifcation,and estimating from laboratory tests results.In this paper,a back analysis calculation is performed to present an equation for estimation of the rock mass modulus of deformation using genetic programming(GP)and numerical modeling.A database of 40,960 datasets,including vertical stress(rz),horizontal to vertical stresses ratio(k),Poisson’s ratio(m),radius of circular tunnel(r)and wall displacement of circular tunnel on the horizontal diameter(d)for input parameters and modulus of deformation for output,was established.The selected parameters are easy to determine and rock mass modulus of deformation can be obtained from instrumentation data of any size circular galleries.The resulting RMSE of 0.86 and correlation coeffcient of97%of the proposed equation demonstrated the capability of the computer program(CP)generated by GP.
文摘The nanocrystalline Fe-Ni-Cr coatings were electrodeposited by using the pulse current technique.The SEM results showed that the coatings had a mixed morphology of small nodules and fine cauliflower structures at low current densities.Also,the Cr content was increased at expense of Fe and Ni contents at high current densities.XRD patterns confirmed that the pulse current density had a positive effect on the grain refinement.The results of vibrating sample magnetometer(VSM)measurements demonstrated that by increasing the current density,the saturation magnetization was decreased and the coercivity was increased due to the enhancement of Cr content and the reduction of the grain size.The friction coefficient and wear rate values were decreased by increasing the pulse current density.Also,both the adhesive and abrasive wear mechanisms were observed on the worn surfaces.The abrasive grooves and the amount of wear debris were decreased by increasing the pulse current density.
基金supported by the Iranian National Science Foundation (INSF)
文摘A new non-isothermal method of kinetic analysis was employed to investigate the thermal decomposition kinetic modeling of the basic carbonate cobalt nanosheets（n-BCoC） synthesized from spent lithium-ion batteries（LIBs）. Fraser–Suzuki function was applied to deconvoluting overlapping complex processes from the overall differential thermal curves obtained under the linear heating rate conditions, followed by the kinetic analysis of the discrete processes using a new kinetic analysis method. Results showed that the decomposition of n-BCo C in air occurred through two consecutive reactions in the 136-270 ℃ temperature intervals. Decomposition started by hydroxide component（Co（OH）2） decomposition until to 65% and simultaneously carbonate phase decarbonation began. The process was continued by CO2 evolution and finally carbonate cobalt nanosheets have been produced. The reaction mechanism of the whole process can be kinetically characterized by two successive reactions： a phase boundary contracting reaction followed by an Avrami-Erofeev equation. Mechanistic information obtained by the kinetic study was in good agreement with FT-IR（Fourier transform infrared spectroscopy） and SEM（scanning electron microscopy） results.
基金the International Center for Science, High Technology & Environmental Sciences for financial support of this work (No. 1.213)
文摘In this paper, recovery of silver from anode slime of Sarcheshmeh copper complex in lran and subsequent synthesis of silver nanoparticles from leaching solution is investigated. Sarcheshmeh anode slime is mainly consisted ofCu, Ag, Pb and Se. Amount of Ag in the considered anode slime was 5.4% （by weight）. The goal was to recover as much as possible Ag from anode slime at atmospheric pressure to synthesize Ag nanoparticles. Therefore, acid leaching was used for this purpose. The anode slime was leached with sulfuric and nitric acid from room to 90 ~C at different acid concentrations and the run which yielded the most recovery of Ag was selected for Ag nanoparticles synthesis. At this condition, Cu, Pb and Se are lea- ched as well as Ag. To separate Ag from leach solution HCI was added and silver was precipitated as AgCl which were then dissolved by ammonia solution. The Ag nanoparticles are synthesized from this solution by chemical reduction method by aid of sodium borohydride in the presence of PVP and PEG as stabilizers. The synthesized Ag nanoparticles showed a peak of 394 nm in UV-vis spectrum and TEM images showed a rather uniform Ag nanoparticles of 12 nm.